Ce掺杂ZnO光催化氧化脱硫性能

doi:10.16085/j.issn.1000-6613.2018-0261

摘要/Abstract

摘要： 以水热反应制备前体和随后高温煅烧的方法制得了稀土元素Ce掺杂的ZnO光催化剂。利用X射线衍射、紫外可见、扫描电镜和能谱仪（EDS）对样品进行了物理性质表征，考察了催化剂制备条件、催化剂中Ce、Zn掺杂比和实验条件对催化剂光催化氧化脱硫性能的影响。结果表明，Ce和Zn的摩尔比对Zn_（1-x）Ce_xO催化剂的光催化氧化脱硫性能有显著影响；最佳条件100℃水热反应4h、300℃煅烧2h，制得的Zn_0.89Ce_0.11O催化剂在模拟油200mL（含硫量300mg/L）、n（O）/n（S）为39（H₂O₂ 15mL）、催化剂0.3g和紫外光照射1.5h的条件下脱硫率高达98.9%，经过5次再生循环使用后脱硫率没有明显降低。

关键词: 水热合成, 铈, 氧化锌, 光催化, 氧化, 脱硫

Abstract: The rare earth Ce doped ZnO has been prepared with the precursor prepared by hydrothermal method and subsequently calcinated at high temperature. The samples were characterized by X-ray diffraction (XRD), UV-vis, field emission scanning electron microscopy (FESEM) and EDS, respectively. The effects of various experimental parameters on the photocatalytic oxidation desulfurization were investigated. The results showed that the molar ratio of Ce to Zn had significant influence on the photocatalytic oxidation desulfurization properties of the Zn_(1-x)Ce_xO catalyst. The optimum preparation parameters were hydrothermal time of 4h at 100℃, calcination treatment of 300℃ at 2h to the Zn_0.89Ce_0.11O catalyst, 200mL model oil (sulfur content of 300mg/L), n(O)/n(S) molar ratio of 39 (H₂O₂ 15mL), 0.3g catalyst and irradiated under UV-light for 1.5h. The maximum desulfurization rate of the model oil was 98.9% under the above optimum conditions. The desulfurization rate of the catalyst did not decrease obviously after reused for five times.

Key words: hydrothermal method, cerium, zinc oxide, photocatalytic, oxidation, desulfurization

中图分类号:

TQ028.2

梁鹏举, 管荣新, 王伟华, 秦少伟, 穆金城, 丁慧萍, 姜建辉. Ce掺杂ZnO光催化氧化脱硫性能[J]. 化工进展, 2018, 37(12): 4701-4708.

LIANG Pengju, GUAN Rongxin, WANG Weihua, QIN Shaowei, MU Jincheng, DING Huiping, JIANG Jianhui. Photocatalytic oxidation desulfurization properties of Ce-doped ZnO[J]. Chemical Industry and Engineering Progress, 2018, 37(12): 4701-4708.

参考文献

[1] HE J, WU P W, WU Y C, et al. Taming interfacial oxygen vacancies of amphiphilic tungsten oxide for enhanced catalysis in oxidation desulfurization[J]. ACS Sustain. Chem. Eng., 2017, 5(10):8930-8938.
[2] ZHAO R J, WANG J L, ZHANG D D, et al. Deep catalytic oxidative desulfurization of model fuel based on modified iron porphyrins in ionic liquids:anionic ligand effect[J]. ACS Sustain. Chem. Eng., 2017, 5(3):2050-2055.
[3] ZHAO H, BAKER G A. Oxidative desulfurization of fuels using ionic liquids:a review[J]. Front. Chem. Sci. Eng., 2015, 9(3):262-279.
[4] BAZYARI A, KHODADADI A A, HAGHIGHAT M A, et al. Microporous titania-silica nanocomposite catalyst-adsorbent for ultra-deep oxidative desulfurization[J]. Appl. Catal. B:Environ., 2016, 180:65-77.
[5] 张海燕, 代跃利, 蔡蕾. 杂多酸催化剂催化氧化脱硫研究进展[J].化工进展, 2013, 32(4):809-815. ZHANG H Y, DAI Y L, CAI L. Research progress of heteropoly acid catalyzed oxidative desulfurization[J]. Chemical Industry and Engineering Progress, 2013, 32(4):809-815.
[6] 于凤丽, 唐会宝, 柳春玉,等. 氧化-温控双功能离子液体催化O₂氧化模拟柴油脱硫[J]. 化学学报, 2014, 72:1152-1156. YU F L, TANG H B, LIU C Y, et al. Oxidative desulfurization of model diesel with O₂ catalyzed by oxidative-thermoregulated bifunctional ionic liquids[J]. Acta Chimica Sinica, 2014, 72:1152-1156.
[7] CHAMACK M, MAHJOUB A R, AGHAYAN H. Catalytic performance of vanadium-substituted molybdophosphoric acid supported on zirconium modified mesoporous silica in oxidative desulfurization[J]. Chemical Engineering Research & Design, 2015, 94:565-572.
[8] 李瑞丽, 吕本震, 蒋善良, 等. 磷钨酸/SBA-15催化氧化-萃取柴油脱硫[J].化工进展, 2016, 35(9):2790-2795. LI R L, LV B Z, JIANG S L, et al. Diesel desulfurization by phosphotungstic acid/SBA-15 catalytic oxidation-extraction[J]. Chemical Industry and Engineering Progress, 2016, 35(9):2790-2795.
[9] 侯影飞, 李力军, 蒋驰. 活性炭负载磷钨酸催化剂的制备及其催化氧化脱硫性能[J]. 化工进展, 2017, 36(11):4072-4079. HOU Y F, LI L J, JIANG C. Preparation and performance of phosphotungstic acid/activated carbon catalyst for catalytic oxidative desulfurization[J]. Chemical Industry and Engineering Progress, 2017, 36(11):4072-4079.
[10] 张娟, 胡颜荟, 任腾杰, 等. Ti-MCM-41负载酞菁铁光催化氧化脱硫[J]. 化工学报, 2015, 66(9):3437-3443. ZHANG J, HU Y H, REN T J, et al. Photocatalytic oxidation desulfurization by iron phthalocyanine supported on Ti-MCM-41[J]. CIESC Journal, 2015, 66(9):3437-3443.
[11] 张璐璐, 孙悦, 王喆, 等.TiO₂/SBA-15的制备及光催化氧化脱硫性能[J]. 硅酸盐学报, 2016, 44(1):56-62. ZHANG L L, SUN Y, WANG Z, et al. Preparation and photocatalytic oxidation desulfurization performance of TiO₂/SBA-15[J]. Journal of the Chinese Ceramic Society, 2016, 44(1):56-62.
[12] 张璐璐, 詹金友, 孙尧, 等. WO₃-TiO₂/SBA-15的制备及其光催化氧化脱硫性能[J]. 燃料化学学报, 2016, 44(6):754-762. ZHANG L L, ZHAN J Y, SUN Y, et al. Preparation of WO₃-TiO₂/SBA-15 catalyst and its photocatalytic performance in oxidative desulfurization[J]. Journal of Fuel Chemistry and Technology, 2016, 44(6):754-762.
[13] WANG C, ZHU W S, XU Y H, Preparation of TiO₂/g-C₃N₄ composites and their application in photocatalytic oxidative desulfurization[J]. Ceramics International, 2014, 40(8):11627-11635.
[14] 叶飞燕, 梅亮, 肖静. Ti-Si-O双功能催化吸附材料的汽油光催化-吸附耦合脱硫性能[J]. 化工学报, 2015, 66(12):4858-4864. YE F Y, MEI L, XIAO J. UV photocatalysis-assisted adsorptive desulfurization of gasoline using bi-functional Ti-Si-O material[J]. CIESC Journal, 2015, 66(12):4858-4864.
[15] 甄延忠, 王杰, 付梦溪. AgI/h-MoO₃异质结的构筑及其模拟燃油光催化氧化脱硫活性[J]. 无机化学学报, 2017, 33(10):1731-1740. ZHEN Y Z, WANG J, FU M X. AgI/h-MoO₃ heterojunctions:fabrication and photocatalytic oxidative desulfurization activity of simulation fuel[J]. Chinese Journal of Inorganic Chemistry, 2017, 33(10):1731-1740.
[16] 李鑫, 童靖予, 张伟. TiO₂-CeO₂光催化吸附协同脱除柴油中的有机硫[J]. 燃料化学学报, 2017, 45(5):608-615. LI X, TONG J Y, ZHANG W. Synergy of photocatalysis and adsorption on TiO₂-CeO₂ for the removal of organosulfur compounds from diesel fuel[J]. Journal of Fuel Chemistry and Technology, 2017, 45(5):608-615.
[17] 陈颖, 马金丽, 李金莲, 等. 改性TiO₂催化剂光催化氧化脱硫[J]. 化工进展, 2007, 26(12):1749-1753. CHEN Y, MA J L, LI J L, et al. Photocatalytic oxidation desulfurization with modified TiO₂[J]. Chemical Industry and Engineering Progress, 2007, 26(12):1749-1753.
[18] UMAIR A, AZAM K, WASEEM R, et al. Highly efficient Y and V co-doped ZnO photocatalyst with enhanced dye sensitized visible light photocatalytic activity[J]. Catalysis Today, 2017, 284:169-178.
[19] 孟庆明, 王鉴. 并流沉淀法合成Fe掺杂ZnO及其光催化脱氮性能[J]. 化工学报, 2017, 68(1):437-443. MENG Q M, WANG J. Synthesis of Fe-doped ZnO by parallel flow precipitation method and its photocatalytic denitrification performance[J]. CIESC Journal, 2017, 68(1):437-443.
[20] MORASAE Samadi, MOHAMMAD Zirak, AMENE Naseri, et al. Recent progress on doped ZnO nanostructures for visible-light photocatalysis[J]. Thin Solid Films, 2016, 605:2-19.
[21] 陈枭, 石倩, 杨乐, 等. 纳米氧化锌表面修饰及其应用研究进展[J]. 化工进展, 2018, 37(2):621-627. CHEN X, SHI Q, YANG L, et al. Research progress in surface-modification and applications of nano zinc oxide[J]. Chemical Industry and Engineering Progress, 2018, 37(2):621-627.
[22] MIAO G, HUANG D S, REN X L. Visible-light induced photocatalytic oxidative desulfurization using BiVO₄/C₃N₄@SiO₂ with air/cumene hydroperoxide under ambient conditions[J]. Appl. Catal. B:Environ., 2016, 192:72-79.
[23] CAI L, REN F, WANG M, et al. V ions implanted ZnO nanorod arrays for photoelectrochemical water splitting under visible light[J]. Int. J. Hydrog. Energy, 2015, 40:1394-1401.
[24] SANOOP P K, ANAS S, ANANTHAKUMAR S, et al. Synthesis of yttrium doped nanocrystalline ZnO and its photocatalytic activity in methylene blue degradation[J]. Arab. J. Chem., 2016, 9(2):S1618-S1626.
[25] LI F, YAN B, ZHANG J, et al. Study on desulfmization efficiency and products of Ce-doped nanosized ZnO desulfwizer at ambient tempemtm[J]. Journal of Rare Earths, 2007, 25:306-310.
[26] LI X S, LIU Y J, ZENG Z Y, et al. Equilibrium hydrate formation conditions for the mixtures of methane+ionic liquids+water[J]. Journal of Chemical and Engineering Data, 2011, 56(1):119-123.
[27] XIAO C W, ADIDHARMA H. Dual function inhibitors for methane hydrate[J]. Chemical Engineering Science, 2009, 64(7):1522-1527.
[28] THI V H-T, LEE B-K. Effective photocatalytic degradation of paracetamol using La-doped ZnO photocatalyst under visible light irradiation[J]. Mater. Res. Bull., 2017, 96:171-182.
[29] 郎集会, 韩强, 张旗, 等. 水热温度对稀土Ce掺杂ZnO纳米棒的结构和光学性能影响[J]. 江苏大学学报(自然科学版), 2015, 2:224-227. LANG J H, HAN Q, ZHANG Q, et al. Influence of hydrothermal temperature on structure and photoluminescence property of Ce-doped ZnO nanorods[J]. Journal of Jiangsu University(Natural Science Edition), 2015, 2:224-227.
[30] 梁鹏举, 白红进, 姜建辉, 等. 三维多孔CuCo₂O₄的制备及其超级电容性能研究[J].化工新型材料, 2016, 44(10):179-181. LANG P J, BAI H J, JIANG J H, et al. Synthesis of three-dimensional porous CuCo₂O₄ and its supercapacitor property[J]. New Chemical Materials, 2016, 44(10):179-181.
[31] WANG L, JI Z Y, LIN J J, et al. Preparation and optical and photocatalytic properties of Ce-doped ZnO microstructures by simple solution method[J]. Mat. Sci. Semicon. Proc., 2017, 71:401-408.
[32] KOAO L F, DEJENE F B, TSEGA M, et al. Annealed Ce³⁺-doped ZnO flower-like morphology synthesized by chemical bath deposition method[J]. Physica B, 2016, 480:53-57.
[33] SIN J C, LAM S M, LEE K T, et al. Preparation of cerium-doped ZnO hierarchical micro/nanospheres with enhanced photocatalytic performance for phenol degradation under visible light[J]. J. Mol. Catal. A:Chem., 2015, 409:1-10.
[34] LI L, ZHANG J, SHEN C, et al. Oxidative desulfurization of model fuels with pure nano-TiO₂ as catalyst directly without UV irradiation[J]. Fuel, 2016, 167:9-16.