The effect of chlorine elimination on the structure of PtSnNa/Al2O3 catalyst for propane dehydrogenation

doi:10.16085/j.issn.1000-6613.2017-2047

Abstract

Abstract: The effect of chlorine elimination on the catalytic performance and structure of PtSnNa/Al₂O₃ catalyst for propane dehydrogenation was studied. The catalysts were characterized by XRD, N₂ adsorption-desorption, TPR, NH₃-TPD, TEM and Raman spectroscopy, respectively. The results showed that the chlorine elimination temperature affected the properties of the catalysts greatly, such as acidity, specific surface area, pore volume, mean pore diameter and the size of Pt particle. With the increase of the treatment temperature, the acidity the specific surface area and pore volume of the catalyst,dramatically decreased, whereas the mean pore diameter increased. Meantime, the extent of Pt sintering was aggravated. At higher treatment temperature, the catalyst has lower initial activity and higher propylene selectivity. But the stability increased firstly and then decreased with the raising of treatment temperature. The highest yield of propylene was obtained with the treatment temperature of 540℃, and the PtSnNa/Al₂O₃ catalyst exhibited the best performance of propane dehydrogenation and stability.

Key words: propane, hydrogen, hydrothermal, treatment temperature, chlorine elimination, sintering

摘要： 考察了氯的脱除对丙烷脱氢铂锡催化剂结构和反应性能的影响，并采用XRD、N₂吸脱附、TPR、NH₃-TPD、TEM和Raman等方法进行表征。结果表明，氯的脱除温度显著影响催化剂的酸性、孔体积、比表面积、孔径和Pt颗粒尺寸。随着处理温度的提高，催化剂酸性、比表面积、孔体积都呈现下降的趋势，平均孔径增加，Pt颗粒的烧结程度加剧。随着处理温度的增加，催化剂初活性逐渐降低，丙烯选择性增加，稳定性出现先增加后降低趋势。研究表明，氯的较佳的脱除温度为540℃，催化剂具有很好的脱氢性能和稳定性，收率最高。

关键词: 丙烷, 氢, 水热, 处理温度, 氯的脱除, 烧结

CLC Number:

O623.254.3

ZHANG Haijuan, ZHAO Yue, WAN Hai, GAO Jie, GAO Wenyi, ZHAO Zhenzhen. The effect of chlorine elimination on the structure of PtSnNa/Al₂O₃ catalyst for propane dehydrogenation[J]. Chemical Industry and Engineering Progress, 2018, 37(09): 3424-3429.

张海娟, 赵悦, 万海, 高杰, 高文艺, 赵珍珍. 氯的脱除对丙烷脱氢PtSnNa/Al₂O₃催化剂结构的影响[J]. 化工进展, 2018, 37(09): 3424-3429.

References

[1] IGLESIAS-JUEZ A, BEALE A M, MAAIJEN K, et al. A combined in situ time-resolved UV-vis, Raman and high-energy resolution X-ray absorption spectroscopy study on the deactivation behavior of Pt and PtSn propane dehydrogenation catalysts under industrial reaction conditions[J]. Journal of Catalysis, 2010, 276(2):268-279.
[2] DOMENICO S, IVANO M. Dehydrogenation of paraffins:synergies between catalystdesign and reactor engineering[J]. Catalysis Today, 2006, 111(1):133-139.
[3] TALLMAN M J, KLAVERS R R. North American olefin producers riding the shale gas wave[J]. Hydrocarbon Process, 2013, 4:37-40.
[4] 张海娟, 高杰, 张浩楠, 等. 低碳烷烃深加工制烯烃技术的研究进展[J]. 石油化工, 2016, 45(12):1411-1418. ZHANG Haijuan, GAO Jie, ZHANG Haonan, et al. Progresses in processes and catalysts for dehydrogenation of light paraffins to olefins[J]. Petrochemical Technology, 2016, 45(12):1411-1418.
[5] SAQER S M, KONDARIDES D I, VERYKIOS X E. Catalytic activity of supported platinum and metal oxide catalysts for toluene oxidation[J]. Topics in Catalysis, 2009, 52(5):517-527.
[6] ZANGENEH T F, TAEBA A, GHOLIVANDC K, et al. The effect of mixed HCl^- KCl competitive adsorbate on Pt adsorptionand catalytic properties of Pt-Sn/Al₂O₃ catalysts in propane dehydrogenation[J]. Applied Surface Science, 2015, 357(7):172-178.
[7] LIU J, LIU C, MA A, et al. Effects of Al₂O₃ phase and Cl component on dehydrogenation of propane[J]. Applied Surface Science, 2016, 368:233-240.
[8] ARTEAGA G J, ANDERSON J A, ROCHESTER C H. Effects of catalyst regeneration with and without chlorine on heptane reforming reactions over Pt/Al₂O₃ and Pt-Sn/Al₂O₃[J]. Journal of Catalysis, 1999, 187(1):219-229.
[9] ZHANG Y, ZHOU Y, LIU H, et al. Influence of the different dechlorination time on catalytic performances of PtSnNa/ZSM-5 catalyst for propane dehydrogenation[J]. Fuel Processing Technology, 2009, 90(12):1524-1531.
[10] COTTRIGHT D, LEVIN E, DUMESIC A. Kinetic studies of isobutane dehydrogenation and ispbutene over Pt-Sn-based catalysts[J]. Industrial & Engineering Chemistry Research, 1986, 37(8):1717-1723.
[11] GRACIA F J, MILLER J T, KROPF A J, et al. Kinetics, FTIR, and controlled atmosphere exafs study of the effect of chlorine on Pt-supported catalysts during oxidation reactions[J]. Journal of Catalysis, 2002, 209(2):341-354.
[12] PAULIS M, PEYRARD H, MONTES M. Influence of chlorine on the activity and stability of Pt/Al₂O₃ catalysts in the complete oxidation of toluene[J]. Journal of Catalysis, 2001, 199(1):30-40.
[13] KAMIUCHI N, TAGUCHI K, MATSUI T, et al. Sintering and redispersion of platinum catalysts supported on tin oxide[J]. Applied Catalysis B, 2009, 89(1/2):65-72.
[14] DUMONT M, CHOLLON G, DOURGES M A, et al. Chemical, microstructural and thermal analyses of a naphthalene-derived mesophase pitch[J]. Carbon, 2002, 40(9):1475-1486.
[15] BAO K V, SONG M B, AHN I Y, et al. Location and structure of coke generated over Pt-Sn/Al₂O₃ in propane dehydrogenation[J]. Journal of Industrial and Engineering Chemistry, 2011, 17(1):71-76.
[16] 张海娟, 王申, 高文艺, 等. 丙烷脱氢PtSn/Al₂O₃ 催化剂积炭行为研究[J]. 燃料化学学报, 2017, 45(9):1131-1136. ZHANG Haijuan, WANG Shen, GAO Wenyi, et al. Study of deactivated catalyst structure on PtSn/Al₂O₃ propane dehydrogenation catalyst[J]. Journal of Fuel Chemistry and Technology, 2017, 45(9):1131-1136.
[17] KUMAR M S, CHEN D, WALMSLEY J C, et al.Dehydrogenation of propane over Pt-SBA-15:effect of Pt particle size[J]. Catalysis Communications, 2008, 9(5):747-750.
[18] 李庆, 隋志军, 朱贻安, 等. Pt催化丙烷脱氢过程中结焦反应的粒径效应与Sn的作用[J]. 化工学报, 2013, 64(2):525-531. LI Qing, SUI Zhijun, ZHU Yian, et al. Formation of coke on Pt catalysts during propane dehydrogenation:effect of Pt particle size and Sn addition[J]. CIESC Journal, 2013, 64(2):525-531.

The effect of chlorine elimination on the structure of PtSnNa/Al₂O₃ catalyst for propane dehydrogenation

氯的脱除对丙烷脱氢PtSnNa/Al₂O₃催化剂结构的影响

PDF (PC)

Knowledge

Abstract

Cite this article

share this article

References

Related Articles 15

Recommended Articles

Metrics

Comments

[1]	SHI Yongxing, LIN Gang, SUN Xiaohang, JIANG Weigeng, QIAO Dawei, YAN Binhang. Research progress on active sites in Cu-based catalysts for CO₂ hydrogenation to methanol [J]. Chemical Industry and Engineering Progress, 2023, 42(S1): 287-298.
[2]	XIE Luyao, CHEN Songzhe, WANG Laijun, ZHANG Ping. Platinum-based catalysts for SO₂ depolarized electrolysis [J]. Chemical Industry and Engineering Progress, 2023, 42(S1): 299-309.
[3]	YANG Jianping. PSE for feedstock consumption reduction in reaction system of HPPO plant [J]. Chemical Industry and Engineering Progress, 2023, 42(S1): 21-32.
[4]	WANG Jingang, ZHANG Jianbo, TANG Xuejiao, LIU Jinpeng, JU Meiting. Research progress on modification of Cu-SSZ-13 catalyst for denitration of automobile exhaust gas [J]. Chemical Industry and Engineering Progress, 2023, 42(9): 4636-4648.
[5]	GE Quanqian, XU Mai, LIANG Xian, WANG Fengwu. Research progress on the application of MOFs in photoelectrocatalysis [J]. Chemical Industry and Engineering Progress, 2023, 42(9): 4692-4705.
[6]	SHI Keke, LIU Muzi, ZHAO Qiang, LI Jinping, LIU Guang. Properties and research progress of magnesium based hydrogen storage materials [J]. Chemical Industry and Engineering Progress, 2023, 42(9): 4731-4745.
[7]	LIU Muzi, SHI Keke, ZHAO Qiang, LI Jinping, LIU Guang. Research progress of solid hydrogen storage materials [J]. Chemical Industry and Engineering Progress, 2023, 42(9): 4746-4769.
[8]	WANG Xueting, GU Xia, XU Xianbao, ZHAO Lei, XUE Gang, LI Xiang. Effectiveness of hydrothermal pretreatment on valeric acid production during food waste fermentation [J]. Chemical Industry and Engineering Progress, 2023, 42(9): 4994-5002.
[9]	MAO Shanjun, WANG Zhe, WANG Yong. Group recognition hydrogenation: From concept to application [J]. Chemical Industry and Engineering Progress, 2023, 42(8): 3917-3922.
[10]	WANG Lanjiang, LIANG Yu, TANG Qiong, TANG Mingxing, LI Xuekuan, LIU Lei, DONG Jinxiang. Synthesis of highly dispersed Pt/HY catalyst by rapid pyrolysis of platinum precursors and its performance for deep naphthalene hydrogenation [J]. Chemical Industry and Engineering Progress, 2023, 42(8): 4159-4166.
[11]	GUO Jin, ZHANG Geng, CHEN Guohua, ZHU Ming, TAN Yue, LI Wei, XIA Li, HU Kun. Research progress on vehicle liquid hydrogen cylinder design [J]. Chemical Industry and Engineering Progress, 2023, 42(8): 4221-4229.
[12]	ZHANG Yajuan, XU Hui, HU Bei, SHI Xingwei. Preparation of NiCoP/rGO/NF electrocatalyst by eletroless plating for efficient hydrogen evolution reaction [J]. Chemical Industry and Engineering Progress, 2023, 42(8): 4275-4282.
[13]	WANG Xiaohan, ZHOU Yasong, YU Zhiqing, WEI Qiang, SUN Jinxiao, JIANG Peng. Synthesis and hydrocracking performance of Y molecular sieves with different crystal sizes [J]. Chemical Industry and Engineering Progress, 2023, 42(8): 4283-4295.
[14]	CHU Tiantian, LIU Runzhu, DU Gaohua, MA Jiahao, ZHANG Xiao’a, WANG Chengzhong, ZHANG Junying. Preparation and chemical degradability of organoguanidine-catalyzed dehydrogenation type RTV silicone rubbers [J]. Chemical Industry and Engineering Progress, 2023, 42(7): 3664-3673.
[15]	YU Shan, DUAN Yuangang, ZHANG Yixin, TANG Chun, FU Mengyao, HUANG Jinyuan, ZHOU Ying. Research progress of catalysts for two-step hydrogen sulfide decomposition to produce hydrogen and sulfur [J]. Chemical Industry and Engineering Progress, 2023, 42(7): 3780-3790.