Epoxidation of cyclohexene over SiO2 supported cobalt catalyst

doi:10.16085/j.issn.1000-6613.2018-2426

Abstract

Abstract:

SiO₂ （silica gel) supported cobalt oxide catalysts with different loadings were prepared by sedimentation precipitation method. The catalyst was characterized by X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), transmission electron microscopy (TEM), N₂ adsorption and desorption. The results showed that the cobalt-based oxide was Co₃O₄, and the cobalt oxide was uniformly distributed on the SiO₂ support. The particle size of most active component was between 2－10nm. The prepared catalyst is then used for the epoxidation of cyclohexene with cyclohexene and molecular oxygen as raw materials, isobutyraldehyde as catalytic auxiliary, and N,N-dimethylformamide (DMF) as reaction solvent . The reaction was carried out in an autoclave and the performance of the Co₃O₄/SiO₂ catalyst was compared with that of the cobalt catalysts supported on two different supports(ZrO₂ or Al₂O₃). The conversion of cyclohexene and the selectivity reached 66.56% and 71.03% under the experimental conditions of 0.20g 3% Co₃O₄/SiO₂, cyclohexene 2g, 50℃ and 4MPa.

Key words: silica, cobalt oxide catalyst, support, oxygen, cyclohexene, epoxidation, selectivity

摘要：

采用沉积沉淀法制备不同负载量的SiO₂（硅胶）负载钴氧化物催化剂，采用X射线衍射（XRD）、X射线光电子能谱（XPS）、透射电镜（TEM）、N₂吸脱附等手段对催化剂进行表征，结果表明钴系氧化物为Co₃O₄，并且钴氧化物均匀地负载在SiO₂（硅胶）载体上，其活性组分的粒子大小集中分布在2～10nm。将制备的催化剂应用于环己烯环氧化反应，以环己烯、分子氧为原料，异丁醛为催化助剂，N,N-二甲基甲酰胺（DMF）为反应溶剂，在高压釜中进行。同时将SiO₂负载钴氧化物催化剂与不同载体上制备的钴系催化剂进行比较，发现催化剂用量0.20g、环己烯2.00g、异丁醛3.50g、反应温度50℃、反应时间5h、氧气压力4MPa时，环己烯的转化率和环氧环己烷的选择性分别可达到66.56%和71.03%。

关键词: 二氧化硅, 钴氧化物催化剂, 载体, 分子氧, 环己烯, 环氧化, 选择性

CLC Number:

TQ426.8

Bin ZHANG,Huan LIU,Xuelong ZHANG,Zhen GUO,Yanghui QIAN,Lüqiang WANG,Xiaoyun RUAN,Bin SHI. Epoxidation of cyclohexene over SiO₂ supported cobalt catalyst[J]. Chemical Industry and Engineering Progress, 2019, 38(10): 4582-4587.

章彬,刘欢,张学龙,郭振,钱洋慧,王律强,阮小云,石斌. SiO₂负载钴系催化剂的环己烯环氧化性能[J]. 化工进展, 2019, 38(10): 4582-4587.

Figures/Tables 10

References 23

1	高鹏飞，张铁明，周媛，等 . Co(Ⅲ)官能化SBA-15的制备、表征及其催化环己烯环氧化[J]. 催化学报, 2011, 32(1): 166-171.
	GAO P F , ZHANG T M , ZHOU Y ,et al . Co(Ⅲ)-modified SBA-15: preparation, characterization and catalytic performance for epoxidation of cyclohexene[J]. Journal of Catalysis, 2011, 32(1): 166-171.
2	CAI Z , ZHU M , CHEN J , et al . Solvent-free oxidation of cyclohexene over catalysts Au/OMS-2 and Au/La-OMS-2 with molecular oxygen[J]. Catalysis Communications, 2010, 12(3): 197-201.
3	ANGELESCU E , IONESCU R , PAVEL O D , et al . Epoxidation of cyclohexene with O₂ and isobutyraldehyde catalysed by cobalt modified hydrotalcites[J]. Journal of Molecular Catalysis A: Chemical, 2010, 315(2): 178-186.
4	GODHANI D R , NAKUM H D , PARMAR D K , et al . Tuning of the reaction parameters to optimize allylic oxidation of cyclohexene catalyzed by zeolite-Y entrapped transition metal complexes[J]. Journal of Molecular Catalysis A: Chemical, 2016, 415: 37-55.
5	JIANG J , MA K , ZHENG Y , et al . Cobalt salophen complex immobilized into montmorillonite as catalyst for the epoxidation of cyclohexene by air[J]. Applied Clay Science, 2009, 45(3): 117-122.
6	孟静 . 烯烃环氧化反应研究[D]. 上海: 华东师范大学, 2009.
	MENG J . Study on epoxidation of alkenes[D]. Shanghai: East China Normal University, 2009.
7	韩飞 . 环氧环己烷的综合利用[J]. 精细石油化工, 1998(5): 1-5.
	HAN F . Comprehensive utilization of epoxycyclohexane[J]. Special Petrochemicals, 1998(5): 1-5.
8	贾义霞，徐亚雄，俞开新，等 . 1,2-环氧环己烷的合成及应用[J]. 化工时刊, 2002(4): 11-14.
	JIA Y X , XU Y X , YU K X , et al . Synthesis and application of 1,2-epoxycyclohexane[J]. Comments & Reviews C.I., 2002(4): 11-14.
9	WANG Y , DENG J , ZHANG C , et al . Epoxidation of cyclohexene with molecular oxygen by electrolysis combined with chemical catalysis[J]. Journal of the Iranian Chemical Society, 2014, 11(6): 1723-1729.
10	BELAIDI N , BEDRANE S , CHOUKCHOU-BRAHAM A , et al . Novel vanadium-chromium-bentonite green catalysts for cyclohexene epoxidation[J]. Applied Clay Science, 2015, 107: 14-20.
11	谢娟，魏雨，李艳廷，等 . 金属卟啉配合物在催化空气氧化环己烷反应中的应用[J]. 化工进展，2009, 28(3): 406-411.
	XIE J , WEI Y , LI Y T , et al . Application of metal porphyrin complexes in catalytic oxidation of cyclohexane[J]. Chemical Industry and Engineering Progress, 2009, 28(3): 406-411.
12	ZHANG P , LV X P , YANG M , et al . Epoxidation of cyclohexene with oxygen in ultrasound airlift loop reactor[J]. Chin. J. Chem. Eng., 2007, 15(2): 196-199.
13	李祖林，陈勤勇，董成北 . 环氧环己烷的研制[J]. 应用化工, 2003(5): 43-45.
	LI Z L , CHEN Q Y , DONG C B . Synthesis of cyclohexene oxide[J]. Applied Chemical Industry, 2003(5): 43-45.
14	雷忠华 . 1. 2-环氧环己烷[J]. 湖南化工, 1989, 27(2): 63.
	LEI Z H . 1, 2-epoxycyclohexane[J]. Hunan Chemical Industry, 1989, 27(2): 63.
15	王亚新，张结实 . 环氧环己烷的市场分析及应用前景[J]. 化工新型材料, 2008(6): 19-20.
	WANG Y X , ZHANG J S . Market analysis and application foreground for epoxycyclohexane[J]. New Chemical Materials, 2008(6): 19-20.
16	GHIACI M , AGHABARARI B , BOTELHO D R A M , et al . Efficient allylic oxidation of cyclohexene catalyzed by trimetallic hybrid nano-mixed oxide (Ru/Co/Ce)[J]. Applied Catalysis A: General, 2011, 393(1/2): 225-230.
17	ZHOU X , JI H , XU J , et al . Enzymatic-like mediated olefins epoxidation by molecular oxygen under mild conditions[J]. Tetrahedron Letters, 2007, 48(15): 2691-2695.
18	DOU J , TAO F F . Selective epoxidation of cyclohexene with molecular oxygen on catalyst of nanoporous Au integrated with MoO₃ nanoparticles[J]. Applied Catalysis A: General, 2017, 529: 134-142.
19	常慧 . 烯烃环氧化技术及其催化剂发展概述[J]. 石油化工技术与经济, 2015(6): 45-49.
	CHANG H . Review of olefin epoxidation technology and its catalyst development[J]. Technology & Economics in Petrochemicals, 2015(6): 45-49.
20	章亚东，蒋登高，高晓蕾 . 环己烯液相环氧化催化剂的研究进展[J]. 现代化工, 2002, 22(9): 20-23.
	ZHANG Y D , JIANG D G , GAO X L . Research progress of cyclohexene liquid phase epoxidation catalyst [J]. Modern Chemical Industry , 2002, 22(9): 20-23.
21	宋国强，郑晓林，陶菊凤 . 分子氧/乙醛/过渡金属盐体系氧化环己烯的研究[J]. 化工进展, 2004, 23(6): 638-640.
	SONG G Q , ZHENG X L , TAO J F , et al . Study on oxidation of cyclohexene by molecular oxygen/acetaldehyde/transition metal salt system[J]. Chemical Industry and Engineering Progress, 2004, 23(6): 638-640.
22	杨国玉，朱海林，周文峰，等 . 内标法测定环己烯氧化产物中环己烯和环氧环己烷含量[C]//首届中国中西部地区色谱学术交流会. 2006: 427-430.
	YANG G Y , ZHU H L , ZHOU W F , et al . Determination of cyclohexene and epoxycyclohexane in cyclohexene oxidation products by internal standard method[C]// The First China Central and Western Region Chromatography Academic Exchange Conference. 2006: 427-430.
23	BIESINGER M C , PAYNE B P , GROSVENOR A P , et al . Resolving surface chemical states in XPS analysis of first row transition metals, oxides and hydroxides: Cr, Mn, Fe, Co and Ni[J]. Applied Surface Science, 2011, 257(7): 2717-2730.

催化剂	比表面积/m²·g^-1	孔体积/cm³·g^-1	孔径/nm
1%Co₃O₄/SiO₂	362.14	1.05	10.16
3%Co₃O₄/SiO₂	343.60	0.97	10.15
5%Co₃O₄/SiO₂	320.36	0.86	10.15

催化剂	比表面积/m²·g^-1	孔体积/cm³·g^-1	孔径/nm
1%Co₃O₄/SiO₂	362.14	1.05	10.16
3%Co₃O₄/SiO₂	343.60	0.97	10.15
5%Co₃O₄/SiO₂	320.36	0.86	10.15

催化剂用量/g	转化率/%	选择性/%
催化剂用量/g	转化率/%	环氧环己烷	环己烯醇	环己烯酮
0	18.15	56.12	15.32	28.56
0.10	42.55	60.36	16.25	23.39
0.15	56.36	58.16	12.36	29.48
0.20	62.38	69.23	12.01	18.76
0.25	63.02	62.33	12.91	24.76

催化剂用量/g	转化率/%	选择性/%
催化剂用量/g	转化率/%	环氧环己烷	环己烯醇	环己烯酮
0	18.15	56.12	15.32	28.56
0.10	42.55	60.36	16.25	23.39
0.15	56.36	58.16	12.36	29.48
0.20	62.38	69.23	12.01	18.76
0.25	63.02	62.33	12.91	24.76

催化剂负载量	转化率/%	选择性/%
催化剂负载量	转化率/%	环氧环己烷	环己烯醇	环己烯酮
1%Co₃O₄/SiO₂	49.45	65.20	15.06	19.74
2%Co₃O₄/SiO₂	58.78	55.49	23.44	21.07
3%Co₃O₄/SiO₂	62.38	69.23	12.01	18.76
4%Co₃O₄/SiO₂	60.88	63.67	16.54	19.79
5%Co₃O₄/SiO₂	58.46	63.73	15.86	20.41

Epoxidation of cyclohexene over SiO₂ supported cobalt catalyst

SiO₂负载钴系催化剂的环己烯环氧化性能

RichHTML

PDF (PC)

Knowledge

Abstract

Cite this article

share this article

Figures/Tables 10

References 23

Related Articles 15

Recommended Articles

Metrics

Comments

[1]	WANG Fu'an. Consumption and emission reduction of the reactor of 300kt/a propylene oxide process [J]. Chemical Industry and Engineering Progress, 2023, 42(S1): 213-218.
[2]	ZHENG Qian, GUAN Xiushuai, JIN Shanbiao, ZHANG Changming, ZHANG Xiaochao. Photothermal catalysis synthesis of DMC from CO₂ and methanol over Ce_0.25Zr_0.75O₂ solid solution [J]. Chemical Industry and Engineering Progress, 2023, 42(S1): 319-327.
[3]	CUI Shoucheng, XU Hongbo, PENG Nan. Simulation analysis of two MOFs materials for O₂/He adsorption separation [J]. Chemical Industry and Engineering Progress, 2023, 42(S1): 382-390.
[4]	GAO Yufei, LU Jinfeng. Mechanism of heterogeneous catalytic ozone oxidation:A review [J]. Chemical Industry and Engineering Progress, 2023, 42(S1): 430-438.
[5]	ZHU Jie, JIN Jing, DING Zhenghao, YANG Huipan, HOU Fengxiao. Modification of CaSO₄ oxygen carrier by Zhundong coal ash in chemical looping gasification and its mechanism [J]. Chemical Industry and Engineering Progress, 2023, 42(9): 4628-4635.
[6]	GAO Yanjing. Analysis of international research trend of single-atom catalysis technology [J]. Chemical Industry and Engineering Progress, 2023, 42(9): 4667-4676.
[7]	ZHANG Qi, ZHAO Hong, RONG Junfeng. Research progress of anti-toxicity electrocatalysts for oxygen reduction reaction in PEMFC [J]. Chemical Industry and Engineering Progress, 2023, 42(9): 4677-4691.
[8]	WANG Shangbin, OU Hongxiang, XUE Honglai, CAO Haizhen, WANG Junqi, BI Haipu. Effect of xanthan gum and nano silica on the properties of fluorine-free surfactant mixed solution foam [J]. Chemical Industry and Engineering Progress, 2023, 42(9): 4856-4862.
[9]	SONG Weitao, SONG Huiping, FAN Zhenlian, FAN Biao, XUE Fangbin. Research progress of fly ash in anti-corrosion coatings [J]. Chemical Industry and Engineering Progress, 2023, 42(9): 4894-4904.
[10]	ZHU Chuanqiang, RU Jinbo, SUN Tingting, XIE Xingwang, LI Changming, GAO Shiqiu. Characteristics of selective non-catalytic reduction of NO _x with solid polymer denitration agent [J]. Chemical Industry and Engineering Progress, 2023, 42(9): 4939-4946.
[11]	MAO Shanjun, WANG Zhe, WANG Yong. Group recognition hydrogenation: From concept to application [J]. Chemical Industry and Engineering Progress, 2023, 42(8): 3917-3922.
[12]	WANG Baoying, WANG Huangying, YAN Junying, WANG Yaoming, XU Tongwen. Research progress of polymer inclusion membrane in metal separation and recovery [J]. Chemical Industry and Engineering Progress, 2023, 42(8): 3990-4004.
[13]	XIANG Yang, HUANG Xun, WEI Zidong. Recent progresses in the activity and selectivity improvement of electrocatalytic organic synthesis [J]. Chemical Industry and Engineering Progress, 2023, 42(8): 4005-4014.
[14]	WANG Yaogang, HAN Zishan, GAO Jiachen, WANG Xinyu, LI Siqi, YANG Quanhong, WENG Zhe. Strategies for regulating product selectivity of copper-based catalysts in electrochemical CO₂ reduction [J]. Chemical Industry and Engineering Progress, 2023, 42(8): 4043-4057.
[15]	WANG Xiaohan, ZHOU Yasong, YU Zhiqing, WEI Qiang, SUN Jinxiao, JIANG Peng. Synthesis and hydrocracking performance of Y molecular sieves with different crystal sizes [J]. Chemical Industry and Engineering Progress, 2023, 42(8): 4283-4295.

催化剂	转化率/%	选择性/%
催化剂	转化率/%	环氧环己烷	环己烯醇	环己烯酮
3%Co₃O₄/Al₂O₃	50.43	68.61	14.90	16.47
3%Co₃O₄/SiO₂	66.56	71.03	10.03	18.94
3%Co₃O₄/ZrO₂	42.45	65.31	12.35	22.34

催化剂	转化率/%	选择性/%
催化剂	转化率/%	环氧环己烷	环己烯醇	环己烯酮
3%Co₃O₄/Al₂O₃	50.43	68.61	14.90	16.47
3%Co₃O₄/SiO₂	66.56	71.03	10.03	18.94
3%Co₃O₄/ZrO₂	42.45	65.31	12.35	22.34