One-pot synthesis of polyether amine by supercritical method

YAN Jixiao,JIN Yifeng,JIA Gengmei   

  1. Zhejiang Huangma Technology Co.,Ltd.,Shangyu 312363,Zhejiang,China
  • Online:2013-07-05 Published:2013-07-05

摘要: 采用超临界流体技术,一步反应合成了聚醚胺,旨在解决羟基胺化的技术瓶颈。主要研究了催化剂用量、物料配比、反应时间、反应温度、临氢压力对转化率的影响。确立了较佳反应条件为:催化剂用量7.5%,液氨对聚醚质量比1.5∶1,反应时间7.5 h,反应温度160 ℃,临氢压力1.0 MPa。最后,利用了核磁共振波谱技术对产品结构进行了表征。此工艺路线的成功开发,将为替代聚醚胺传统釜式间歇生产工艺,实现连续生产提供强有力的依据。

关键词: 聚醚胺, 超临界, 胺化

Abstract: In order to overcome technical bottleneck of hydroamination,the influences of catalyst dosage,m(NH3)/m(polyether),reaction time,temperature and pressure on the conversion of one-pot synthesis of polyether amine by the supercritical method were investigated. The results showed the suitable reaction conditions:catalyst dosage 7.5%,m(NH3)/m(polyether)=1.5,7.5 h,160 ℃, 1.0 MPa. The products was characterized with NMR. The development of this technology will provide strong basis for continuous production instead of traditional batch production.

Key words: polyether amine, supercritical, amination