不同金属助剂对HZSM-5分子筛催化分解甲硫醇性能的影响

doi:10.16085/j.issn.1000-6613.2017-1192

摘要/Abstract

摘要： 采用浸渍的方式制备不同系列金属（Cr、La和Na）改性HZSM-5催化剂，并研究其对甲硫醇催化分解活性的影响以及分析相关性能差异的原因。通过XRD、BET、SEM、NH₃-TPD、CO₂-TPD、H₂-TPR和XPS等表征手段对催化剂的物化性质进行测定，结果表明：不同系列金属改性HZSM-5对甲硫醇表现出不同的催化活性及影响效果，其中Cr和La改性HZSM-5能明显提高催化剂的催化活性，在500℃下可实现甲硫醇的完全催化转化，这主要归因于Cr的引入提高了催化剂的氧化还原能力，从而促进甲硫醇的催化分解；La的引入增加了催化剂表面的碱性位点，有利于甲硫醇在催化剂表面的吸附和活化。而Na改性HZSM-5表现出较差的催化活性，主要是由于过多Na的添加严重破坏了HZSM-5的骨架结构，从而导致催化剂的催化稳定性能降低。

关键词: 甲硫醇, 分子筛, 金属改性, 催化, 降解

Abstract: The metal oxides of Cr,La and Na supported on bare HZSM-5 were prepared by an incipient-wetness impregnation method and used for CH₃SH catalytic decomposition tests. XRD,BET,SEM,NH₃-TPD,CO₂-TPD,H₂-TPR and XPS measurements were carried out to investigate the effects of these promoters on the structural and physicochemical properties of the supported HZSM-5 zeolite catalysts. It is found that Cr/HZSM-5 and La/HZSM-5 catalysts exhibit greatly improved catalytic activity owing to the improved redox capacity and the increased amounts of basic sites of the Cr and La doped HZSM-5 catalysts. CH₃SH can be completely converted over Cr and La modified HZSM-5 catalysts at 500℃. For Na modified HZSM-5,the excessive Na,however,may seriously destroy the framework of the catalyst structure and causing the poor catalytic stability of the catalyst.

Key words: methyl mercaptan, moleclar sieves, metal modification, catalysis, degradation

中图分类号:

X512

余杰, 何德东, 陈定凯, 刘峰, 刘江平, 刘攀, 赵雨桐, 许志志, 罗永明. 不同金属助剂对HZSM-5分子筛催化分解甲硫醇性能的影响[J]. 化工进展, 2018, 37(03): 1021-1029.

YU Jie, HE Dedong, CHEN Dingkai, LIU Feng, LIU Jiangping, LIU Pan, ZHAO Yutong, XU Zhizhi, LUO Yongming. Promoter effects on HZSM-5 zeolite catalysts for catalytic decomposition of methyl mercaptan[J]. Chemical Industry and Engineering Progress, 2018, 37(03): 1021-1029.

参考文献

[1] 李俊华,陈建军,郝吉明. 控制大气污染化工技术的研究进展[J]. 化工进展,2005,24(7):703-709. LI Junhua,CHEN Jianjun,HAO Jiming. Recent progress of air pollution control technology[J]. Chemical Industry and Engineering Progress,2005,24(7):703-709.
[2] 方选政,张兴惠,张兴芳. 吸附-光催化法用于降解室内VOC的研究进展[J]. 化工进展,2016,35(7):2215-2221. FANG Xuanzheng,ZHANG Xinghui,ZHANG Xingfang. Research progress on degradation of indoor VOC by using adsorption-photocatalytic method[J]. Chemical Industry and Engineering Progress,2016,35(7):2215-2221.
[3] 赵磊,王筱喃,王新,等. 石化VOC废气深度净化技术开发及工业应用[J]. 环境工程,2016,34(s1):569-571. ZHAO Lei,WANG Xiaonan,WANG Xin,et al. The development and industrial application of deep purification technology of petrochemical VOC emissions[J]. Environmental Engineering,2016,34(s1):569-571.
[4] Zhao S,Yi H,Tang X,et al. Methyl mercaptan removal from gas streams using metal-modified activated carbon[J]. Journal of Cleaner Production,2015,87(1):856-861.
[5] KIM D J,LEE H I,YIE J E,et al. Ordered mesoporous carbons:Implication of surface chemistry,pore structure and adsorption of methyl mercaptan[J]. Carbon,2005,43(9):1868-1873.
[6] Laosiripojana N,Assabumrungrat S. Conversion of poisonous methanethiol to hydrogen-rich gas by chemisorption/reforming over nano-scale CeO₂:the use of CeO₂,as catalyst coating material[J]. Applied Catalysis B:Environmental,2011,102(1/2):267-275.
[7] Whelan M E,Min D H,Rhew R C. Salt marsh vegetation as a carbonyl sulfide (COS) source to the atmosphere[J]. Atmospheric Environment,2013,73(6):131-137.
[8] BrUhl C,Lelieveld J,Crutzen P J,et al. The role of carbonyl sulphide as a source of stratospheric sulphate aerosol and its impact on climate[J]. Atmospheric Chemistry & Physics Discussions,2012,11(7):1239-1253.
[9] Wu T,Wang X M,Li D J,et al. Emission of volatile organic sulfur compounds (VOSCs) during aerobic decomposition of food wastes[J]. Journal of Environmental Sciences,2010,44(39):5065-5071.
[10] 李珊红,李彩亭,谭娅,等. 恶臭气体的治理技术及其进展[J]. 四川环境,2005,24(4):45-49. LI Shanhong,LI Caiting,TAN Ya,et al. Technologies of offensive gas treatment and their new development[J]. Sichuan Environment,2005,24(4):45-49.
[11] 王亚恩,易红宏,唐晓龙,等. 甲硫醇气体治理方法的研究进展[J]. 现代化工,2016,36(6):37-41. WANG Ya'en,YI Honghong,TANG Xiaolong,et al. Research progress of treatment methods for methyl mercaptan[J]. Modern Chemical Industry,2016,36(6):37-41.
[12] Caceres M,Morales M,Martiín R S,et al. Oxidation of volatile reduced sulphur compounds in biotrickling filter inoculated with Thiobacillus thioparus[J]. Electronic Journal of Biotechnology,2010,13(5):292-300.
[13] 龚娟,焦以飞,苏庆泉,等. 沼气中甲硫醇的两段深度脱除法[J]. 现代化工,2013,33(11):97-100. GONG Juan,JIAO Yifei,SU Qingquan,et al. A two-stage method for deep removal of methyl mercaptan in biogas[J]. Modern Chemical Industry,2013,33(11):97-100.
[14] 叶杰旭,诸葛蕾,蔡武,等. 甲硫醇降解菌群筛选及其降解特性研究[J]. 环境科学学报,2017,37(7):2572-2578. YE Jiexu,ZHU Gelei,CAI Wu,et al. Enrichment of a methanthiol-degradation mixed microbial consortium and its degradation characteristics[J]. Acta Scientiae Circumstantiae,2017,37(7):2572-2578.
[15] He D D,Chen D K,Hao H S,et al. Enhanced activity and stability of Sm-doped HZSM-5 zeolite catalysts for catalytic methyl mercaptan (CH₃SH) decomposition[J]. Chemical Engineering Journal,2017,317:60-69.
[16] He D D,Hao H S,Chen D K,et al. Rapid synthesis of nano-scale CeO₂ by microwave-assisted sol-gel method and its application for CH₃SH catalytic decomposition[J]. Journal of Environmental Chemical Engineering,2016,4(1):311-318.
[17] He D D,Wan G P,Hao H S,et al. Microwave-assisted rapid synthesis of CeO₂ nanoparticles and its desulfurization processes for CH₃SH catalytic decomposition[J]. Chemical Engineering Journal,2016,289:161-169.
[18] He D D,Hao H S,Chen D K,et al. Synthesis and application of rare-earth elements (Gd,Sm,and Nd) doped ceria-based solid solutions for methyl mercaptan catalytic decomposition[J]. Catalysis Today,2017,281:559-565.
[19] Mukoyama T,Shimoda N,Satokawa S. Catalytic decomposition of methanethiol to hydrogen sulfide over TiO₂[J]. Fuel Processing Technology,2015,131:117-124.
[20] Hulea V,Huguet E,Cammarano C,et al. Conversion of methyl mercaptan and methanol to hydrocarbons over solid acid catalysts:a comparative study[J]. Applied Catalysis B:Environmental,2014,144(2):547-553.
[21] Huguet E,Coq B,Durand R,et al. A highly efficient process for transforming methyl mercaptan into hydrocarbons and H₂S on solid acid catalysts[J]. Applied Catalysis B:Environmental,2013,134/135(17):344-348.
[22] He D D,Hao H S,Chen D K,et al. Effects of rare-earth (Nd,Er and Y) doping on catalytic performance of HZSM-5 zeolite catalysts for methyl mercaptan (CH₃SH) decomposition[J]. Applied Catalysis A:General,2017,533:66-74.
[23] YU J,HE D D,CHEN D K,et al. Investigating the effects of alkali metal Na addition on catalytic activity of HZSM-5 for methyl mercaptan elimination[J]. Applied Surface Science,2017,420:21-27.
[24] 郝湖生,何德东,陆继长,等. 铈改性对HZSM-5分子筛表面性质及其催化降解甲硫醇(CH₃SH)的研究[J]. 中国稀土学报,2016,34(3):265-272. HAO Husheng,HE Dedong,LU Jichang,et al. Study on the surface properties of HZSM-5 zeolite modified by cerium and its catalytic degradation of methyl mercaptan (CH₃SH)[J]. Journal of the Chinese Society of Rareearths,2016,34(3):265-272.
[25] Cheng Y,Miao C,Hua W,et al. Cr/ZSM-5 for ethane dehydrogenation:enhanced catalytic activity through surface silanol[J]. Applied Catalysis A:General,2017,532:111-119.
[26] Su J,Liu Y,Yao W,et al. Catalytic combustion of dichloromethane over HZSM-5-supported typical transition metal (Cr,Fe,and Cu) oxide catalysts:a stability study[J]. The Journal of Physical Chemistry,2016,120:18046-18054.
[27] Ayari F,Mhamdi M,Ruiz A R G,et al. Cr-ZSM-5 catalysts for ethylene ammoxidation:Effects of precursor nature and Cr/Al molar ratio on the physicochemical and catalytic properties[J]. Microporous & Mesoporous Materials,2013,171(1/2):166-178.
[28] Rahimi N,Karimzadeh R. Catalytic cracking of hydrocarbons over modified ZSM-5 zeolites to produce light olefins:a review[J]. Applied Catalysis A:General,2011,398(1/2):1-17.
[29] CHENG Y T,JAE J,SHI J, et al. Production of renewable aromatic compounds by catalytic fast pyrolysis of lignocellulosic biomass with bifunctional Ga/ZSM-5 catalysts[J]. Angewandte Chemie,2012,124:1416-1419.
[30] Vishwanathan V,Jun K W,Kim J W,et al. Vapour phase dehydration of crude methanol to dimethyl ether over Na-modified H-ZSM-5 catalysts[J]. Applied Catalysis A:General,2004,276(1/2):251-255.
[31] Zhang X,Lin L,Zhang T,et al. Catalytic dehydration of lactic acid to acrylic acid over modified ZSM-5 catalysts[J]. Chemical Engineering Journal,2016,284:934-941.
[32] Zhang L,Han C,Hua W,et al. One-step synthesis of mesoporous nanosized sulfated zirconia via liquid-crystal template (LCT) method[J]. Materials Research Bulletin,2012,47(11):3931-3936.
[33] Sang X,Zhang L,Wang H,et al. Influence of synthetic parameters on structural and catalytic properties of sulfated zirconia nanoparticles prepared by employing sulfate-containing anion surfactants via one-step route[J]. Powder Technology,2014,253(2):590-595.
[34] 成源海,张红漫,胡耀池,等. 焙烧温度对镧改性HZSM-5表面性质及乙醇脱水制乙烯反应性能的影响[J]. 中国稀土学报,2010,28(3):330-334. CHEN Yuanhai,ZHANG Hongman,HU Yaochi,et al. Effect of calcination temperature on surface properties and catalytic performance in dehydration ethanol to ethylene of La-modified HZSM-5[J]. Journal of the Chinese Rare Earth Society,2010,28(3):330-334.
[35] Yang P,Xue X,Meng Z,et al. Enhanced catalytic activity and stability of Ce doping on Cr supported HZSM-5 catalysts for deep oxidation of chlorinated volatile organic compounds[J]. Chemical Engineering Journal,2013,234(12):203-210.
[36] Satoh K,Sawada G,Shiozawa K. Catalytic cracking of n-butane over rare earth-loaded HZSM-5 catalysts[J]. Studies in Surfaceence & Catalysis,1999,125(99):449-456.
[37] Zapata P M C,Parentis M L,Gonzo E E,et al. Acid sites development on Cr³⁺/SiO₂ catalysts obtained by the sol-gel method and hydrothermal treatment:effect of calcination temperature[J]. Applied Catalysis A:General,2013,457(4):26-33.
[38] Botavina M,Agafonov Y,Gaidai N,et al. Towards efficient catalysts for the oxidative dehydrogenation of propane in the presence of CO₂:Cr/SiO₂ systems prepared by direct hydrothermal synthesis[J]. Catalysis Science & Technology,2016,6(3):840-850.
[39] Davydov L,Reddy E P,France P,et al. Transition-metal-substituted titania-loaded MCM-41 as photocatalysts for the degradation of aqueous organics in visible light[J]. Journal of Catalysis,2001,203(1):157-167.
[40] Pradier C M,Rodrigues F,Marcus P,et al. Supported chromia catalysts for oxidation of organic compounds:the state of chromia phase and catalytic performance[J]. Applied Catalysis B:Environmental,2000,27(2):73-85.
[41] Suga S,Imada S,Muro T,et al. La 4d and Mn core absorption magnetic circular dichroism,XPS and inverse photoemission spectroscopy of La_1-xSr_x MnO₃[J]. Journal of Electron Spectroscopy & Related Phenomena,1996,78:283-286.
[42] Kumar B V,Velchuri R,Devi V R,et al. Preparation,characterization,magnetic susceptibility (Eu,Gd and Sm) and XPS studies of Ln₂ZrTiO₇ (Ln=La,Eu,Dy and Gd)[J]. Journal of Solid State Chemistry,2010,184(2):264-272.
[43] SU J,YAO W Y,LIU Y,et al. The impact of CrO_x loading on reaction behaviors of dichloromethane (DCM) catalytic combustion over Cr-O/HZSM-5 catalysts[J]. Applied Surface Science,2017,396:1026-1033.