还原温度对Mo基催化剂物相及其加氢脱氧性能的影响

doi:10.16085/j.issn.1000-6613.2016.05.027

化工进展 ›› 2016, Vol. 35 ›› Issue (05): 1452-1459.DOI: 10.16085/j.issn.1000-6613.2016.05.027

还原温度对Mo基催化剂物相及其加氢脱氧性能的影响

梁俊梅¹, 陈宇², 丁冉冉², 孟永强¹, 王要武², 杨明德², 吴玉龙²

1. 河北科技大学材料科学与工程学院, 河北石家庄 050018;
2. 清华大学核能与新能源技术研究院, 北京 100084

收稿日期:2015-08-17 修回日期:2015-11-01 出版日期:2016-05-05 发布日期:2016-05-05
通讯作者: 吴玉龙,博士,副教授,主要从事新能源化工和工业催化的研究。E-mail wylong@tsinghua.edu.cn。
作者简介:梁俊梅(1990-),女,硕士研究生,研究方向为藻类生物油催化提质。E-mail 1285774390@qq.com。
基金资助:
国家自然科学基金(21376140,21576155)及广东省科技计划(2015B020215004)项目。

Effect of reduction temperature on Mo-based catalyst phase and its activity in hydrodeoxygenation reaction

LIANG Junmei¹, CHEN Yu², DING Ranran², MENG Yongqiang¹, WANG Yaowu², YANG Mingde², WU Yulong²

1. College of Materials Science and Engineering, Hebei University of Science and Technology, Shijiazhuang 050018, Hebei, China;
2. Institute of Nuclear and New Energy Technology, Tsinghua University, Beijing 100084, China

Received:2015-08-17 Revised:2015-11-01 Online:2016-05-05 Published:2016-05-05

摘要/Abstract

摘要： 以碳纳米管(CNTs)为载体,通过控制催化剂合成的还原温度制备了一系列负载型Mo基催化剂。采用XRD、TEM、N₂物理吸附、XPS以及NH₃/H₂-TPD等技术对催化剂进行了表征,并研究了Mo基催化剂对硬脂酸催化加氢脱氧性能的影响。结果表明:随着还原温度的升高,催化剂表面的Mo物种逐渐被还原,还原过程为:MoO₃→MoO₂→Mo→Mo₂C。还原温度为450℃和550℃时,催化剂的活性相为MoO₂;还原温度为600℃时,催化剂的活性相为MoO₂/Mo/β-Mo₂C的混合相;还原温度为650℃和700℃时,催化剂的活性相全部转化为β-Mo₂C。与活性相MoO₂催化剂相比,β-Mo₂C催化剂具有更高的加氢脱氧活性。此外,还原温度为600℃的MoO₂/Mo/β-Mo₂C混合相催化剂因具有较大的比表面积、较多的酸中心数量和较强的H₂吸附能力,使得该催化剂在硬脂酸加氢脱氧反应中表现出最优越的催化活性。

关键词: Mo基催化剂, 还原, 加氢, 活性

Abstract: A series of Mo-based catalysts supported over CNTs were successfully prepared by controlling the reduction temperature during the catalyst synthesis. The properties of the obtained catalysts were systematically characterized by XRD, TEM, N₂ adsorption, XPS and NH₃/H₂-TPD techniques, and the catalytic reactivity for the hydrodeoxygenation of stearic acid was evaluated. The results showed that Mo species on the surface of catalysts were reduced with the increase of reduction temperature, and the reduction process was as followed: MoO₃→MoO₂→Mo→Mo₂C. The active phase was MoO₂when reduction temperature was below 550℃. Further elevating the reduction temperature to 600℃, we found a mixed phase of MoO₂/Mo/β-Mo₂C existed. β-Mo₂C was the main active phase when reduction temperature was over 650℃, and it exhibited higher activity of hydrodeoxygenation than the active phase of MoO₂. In addition, the MoO₂/Mo/β-Mo₂C mixed phase catalyst at 600℃ showed the highest catalytic reactivity in hydrodeoxygenation of stearic acid due to its large specific surface area, more acid sites and stronger H₂ adsorption ability.

Key words: Mo-based catalyst, reduction, hydrogenation, reactivity

中图分类号:

梁俊梅, 陈宇, 丁冉冉, 孟永强, 王要武, 杨明德, 吴玉龙. 还原温度对Mo基催化剂物相及其加氢脱氧性能的影响[J]. 化工进展, 2016, 35(05): 1452-1459.

LIANG Junmei, CHEN Yu, DING Ranran, MENG Yongqiang, WANG Yaowu, YANG Mingde, WU Yulong. Effect of reduction temperature on Mo-based catalyst phase and its activity in hydrodeoxygenation reaction[J]. Chemical Industry and Engineering Progree, 2016, 35(05): 1452-1459.

参考文献

[1] 黄付彬, 冯丽娟, 杨文超, 等. 藻类直接液化制取液体燃料研究进展[J]. 化工进展, 2012, 31(10): 2197-2201.
[2] ROZMYSLOWICZ B, MAKI-ARVELA P, TOKAREV A, et al. Influence of hydrogen in catalytic deoxygenation of fatty acids and their derivatives over Pd/C[J].Ind. Eng. Chem. Res., 2012, 51(26): 8922-8927.
[3] 赵永腾, 李涛, 徐军伟, 等. 微藻碳水化合物生产生物燃料的研究进展[J]. 化工进展, 2014, 33(4): 878-882.
[4] VARDON D R, SHARMA B K, SCOTT J, et al. Chemical properties of biocrude oil from the hydrothermal liquefaction of spirulina algae, swine manure, and digested anaerobic sludge[J].Bioresource Technol., 2011, 102(17): 8295-8303.
[5] CHEN Y, WU Y L, DING R R, et al. Catalytic hydrothermal liquefaction of D. tertiolecta for the production of bio-oil over different acid/base catalysts[J]. AIChE J., 2015, 61(4): 1118-1128.
[6] PENG B X, YAO Y, ZHAO C, et al. Towards quantitative conversion of microalgae oil to diesel-range alkanes with bifunctional catalysts[J]. Angew. Chem., 2012, 124(9): 2114-2117.
[7] ZOU S P, WU Y L, YANG M D, et al. Bio-oil production from sub-and supercritical water liquefaction of microalgae Dunaliella tertiolectaand related properties[J]. Energ. Environ. Sci., 2010, 3(8): 1073-1078.
[8] GOSSELINK R W, STELLWAGEN D R, BITTER J H. Tungsten-based catalysts for selective deoxygenation[J]. Angew. Chem., 2013, 125(19): 5193-5196.
[9] DING R R, WU Y L, CHEN Y, et al. Effective hydrodeoxygenation of palmitic acid to diesel-like hydrocarbons over MoO₂/CNTs catalyst[J]. Chem. Eng. Sci., 2014. DOI: 10.1016/j.ces.2014.10.024.
[10] HAN J X, DUAN J Z, CHEN P, et al. Nanostructured molybdenum carbides supported on carbon nanotubes as efficient catalysts for one-step hydrodeoxygenation and isomerization of vegetable oils[J]. Green Chem., 2011, 13(9): 2561-2568.
[11] WANG J, SHEN L F, DING B, et al. Fabrication of porous carbon spheres for high-performance electrochemical capacitors[J]. RSC Adv., 2014, 4(15): 7538-7544.
[12] LIU C C, LIN M G, JIANG D, et al. Preparation of promoted molybdenum carbides nanowire for CO hydrogenation[J]. Catal. Lett., 2014, 144(4): 567-573.
[13] GALADIMA A, ISMAIL A, ABDULLAHI I, et al. Supported molybdenum carbide as n-hexane upgrading catalyst[J]. Chem. Mat. Res., 2013, 3(11): 73-78.
[14] XIANG M L, LI D B, LI W H, et al. Potassium and nickel doped β-Mo₂C catalysts for mixed alcohols synthesis viasyngas[J]. Catal. Commun., 2007, 8(3): 513-518.
[15] ZHU Q L, ZHANG B, YANG J, et al. The promotion of nickel to Mo₂C/Al₂O₃catalyst for the partial oxidation of methane to syngas[J]. New J. Chem., 2003, 27(11): 1633-1638.
[16] XIANG M L, LI D B, XIAO H C, et al. K/Ni/β-Mo₂C: a highly active and selective catalyst for higher alcohols synthesis from CO hydrogenation[J]. Catal. Today, 2008, 131(1): 489-495.
[17] LI X Y, MA D, CHEN L M, et al. Fabrication of molybdenum carbide catalysts over multi-walled carbon nanotubes by carbothermal hydrogen reduction[J]. Catal. Lett., 2007, 116(1/2): 63-69.
[18] JIANG H, WANG L S, CUI W, et al. Study on the induction period of methane aromatization over Mo/HZSM-5: partial reduction of Mo species and formation of carbonaceous deposit[J].Catal. Lett., 1999, 57(3): 95-102.
[19] CHOI J S, BUGLI G, DJÉGA-MAIADASSOU G. Influence of the degree of carburization on the density of sites and hydrogenating activity of molybdenum carbides[J]. J. Catal., 2000, 193(2): 238-247.
[20] SUN Y M, HU X L, LUO W, et al. Ultrafine MoO₂ nanoparticles embedded in a carbon matrix as a high-capacity and long-life anode for lithium-ion batteries[J]. J. Mater. Chem., 2012, 22(2): 425-431.
[21] XIA F F, HU X L, SUN Y M, et al. Layer-by-layer assembled MoO₂-graphene thin film as a high-capacity and binder-free anode for lithium-ion batteries[J]. Nanoscale, 2012, 4(15): 4707-4711.
[22] MOON D J, RYU J W. Molybdenum carbide water-gas shift catalyst for fuel cell-powered vehicles applications[J]. Catal. Lett., 2004, 92(1/2): 17-24.
[23] CHEN H Y, CHEN L, LU Y, et al. Synthesis, characterization and application of nano-structured Mo₂C thin films[J]. Catal. Today, 2004, 96(3): 161-164.
[24] YANG Z H, CAI P J, SHI L, et al. A facile preparation of nanocrystalline Mo₂C from graphite or carbon nanotubes[J]. J. Solid State Chem., 2006, 179(1): 29-32.
[25] PERRET N, WANG X D, DELANNOY L, et al. Enhanced selective nitroarene hydrogenation over Au supported on β-Mo₂C and β-Mo₂C/Al₂O₃[J]. J. Catal., 2012, 286: 172-183.
[26] SOLYMOSI F, SZÉCHENYI A. Aromatization of n-butane and 1-butene over supported Mo₂C catalyst[J].J. Catal., 2004, 223(1): 221-231.
[27] FARKAS A P, SOLYMOSI F. Adsorption and reactions of ethanol on Mo₂C/Mo (100)[J]. Surf. Sci., 2007, 601(1): 193-200.
[28] 刘长城, 林明桂, 姜东, 等. Mg改性纳米线碳化钼在CO加氢反应中的应用[J]. 天然气化工(C1 化学与化工), 2014, 39(3): 36-41.
[29] EDAMOTO K, SUGIHARA M, OZAWA K, et al. Photoelectron spectroscopy study of oxygen adsorption on Mo₂C (0001)[J]. Surf. Sci., 2004, 561(1): 101-109.
[30] FLORES O G M, HA S. Activity and stability studies of MoO₂ catalyst for the partial oxidation of gasoline[J]. Appl. Catal. A: Gen., 2009, 352(1): 124-132.
[31] TORRES J, ALFONSO J E, LÓPEZ-CARREÑO L D. XPS and X-ray diffraction characterization of MoO₃ thin films prepared by laser evaporation[J]. Phys. Status Solidi(C), 2005, 2(10): 3726-3729.
[32] GAO S, LI G D, LIU Y P, et al. Electrocatalytic H₂ production from seawater over Co, N-codoped nanocarbons[J]. Nanoscale, 2015, 7(6): 2306-2316.
[33] GAO Q, ZHAO X Y, XIAO Y, et al. A mild route to mesoporous Mo₂C-C hybrid nanospheres for high performance lithium-ion batteries[J]. Nanoscale, 2014, 6(11): 6151-6157.
[34] 程新孙, 罗来涛, 鲁勋. Pd/ZrO₂-Al₂O₃催化剂加氢脱硫性能的研究[J]. 环境科学研究, 2008, 21(1): 139-144.
[35] DUAN Y N, WU Y L, ZHANG Q H, et al. Towards conversion of octanoic acid to liquid hydrocarbon via hydrodeoxygenation over Mo promoter nickel-based catalyst[J]. J. Mol. Catal. A: Chem., 2015, 398: 72-78.

还原温度对Mo基催化剂物相及其加氢脱氧性能的影响

Effect of reduction temperature on Mo-based catalyst phase and its activity in hydrodeoxygenation reaction

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价

[1]	时永兴, 林刚, 孙晓航, 蒋韦庚, 乔大伟, 颜彬航. 二氧化碳加氢制甲醇过程中铜基催化剂活性位点研究进展[J]. 化工进展, 2023, 42(S1): 287-298.
[2]	高雨飞, 鲁金凤. 非均相催化臭氧氧化作用机理研究进展[J]. 化工进展, 2023, 42(S1): 430-438.
[3]	王乐乐, 杨万荣, 姚燕, 刘涛, 何川, 刘逍, 苏胜, 孔凡海, 朱仓海, 向军. SCR脱硝催化剂掺废特性及性能影响[J]. 化工进展, 2023, 42(S1): 489-497.
[4]	赵景超, 谭明. 表面活性剂对电渗析减量化工业含盐废水的影响[J]. 化工进展, 2023, 42(S1): 529-535.
[5]	邓丽萍, 时好雨, 刘霄龙, 陈瑶姬, 严晶颖. 非贵金属改性钒钛基催化剂NH₃-SCR脱硝协同控制VOCs[J]. 化工进展, 2023, 42(S1): 542-548.
[6]	王谨航, 何勇, 史伶俐, 龙臻, 梁德青. 气体水合物阻聚剂研究进展[J]. 化工进展, 2023, 42(9): 4587-4602.
[7]	程涛, 崔瑞利, 宋俊男, 张天琪, 张耘赫, 梁世杰, 朴实. 渣油加氢装置杂质沉积规律与压降升高机理分析[J]. 化工进展, 2023, 42(9): 4616-4627.
[8]	王晋刚, 张剑波, 唐雪娇, 刘金鹏, 鞠美庭. 机动车尾气脱硝催化剂Cu-SSZ-13的改性研究进展[J]. 化工进展, 2023, 42(9): 4636-4648.
[9]	张启, 赵红, 荣峻峰. 质子交换膜燃料电池中氧还原反应抗毒性电催化剂研究进展[J]. 化工进展, 2023, 42(9): 4677-4691.
[10]	葛全倩, 徐迈, 梁铣, 王凤武. MOFs材料在光电催化领域应用的研究进展[J]. 化工进展, 2023, 42(9): 4692-4705.
[11]	林晓鹏, 肖友华, 管奕琛, 鲁晓东, 宗文杰, 傅深渊. 离子聚合物-金属复合材料（IPMC）柔性电极的研究进展[J]. 化工进展, 2023, 42(9): 4770-4782.
[12]	朱传强, 茹晋波, 孙亭亭, 谢兴旺, 李长明, 高士秋. 固体高分子脱硝剂选择性非催化还原NO _x 特性[J]. 化工进展, 2023, 42(9): 4939-4946.
[13]	史天茜, 石永辉, 武新颖, 张益豪, 秦哲, 赵春霞, 路达. Fe²⁺对厌氧氨氧化EGSB反应器运行性能的影响[J]. 化工进展, 2023, 42(9): 5003-5010.
[14]	张丽宏, 金要茹, 程芳琴. 煤气化渣资源化利用[J]. 化工进展, 2023, 42(8): 4447-4457.
[15]	毛善俊, 王哲, 王勇. 基团辨识加氢：从概念到应用[J]. 化工进展, 2023, 42(8): 3917-3922.