纳米有序多孔阳极氧化铝制备方法的研究进展

doi:10.16085/j.issn.1000-6613.2015.12.021

摘要/Abstract

摘要： 多孔阳极氧化铝(PAA)模板以六角形元胞紧密排列,孔径大小可调,且化学稳定性好,近年来在催化、传感、过滤和仿生等领域受到了越来越多的关注。PAA模板的制备一直以来都是研究的热点,因为模板的结构和性质直接影响其应用的效果。本文在简要介绍了自组织有序多孔阳极氧化铝的特点及影响因素的基础上,较为全面地综述了制备自组织PAA模板不同方法的研究进展,包括温和阳极氧化法、强烈阳极氧化法、脉冲式阳极氧化法和周期性阳极氧化法。具体分析了不同阳极氧化方法的特点以及各自得到的氧化铝模板不同的特点和应用范围,说明了氧化电压、氧化温度和电解液种类在制备PAA模板时对其孔洞尺寸的重要作用,最后对阳极氧化铝膜的发展前景进行了展望。

关键词: 纳米阳极氧化铝, 结构特点, 制备方法

Abstract: Porous anodic aluminum (PAA) oxide has attracted more and more attention in the fields of catalysis,sensing,filtering and bionic due to their excellent chemical stabilities,hexagonal channel array architecture and controllable pore size. The structure and quality of PAA templates directly affect the results of applications,so the preparation of PAA template has always been a hot research focus. After a brief introduction to the features of self-ordered PAA,this work presents a comprehensive review on the research progress of preparation methods for PAA,including mild anodization method,hard anodization method,plus anodization method and cyclic anodization method. The features of different methods and corresponding PAA templates are analyzed. The importance of anodizing potential,anodizing temperature and type of electrolyte which determine the pore modulation of PAA are demonstrated. Finally,the development prospects of PAA membranes are proposed.

Key words: nanoporous anodic alumina, structure features, preparation methods

中图分类号:

TQ150.1

徐艳芳, 刘皓, 李晓久. 纳米有序多孔阳极氧化铝制备方法的研究进展[J]. 化工进展, 2015, 34(12): 4265-4271.

XU Yanfang, LIU Hao, LI Xiaojiu. Research progress of ordered nanoporous anodic alumina fabrication methods[J]. Chemical Industry and Engineering Progree, 2015, 34(12): 4265-4271.

参考文献

[1] Santos A,Vojkuvka L,Ferré-Borrull J,et al. Cobalt and nickel nanopillars on aluminium substrates by direct current electrodeposition process[J]. Nanoscale Research Letters,2009,4(9):1021-1028.
[2] Sulka G D,Brzzóka A,Zaraska L,et al. Through-hole membranes of nanoporous alumina formed by anodizing in oxalic acid and their applications in fabrication of nanowire arrays[J]. Electrochim Acta,2010,55(14):4368-4376.
[3] Chu S Z,Inoue S,Wada K,et al. Self-organized nanoporous anodic titania films and ordered titania nanodots/nanorods on glass[J]. Advanced Functional Materials,2005,15(8):1343-1349.
[4] Dotzauer D M,Bhattacharjee S,Wen Y,et al. Nanoparticle-containing membranes for the catalytic reduction of nitroaromatic compounds[J]. Langmuir,2009,25(3):1865-1871.
[5] Santos A,Kumeria T,Losic D. Nanoporous anodic alumina:A versatile platform for optical biosensors[J]. Materials,2014,7(6):4297-4320.
[6] Wang M L,Meng G W,Huang Q,et al. Fluorescence detection of trace PCB101 based on PITC immobilized on porous AAO membrane[J]. Analyst,2011,136(2):278-281.
[7] Thormann A,Teuscher N,Pfannmöller M,et al. Nanoporous aluminum oxide membranes for filtration and biofunctionalization[J]. Small,2007,3(6):1032-1040.
[8] Santos A,Ferré-Borrull J,Pallarès J,et al. Hierarchical nanoporous anodic alumina templates by asymmetric two-step anodization[J]. Phys. Status Solidi A,2011,208(3):668-674.
[9] Rahman M M,Marsal L F,Pallarès J,et al. Tuning the photonic stop bands of nanoporous anodic alumina-based distributed bragg reflectors by pore widening[J]. ACS Appl. Mater. Interfaces,2013,5:13375-13381.
[10] Santos A,Vojkuvka L,Alba M,et al. Understanding and morphology control of pore modulations in nanoporous anodic alumina by discontinuous anodization[J]. Phys. Status Solidi A,2012,209(10):2045-2048.
[11] Li J,Li C,Chen C,et al. Facile method for modulating the profiles and periods of self-ordered three-dimensional alumina taper-nanopores[J]. ACS Appl. Mater. Interfaces,2012,4(10):5678-5683.
[12] Santos A,Kumeria T,Wang Y,et al. In situ monitored engineering of inverted nanoporous anodic alumina funnels:On the precise generation of 3D optical nanostructures[J]. Nanoscale,2014,6(17):9991-9999.
[13] 郭鹤桐,王为. 铝阳极氧化的回顾与展望[J]. 材料保护,2000,33(17):43-46.
[14] 侯春阳,陈静,程党国,等. 阳极氧化氧化铝膜研究进展[J]. 化工进展,2010,29(s1):222-227.
[15] Friedman A L,Brittain D,Menon L. Roles of pH and acid type in the anodic growth of porous alumina[J]. J. Chem. Phys.,2007,127(15):154717.
[16] Ono S,Saito M,Asoh H. Self-ordering of anodic porous alumina formed in organic acid electrolytes[J]. Electrochim Acta,2005,51(5):827-33.
[17] Yi L,Ling Z Y,Chen S S,et al. Novel AAO films and hollow nanostructures fabricated by ultra-high voltage hard anodization[J]. Chem. Commun.,2009,46(2):309-311.
[18] Zhang Z,Liu X H,Pan C F,et al. Nano-porous anodic aluminium oxide membranes with 6—19nm pore diameters formed by a low-potential anodizing process[J]. Nanotechnology,2007,18(34):345302.
[19] Lee W,Kim J C,Gösele U. Spontaneous current oscillations during hard anodization of aluminum under potentiostatic conditions[J]. Adv. Funct. Mater.,2010,20(1):21-27.
[20] Sulka G D,Stepniowski W J. Structural features of self-organized nanopore arrays formed by anodization of aluminumin in oxalic acid at relatively high temperatures[J]. Electrochim Acta,2009,54(14):3683-3691.
[21] Santos A,Montero-Moreno J M,Bachmann J,et al. Understanding pore rearrangement during mild to hard transition in bilayered porous anodic alumina membranes[J]. Appl. Mater. Interfaces,2006,3(6):1925-1932.
[22] Nielsch K,Choi J,Schwirn K,et al. Self-ordering regimes of porous alumina:The 10 porosity rule[J]. Nano Letters,2002,2(7):677-680.
[23] Furneaux R C,Rigby W R,Davidson A P. The formation of controlled-porosity membranes from anodically oxidized aluminium[J]. Nature,1989,337:147-149.
[24] Lee W,Park S J. Porous anodic aluminum oxide:Anodization and templated synthesis of functional nanostructures[J]. Chem. Rev.,2014,114(15):7487-7556.
[25] O'Sullivan J P,Wood G C. The morphology and mechanism of formation of porous anodic films on aluminum[J]. Proc. R. Soc. Lond. A,1970,317:511-543.
[26] Li A P,Muller F,Birner A,et al. Hexagonal pore arrays with a 50—420nm interpore distance formed by self-organization in anodic alumina[J]. J. Appl. Phys.,1998,84(11):6023-6026.
[27] Lee W,Ji R,Gösele U,et al. Fast fabrication of long-range ordered porous alumina membranes by hard anodization[J]. Nat. Mater.,2006,5(9):741-747.
[28] Masuda H,Fukuda K. Ordered metal nanohole arrays made by a two-step replication of honeycomb structures of anodic alumina[J]. Science,1995,268(5216):1466-1468.
[29] Masuda H,Satoh M. Fabrication of gold nanodot array using anodic porous alumina as an evaporation mask[J]. Jpn. J. Appl. Phys.,1996,35:L126-L129
[30] Masuda H,Hasegwa F. Self-ordering of cell arrangement of anodic porous alumina formed in sulfuric acid solution[J]. J. Electrochem. Soc.,1997,144(5):L127-L130.
[31] Schwirn K,Lee W,Hillebrand R,et al. Self-ordered anodic aluminum oxide formed by H₂SO₄ hard anodization[J]. ACS Nano.,2008,2:302-310.
[32] Chu S Z,Wada K,Inoue S,et al. Large-scale fabrication of ordered nanoporous alumina films with arbitrary pore intervals by critical-potential anodization[J]. Journal of the Electrochemical Society,2006,153(9):B384-B478.
[33] Sun C,Luo J,Wu L,et al. Self-ordered anodic alumina with continuously tunable pore intervals from 410 to 530nm[J]. ACS Applied Materials &Interfaces,2010,2(5):1299-1302.
[34] 常毅,凌志远. 在混合电解液中制备阳极氧化铝膜[J]. 中国科技论文在线,2012,12(444):1-6.
[35] Qin X F,Zhang J Q,Meng X J,et al. Preparation and analysis of anodic aluminum oxide films with continuously tunable interpore distance[J]. Applied Surface Science,2015,328:459-465.
[36] 刘皓,赵婷婷,李津,等. 基于多孔阳极氧化铝的单层纳米柱阵PMMA膜的制备[J]. 功能材料,2014,11:1115-1117.
[37] Xu Y F,Liu H,Li X J,et al. A novel method for fabricating self-ordered porous anodic alumina with wide interpore distance using phosphoric/oxalic acid mixed electrolyte[J]. Materials Letters,2015,151(15):79-81.
[38] Sheasby P G,Pinner R. The Surface Treatment and Finishing of Aluminum and Its Alloys[M]. 6th ed. UK:Finishing Publications Ltd. & ASM International,2001.
[39] Chu S Z,Wada K,Inoue S,et al. Fabrication of ideally ordered nanoporous alumina films and integrated alumina nanotubule arrays by high-field anodization[J]. Adv. Mater.,2005,17:2115-2119.
[40] Santos A,Formentín P,Ferré-Borrull J,et al. Nanoporous anodic alumina obtained without protective oxide layer by hard anodization[J]. Materials Letters,2012,67(1):296-299.
[41] Kim M,Ha Y C,Nguyen T N. Self-ordered hard anodization in malonic acid and its application in tailoring alumina taper-nanopores with continuously tunable periods in the range of 290—490nm[J]. Electrochimica Acta,2013,112:327-332.
[42] Raj V,Rajaram M R,Balasubramanian G,et al. Pulse anodizing:An overview[J]. Trans. Inst. Met. Finish,2003,81:114-121.
[43] Lee W,Schwirn K,Steinhart M,et al. Structural engineering of nanoporous anodic aluminium oxide by pulse anodization of aluminium[J]. Nat. Nanotechnol.,2008,3(4):234-239.
[44] Lee W,Kim J C. Highly ordered porous alumina with tailor-made pore structures fabricated by pulse anodization[J]. Nanotechnology,2010,21(48):485304.
[45] Sulka G D,Hnida K. Distributed bragg reflector based on porous anodic alumina fabricated by pulse anodization[J]. Nanotechnology,2012,23(7):075303.
[46] Wang Y,Santos A,Evdokiou A,et al. Rational design of ultra-short anodic alumina nanotubes by short-time pulse anodization[J]. Electrochimica Acta,2015,154:379-386.
[47] Losic D,Lillo M,Losic D Jr. Porous alumina with shaped pore geometries and complex pore architectures fabricated by cyclic anodization[J]. Small,2009,5(12):1392-1397.
[48] Losic D,Losic D Jr. Preparation of porous anodic alumina with periodically perforated pores[J]. Langmuir,2009,25(10):5426-5431.