光引发聚合法制备光致失黏胶

doi:10.16085/j.issn.1000-6613.2017.06.038

摘要/Abstract

摘要： 利用光引发聚合法取代传统热聚合合成一种能够制备光致失黏胶的聚丙烯酸酯类共聚物，称为基胶。将基胶与适量的光引发剂及多光敏官能团低聚物复配，得到目标产物。在UV光照前，展现了很好的粘接性能，180°剥离强度可以达到24N/25mm；在20mW/cm²的365nm波长UV光照下照射20s后，光敏树脂反应产生交联，与直链分子形成互穿网络结构，导致180°剥离强度降至几乎为零，从而展示了很好的失黏性能，便于拆离，而不损坏元器件。进一步探究了基胶成分、多光敏官能团低聚物的种类、用量等多个参数对光致失黏胶综合性能的影响。最后通过扫描电镜，对其失黏机理进行讨论，有两个关键因素导致光照后胶黏剂失黏：低聚物交联过程，引起体积的收缩，与基材粘接面积减小；互穿网络结构造成基胶失去橡胶弹性，表现塑料特性。

关键词: 光引发聚合, 失黏胶, 多官能团, 交联

Abstract: A kind of acrylate copolymer called matrical cohesive is synthesized by photopolymerization method to replace the traditional thermal polymerization method. The target-product prepared by the matrical cohesive is compounded with certain amount of initiator and multi-photosentitive-functional groups oligomer or monomer,which exhibits excellent adhesion property under UV irradiation. The 180° peel strength can reach 24N/25mm. However, when exposed to UV light of 20mW/cm² and 365nm for 20s,the multi-photosensitive oligomer can react with each other and form cross-linked structure. Linear polymer penetrates into the cross-linked structure and forms interpenetrating network structure,which decreases the 180°peel strength down to zero. So it is very convenient to detach and have no harm to the jointed objects. Furthermore,the effects of copolymer composition,type of photosensitive oligomer or monomer,and the number of functional groups on the dismantlble property have been investigated. The mechanism is discussed through SEM. The cross-linked structure leads to the volume contraction and reduces the effective bonding area,while the interpenetrating network makes it lose rubber elasticity and exhibit plastic properties.

Key words: photo-polymerization, dismantlble adhesive, multi-functional groups, crosslinking

中图分类号:

TQ433.4⁺3

习峥辉, 解一军. 光引发聚合法制备光致失黏胶[J]. 化工进展, 2017, 36(06): 2236-2241.

XI Zhenghui, XIE Yijun. Preparation of ultra violet dismantlble adhesion by photoinitiation[J]. Chemical Industry and Engineering Progress, 2017, 36(06): 2236-2241.

参考文献

[1] RYU C M,PANG B,KIM H I,et al. Wettability and adhesion characteristics of photo-crosslinkable adhesives for thin silicon wafer[J]. International Journal of Adhesion & Adhesives,2013,40:197-201.
[2] LEE S W,LEE T H,PARK J W,et al. The effect of laser irradiation on peel strength of temporary adhesives for wafer bonding[J]. International Journal of Adhesion & Adhesives,2015,57:9-12.
[3] ISHIKAWA H,SETO K,SHIMOTUMA S,et al. Bond strength and disbonding behavior of elastomer and emulsion-type dismantlable adhesives used for building materials[J]. International Journal of Adhesion & Adhesives,2005,25(3):193-199.
[4] XIE T,XIAO X. Self-peeling reversible dry adhesive system[J]. Chemistry of Materials,2008,20(9):2866-2868.
[5] LUO X,LAUBER K E,MATHER P T. A thermally responsive,rigid,reversible adhesive[J]. Polymer,2010,51(5):1169-1175.
[6] TRENOR S R,LONG T E,LOVE B J. Development of a light-deactivatable PSA via photodimerization[J]. Journal of Adhesion,2005,81:213-229.
[7] KOBAYASHI M,TERADA M,TAKAHARA A. Reversible adhesive-free nanoscale adhesion utilizing oppositely charged polyelectrolyte brushes[J]. Soft Matter,2011,7(12):5717-5722.
[8] SASAKI T,HASHIMOTO S,NOGAMI N,et al. Dismantlable thermosetting adhesives composed of a cross-linkable poly(olefin sulfone) with a photobase generator[J]. ACS Applied Materials & Interfaces,2016,8:5580-5585.
[9] INUI T,SATO E,MATSUMOTO A. Pressure-sensitive adhesion system using acrylate block copolymers in response to photoirradiation,postbaking as the dual external stimuli for on-demand dismantling[J]. ACS Applied Materials & Interfaces,2012,4:2124-2132.
[10] SATO E,TAMURA H,MATSUMOTO A. Cohesive force change induced by polyperoxide degradation for application to dismantlable adhesion[J]. ACS Applied Materials & Interfaces,2010,2(9):2594-2601.
[11] KIM Y B,PARK S C,KIN H K,et al. Dual-curable acrylic pressure-sensitive adhesives based on UV,thermal processes[J]. Macromolecular Research,2008,16(2):128-133.
[12] ISHIKAWA H,SETO K,SHIMOTUMA S,et al. Bond strength and disbonding behavior of elastomer,emulsion-type dismantlable adhesives used for building materials[J]. International Journal of Adhesion & Adhesives,2005,25(3):193-199.
[13] NISHIYAMA Y,UTO N,SATO C,et al. Dismantlement behavior and strength of dismantlable adhesive including thermally expansive particles[J]. International Journal of Adhesion & Adhesives,2003,23(5):377-382.
[14] LEE S W,LEE T H,PARK J W,et al. The effect of laser irradiation on peel strength of temporary adhesives for wafer bonding[J]. International Journal of Adhesion & Adhesives,2014,57:9-12.
[15] HERMANOWSKI J. Thin wafer handling-study oftemporary wafer bonding materials and processes[C]//Proceedings of IEEE International Conference on 3D System Integration,2009:1-5.
[16] ZOSCHKE K,FISCHER T,TOPPER M,et al. Polyimide based temporary wafer bonding technology for high temperature compliant TSV backside processing and thin device handling[C]//Proceedings of IEEE 62nd Electronic Components and Technology Conference,2012:1054-1061.
[17] ZUSSMAN M P,MILASINCIC C,PARDIN A,et al. Using permanent and temporary polyimide adhesives in 3D-TSV processing to avoid thin wafer handling[J]. Journal of Microelectronics & Electronic Packaging,2010,7(4):214-219.
[18] GATTY H K,MIKLAUS F,STEMME G,et al. Temporary wafer bonding and debonding by an electrochemically active polymer adhesive for 3D integration[C]//Proceedings of IEEE 26th International Conference on Micro Electro Mechanical Systems,2013:381-384.
[19] WAMG Y Z,LI L,DU F S,et al. A facile approach to catechol containing UV dismantlable adhesives[J]. Polymer,2015,68:270-278.
[20] 王艳,解一军. 紫外光引发丙烯酸酯类单体的聚合反应[J]. 高分子材料科学与工程,2014(5):29-33. WANG Y,XIE Y J. Ultraviolet-irradiated polymerization process of acrylate monomers[J]. Polymer Materials Science and Engineering,2014(5):29-33.
[21] 华幼卿. 高分子物理[M]. 4版. 北京:化学工业出版社,2013. HUA Y Q. Polymer physics[M]. 4th ed. Beijing:Chemical Industry Press,2013.
[22] 张绪刚,李坚辉,张斌,等. 高强度耐热丙烯酸酯压敏胶研究Ⅱ——结构与性能研究[J]. 化学与粘合,2012,34(6):19-21. ZHANG X G,LEE J H,ZHANG B,et al. Study on polyacrylate pressure sensitive adhesive with high strength and heat resistant propertiesⅡ—Study on structure and properties[J] Chemistry and Adhesion,2012,34(6):19-21.
[23] 王丽娜. 高性能水性丙烯酸酯压敏胶的研究[D]. 广州: 华南理工大学,2012. WANG L N. High-performance waterborne acrylic pressure-sensitive adhesive[D]. Guangzhou:South China University of Technology,2012.
[24] EBE K,SENO H,HORIGOME K. UV curable pressure-sensitive adhesives for fabricating semiconductors. I. Development of easily peelable dicing tapes[J]. Journal of Applied Polymer Science,2003,90(2):436-441.