Co-MOF-74的合成及其吸附正己烷/1-己烯性能

doi:10.16085/j.issn.1000-6613.2019-0683

化工进展 ›› 2019, Vol. 38 ›› Issue (s1): 179-185.DOI: 10.16085/j.issn.1000-6613.2019-0683

Co-MOF-74的合成及其吸附正己烷/1-己烯性能

刘露¹, 任丹妮², 刘继三¹

1 华陆工程科技有限责任公司, 陕西西安 710065;
2 华东理工大学石油加工研究所, 上海 200237

收稿日期:2019-04-29 修回日期:2019-08-30 出版日期:2019-11-16 发布日期:2019-11-16
通讯作者: 刘露(1986-),女,硕士,工程师。
作者简介:刘露(1986-),女,硕士,工程师。E-mail:ll2359@hlet.com。

Synthesis and the performance of Co-MOF-74 for n-hexane/1-hexene adsorption separation

LIU Lu¹, REN Danni², LIU Jisan¹

1 Hualu Engineering&Technology Co., Ltd., Xi'an 710065, Shaanxi, China;
2 Petroleum Processing Research Center, East China University of Science and Technology, Shanghai 200237, China

Received:2019-04-29 Revised:2019-08-30 Online:2019-11-16 Published:2019-11-16

摘要/Abstract

摘要： 采用溶剂热方法合成了Co-MOF-74，采用X射线衍射（XRD）、氮气吸附、红外光谱（FTIR）、热重-差热分析（TG-DSC）和扫描电子显微镜（SEM）对其进行表征，研究其吸附正己烷/1-己烯性能。结果表明，优化的Co-MOF-74合成工艺条件为：原料配比n[Co（NO₃）₂·6H₂O]：n（DHTP）：n（THF）：n（H₂O）=2：1：165：750，晶化温度100℃，晶化时间24h，150℃活化2h。合成Co-MOF-74对1-己烯和正己烷的静态饱和吸附量分别为125.6mg/g和72.9mg/g，BET比表面积为1209m²/g，孔体积为0.41cm³/g，微孔平均孔径为0.66nm。L-F吸附模型能较好地解释Co-MOF-74材料对1-己烯的吸附等温线数据，Co-MOF-74吸附1-己烯的过程是热力学自发放热过程。

关键词: 合成, 吸附, 烷烃, 分离

Abstract: Co-MOF-74 was synthesized through solvothermal process. Samples were characterized by using XRD, N₂ adsorption, FTIR, TG-DSC and SEM. In addition, the adsorption performances for n-hexane/1-hexene were evaluated. The optimal synthesis conditions were observed as follows:the ratio of raw materials of n[Co (NO₃) ₂·6H₂O]:n (DHTP):n (THF):n (H₂O)=2:1:165:750, crystallization temperature of 100℃, crystallization time of 24h, activation temperature of 150℃, activation time of 2h. It is indicated that synthesized Co-MOF-74 has static adsorption capacities of 125.6mg/g and 72.9mg/g for 1-hexene and n-hexane, respectively. The BET specific surface area, pore volume and average micropore size are 1209m²/g, 0.41cm³/g and 0.66nm, respectively. The maximum adsorption amount is determined to be around 130mg/g at adsorption temperature range of 283K to 313K. Furthermore, the adsorption isotherms for 1-hexene on Co-MOF-74 can be explained by using L-F model very well. 1-hexene adsorption onto Co-MOF-74 is confirmed to be a spontaneous exothermic process.

Key words: synthesis, adsorption, alkane, separation

中图分类号:

TQ028

刘露, 任丹妮, 刘继三. Co-MOF-74的合成及其吸附正己烷/1-己烯性能[J]. 化工进展, 2019, 38(s1): 179-185.

LIU Lu, REN Danni, LIU Jisan. Synthesis and the performance of Co-MOF-74 for n-hexane/1-hexene adsorption separation[J]. Chemical Industry and Engineering Progress, 2019, 38(s1): 179-185.

参考文献

[1] BAO Z B, WANG J W, ZHANG Z G, et al. Molecular sieving of ethane from ethylene through the molecular cross-section size differentiation in gallate-based metal-organic frameworks[J]. Angewandte Chemie:International Edition, 2018, 57:16020-16025.
[2] BLOCH E D, QUEEN W L, KRISHNA R, et al. Hydrocarbon separations in a metal-organic framework with open iron(II) coordination sites[J]. Science, 2012, 335:1606-1610.
[3] SHOLL D S, LIVELY R P. Seven chemical separations to change the world[J]. Nature, 2016, 532:435-437.
[4] REN T, PATEL M, BLOK K. Olefins from conventional and heavy feedstocks:energy use in steam cracking and alternative processes[J]. Energy, 2006, 31:425-451.
[5] KHODAKOV A, CHU W, FONGARLAND P. Advances in the development of novel cobalt Fischer-Tropsch catalysts for synthesis of long-chain hydrocarbons and clean fuels[J]. Chemical Reviews, 2017, 107:1692-1744.
[6] DRY M E. The Fischer-Tropsch process:1950-2000[J]. Catalysis Today, 2002, 71:227-241.
[7] ADIL K, BELMABKHOUT Y, PILLAI R S, et al. Gas/vapour separation using ultra-microporous metal-organic frameworks:insights into the structure/separation relationship[J]. Chemical Society Reviews, 2017, 46:3402-3430.
[8] BAO Z B, CHANG G G, XING H B, et al. Potential of microporous metal-organic frameworks for separation of hydrocarbon mixtures[J]. Energy & Environmental Science, 2016, 9:3612-3641.
[9] PADIN J, YANG R. New sorbents for olefin/paraffin separations by adsorption via pi-complexation:synthesis and effects of substrates[J]. Chemical Engineering Science, 2000, 55:2607-2616.
[10] BERNARDO P, DRIOLI E, GOLEMME G. Membrane gas separation:a review/state of the art[J]. Industrial & Engineering Chemistry Research, 2009, 48:4638-4663.
[11] CARTA M, MALPASS-EVANS R, CROAD M, et al. An efficient polymer molecular sieve for membrane gas separations[J]. Science, 2013, 339:303-307.
[12] CARTA M, CROAD M, MALPASS-EVANS R, et al. Triptycene induced enhancement of membrane gas selectivity for microporous troger's base polymers[J]. Advanced Materials, 2014, 26:3526-3531.
[13] BESSARABOV D, THERON J, SANDERSON R, et al. Separation of 1-hexene/n-hexane mixtures using a hybrid membrane/extraction system[J]. Separation & Purification Technology, 1999, 16(2):167-174.
[14] HUANG J F, LUO H M, LIANG C D, et al. Advanced liquid membranes based on novel ionic liquids for selective separation of olefin/paraffin via olefin-facilitated transport[J]. Industrial & Engineering Chemistry Research, 2008, 47:881-888.
[15] TRANCHEMONTAGNE D J, HUNT J R, YAGHI O M. Room temperature synthesis of metal-organic frameworks:MOF-5, MOF-74, MOF-177, MOF-199, and IRMOF[J]. Tetrahedron, 2008, 64(36):8553-8557.
[16] MUNDSTOCK A, BOEHME U, BARTH B, et al. Propylene/propane separation in fixed-bed adsorber and membrane permeation[J]. Chemical Engineering & Technology, 2013, 85(11):1694-1699.
[17] CHEN D L, SHANG H, ZHU W, et al. Transient breakthroughs of CO₂/CH₄ and C₃H₆/C₃H₈ mixtures in fixed beds packed with Ni-MOF-74[J]. Chemical Engineering Science, 2014, 117:407-415.
[18] JIAO Y, MORELOCK C, BURTCH N, et al. Tuning the kinetic water stability and adsorption interactions of Mg-MOF-74 by partial substitution with Co or Ni[J]. Industrial & Engineering Chemistry Research, 2015, 54:12408-12414.
[19] HOWE J D, MORELOCK C R, Jiao Y, et al. Understanding structure, metal distribution, and water adsorption in mixed-metal MOF-74[J]. The Journal of Physical Chemistry C, 2017, 121(1):627-635.
[20] WANG D, WANG Q, WANG T. Morphology-controllable synthesis of cobalt oxalates and their conversion to mesoporous Co₃O₄ nanostructures for application in supercapacitors[J]. Inorganic Chemistry, 2011, 50(14):6482-6492.

Co-MOF-74的合成及其吸附正己烷/1-己烯性能

Synthesis and the performance of Co-MOF-74 for n-hexane/1-hexene adsorption separation

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价

[1]	王胜岩, 邓帅, 赵睿恺. 变电吸附二氧化碳捕集技术研究进展[J]. 化工进展, 2023, 42(S1): 233-245.
[2]	贺美晋. 分子管理在炼油领域分离技术中的应用和发展趋势[J]. 化工进展, 2023, 42(S1): 260-266.
[3]	时永兴, 林刚, 孙晓航, 蒋韦庚, 乔大伟, 颜彬航. 二氧化碳加氢制甲醇过程中铜基催化剂活性位点研究进展[J]. 化工进展, 2023, 42(S1): 287-298.
[4]	杨霞珍, 彭伊凡, 刘化章, 霍超. 熔铁催化剂活性相的调控及其费托反应性能[J]. 化工进展, 2023, 42(S1): 310-318.
[5]	崔守成, 徐洪波, 彭楠. 两种MOFs材料用于O₂/He吸附分离的模拟分析[J]. 化工进展, 2023, 42(S1): 382-390.
[6]	赵巍, 赵德银, 李世瀚, 刘洪达, 孙进, 郭艳秋. 三嗪型天然气管道缓蚀型减阻剂合成与应用[J]. 化工进展, 2023, 42(S1): 391-399.
[7]	王正坤, 黎四芳. 双子表面活性剂癸炔二醇的绿色合成[J]. 化工进展, 2023, 42(S1): 400-410.
[8]	陈崇明, 陈秋, 宫云茜, 车凯, 郁金星, 孙楠楠. 分子筛基CO₂吸附剂研究进展[J]. 化工进展, 2023, 42(S1): 411-419.
[9]	李世霖, 胡景泽, 王毅霖, 王庆吉, 邵磊. 电渗析分离提取高值组分的研究进展[J]. 化工进展, 2023, 42(S1): 420-429.
[10]	许春树, 姚庆达, 梁永贤, 周华龙. 共价有机框架材料功能化策略及其对Hg(Ⅱ)和Cr(Ⅵ)的吸附性能研究进展[J]. 化工进展, 2023, 42(S1): 461-478.
[11]	顾永正, 张永生. HBr改性飞灰对Hg⁰的动态吸附及动力学模型[J]. 化工进展, 2023, 42(S1): 498-509.
[12]	郭强, 赵文凯, 肖永厚. 增强流体扰动强化变压吸附甲硫醚/氮气分离的数值模拟[J]. 化工进展, 2023, 42(S1): 64-72.
[13]	许友好, 王维, 鲁波娜, 徐惠, 何鸣元. 中国炼油创新技术MIP的开发策略及启示[J]. 化工进展, 2023, 42(9): 4465-4470.
[14]	廖志新, 罗涛, 王红, 孔佳骏, 申海平, 管翠诗, 王翠红, 佘玉成. 溶剂脱沥青技术应用与进展[J]. 化工进展, 2023, 42(9): 4573-4586.
[15]	葛亚粉, 孙宇, 肖鹏, 刘琦, 刘波, 孙成蓥, 巩雁军. 分子筛去除VOCs的研究进展[J]. 化工进展, 2023, 42(9): 4716-4730.