负载型铂催化剂催化氧化甲醛的研究进展

doi:10.16085/j.issn.1000-6613.2017-0064

摘要/Abstract

摘要： 建筑和装饰材料中缓慢释放的甲醛是一种主要的室内空气污染物，长期暴露在较低浓度的甲醛环境里会严重危害人类的身体健康。催化氧化法是一种非常有效的消除甲醛技术，能在较为温和的条件下将甲醛完全转化为二氧化碳和水。负载型铂催化剂对甲醛催化氧化反应表现出较为优异的催化性能，受到广泛研究和关注。本文综述了近年来该类催化剂的研究进展，主要探讨了制备方法、载体种类和形貌、添加助剂及反应条件参数等因素对负载型铂催化剂上甲醛催化氧化性能的影响；并归纳了一部分甲醛催化氧化的反应机理。分析认为：负载型铂催化剂在低温条件下具有很强的活化分子氧的能力，从而使其对甲醛低温催化氧化反应表现出很高的催化活性。另外还对负载型铂催化剂未来的研究发展方向进行了展望：应通过优化和改进催化剂制备方法和策略，提高铂原子的利用率，产生更多的表面/界面活性中心，继而进一步提高催化剂的性能；借助一些先进的表征技术如氧同位素示踪技术和理论计算的方法深入研究甲醛催化氧化反应机理等基础问题。

关键词: 甲醛, 催化, 氧化, 负载型铂催化剂, 活性

Abstract: Formaldehyde(HCHO),emitted from buildings and decorative materials,is a major indoor air pollutant. Long-term exposure to low concentration of HCHO may cause serious health problems to human being. Catalytic oxidation of HCHO is one of the most effective approaches since it can completely convert HCHO into CO₂ and H₂O at relatively mild operating conditions. Among numerous catalyst systems,supported platinum(Pt)catalysts have been extensively studied due to their superior catalytic performance for the oxidation of HCHO. In this paper,the recent progresses of the supported Pt catalysts in catalytic oxidation of HCHO have been summarized,and the main factors that influence the catalytic properties have been reviewed in terms of preparation methods,the types and the morphologies of the supports,the addition of promoters,as well as the reaction conditions. Besides,the reaction mechanisms for catalytic oxidation of HCHO over some supported Pt catalysts have also been summarized. It is believed that the outstanding ability of the supported Pt catalysts to activate oxygen molecules at low-temperature is mainly responsible for their excellent catalytic performance in low-temperature oxidation of HCHO. The opportunities for future research are as follows: to further enhance the catalytic activity of the supported Pt catalysts by improving the utilization of Pt atoms and producing more surface/interface active sites through optimizing catalyst preparation methods and strategies; to deeply reveal the reaction mechanisms for catalytic oxidation of HCHO over some representative supported Pt catalysts by combining some advanced characterization techniques like oxygen isotopic tracer technique and theroretical computations.

Key words: formaldehyde, catalysis, oxidation, supported platinum catalysts, reactivity

中图分类号:

TQ426

崔维怡, 惠继星, 谭乃迪. 负载型铂催化剂催化氧化甲醛的研究进展[J]. 化工进展, 2017, 36(10): 3711-3719.

CUI Weiyi, HUI Jixing, TAN Naidi. Research progress on catalytic oxidation of formaldehyde over supported platinum catalysts[J]. Chemical Industry and Engineering Progress, 2017, 36(10): 3711-3719.

参考文献

[1] ANN P,MAGNUS B.Formaldehyde[J].Dermatitis,2015,26:1-6.
[2] TUNGA S,SIBEL M,RAINER M.Formaldehyde in the indoor environment[J].Chemical Reviews,2010,110:2536-2572.
[3] 何运兵,纪红兵,王乐夫.室内甲醛催化氧化脱除的研究进展[J].化工进展,2007,26(8):1104-1109.HE Y B,JI H B,WANG L F.Development of the removal of indoor formaldehyde with catalytic oxidation[J].Chemical Industry and Engineering Progress,2007,26(8):1104-1109.
[4] TANG X J,BAI Y,DUONG A,et al.Formaldehyde in China:production,consumption,exposure levels,and health effects[J].Environment International,2009,35:1210-1224.
[5] ZHAI L,ZHAO J,XU B,et al.Influence of indoor formaldehyde pollution on respiratory system health in the urban area of Shenyang,China[J].African Health Sciences,2013,13:137-143.
[6] PEDER W,GUNNAR D N.Non-cancer effects of formaldehyde and relevance for setting an indoor air guideline[J].Environment International,2010,36:788-799.
[7] 李玮,黄丽丽,翟友存,等.新型 Cu-Mn/TiO₂ 和 Cu-Mn/γ-Al₂O₃甲醛催化氧化催化剂的研制及活性[J].化工进展,2015,34(1):127-132.LI W,HUANG L L,ZHAI Y C,et al.Catalytic oxidation of formaldehyde over Cu-Mn catalysts supported on TiO₂ and γ-Al₂O₃ dioxide[J].Chemical Industry and Engineering Progress,2015,34(1):127-132.
[8] ABDUNASER M E,MICHAEL A M,SIDDHARTH V P,et al.Removal of formaldehyde from air using functionalized silica supports[J].Environmental Science & Technology,2012,46:13354-13360.
[9] DARIA K,MOHAMAD S,JAVIERA C S,et al.Adsorption and photocatalytic oxidation of formaldehyde on a clay-TiO₂ composite[J].Journal of Hazardous Materials,2012,211/212:233-239.
[10] JHON Q T,SEBASTIEN Y,BELLAT J P,et al.Formaldehyde:catalytic oxidation as a promising soft way of elimination[J].ChemSusChem,2013,6:578-592.
[11] NIE L H,YU J G,JARONIEC M,et al.Room-temperature catalytic oxidation of formaldehyde on catalysts[J].Catalysis Science & Technology,2016,6:3649-3669.
[12] BAI B Y,QIAO Q,LI J H,et al.Progress in research on catalysts for catalytic oxidation of formaldehyde[J].Chinese Journal of Catalysis,2016,37:102-122.
[13] 董冰岩,施志勇,何俊文,等.脉冲放电等离子体协同Mn/TiO₂-分子筛、Fe/TiO₂-分子筛、Cu/TiO₂-分子筛催化剂降解甲醛[J].化工进展,2015,35(9):3337-3344.DONG B Y,SHI Z Y,HE J W,et al.Research of pulse discharge plasma combined with Mn/TiO₂-molecular、Fe/TiO₂-molecular、Cu/TiO₂-molecular sieve catalysts decomposition of formaldehyde[J].Chemical Industry and Engineering Progress,2015,35(9):3337-3344.
[14] LU N,PEI J J,ZHAO Y X,et al.Performance of a biological degradation method for indoor formaldehyde removal[J].Building and Environment,2012,57:253-258.
[15] WANG Z,WANG W Z,ZHANG L,et al.Surface oxygen vacancies on Co₃O₄ mediated catalytic formaldehyde oxidation at room temperature[J].Catalysis Science & Technology,2016,6:3845-3853.
[16] ZHANG J H,LI Y B,WANG L,et al.Catalytic oxidation of formaldehyde over manganese oxides with different crystal structures[J].Catalysis Science & Technology,2015,5:2305-2313.
[17] HUANG Y C,LI H B,BALOGUN M S,et al.Three-dimensional TiO₂/CeO₂ nanowire composite for efficient formaldehyde oxidation at low temperature[J].RSC Advances,2015,5:7729-7733.
[18] XU Q L,LEI W Y,LI X Y,et al.Efficient removal of formaldehyde by nanosized gold on well-defined CeO₂ nanorods at room temperature[J].Environmental Science & Technology,2014,48:9702-9708.
[19] AN N H,YU Q S,LIU G,et al.Complete oxidation of formaldehyde at ambient temperature over supported Pt/Fe₂O₃ catalysts prepared by colloid-deposition method[J].Journal of Hazardous Materials,2011,186:1392-1397.
[20] LI Y B,ZHANG C B,HE H,et al.Influence of alkali metals on Pd/TiO₂ catalysts for catalytic oxidation of formaldehyde at room temperature[J].Catalysis Science Technology,2016,6:2289-2295.
[21] BAI B Y,QIAO Q,ARANDIYAN H,et al.Three-dimensional ordered mesoporous MnO₂-supported Ag nanoparticles for catalytic removal of formaldehyde[J].Environmental Science & Technology,2016,50:2635-2640.
[22] ZHANG C B,HE H,TANAKA K.Perfect catalytic oxidation of formaldehyde over a Pt/TiO₂ catalyst at room temperature[J].Catalysis Communications,2005,6:211-214.
[23] AN N H,ZHANG W L,YUAN X L,et al.Catalytic oxidation of formaldehyde over different silica supported platinum catalysts[J].Chemical Engineering Journal,2013,215/216:1-6.
[24] YAN Z X,XU Z H,YU J G,et al.Enhanced formaldehyde oxidation on CeO₂/AlOOH-supported Pt catalyst at room temperature[J].Applied Catalysis B:Environmental,2016,199:458-465.
[25] NIE L H,MENG A Y,TENG F,et al.Hierarchically macro-mesoporous flowerlike Pt/NiO composite microspheres for efficient formaldehyde oxidation at room temperature[J].RSC Advances,2015,5:83997-84003.
[26] ZHANG C B,HE H,TANAKA K.Catalytic performance and mechanism of a Pt/TiO₂ catalyst for the oxidation of formaldehyde at room temperature[J].Applied Catalysis B:Environmental,2006,65:37-43.
[27] ZHANG C B,HE H.A comparative study of TiO₂ supported noble metal catalysts for the oxidation of formaldehyde at room temperature[J].Catalysis Today,2007,126:345-350.
[28] PENG J,WANG S.Performance and characterization of supported metal catalysts for complete oxidation of formaldehyde at low temperatures[J].Applied Catalysis B:Environmental,2007,73(3/4):282-291.
[29] HUANG H B,LEUNG D Y C.Complete elimination of indoor formaldehyde over supported Pt catalysts with extremely low Pt content at ambient temperature[J].Journal of Catalysis,2011,280(1):60-67.
[30] HUANG H B,LEUNG D Y C,YE D.Effect of reduction treatment on structural properties of TiO₂ supported Pt nanoparticles and their catalytic activity for formaldehyde oxidation[J].Journal of Materials Chemistry,2011,21:9647-9652.
[31] HUANG H B,HU P,HUANG H L,et al.Highly dispersed and active supported Pt nanoparticles for gaseous formaldehyde oxidation:influence of particle size[J].Chemical Engineering Journal,2014,252:320-326.
[32] ZHANG C B,LIU,F D,ZHAI Y P,et al.Alkali-metal-promoted Pt/TiO₂ opens a more efficient pathway to formaldehyde oxidation at ambient temperatures[J].Angewandte Chemie-International Edition,2012,51:9628-9632.
[33] NIE L H,YU J G,LI X Y,et al.Enhanced performance of NaOH-modified Pt/TiO₂ toward room temperature selective oxidation of formaldehyde[J].Environmental Science & Technology,2013,47:2777-2783.
[34] LIU B T,HSIEH C H,WANG W H,et al.Enhanced catalytic oxidation of formaldehyde over dual-site supported catalysts at ambient temperature[J].Chemical Engineering Journal,2013,232:434-441.
[35] ZHOU P,YU J G,NIE L H,et al.Dual-dehydrogenation-promoted catalytic oxidation of formaldehyde on alkali-treated Pt clusters at room temperature[J].Journal Materials Chemical A,2015,3:10432-10438.
[36] CHEN H Y,RUI Z B,JI H B.Monolith-like TiO₂ nanotube array supported Pt catalyst for HCHO removal under mild conditions[J].Industrial & Engineering Chemistry Research,2014,53:7629-7636.
[37] NIE L H,YU J G,FU J W,et al.Complete decomposition of formaldehyde at room temperature over a platinum-decorated hierarchically porous electrospun titania nanofiber mat[J].ChemCatChem,2014,6:1983-1989.
[38] QI L F,HO W K,WANG J L,et al.Enhanced catalytic activity of hierarchically macro-/mesoporous Pt/TiO₂ toward room temperature decomposition of formaldehyde[J].Catalysis,Science,Technology,2015,5:2366-2377.
[39] QI L F,CHENG B,YU J G,et al.High-surface area mesoporous Pt/TiO₂ hollow chains for efficient formaldehyde decomposition at ambient temperature[J].Journal of Hazardous Materials,2016,301:522-530.
[40] ZHOU P,ZHU X F,YU J G,et al.Effects of adsorbed F,OH,and Cl ions on formaldehyde adsorption performance and mechanism of anatase TiO₂nanosheets with exposed{001} facets[J].ACS Applied Materials Interfaces,2013,5:8165-8172.
[41] NIE L H,ZHOU P,YU J G,et al.Deactivation and regeneration ofPt/TiO₂ nanosheet-type catalysts with exposed (001) facets for roomtemperature oxidation of formaldehyde[J].Journal of MolecularCatalysis A:Chemical,2014,390:7-13.
[42] ZHU X F,CHENG B,YU J G,et al.Halogen poisoning effect ofPt-TiO₂ for formaldehyde catalytic oxidation performance at roomtemperature[J].Applied Surface Science,2016,364:808-814.
[43] TANG X,CHEN J,HUANG X,et al.Pt/MnO_x-CeO₂ catalysts for thecomplete oxidation of formaldehyde at ambient temperature[J].Applied Catalysis B:Environmental,2008,81(1/2):115-121.
[44] AN N H,WU P,LI S Y,et al.Catalytic oxidation of formaldehydeover Pt/Fe₂O₃ catalysts prepared by different method[J].AppliedSurface Science,2013,285P:805-809.
[45] LIU L L,TIAN H,HE J H,et al.Preparation of birnessite-supportedPt nanoparticles and their application in catalytic oxidation offormaldehyde[J].Journal of Environmental Sciences,2012,24(6):1117-1124.
[46] YU X H,HE J H,WANG D H,et al.Facile controlled synthesis ofPt/MnO₂ nanostructured catalysts and catalytic performance foroxidative decomposition of formaldehyde[J].Journal Physical.Chemistry C,2012,116:851-860.
[47] NIE L H, MENG A Y, YU J G, et al.Hierarchicallymacro-mesoporous Pt/Al₂O₃ composite microspheres fo efficientformaldehyde oxidation at room temperature[J].Scientific Reports,2013,3215:1-7.
[48] NIE L H,ZHANG Y Q,YU J G.Efficient decomposition offormaldehyde at room temperature over Pt/honeycomb ceramics withultra-low Pt content[J].Dalton Transactions,2014,43:12935-12942.
[49] CHEN Y,HE J H,TIAN H,et al.Enhanced formaldehyde oxidationon Pt/MnO₂ catalysts modified with alkali metal salts[J].Journal ofColloid and Interface Science,2014,428:1-7.
[50] YAN Z X,XU Z H,YU J G,et al.Highly active mesoporousferrihydrite supported Pt catalyst for formaldehyde removal at roomtemperature[J].Environmental Science & Technology,2015,49:6637-6644.
[51] CHEN H Y,RUI Z B,WANG X Y,et al.Multifunctional Pt/ZSM-5catalyst for complete oxidation of gaseous formaldehyde at ambienttemperature[J].Catalysis Today,2015,258:56-63.
[52] CUI W Y,YUAN X L,WU P,et al.Catalytic properties of Al₂O₃supported Pt-FeO_x catalysts for complete oxidation of formaldehyde atambient temperature[J].RSC Adances,2015,5:104330-104336.
[53] CHEN H Y,TANG M N,RUI Z B,et al.MnO₂ promoted TiO₂ nanotube array supported Pt catalyst for formaldehyde oxidation withenhanced efficiency[J].Industrial Engineering Chemistry Research,2015,54:8900-8907.
[54] MA Y, ZHANG G K.Sepiolite nanofiber-supported platinumnanoparticle catalysts toward the catalytic oxidation of formaldehydeat ambient temperature:efficient and stable performance andmechanism[J].Chemical Engineering Journal,2016,288:70-78.
[55] YAN Z X,XU Z H,YU J G,et al.Enhanced formaldehyde oxidationon CeO₂/AlOOH-supported Pt catalyst at room temperature[J].Applied Catalysis B:Environmental,2016,199:458-465.
[56] YANG T F,HUO Y,LIU Y,et al.Efficient formaldehyde oxidationover nickel hydroxide promoted Pt/Al₂O₃ with a low Pt content[J].Applied Catalysis B:Environmental,2017,200:543-551.