基于热分解动力学的中密度聚乙烯光氧老化行为分析

doi:10.16085/j.issn.1000-6613.2016.09.036

化工进展 ›› 2016, Vol. 35 ›› Issue (09): 2905-2911.DOI: 10.16085/j.issn.1000-6613.2016.09.036

基于热分解动力学的中密度聚乙烯光氧老化行为分析

代军¹, 晏华¹, 郭骏骏², 胡志德¹, 杨健健¹, 张寒松¹

1 中国人民解放军后勤工程学院化学与材料工程系, 重庆 401331;
2 73801部队, 江苏无锡 214000

收稿日期:2016-05-12 修回日期:2016-06-14 出版日期:2016-09-05 发布日期:2016-09-05
通讯作者: 晏华,教授,博士生导师,主要从事功能高分子材料和智能材料研究。E-mail:yanhuacq@sina.com。
作者简介:代军(1992-),男,硕士研究生,从事高分子材料环境失效及老化研究。E-mail:daijunhg@126.com。
基金资助:
国家863计划（2006AA03Z104）、国家科技支撑计划（2012BAF06B04）及重庆市研究生科研创新项目（CYS16239）。

Degradation behavior of medium density polyethylene under xeon photo-oxidation environment based on thermal degradation kinetics

DAI Jun¹, YAN Hua¹, GUO Junjun², HU Zhide¹, YANG Jianjian¹, ZHANG Hansong¹

1 Department of Chemistry & Material Engineering, Logistical Engineering University, Chongqing 401331, China;
2 Unit 73801, Wuxi 214000, Jiangsu, China

Received:2016-05-12 Revised:2016-06-14 Online:2016-09-05 Published:2016-09-05

摘要/Abstract

摘要： 在氙灯光氧环境中对中密度聚乙烯（MDPE）进行了64天的人工加速老化实验，以研究其在光氧环境下的老化行为及规律。本文利用热重分析法（TG）、衰减全反射红外光谱技术（ATR-FTIR）、力学试验和热分解动力学方法分别研究了中密度聚乙烯（MDPE）在光氧老化环境中热稳定性、化学结构、力学强度和包括活化能及指前因子的动力学参数的变化规律，探究了MDPE的老化行为及老化机理。结果表明：随老化时间增加，MDPE热稳定性能下降，分子结构中产生羰基、羟基等含氧基团，分子链断裂，支链增加，弯曲强度和冲击强度下降。老化64天后，弯曲强度和冲击强度分别下降了17.4%和47.3%。采用Coats-Redfern和Kissinger方法均表明MDPE活化能均随着老化时间增加而减小，且老化初期下降更明显，表明初期MDPE老化作用更加剧烈。

关键词: 动力学, 中密度聚乙烯, 氧化, 降解, 光氧老化, 活化能

Abstract: In this article,the artificial accelerated aging test of medium density polyethylene(MDPE) was carried out for 64 days under Xeon environment. The characteristics of thermal stability,chemical structure, mechanical properties and kinetics parameters including the activation energy and pre-exponential factor evolution of MDPE after photo-oxidation aging were studied by thermogravimetric analysis(TG),attenuated total reflection infrared spectroscopy(ATR-FTIR), mechanical test and thermal degradation kinetics methods including Coats-Redfern method and Kissinger method. The degradation behavior and aging mechanism of MDPE were explored. The results showed that during the aging period,the thermal stability decreased and the concentration of carbonyl and hydroxyl groups increased,the rupture of molecular chain was intensified while the bending and impact strength reduced gradually.After 64 days of aging,the bending and impact strength of MDPE declined by 17.4% and 47.3%,respectively.With the increase of aging time,the activation energy of MDPE decreased obviously and dominated in the early stage of aging,at which the aging phenomenon is more significant.

Key words: kinetics, medium density polyethylene (MDPE), oxidation, degradation, photo-oxidation

中图分类号:

O632.1

代军, 晏华, 郭骏骏, 胡志德, 杨健健, 张寒松. 基于热分解动力学的中密度聚乙烯光氧老化行为分析[J]. 化工进展, 2016, 35(09): 2905-2911.

DAI Jun, YAN Hua, GUO Junjun, HU Zhide, YANG Jianjian, ZHANG Hansong. Degradation behavior of medium density polyethylene under xeon photo-oxidation environment based on thermal degradation kinetics[J]. Chemical Industry and Engineering Progree, 2016, 35(09): 2905-2911.

参考文献

[1] BAEK B K,LA Y H,NA W J,et al. A kinetic study on the supercritical decrosslinking reaction of silane-crosslinked polyethylene in a continuous process[J]. Polymer Degradation and Stability,2016,126:75-80.
[2] CHENG J,PAN Y,YAO J,et al. Mechanisms and kinetics studies on the thermal decomposition of micron poly(methyl methacrylate) and polystyrene[J]. Journal of Loss Prevention in the Process Industries,2016,40(1):139-146.
[3] 郭骏骏,晏华,包河彬,等. 衰减全反射红外光谱法的高密度聚乙烯自然老化特性研究[J]. 光谱学与光谱分析,2015,35(6):1520-1524.
[4] YANG Rui,YU Jian,LIU Ying,et al. Effects of coupling agents on the natural aging behavior and oxidation profile of high-density polyethylene/sericite composites[J]. Journal of Applied Polymer Science,2008,107(1):610-617.
[5] KLEMENS G,SUSANNE B,GERNOT M. Characterization of theinfluence of specimen thickness on the aging behavior of a polypropylene based model compound[J]. Polymer Degradation and Stability,2015,111:185-193.
[6] 梁兴泉,刘举,林宝凤,等. 四氧化三铁存在下LDPE热分解动力学研究[J]. 应用化工,2012,41(6):1010-1014.
[7] 黄玲,王正洲,梁好均. 无卤阻燃聚乙烯的热分解动力学研究[J]. 中国科学技术大学学报,2006,36(1):34-36.
[8] JIN W P,SEA C O,HAE P L,et al. A kinetic analysis of thermal degradation of polymers using a dynamic method[J]. Polymer Degradation and Stability,2015,67:535-540.
[9] LIANG J Z,WANG J Z,TSUI G C,et al. Thermal decomposition kinetics of polypropylene composites filled with grapheme nanoplatelets[J]. Polymer Testing,2015,48:97-103.
[10] 刘如,曹金珍,彭尧. 木粉组分对木塑复合材料性能的影响研究进展[J]. 化工进展,2014,32(8):2072-2083.
[11] 姚培培,李琛,肖生苓. 紫外老化对聚苯乙烯泡沫性能的影响[J]. 化工学报,2014,65(11):4620-4626.
[12] 张敏华,李春华,姜浩锡. 热重质谱法研究聚苯乙烯热降解机理[J]. 化工进展,2008,27(4):609-612.
[13] MALLAKPOUR S,TAGHAVI M. Direct polyamidation in green media:studies on thermal degradation of novel orgaosoluble and optically active flame retardant polyamides[J]. Reactive & Functional Polymers,2009,69(3):206-215.
[14] DING Y,MCKINNON M B,STOLIAROV S I,et al. Determination of kinetics and thermodynamics of thermal decomposition for polymers containing reactive flame retardants:application to poly (lactic acid) blended with melamine and ammonium polyphosphate[J]. Polymer Degradation and Stability,2016,129:347-362.

[1]	黄益平, 李婷, 郑龙云, 戚傲, 陈政霖, 史天昊, 张新宇, 郭凯, 胡猛, 倪泽雨, 刘辉, 夏苗, 主凯, 刘春江. 三级环流反应器中气液流动与传质规律[J]. 化工进展, 2023, 42(S1): 175-188.
[2]	杨寒月, 孔令真, 陈家庆, 孙欢, 宋家恺, 王思诚, 孔标. 微气泡型下向流管式气液接触器脱碳性能[J]. 化工进展, 2023, 42(S1): 197-204.
[3]	杨建平. 降低HPPO装置反应系统原料消耗的PSE[J]. 化工进展, 2023, 42(S1): 21-32.
[4]	王福安. 300kt/a环氧丙烷工艺反应器降耗减排分析[J]. 化工进展, 2023, 42(S1): 213-218.
[5]	王胜岩, 邓帅, 赵睿恺. 变电吸附二氧化碳捕集技术研究进展[J]. 化工进展, 2023, 42(S1): 233-245.
[6]	张明焱, 刘燕, 张雪婷, 刘亚科, 李从举, 张秀玲. 非贵金属双功能催化剂在锌空气电池研究进展[J]. 化工进展, 2023, 42(S1): 276-286.
[7]	时永兴, 林刚, 孙晓航, 蒋韦庚, 乔大伟, 颜彬航. 二氧化碳加氢制甲醇过程中铜基催化剂活性位点研究进展[J]. 化工进展, 2023, 42(S1): 287-298.
[8]	谢璐垚, 陈崧哲, 王来军, 张平. 用于SO₂去极化电解制氢的铂基催化剂[J]. 化工进展, 2023, 42(S1): 299-309.
[9]	杨霞珍, 彭伊凡, 刘化章, 霍超. 熔铁催化剂活性相的调控及其费托反应性能[J]. 化工进展, 2023, 42(S1): 310-318.
[10]	郑谦, 官修帅, 靳山彪, 张长明, 张小超. 铈锆固溶体Ce_0.25Zr_0.75O₂光热协同催化CO₂与甲醇合成DMC[J]. 化工进展, 2023, 42(S1): 319-327.
[11]	戴欢涛, 曹苓玉, 游新秀, 徐浩亮, 汪涛, 项玮, 张学杨. 木质素浸渍柚子皮生物炭吸附CO₂特性[J]. 化工进展, 2023, 42(S1): 356-363.
[12]	高雨飞, 鲁金凤. 非均相催化臭氧氧化作用机理研究进展[J]. 化工进展, 2023, 42(S1): 430-438.
[13]	顾永正, 张永生. HBr改性飞灰对Hg⁰的动态吸附及动力学模型[J]. 化工进展, 2023, 42(S1): 498-509.
[14]	汪鹏, 张洋, 范兵强, 何登波, 申长帅, 张贺东, 郑诗礼, 邹兴. 高碳铬铁盐酸浸出过程工艺及动力学[J]. 化工进展, 2023, 42(S1): 510-517.
[15]	孙玉玉, 蔡鑫磊, 汤吉海, 黄晶晶, 黄益平, 刘杰. 反应精馏合成甲基丙烯酸甲酯工艺优化及节能[J]. 化工进展, 2023, 42(S1): 56-63.

基于热分解动力学的中密度聚乙烯光氧老化行为分析

Degradation behavior of medium density polyethylene under xeon photo-oxidation environment based on thermal degradation kinetics

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价