Selective catalytic reduction of nitric oxide with propylene over CuCe-SAPO-34 catalysts under diesel engine exhaust

doi:10.16085/j.issn.1000-6613.2023-0746

Abstract

Abstract:

CuCe-SAPO-44 zeolite catalysts were prepared by incipient wet impregnation method, and their activities of selective catalytic reduction of nitric oxide with propylene (C₃H₆-SCR) were investigated under lean burning condition. These catalysts were characterized by X-ray diffraction (XRD), N₂ adsorption-desorption, UV-vis spectroscopy (UV-Vis), H₂ temperature-programmed reduction (H₂-TPR) and NH₃ temperature-programmed desorption (NH₃-TPD). The results had shown that the interaction between the introduced cerium and copper species was beneficial for generating more isolated Cu²⁺ species which improved the low-temperature redox performance of the CuCe-SAPO-34 zeolite catalysts, and thus enhanced the low-temperature SCR activity. There were abundant Lewis acid sites on the skeleton of the bimetallic zeolite catalysts, which were favorable for the adsorption and activation of NO _x and C₃H₆. When Cu∶Ce=4∶2, CuCe-SAPO-34 exhibited the best de-NO _x activity with a conversion of NO _x more than at 90% when the diesel engine exhaust contained 10% O₂ and 5% H₂O at 250℃.

Key words: zeolite catalysts, cerium, selective catalytic reduction, nitrogen oxide, propylene

摘要：

采用等体积浸渍法制备CuCe-SAPO-44分子筛催化剂，用于选择性催化丙烯还原柴油车尾气氮氧化物（C₃H₆-SCR）。采用X射线衍射（XRD）、N₂吸附-脱附、紫外可见光谱（UV-Vis）、H₂程序升温还原（H₂-TPR）和NH₃程序升温脱附（NH₃-TPD）等方法对催化剂的物理化学性质进行表征。研究表明，引入的铈与铜物种之间存在相互作用，有利于生成更多的孤立Cu²⁺物种，提高了分子筛催化剂的低温氧化还原性能，从而提高了CuCe-SAPO-34的低温脱硝活性。同时，双金属分子筛骨架上具有丰富的Lewis酸性位，有助于C₃H₆和NO _x 的吸附和活化。当Cu∶Ce=4∶2时，CuCe-SAPO-34催化剂具有最佳的脱硝性能，在含有10%O₂和5%H₂O的柴油车尾气氛围中，在250℃最高能实现90%以上的脱硝效率。

关键词: 分子筛催化剂, 铈, 选择催化还原, 氮氧化物, 丙烯

CLC Number:

X511

ZHOU Hao, WANG Xurui, ZHAO Huishuang, WEN Nini, SU Yaxin. Selective catalytic reduction of nitric oxide with propylene over CuCe-SAPO-34 catalysts under diesel engine exhaust[J]. Chemical Industry and Engineering Progress, 2024, 43(6): 3093-3099.

周皞, 王旭瑞, 赵辉爽, 温妮妮, 苏亚欣. CuCe-SAPO-34选择性催化丙烯还原柴油车尾气氮氧化物[J]. 化工进展, 2024, 43(6): 3093-3099.

Figures/Tables 9

References 27

1	中华人民共和国生态环境部. 中国机动车污染防治年报[J]. 2022.
	Ministry of Ecology and Environmental Protection of the People's Republic of China, China Mobile Source Environmental Management Annual Report[J]. 2022.
2	刘颖帅, 胡广地, 齐宝华. 固态SCR技术降低柴油机尾气NO _x 的排放[J]. 环境工程学报, 2021, 15(2): 626-634.
	LIU Yingshuai, HU Guangdi, QI Baohua. Reduction of NO _x emissions from diesel engines by solid SCR technology[J]. Chinese Journal of Environmental Engineering, 2021, 15(2): 626-634.
3	王晋刚, 张剑波, 唐雪娇, 等. 机动车尾气脱硝催化剂Cu-SSZ-13的改性研究进展[J]. 化工进展, 2023，42（9）：4636-4648.
	WANG Jingang, ZHANG Jianbo, TANG Xuejiao, et al. Research progress on modification of Cu-SSZ-13 catalyst for denitration of automobile exhaust gas[J]. Chemical Industry and Engineering Progress, 2023， 42（9）：4636-4648.
4	ZHANG Ling, WU Qinming, MENG Xiangju, et al. Recent advances in the preparation of zeolites for the selective catalytic reduction of NO _x in diesel engines[J]. Reaction Chemistry & Engineering, 2019, 4(6): 975-985.
5	张恒, 周皞, 温妮妮, 等. Cu-SAPO-44选择性催化丙烯还原NO性能研究 [J]. 燃料化学学报, 2022, 50(8): 1064-1074.
	ZHANG Heng, ZHOU Hao, WEN Nini, et al. Selective catalytic reduction of nitric oxide with propylene over one-step synthesized Cu-SAPO-44 catalysts[J]. Journal of Fuel Chemistry and Technology, 2022, 50(8): 1064-1074.
6	宁淑英, 苏亚欣, 杨洪海, 等. 用于HC-SCR还原NO _x 的Cu基分子筛催化剂研究进展[J]. 化工进展, 2023, 42(3): 1308-1320.
	NING Shuying， SU Yaxin， YANG Honghai, et al. Research progress on supported Cu-based zeolite catalysts for the selective catalytic reduction of NO _x with hydrocarbons[J]. Chemical Industry and Engineering Progress, 2023, 42(3): 1308-1320.
7	YANG Di, ZHOU Hao, WANG Congying, et al. NO selective catalytic reduction with propylene over one-pot synthesized Fe-SAPO-34 catalyst under diesel exhaust conditions[J]. Fuel, 2021, 290:119822.
8	GAO Zhongnan, ZHAO Dongyue, YANG Yuexi, et al. Influence of copper locations on catalytic properties and activities of Cu/SAPO-34 in C₃H₆-SCR[J]. Industrial & Engineering Chemistry Research, 2021, 60(19): 6940-6949.
9	ZHOU Jiayi, LI Nan, WANG Xurui, et al. Effects of the preparation method of Cu-SAPO-34 catalysts in de-NO _x SCR by propylene[J]. Journal of Environmental Chemical Engineering, 2022, 10(4): 108160.
10	殷成阳, 侯铭, 杨爽, 等. 过渡金属改性Cu-SSZ-13分子筛脱硝催化剂研究进展[J]. 化工进展, 2023, 42(6):2963-2974.
	YIN Chengyang, HOU Ming, YANG Shuanget al. Research progress in transition metals modified Cu-SSZ-13 zeolite denitration catalysts[J]. Chemical Industry and Engineering Progress, 2023, 42(6):2963-2974.
11	周皞, 苏亚欣, 邓文义, 等. 负载金属分子筛类催化剂上HC-SCR研究进展[J]. 环境科学与技术, 2015, 38(10): 64-73.
	ZHOU Hao, SU Yaxin, DENG Wenyi, et al. A review of HC-SCR over metal-based zeolite catalysts[J]. Environmental Science & Technology, 2015, 38(10): 64-73.
12	CAO Yi, ZOU Sha, LAN Li, et al. Promotional effect of Ce on Cu-SAPO-34 monolith catalyst for selective catalytic reduction of NO _x with ammonia[J]. Journal of Molecular Catalysis A: Chemical, 2015, 398: 304-311.
13	刘崇飞, 王学涛, 邢利利, 等. 双金属Cu-Ce/SAPO-34催化剂的制备及其NH₃-SCR脱硝性能研究[J]. 燃料化学学报, 2022, 50(10): 1316-1323.
	LIU Chongfei, WANG Xuetao, XING Lili, et al. Study on Preparation and denitrification performance of NH₃-SCR of bimetallic Cu-Ce/SAPO-34 catalyst[J]. Journal of Fuel Chemistry and Technology, 2022, 2022, 50(10): 1316-1323.
14	张雷, 孙敬方, 熊燕, 等. CeO₂表面分散态WO₃的氨选择性催化还原性能[J]. 催化学报, 2017, 38(10): 1749-1758.
	ZHANG Lei, SUN Jingfang, XIONG Yan, et al. Catalytic performance of highly dispersed WO₃ loaded on CeO₂ in the selective catalytic reduction of NO by NH₃ [J]. Chinese Journal of Catalysis, 2017, 38(10): 1749-1758.
15	ZHOU Xiaoming, CHEN Zhuoyuan, GUO Zhiyong, et al. One-pot hydrothermal synthesis of dual metal incorporated CuCe-SAPO-34 zeolite for enhancing ammonia selective catalytic reduction[J]. Journal of Hazardous Materials, 2021, 405: 124177.
16	ZHANG Qiongdan, WANG Qiongsheng, WANG Shiming. Efficient heterogeneous Fenton-like catalysis of Fe-doped SAPO-44 zeolite synthesized from bauxite and rice husk[J]. Chemical Physics Letters, 2020, 753: 137598.
17	NIU Can, SHI Xiaoyan, LIU Fudong, et al. High hydrothermal stability of Cu-SAPO-34 catalysts for the NH₃-SCR of NO _x [J]. Chemical Engineering Journal, 2016, 294: 254-263.
18	CAO Yi, FENG Xi, XU Haidi, et al. Novel promotional effect of yttrium on Cu-SAPO-34 monolith catalyst for selective catalytic reduction of NO _x by NH₃ (NH₃-SCR)[J]. Catalysis Communications, 2016, 76: 33-36.
19	LIU Lianjun, CAO Yuan, SUN Wenjing, et al. Morphology and nanosize effects of ceria from different precursors on the activity for NO reduction[J]. Catalysis Today, 2011, 175(1): 48-54.
20	SHAN Yulong, SHI Xiaoyan, DU Jinpeng, et al. Cu-exchanged RTH-type zeolites for NH₃-selective catalytic reduction of NO _x : Cu distribution and hydrothermal stability[J]. Catalysis Science & Technology, 2019, 9(1): 106-115.
21	HUANG Bichun, FANG Hansun, HUANG Huajun, et al. A one-pot synthesis of Cu-modified Mn-rich MnSAPO-34 catalyst with excellent low temperature NH₃-selective catalytic reduction performance and H₂O resistance[J]. Journal of Industrial and Engineering Chemistry, 2021, 95: 252-259.
22	周皞, 杨迪, 王聪颖, 等. 一步水热合成Cu-SAPO-34选择性催化丙烯还原氮氧化物[J]. 无机化学学报, 2020, 36(10): 1997-2004.
	ZHOU Hao, YANG Di, WANG Congying, et al. Selective catalytic reduction of nitric oxide with propylene over one-step synthesized Cu-SAPO-34 catalysts[J]. Chinese Journal of Inorganic Chemistry. 2020, 36(10):1997-2004.
23	GAO Feng, WASHTON Nancy M, WANG Yilin, et al. Effects of Si/Al ratio on Cu/SSZ-13 NH₃-SCR catalysts: Implications for the active Cu species and the roles of Brønsted acidity[J]. Journal of Catalysis, 2015, 331: 25-38.
24	LEZCANO-GONZALEZ I, DEKA U, ARSTAD B, et al. Determining the storage, availability and reactivity of NH₃ within Cu-Chabazite-based Ammonia Selective Catalytic Reduction systems[J]. Physical Chemistry Chemical Physics, 2014, 16(4): 1639-1650.
25	WEN Nini, SU Yaxin, DENG Wenyi, et al. Synergy of CuNiFe-LDH based catalysts for enhancing low-temperature SCR-C₃H₆ performance: Surface properties and reaction mechanism[J]. Chemical Engineering Journal, 2022, 438: 135570.
26	LI Junhua, ZHU Yongqing, KE Rui, et al. Improvement of catalytic activity and sulfur-resistance of Ag/TiO₂-Al₂O₃ for NO reduction with propene under lean burn conditions[J]. Applied Catalysis B: Environmental, 2008, 80(3/4): 202-213.
27	BRANDENBERGER Sandro, Oliver KRÖCHER, WOKAUN Alexander, et al. The role of Brønsted acidity in the selective catalytic reduction of NO with ammonia over Fe-ZSM-5[J]. Journal of Catalysis, 2009, 268(2): 297-306.

样品	元素质量分数/%
样品	Al	Cu	P	Si	Ce
4Cu4Ce-SAPO-34	16.72	4.19	16.72	3.98	4.17
4Cu2Ce-SAPO-34	17.76	4.28	17.95	4.13	2.04
4Cu1Ce-SAPO-34	18.26	4.39	18.47	4.28	1.14
4Ce-SAPO-34	17.53	—	17.63	4.05	3.98
4Cu-SAPO-34	15.75	4.01	16.35	3.46	—

样品	元素质量分数/%
样品	Al	Cu	P	Si	Ce
4Cu4Ce-SAPO-34	16.72	4.19	16.72	3.98	4.17
4Cu2Ce-SAPO-34	17.76	4.28	17.95	4.13	2.04
4Cu1Ce-SAPO-34	18.26	4.39	18.47	4.28	1.14
4Ce-SAPO-34	17.53	—	17.63	4.05	3.98
4Cu-SAPO-34	15.75	4.01	16.35	3.46	—

样品	比表面积 /m²·g^-1	微孔面积 /m²·g^-1	孔隙体积 /cm³·g^-1
4Cu4Ce-SAPO-34	421.2	395.6	0.148
4Cu2Ce-SAPO-34	555.7	535.0	0.198
4Cu1Ce-SAPO-34	557.7	544.2	0.201
4Cu-SAPO-34	592.5	575.9	0.225
4Ce-SAPO-34	613.5	581.7	0.214

样品	比表面积 /m²·g^-1	微孔面积 /m²·g^-1	孔隙体积 /cm³·g^-1
4Cu4Ce-SAPO-34	421.2	395.6	0.148
4Cu2Ce-SAPO-34	555.7	535.0	0.198
4Cu1Ce-SAPO-34	557.7	544.2	0.201
4Cu-SAPO-34	592.5	575.9	0.225
4Ce-SAPO-34	613.5	581.7	0.214

[1]	GAO Fei, LIU Zhisong, PAN Keke, LIU Minmin, DAI Bin, DAN Jianming, YU Feng. Vermiculite-supported FeCe bimetallic catalyst for selective catalytic reduction of NO with CO [J]. Chemical Industry and Engineering Progress, 2024, 43(4): 1851-1862.
[2]	WANG Xudong, LIU Dunyu, XU Kailong, LIU Qiuqi, FAN Yunpei, JIN Jing. Impacts of CeO₂ oxygen carriers on the conversion of mercury in chemical looping combustion of coal [J]. Chemical Industry and Engineering Progress, 2024, 43(4): 2191-2200.
[3]	WANG Xiong, KANG Wenqian, REN Yue, QIAO Tongsen, ZHANG Peng, HUANG Anping, LI Guangquan. Pilot scale production of porous organic polymers and their application in polyolefin catalysts [J]. Chemical Industry and Engineering Progress, 2024, 43(3): 1412-1417.
[4]	WANG Lele, YANG Wanrong, YAO Yan, LIU Tao, HE Chuan, LIU Xiao, SU Sheng, KONG Fanhai, ZHU Canghai, XIANG Jun. Influence of spent SCR catalyst blending on the characteristics and deNO _x performance for new SCR catalyst [J]. Chemical Industry and Engineering Progress, 2023, 42(S1): 489-497.
[5]	DENG Liping, SHI Haoyu, LIU Xiaolong, CHEN Yaoji, YAN Jingying. Non-noble metal modified vanadium titanium-based catalyst for NH₃-SCR denitrification simultaneous control VOCs [J]. Chemical Industry and Engineering Progress, 2023, 42(S1): 542-548.
[6]	YANG Jianping. PSE for feedstock consumption reduction in reaction system of HPPO plant [J]. Chemical Industry and Engineering Progress, 2023, 42(S1): 21-32.
[7]	WANG Fu'an. Consumption and emission reduction of the reactor of 300kt/a propylene oxide process [J]. Chemical Industry and Engineering Progress, 2023, 42(S1): 213-218.
[8]	LAI Shini, JIANG Lixia, LI Jun, HUANG Hongyu, KOBAYASHI Noriyuki. Research progress of ammonia blended fossil fuel [J]. Chemical Industry and Engineering Progress, 2023, 42(9): 4603-4615.
[9]	LI Jia, FAN Xing, CHEN Li, LI Jian. Research progress of simultaneous removal of NO _x and N₂O from the tail gas of nitric acid production [J]. Chemical Industry and Engineering Progress, 2023, 42(7): 3770-3779.
[10]	ZHANG Wei, QIN Chuan, XIE Kang, ZHOU Yunhe, DONG Mengyao, LI Jie, TANG Yunhao, MA Ying, SONG Jian. Application and performance enhancement challenges of H₂-SCR modified platinum-based catalysts for low-temperature denitrification [J]. Chemical Industry and Engineering Progress, 2023, 42(6): 2954-2962.
[11]	YIN Chengyang, HOU Ming, YANG Shuang, MAO Di, LIU Junyan. Research progress in transition metals modified Cu-SSZ-13 zeolite denitration catalysts [J]. Chemical Industry and Engineering Progress, 2023, 42(6): 2963-2974.
[12]	HE Chuan, WU Guoxun, LI Ang, ZHANG Fajie, BIAN Zijun, LU Chengzheng, WANG Lipeng, ZHAO Min. Characteristics of calcium and magnesium deactivation and regeneration of waste incineration SCR catalyst [J]. Chemical Industry and Engineering Progress, 2023, 42(5): 2413-2420.
[13]	WANG Zizong, LIU Gang, WANG Zhenwei. Progress and reflection on process intensification technology for ethylene/propylene production [J]. Chemical Industry and Engineering Progress, 2023, 42(4): 1669-1676.
[14]	CHANG Xiaoqing, PENG Donglai, LI Dongyang, ZHANG Yanwu, WANG Jing, ZHANG Yatao. Recent progress on mixed matrix membrane for efficient C₃H₆/C₃H₈ separation [J]. Chemical Industry and Engineering Progress, 2023, 42(4): 1961-1973.
[15]	LAI Huaidong, CHENG Deshu, WANG Jian, LUO Juxiang. Preparation and application of α-methyl styrene maleic anhydride copolymer microspheres immobilized β-cyclodextrin [J]. Chemical Industry and Engineering Progress, 2023, 42(4): 2038-2046.