超双疏表面的构筑及研究进展

doi:10.16085/j.issn.1000-6613.2015.02.022

摘要/Abstract

摘要： 超双疏表面拒水又拒油的特性指导着油水共存环境下材料表面的设计。本文概述了其构筑方法包括溶胶-凝胶法、自组装法、相分离法等自下而上的方法,以及刻蚀法、纳米压印法等自上而下的方法,并指出后者相比前者更易于构筑有利于形成超双疏表面的倒悬结构,但往往存在制备过程繁琐的问题。此外,文中简述了超双疏特性主要用于构建油污环境下的自清洁表面,提高表面抗黏附能力,实现油水环境下的减阻作用等,并提出可进一步探索该特性在微流控管道设计领域的应用。最后展望了该领域未来的研究重点是探索简易的制备方法来构筑超双疏表面,在确保良好超双疏特性的前提下提高其耐久性,以满足在实际环境中的应用。

关键词: 超双疏, 表面, 加工制造, 纳米结构, 微尺度

Abstract: Superamphiphobic surface with water and oil repellent properties guides the design of surface under oil and/or water environment. In this review,we focus on the fabrication and application of superamphiphobic surface. Primarily,we highlight the bottom-up methods like sol-gel method,self-assembly and phase separation,and the top-down methods like etching process and nanoimprint lithography technology for the fabrication of superamphiphobic surface. The top-down methods are more efficient to fabricate an overhang structure which makes the superamphiphobic property stable,while the processes tend to be complex. Next,we propose hat these unique surfaces are promising in self-cleaning,anti-adhesion,anti-corrosion and drag reduction under oil and/or water environment and the application to microfluidic device should be further explored. Additionally,long durability of superamphiphobic surface in practical application is important. Finally,we prospect that research emphasis of superamphiphobic surface is to prepare superamphiphobic surface with enhanced durability to fulfill practical applications by an easier method.

Key words: superamphiphobicity, surface, fabrication, nanostructure, microscale

中图分类号:

TB381

辛忠, 张雯斐. 超双疏表面的构筑及研究进展[J]. 化工进展, 2015, 34(02): 447-455,478.

XIN Zhong, ZHANG Wenfei. Research progress of fabrication and application of superamphiphobic surface[J]. Chemical Industry and Engineering Progree, 2015, 34(02): 447-455,478.

参考文献

[1] Kamegawa T,Shimizu Y,Yamashita H. Superhydrophobic surfaces with photocatalytic self-cleaning properties by nanocomposite coating of TiO₂ and polytetrafluoroethylene[J]. Adv. Mater.,2012,24(27):3697-3700.
[2] Deng X,Schellenberger F,Papadopoulos P,et al. Liquid drops impacting superamphiphobic coatings[J]. Langmuir,2013,29(25):7847-7856.
[3] Xue Z,Liu M,Jiang L. Recent developments in polymeric superoleophobic surfaces[J]. Journal of Polymer Science Part B:Polymer Physics,2012,50(17):1209-1224.
[4] Sheen Y C,Huang Y C,Liao C S,et al. New approach to fabricate an extremely super-amphiphobic surface based on fluorinated silica nanoparticles[J]. Journal of Polymer Science Part B:Polymer Physics,2008,46(18):1984-1990.
[5] Butt H J,Semprebon C,Papadopoulos P,et al. Design principles for superamphiphobic surfaces[J]. Soft Matter,2013,9(2):418-428.
[6] Neinhuis C,Barthlott W. Characterization and distribution of water-repellent,self-cleaning plant surfaces[J]. Annals of Botany,1997,79:667-677.
[7] Zhang L,Wu J,Wang Y,et al. Combination of bioinspiration:A general route to superhydrophobic particles[J]. J. Am. Chem. Soc.,2012,134(24):9879-9881.
[8] Hak Jong Choi,Choo Soyoung,Shin Ju Hyeon,et al. Fabrication of superhydrophobic and oleophobic surfaces with overhang structure by reverse nanoimprint lithography[J]. J. Phys. Chem. C,2013,117(46):24354-24359.
[9] 曹国忠,王颖. 纳米结构和纳米材料:合成、性能及应用[M]. 第2版. 北京:北京高等教育出版社,2012:6-7.
[10] He Z,Ma M,Lan X,et al. Fabrication of a transparent superamphiphobic coating with improved stability[J]. Soft Matter,2011,7(14):6435-6443.
[11] Hayase G,Kanamori K,Hasegawa G,et al. A superamphiphobic macroporous silicone monolith with marshmallow-like flexibility[J]. Angew. Chem. Int. Ed.,2013,52:10788-10791.
[12] Abadi S R H,Sebzari M R,Hemati M,et al. Ceramic membrane performance in microfiltration of oily wastewater[J]. Desalination,2011,265(1-3):222-228.
[13] 云南银峰新材料有限公司. 一种含氟碳链纳米超双疏涂料的制备方法:中国,103450727A[P]. 2013-12-18.
[14] Xu X,Zhang Z,Guo F,et al. Superamphiphobic self-assembled monolayer of thiol on the structured Zn surface[J]. Colloids and Surfaces A:Physicochemical and Engineering Aspects,2012,396:90-95.
[15] Xie Qiongdan,Xu Jian,Lin Feng,et al. Facile creation of a super-amphiphobic coating surface with bionic micros ucture[J]. Adv. Mater.,2004,16(4):302-305.
[16] Pereira C,Alves C,Monteiro A,et al. Designing novel hybrid materials by one-pot co-condensation:From hydrophobic mesoporous silica nanoparticles to superamphiphobic cotton textiles[J]. ACS Appl. Mater. Interfaces,2011,3(7):2289-2299.
[17] Wang H,Xue Y,Lin T. One-step vapour-phase formation of patternable,electrically conductive,superamphiphobic coatings on fibrous materials[J]. Soft Matter,2011,7(18):8158-5161.
[18] Zhang G,Lin S,Wyman I,et al. Robust superamphiphobic coatings based on silica particles bearing bifunctional random copolymers[J]. ACS Appl. Mater. Interfaces,2013,5(24):13466-13477.
[19] Xiong D,Liu G,Hong L,et al. Superamphiphobic diblock copolymer coatings[J]. Chemistry of Materials,2011,23(19):4357-4366.
[20] Yoshida E. Preparation of micro-and nanospheres with superamphiphobic surfaces by dispersion polymerization[J]. Colloid and Polymer Science,2011,290(6):525-530.
[21] Choi G R,Park J,Ha J W,et al. Superamphiphobic web of PTFEMA fibers via simple electrospinning without functionalization[J]. Macromolecular Materials and Engineering,2010,295(11):995-1002.
[22] Ganesh V A,Dinachali S S,Nair A S,et al. Robust superamphiphobic film from electrospun TiO₂ nanostructures[J]. ACS Appl. Mater. Interfaces,2013,5(5):1527-1532.
[23] Bai H,Li C,Shi G. Electrochemical fabrication of superhydrophobic surfaces on metal and semiconductor substrates[J]. Journal of Adhesion Science and Technology,2008,22(15):1819-1839.
[24] Xu L,Chen W,Mulchandani A,et al. Reversible conversion of conducting polymer films from superhydrophobic to superhydrophilic[J]. Angew. Chem. Int. Ed.,2005,44(37):6009-6012.
[25] 中国科学院兰州化学物理研究所. 一种超疏水超双疏表面制备技术:中国,101748461A[P]. 2010-06-23.
[26] 中国科学院化学研究所. 用于金属防腐和油污自清洁功效的超双疏表面的制备方法:中国,101492829[P]. 2009-07-29.
[27] 哈尔滨工业大学. 铝及其合金超双疏表面制备方法:中国,103290418A[P]. 2013-09-11.
[28] Barthwal S,Kim Y S,Lim S H. Fabrication of amphiphobic surface by using titanium anodization for large-area three-dimensional substrates[J]. J. Colloid Interface Sci.,2013,400:123-129.
[29] Wang C F,Chiou S F,Ko F H,et al. Fabrication of biomimetic super-amphiphobic surfaces through plasma modification of benzoxazine films[J]. Macromolecular Rapid Communications,2006,27(5):333-337.
[30] Ramasamy Thangavelu Rajendra Kumar,Klaus Bo Mogensen,Peter Bøggild. Simple approach to superamphiphobic overhanging silicon nanostructures[J]. J. Phys. Chem. C.,2010,114:2936-2940.
[31] Li L,Breedveld V,Hess D W. Design and fabrication of superamphiphobic paper surfaces[J]. ACS Appl. Mater. Interfaces,2013,5(11):5381-5386.
[32] Chou S Y. Imprint of sub-25nm vias and trenches in polymers[J]. Appl. Phys. Lett.,1995,67:3114-3116.
[33] 中南林业科技大学. 一种超双疏自清洁表面精细纳米结构的人工种植方法:中国,103143493A[P]. 2013-02-26.
[34] Deng X,Mammen L,Butt H J,et al. Candle soot as a template for a transparent robust superamphiphobic coating[J]. Science,2012,335(6064):67-70.
[35] Ensikat H J,Ditsche Kuru P,Neinhuis C,et al. Superhydrophobicity in perfection:the outstanding properties of the lotus leaf[J]. Beilstein J. Nanotechnol.,2011,2:152-161.
[36] 冯河. 超双疏纳米界面材料在厕具上的应用:中国,1469021[P]. 2004-01-21.
[37] 朱丽丽,陈银艳,张琳,等. 超双疏自清洁变色织物[J]. 科技资讯,2012,31:60.
[38] Lee S G,Ham D S,Lee D Y,et al. Transparent superhydrophobic/translucent superamphiphobic coatings based on silica-fluoropolymer hybrid nanoparticles[J]. Langmuir,2013,29:15051-15057.
[39] Saifaldeen Z S,Khedir K R,Cansizoglu M F,et al. Superamphiphobic aluminum alloy surfaces with micro and nanoscale hierarchical roughness produced by a simple and environmentally friendly technique[J]. Journal of Materials Science,2013,49(4):1839-1853.
[40] 周继根. 超双疏表面的制备及其润湿性研究[D]. 山东:青岛理工大学,2010.
[41] Cao L,Jones A K,Sikka V K,et al. Anti-icing superhydrophobic coatings[J]. Langmuir,2009,25(21):12444-12448.
[42] 赵坤,杨保平,张俊彦. 铝合金基体超疏水表面的制备及防冰霜性能研究[J]. 功能材料,2010,41(s1):80-83.
[43] Bird J C,Dhiman R,Kwon H M,et al. Reducing the contact time of a bouncing drop[J]. Nature,2013,503(7476):385-388.
[44] Zhou H,Wang H,Niu H,et al. Robust,Self-healing superamphiphobic fabrics prepared by two-step coating of fluoro-containing polymer,fluoroalkyl silane,and modified silica nanoparticles[J]. Advanced Functional Materials,2013,23(13):1664-1670.
[45] Zhou H,Wang H,Niu H,et al. Superphobicity/philicity janus fabrics with switchable,spontaneous,directional transport ability to water and oil fluids[J]. Sci. Rep.,2013,3:2960-2964.
[46] Bardaweel H K,Zamuruyev K,Delplanque J P,et al. Wettability-gradient-driven micropump for transporting discrete liquid drops[J]. Journal of Micromechanics and Microengineering,2013,23(3):035036.
[47] Su B,Li M,Lu Q. Toward understanding whether superhydrophobic surfaces can really decrease fluidic friction drag[J]. Langmuir,2010,26(8):6048-6052.
[48] Liu C. Rapid fabrication of microfluidic chip with three-dimensional structures using natural lotus leaf template[J]. Microfluidics and Nanofluidics,2010,9(4-5):923-931.