张军华1,国海光1,郇昌永1,姜 莉2,沈 强1   

  1. 1杭州凯大催化金属材料有限公司,浙江 杭州310015;2浙江传化股份有限公司,浙江 杭州 311215
  • 出版日期:2012-09-05 发布日期:2012-09-05

Preparation of 4,4'-diaminostilbene-2,2'-disulfonic acid by Pt/C catalytic hydrogenation

ZHANG Junhua1,GUO Haiguang1,HUAN Changyong1,JIANG Li2,SHEN Qiang1   

  1. 1Hangzhou Kaida Metal Catalyst & Compounds Co. Ltd.,Hangzhou 310015,Zhejiang,China; 2Zhejiang Transfar Co. Ltd.,Hangzhou 211215,Zhejiang,China
  • Online:2012-09-05 Published:2012-09-05

摘要: 以水为反应介质,Pt/C为催化剂, 研究了液相催化加氢法制备4,4′-二氨基二苯乙烯-2,2′-二磺酸(DSD酸)。通过一系列条件实验,得到的最佳工艺条件是:原料DNS酸二钠盐60g(湿),水200mL, 3%Pt/C催化剂0.3g(干重),反应温度为45~50℃,反应压力为0.5~0.65 MPa,反应体系pH=5~7。在此工艺条件下,得到的DSD酸产品质量分数大于99%,苄基物含量小于0.15%,醛含量小于0.15%。产品收率大于98.5%。并且,通过独有的催化剂再生技术,催化剂可重复利用20次以上,大大降低了其使用成本,为工业化奠定基础。

关键词: 4,4′-二氨基二苯乙烯-2,2′-二磺酸(DSD酸), 催化加氢, Pt/C, 催化剂套用, 4, 4′-二氨基二苯乙烯-2, 2′-二磺酸(DSD酸), 催化加氢, Pt/C, 催化剂套用

Abstract: Preparation of 4,4'-diaminostilbene-2,2'-disulfonic acid (DSD acid) with the liquid-phase catalytic hydrogenation method using Pt/C as catalyst in water medium was studied. The optimum technical conditions determined by a series of experiments were as follows: 60 g (wet) of feed material DNS,200 mL of H2O,0.3 g (dry) of catalyst 3%Pt/C,reaction temperature of 45—50 ℃,reaction pressure of 0.5—0.65 MPa and pH value of 5—7 in the reaction system. Under these optimum technical conditions,purity of the product could exceed 99%,by-products of benzyl and aldehyde compounds were less than 0.15%. The yield of product came up to 98.5%. And,through a proprietary catalyst regeneration technology,the catalyst could be reused more than 20 times,reducing the cost greatly and providing the foundation for its commercialization.

Key words: 4,4’-diaminostilbene-2,2’-disulfonic acid(DSD acid), catalytic hydrogenation, Pt/C, reused of catalyst., 4,4'-diaminostilbene-2,2'-disulfonic acid (DSD acid), catalytic hydrogenation, Pt/C, reuse of catalyst