结晶度对高密度聚乙烯光氧老化特性的影响

doi:10.16085/j.issn.1000-6613.2017.03.032

化工进展 ›› 2017, Vol. 36 ›› Issue (03): 1003-1011.DOI: 10.16085/j.issn.1000-6613.2017.03.032

结晶度对高密度聚乙烯光氧老化特性的影响

代军¹, 晏华¹, 王雪梅¹, 郭骏骏², 桑练勇¹

1 中国人民解放军后勤工程学院化学与材料工程系, 重庆 401331;
2 73801部队, 江苏无锡 214000

收稿日期:2016-07-07 修回日期:2016-09-10 出版日期:2017-03-05 发布日期:2017-03-05
通讯作者: 晏华,教授,博士生导师,主要从事功能高分子材料和智能材料研究。
作者简介:代军(1992-),男,硕士研究生,从事高分子材料环境失效及老化研究。E-mail:daijunhg@126.com。
基金资助:
国家科技支撑计划（2012BAF06B04）及重庆市研究生科研创新项目（CYS16239）。

Influence of crystallinity on degradation properties of high density polyethylene by photo-oxidation aging

DAI Jun¹, YAN Hua¹, WANG Xuemei¹, GUO Junjun², SANG Lianyong¹

1 Department of Chemistry and Material Engineering, Logistical Engineering University, Chongqing 401331, China;
2 Unit 73801, Wuxi 214000, Jiangsu, China

Received:2016-07-07 Revised:2016-09-10 Online:2017-03-05 Published:2017-03-05

摘要/Abstract

摘要：

利用力学试验、衰减全反射红外光谱技术（ATR-FTIR）、热重分析法（TG）、差示扫描量热法（DSC）、凝胶渗透色谱（GPC）、扫描电子显微镜（SEM）比较研究了3种不同结晶度高密度聚乙烯（HDPE）的光氧老化特性，分析了结晶度对HDPE力学性能、化学结构、热稳定性、熔融特性、分子量和表面微观形貌的影响规律。结果表明结晶度越高，HDPE弯曲强度、弯曲模量和冲击强度下降最明显；不饱和度增长越剧烈，支化作用和断链作用更明显，且区别主要集中于老化初期；羰基指数和羟基指数增长越快，热分解特征温度下降最明显，热稳定性下降更强烈，但熔融特征温度和氧化诱导温度下降更不明显，相对分子质量下降更强烈，表面破坏更严重，老化作用更剧烈。结晶度越高，HDPE缺陷也就越多，在热氧环境中越容易发生氧化，老化现象更严重。

关键词: 结晶度, 高密度聚乙烯, 光氧老化, 降解, 氧化, 色谱

Abstract:

In this article,the influence different degree of crystallinity on the mechanical properties, chemical structure,thermal stability,melting characteristic,average molecular weight and surface morphology evolution of HDPE after xeon photo-oxidation aging were studied by mechanics experiment,attenuated total reflection infrared spectroscopy(ATR-FTIR),thermogravimetry analysis (TGA),differential scanning calorimetry(DSC),gel permeation chromatography(GPC) and scanning electron microscope(SEM),respectively. The results show that higher degree of crystallinity in the HDPE results in a faster decrease in the bending strength,bending modulus and impact strength. The degree of unsaturation,carbonyl index and hydroxyl index increase significantly and the chain branching and chain breaking are more obviously and mainly concentrated in the early part of aging. The thermogravimetry analysis characteristic temperature decreases faster,but the melting peak temperature and the oxidation induction temperature decrease less significantly. The average molecular weight decreases more intensely and the aging degree of surface microstructure is more severe. The higher crystallinity the more the flaws in HDPE,which facilitates oxidation under thermo-oxidation environment and the aging phenomenon is more severe.

Key words: crystallinity, high density polyethylene, photo-oxidation aging, degradation, oxidation, chromatography

中图分类号:

O632.1

代军, 晏华, 王雪梅, 郭骏骏, 桑练勇. 结晶度对高密度聚乙烯光氧老化特性的影响[J]. 化工进展, 2017, 36(03): 1003-1011.

DAI Jun, YAN Hua, WANG Xuemei, GUO Junjun, SANG Lianyong. Influence of crystallinity on degradation properties of high density polyethylene by photo-oxidation aging[J]. Chemical Industry and Engineering Progress, 2017, 36(03): 1003-1011.

参考文献

[1] AMMALA A,BATEMAN S,DEAN K,et al. An overview of degradable and biodegradable polyolefins[J]. Progress in Polymer Science,2011,36(8):1015-1049.
[2] 刘如,曹金珍,彭尧. 木粉组分对木塑复合材料性能的影响研究进展[J]. 化工进展,2014,32(8):2072-2083. LIU R,CAO J Z,PENG Y. Influences of wood components on the property of wood-plastic composites[J]. Chemical Industry and Engineering Progress,2014,32(8):2072-2083.
[3] 姚培培,李琛,肖生苓. 紫外老化对聚苯乙烯泡沫性能的影响[J]. 化工学报,2014,65(11):4620-4626. YAO P P,LI C,XIAO S L,Effect of ultraviolet aging on properties and structure of Polystyrene[J]. CIESC Journal,2014,65(11):4620-4626.
[4] 张敏华,李春华,姜浩锡. 热重质谱法研究聚苯乙烯热降解机理[J]. 化工进展,2008,27(4):609-612. ZHANG M H,LI C H,JIANG H X. Thermal degradation mechanism of polystyrene by TG-MS[J]. Chemical Industry and Engineering Progress,2008,27(4):609-612.
[5] KLEMENS G,SUSANME B,GERNOT M. Characterization of the influence of specimen thickness on the aging behavior of a polypropylene based model compound[J]. Polymer Degradation and Stability,2015,111:185-193.
[6] SUGIMOTO M,SHIMADA A,KUDOH H,et al. Product analysis for polyethylene degradation by radiation and thermal ageing[J]. Radiation Physics and Chemistry,2013,82:69-73.
[7] 杨素,杨苏平,陈枫,等. 聚乙烯短支链与其结晶度关系的定量研究[J]. 现代塑料加工应用,2006,18(2):33-35. YANG S,YANG S P,CHEN F,et al. Quantitative analysis of the relationship between short branched chain and crystallinity in polyethylene[J]. Modern Plastics Processing and Applications,2006, 18(2):33-35.
[8] 江云涛,黄佃平,邵华锋,等. 结晶度对聚丁烯-1力学性能的影响[J]. 现代塑料加工应用,2008,20(1):26-29. JIANG Y T,HUANG D P,SHAO H F,et al. Effect of crystallinity on mechanics property of polybutene-1[J]. Modern Plastics Processing and Applications,2008,20(1):26-29.
[9] 郭骏骏,晏华,包河彬,等. 衰减全反射红外光谱法的高密度聚乙烯自然老化特性研究[J]. 光谱学与光谱分析,2015,35(6):1520-1524. GUO J J,YAN H,BAO H B,et al. Attenuated total reflection infrared spectroscopy for degradation profile of high density polyethylene after weathering aging[J]. Spectroscopy and Spectral Analysis,2015, 35(6):1520-1524.
[10] GAUTHIER E,LAYCOCK B,CUOQ F J J M,et al. Correlation between chain microstructural changes and embrittlement of LLDPE-based films during photo- and thermo-oxidative degradation[J]. Polymer Degradation and Stability,2013,98(1):425-435.
[11] BAEK B K,LA Y H,NA W J,et al. A kinetic study on the supercritical decrosslinking reaction of silane-crosslinked polyethylene in a continuous process[J]. Polymer Degradation and Stability,2016,126:75-80.
[12] DING Y,MCKINNOM M B,STOLIAROY S I,et al. Determination of kinetics and thermodynamics of thermal decomposition for polymers containing reactive flame retardants:application to poly(lactic acid) blended with melamine and ammonium polyphosphate[J]. Polymer Degradation and Stability,2016(129):347-362.
[13] 郭骏骏,晏华,胡志德,等. 基于主成分分析的高密度聚乙烯环境适应性行为研究[J]. 材料工程,2015,43(1):96-103. GUO J J,YAN H,HU Z D,et al. Adaptive behavior to environment of HDPE by principal component analysis[J]. Journal of Materials Engineering,2015,43(1):96-103.

[1]	杨寒月, 孔令真, 陈家庆, 孙欢, 宋家恺, 王思诚, 孔标. 微气泡型下向流管式气液接触器脱碳性能[J]. 化工进展, 2023, 42(S1): 197-204.
[2]	杨建平. 降低HPPO装置反应系统原料消耗的PSE[J]. 化工进展, 2023, 42(S1): 21-32.
[3]	王福安. 300kt/a环氧丙烷工艺反应器降耗减排分析[J]. 化工进展, 2023, 42(S1): 213-218.
[4]	王胜岩, 邓帅, 赵睿恺. 变电吸附二氧化碳捕集技术研究进展[J]. 化工进展, 2023, 42(S1): 233-245.
[5]	张明焱, 刘燕, 张雪婷, 刘亚科, 李从举, 张秀玲. 非贵金属双功能催化剂在锌空气电池研究进展[J]. 化工进展, 2023, 42(S1): 276-286.
[6]	时永兴, 林刚, 孙晓航, 蒋韦庚, 乔大伟, 颜彬航. 二氧化碳加氢制甲醇过程中铜基催化剂活性位点研究进展[J]. 化工进展, 2023, 42(S1): 287-298.
[7]	谢璐垚, 陈崧哲, 王来军, 张平. 用于SO₂去极化电解制氢的铂基催化剂[J]. 化工进展, 2023, 42(S1): 299-309.
[8]	杨霞珍, 彭伊凡, 刘化章, 霍超. 熔铁催化剂活性相的调控及其费托反应性能[J]. 化工进展, 2023, 42(S1): 310-318.
[9]	郑谦, 官修帅, 靳山彪, 张长明, 张小超. 铈锆固溶体Ce_0.25Zr_0.75O₂光热协同催化CO₂与甲醇合成DMC[J]. 化工进展, 2023, 42(S1): 319-327.
[10]	戴欢涛, 曹苓玉, 游新秀, 徐浩亮, 汪涛, 项玮, 张学杨. 木质素浸渍柚子皮生物炭吸附CO₂特性[J]. 化工进展, 2023, 42(S1): 356-363.
[11]	高雨飞, 鲁金凤. 非均相催化臭氧氧化作用机理研究进展[J]. 化工进展, 2023, 42(S1): 430-438.
[12]	顾永正, 张永生. HBr改性飞灰对Hg⁰的动态吸附及动力学模型[J]. 化工进展, 2023, 42(S1): 498-509.
[13]	孙玉玉, 蔡鑫磊, 汤吉海, 黄晶晶, 黄益平, 刘杰. 反应精馏合成甲基丙烯酸甲酯工艺优化及节能[J]. 化工进展, 2023, 42(S1): 56-63.
[14]	赖诗妮, 江丽霞, 李军, 黄宏宇, 小林敬幸. 含碳掺氨燃料的研究进展[J]. 化工进展, 2023, 42(9): 4603-4615.
[15]	王鹏, 史会兵, 赵德明, 冯保林, 陈倩, 杨妲. 过渡金属催化氯代物的羰基化反应研究进展[J]. 化工进展, 2023, 42(9): 4649-4666.

结晶度对高密度聚乙烯光氧老化特性的影响

Influence of crystallinity on degradation properties of high density polyethylene by photo-oxidation aging

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价