胶乳互穿网络聚合物（LIPN）的阻尼性能研究与应用进展

doi:10.16085/j.issn.1000-6613.2017-1390

摘要/Abstract

摘要： 介绍了胶乳互穿网络聚合物的微观结构形态、阻尼原理、合成过程和类别，讨论了其阻尼性能的影响因素，同时对胶乳互穿网络聚合物在不同领域的应用进行了总结，并对胶乳互穿网络聚合物的发展方向进行了展望。指出了胶乳互穿网络聚合物结构与阻尼性能的关系，在其合成过程中，其阻尼性能受到交联剂含量、网络配比、加料顺序、加料方式和填料的影响，其在阻尼涂料、皮革涂饰剂和涂料印花等领域有广泛的应用。同时也指出了目前关于胶乳互穿网络聚合物的研究遇到的瓶颈，未来的研究应从新的聚合工艺、新的表征方法和组成多样性寻求突破。

关键词: 互穿网络, 阻尼, 复合材料, 化学反应, 聚合物

Abstract: In this paper,the microstructure morphology,damping principle,synthesis and classification of latex interpenetrating polymer networks (LIPN)are introduced. The damping performance influencing factors,the application areas and the research outlook of latex interpenetrating polymer networks are also discussed. The relationship between the damping performance and the structure of LIPN is explained. In the synthesis process,the damping performance is influenced by the crosslinking agent content,ratio of networks,feeding sequence,feeding methods and the filler. LIPN is widely applied in damping coating,leather finishing agent and pigment printing binder. This paper also points out the bottlenecks of current research of latex interpenetrating polymer networks and the future research breakthroughs should focus on new polymerization process,diversity of composition and new characterization methods.

Key words: interpenetrating polymer networks, damping, composite, chemical reaction, polymer

中图分类号:

TQ323.8

阳红军, 王锋, 胡剑青, 涂伟萍. 胶乳互穿网络聚合物（LIPN）的阻尼性能研究与应用进展[J]. 化工进展, 2018, 37(05): 1843-1851.

YANG Hongjun, WANG Feng, HU Jianqing, TU Weiping. Research progress on the performance and application of latex interpenetrating polymer networks[J]. Chemical Industry and Engineering Progress, 2018, 37(05): 1843-1851.

参考文献

[1] 常冠军. 粘弹性阻尼材料[M]. 北京:国防工业出版社,2012:69. CHANG G J. Viscoelasticity damping materials[M]. Beijing:National Defense Industry Press,2012:69.
[2] 胥正安,陆建辉,严向军,等. 互穿网络型涂料印花粘合剂的应用[J]. 纺织导报,2008(8):95-97. XU Z A,LU J H,YANG X J,et al. Application of interpenetrating pigment printing binding agent[J]. China Textile Leader,2008(8):95-97.
[3] 刘鑫,刘宇,高闪,等. 水性阻尼涂料用LIPN的研究现状及发展[J].化学与粘合,2013(4):71-74. LIU X,LIU Y,GAO S,et al. Present status of research on LIPN for water-based damping coating[J]. Chemistry and Adhesion,2013(4):71-74.
[4] 王晓雯,何玉凤,王荣民,等. 功能性丙烯酸酯乳液的制备与应用研究进展[J]. 化工进展,2012,31(9):2011-2018. WANG X W,HE Y F,WANG R M,et al. Review on preparation and application of functional acrylate emulsion[J]. Chemical Industry and Engineering Progress,2012,31(9):2011-2018.
[5] 黄茂福. 互穿网络聚合物在印花工艺上的应用[J]. 印染助剂,2005,22(5):1-3. HUANG M F. Application of interpenetrating polymer networks in pigment printing[J]. Textile Auxiliaries,2005,22(5):1-3.
[6] 张留成,李秀错. 胶乳型互穿网络聚合物(LIPN)[J]. 工程塑料应用,1990(3):46-52. ZHANG L C,LI X C. Interpenetrating polymer networks[J]. Engineering Plastics Application,1990(3):46-52.
[7] 马丽红,孙志强,杨继敏,等. 胶乳互穿网络聚合物的研究进展[C]//杭州:"2006年拜耳杯"全国环境友好型高功能涂料涂装技术研讨会,2006. MA L H,SUN Z Q,YANG J M,et al. Research process on Latex interpenetrating polymer networks[C]//Hangzhou:"Bayer Cup in 2006" The Environmentally Friendly High Functional Coatings Coating Technology Seminar,2006.
[8] ZHANG J D,YANG M J,ZHU Y R,et al. Synthesis and characterization of crosslinkable latex with interpenetrating network structure based on polystyrene and polyacrylate[J]. Polymer International,2006,55(8):951-960.
[9] 晏欣,姚树人. PMMA/PBA乳胶IPN阻尼材料的研究[J]. 高分子材料科学与工程,1994,10(3):74-79. YAN X,YAO S R. Research on the damping properties of PMMA/PBA IPN[J]. Polymer Materials Science and Engineering,1994,10(3):74-79.
[10] YANG X B. Study on damping properties of the LIPN of MMA/EMA/EA[J]. New Chemical Materials,2002,30(12):21-23.
[11] ZHANG M Z,LI S C,LU X P,et al. Study on the performance of multicomponent acrylic LIPN[J]. Paint & Coatings Industry,1999(3):1-3.
[12] 晏欣,周赟,江盛玲,等. 室温界面自交联对PS/PBA乳胶IPN力学和阻尼性能的影响[J]. 高分子材料科学与工程,2010,26(6):60-63. YAN X,ZHOU B,JIANG S L,et al. Influence of ambient interfacial self-crosslinking on mechanical and damping properties of PS/PBA IPNs[J]. Polymer Materials Science & Engineering,2010,26(6):60-63.
[13] PENG W J,LI S C. Studies on damping behavior of PS/P(EA-nBA) LIPNs[J]. Journal of Applied Polymer Science,2010,58(6):967-971.
[14] TANG E,TIAN B,FU C. Apparent kinetic study of latex interpenetrating polymer networks P(ethyl acrylate)/P(styrene) and P(styrene)/P(ethyl acrylate) by two stage emulsion polymerization[J]. Colloids and Surfaces A:Physicochemical and Engineering Aspects,2009,333(1):7-11.
[15] 王志玲. 聚氨酯-丙烯酸酯LIPN结构的研究[J]. 皮革与化工,2002,19(5):4-7. WANG Z L. Study on LIPN structure of polyurethane-polyacrylate[J]. Leather Chemicals,2002,19(5):4-7
[16] 徐磊,单国荣. 聚氨酯/聚甲基丙烯酸甲酯互穿网络的阻尼性能及相态[J]. 化工学报,2013,64(9):3467-3473. XU L,SHAN G R. Damping performance and morphology of polyurethane and poly(methyl methacrylate) simultaneously interpenetrating polymer networks[J]. CIESC Journal,2013,64(9):3467-3473.
[17] 张静丽,吴冬梅,张勤勤,等. PU/BA-HEMA互穿网络型聚合物的合成及性能[J]. 化工进展,2009,28(9):1609-1612. ZHANG J L,WU D M,ZHANG Q Q,et al. Preparation and properties of interpenetrating polymer networks from PU/BA-HEMA[J]. Chemical Industry and Engineering Progress,2009,28(9):1609-1612.
[18] 刘玉涛,李欣闻,孙树林,等. 丙烯酸酯LIPN聚合物阻尼性能研究[J]. 弹性体,2010,20(1):38-41. LIU Y T,LI X W,SUN S L,et al. Research on the damping properties of polyacrylate LIPN[J]. China Elastomerics,2010,20(1):38-41.
[19] ZAHEDI F,AMRAEI I A,FATHIZADE M A. Investigation of dynamic-mechanical properties of multilayer latex IPNs(MLIPNs)with core/shell morphology:synthesis and characterization[J]. Polymer,2016,83:162-171.
[20] 曾威,李树材. 胶乳型互穿聚合物网络(LIPN)阻尼材料[J]. 高分子通报,2001(1):68-73. ZENG W,LI S C. Latex interpenetrating polymer networks(LIPN)damping materials[J]. Polymer Bulletin,2001(1):68-73.
[21] CHEN P,WANG J,LI Y. Preparation of aqueous PS/PA LIPN chipping-resistant coating for automobile primer[J]. Journal of Functional Materials,2013,2:285-288.
[22] 张学敏. 互穿聚合物网络在汽车涂料中的应用[J]. 涂料工业,1994(5):39-41. ZHANG X M. Application of interpenetrating polymer network in automobile coating[J]. Paint & Coatings Industry,1994(5):39-41.
[23] 蒋巍,佀庆波. 汽车用水性阻尼涂料的制备及性能研究[J]. 化学世界,2014,55(4):208-210. JIANG W,SI Q B. Preparation and performance testing of waterborne damping coating[J]. Chemical World,2014,55(4):208-210.
[24] 胡昌悌. 一种船舶专用高分子阻尼涂料:104263185A[P]. 2015-01-07. HU C T. A special polymer damping coating for the ship:104263185A[P]. 2015-01-07.
[25] 俞成丙,杨丹,殷雯青,等. 一种水性重质船用隔声阻尼涂料及其制备方法:103897509A[P]. 2014-07-02. YU C B,YANG D,YIN W Q,et al. A waterborne heavy marine acoustic damping coatings and their preparation methods:103897509A[P]. 2014-07-02.
[26] 孙巍,孙云,毛亮. 新型高性能阻尼涂料的开发及应用研究[J]. 黑龙江科学,2010(2):55-57. SUN W,SUN Y,MAO L. Development and application of new high performance damping coatings[J]. Heilongjiang Science,2010(2):55-57.
[27] 陈云传,郑耀卿,胡红梅,等. 高铁车辆阻尼用聚氨酯-聚丙烯酸酯互穿聚合物网络的合成及应用研究[J]. 涂料工业,2013,43(7):19-23. CHEN Y C,ZHEN Y Q,HU H M,et al. High-speed rail vehicle damping with polyurethane-polyacrylic ester synthesis and application of interpenetrating polymer network research[J]. Paint & Coatings Industry,2013,43(7):19-23.
[28] 郝博. 铁道车辆用水性聚氨酯-丙烯酸酯IPN阻尼涂料的研究[D]. 长春:吉林大学,2002. HAO B. Research on waterborne PU/PA IPN damping coatings for Railway vehicle[D]. Changchun:Jilin University,2002.
[29] 孙天宝,谢金彪. 用于喷涂内层的高铁车辆阻尼涂料及其制备方法:106433352A[P]. 2017-07-22. SUN T B,XIE J B. The damping coating and preparation method of high-iron vehicle used for spraying the inner layer:106433352A[P]. 2017-07-22.
[30] 李文安. PSt/PBA/PMMA LIPN涂料的制备[J]. 应用化工,2007,36(6):625-627. LI W A. Preparation of PSt/PBA/PMMA[J]. Applied Chemical Industry,2007,36(6):625-627.
[31] LV X,HUANG Z,HUANG C,et al. Damping properties and the morphology analysis of the polyurethane/epoxy continuous gradient IPN materials[J]. Composites Part B:Engineering,2016,88:139-149.
[32] 祝阳,吕满庚,孔中平,等. 丙烯酸酯改性水性聚氨酯皮革涂饰剂研究进展[J]. 聚氨酯工业,2008,23(1):9-12. ZHU Yang,LV Mangeng,KONG Zhangping,et al. The advance of acrylic modified aqueous polyurethane dispersion as leather finishing agent[J]. Polyureihane Industry,2008,23(1):9-12.
[33] 耿耀宗,肖继君,唐二军. 一种新型聚氨酯/聚丙烯酸酯胶乳互穿网络聚合物乳液材料及其合成工艺:1597739[P]. 2005-03-23. GENG Y Z,XIAO J J,TANG E J. A new type of polyurethane/polyacrylate latex interpenetrating network polymer emulsion material and its synthesis process:1597739[P]. 2005-03-23.
[34] 郭银海. 聚氨酯(PU)/聚丙烯酸酯(PA)的合成及在皮革涂饰剂领域的应用研究[J]. 河南化工,2010(6):58. GUO Y H. Polyurethane(PU)/polyacrylate(PA) in the synthesis and application research in the field of leather finishing agent[J]. Henan Chmical Industry,2010(6):58
[35] 吴育彪,吴天昊,关正祥,等. 胶乳型互穿聚合物网络丙烯酸酯涂饰剂的制备及性能研究[J]. 皮革科学与工程,2016,26(6):11-16. WU Y B,WU T H,GUAN Z X,et,al. Type rubber latex interpenetrating polymer network study the preparation and properties of acrylic resin finishing agent[J]. Leather Science and Engineering,2016,26(6):11-16.
[36] 顾东民,吴春明,蔡明训. 新型环保印花粘合剂的合成及IPN结构在涂料印花中初探[J]. 印染助剂,2003,20(3):42-44. GU D M,WU C M,CAI M X. The synthesis of new environmental protection printing adhesive used in pigment printing and IPN structure[J]. Textile Auxiliaries,2003,20(3):42-44.
[37] 钟欣. 互穿网络型涂料印花粘合剂的研制及应用[D]. 上海:东华大学,2016. ZHONG X. Interpenetrating network development and application of pigment printing adhesive[D]. Shanghai:Donghua University,2016.
[38] 刘锦,赵振河,施建刚. 互穿网络结构WPUA复合乳液在织物整理和涂料印花中的应用[J]. 粘接,2014(12):46-50. LIU J,ZHAO Z H,SHI J G. Interpenetrating network structure in textile finishing WPUA hybrid emulsion and the application of pigment printing[J]. Adhesion,2014(12):46-50.
[39] 刘顺,叶荣森. 水性木器漆用纳米聚丙烯酸酯乳液及其制备方法:101638451A[P]. 2010-02-03. LIU S,YE R S,Waterborne wood coatings with nano polyacrylate emulsion and its preparation method:101638451A[P]. 2010-02-03.
[40] BHATTACHARYYA R,NANDI S. Modification of the properties of PVC by full IPN formation with polybutyl acrylate[J]. International Journal of Advanced Research in Science,Engineering and Technology,2015,2(1):387-391.
[41] 王留方,赵宝华,朱亚君,等. 石油管道及设备用水性防腐涂料的研究[J]. 涂料工业,2008,38(7):17-21. WANG L F,ZHAO B H,ZHU Y J,et. al. Research on oil pipeline and equipment of waterborne anticorrosion coating[J]. Paint & Coatings Industry,2008,38(7):17-21.
[42] CHEN S,CHEN L. Structure and properties of polyurethane/polyacrylate latex interpenetrating networks hybrid emulsions[J]. Colloid & Polymer Science,2003,282(1):14-20.
[43] WANG H,ZHOU H,CHEN Y,et al. Synthesis of fluorinated gradient copolymers by RAFT emulsifier-free emulsion polymerization and their compatibilization in copolymer blends[J]. Colloid & Polymer Science,2014,292(11):2803.
[44] 全凤玉,夏延致,纪全,等. 聚乙烯醇/二氧化硅互穿网络膜的研究[J]. 精细化工,2008,25(10):937-939. QUAN F Y,XIA Y Z,JI Q,et al. Research on poly(vinyl alcohol)/silica membrane interpenetrating network[J]. Fine Chemicals,2008,25(10):937-939.