Effect of precipitating agent on the performance of Co3O4-catalyzed decomposition of N2O

doi:10.16085/j.issn.1000-6613.2023-0579

Abstract

Abstract:

The Co₃O₄ composite metal oxides were prepared by the hydrothermal method using cobalt acetate as the cobalt source. The physicochemical properties of the catalysts were characterized by XRD, FTIR, TEM, SEM, BET, H₂-TPR, O₂-TPD and XPS. The catalyst catalytic decomposition activity of N₂O was evaluated in a fixed-bed microreactor, and the effect of precipitants (NaOH、 Na₂CO₃、 NaHCO₃、 H₂NCONH₂、 CH₈N₂O₃、 NH₃·H₂O) on the catalytic decomposition performance of N₂O was investigated. The results showed that the Co₃O₄ catalysts prepared by the hydrothermal method were all of spinel structure, and different precipitating agents affected the catalyst morphology, redox performance and catalytic decomposition N₂O activity. The activity of the catalysts prepared with sodium precipitant was higher than that of other catalysts because it promoted the reduction process of Co³⁺ to Co²⁺, influenced the chemical environment of cobalt ions, improved the electron donating capability, weakened the Co—O bond in the catalyst, and accelerated the regeneration of oxygen vacancies during the catalytic reaction. The Co₃O₄-NaOH catalyst, which contained a small amount of Na ions, had a strong redox ability, a large O_ads/O_latt ratio, resulting in a large amount of oxygen adsorbed on the surface, and a low N₂O decomposition temperature. Under the conditions of the reaction gas composition of 0.88% O₂, 0.65% N₂O, and N₂ as equilibrium gas (flow rate of 80mL/min), T₁₀ and T₉₅ were 330℃ and 470℃, respectively.

Key words: precipitating agent, nitrous oxide, tricobalt tetraoxide, sodium ion, oxygen vacancy

摘要：

以乙酸钴为钴源采用水热法制备了Co₃O₄催化剂，通过X射线衍射仪、傅里叶变换红外光谱仪、透射电子显微镜、扫描电子显微镜、N₂物理吸附脱附测试、H₂程序升温还原、氧的程序升温脱附和X射线光电子能谱等表征手段对Co₃O₄催化剂的物理化学性质进行表征，在固定床微型反应器中评价催化剂催化分解N₂O活性，考察了不同沉淀剂（氢氧化钠、碳酸钠、碳酸氢钠、尿素、碳酸铵、氨水）对催化剂催化分解N₂O的性能影响。结果表明，水热法制备的Co₃O₄催化剂均为尖晶石结构，不同沉淀剂影响催化剂形貌、氧化还原性能和催化分解N₂O活性；含有钠离子沉淀剂制备而得的催化剂活性高于其他催化剂，其促进了Co³⁺到Co²⁺的还原过程，影响了钴离子化学环境，提高了给电子能力，弱化了催化剂中的Co—O键，加快了反应过程中氧空位的再生，进而提高了自身的催化活性；其中含少量Na离子的Co₃O₄-NaOH催化剂具有较强的氧化还原性，O_ads/O_latt较大，表面吸附氧数量多，N₂O分解温度较低，在反应气体组成为0.88% O₂、0.65% N₂O，N₂为平衡气的（流量为80mL/min）条件下，T₁₀和T₉₅分别为330℃和470℃。

关键词: 沉淀剂, 氧化亚氮, 四氧化三钴, 钠离子, 氧空位

CLC Number:

TQ426.6

SUN Jinru, SONG Aolei, ZHAO Mingxin, ZHAO Tiantian, WANG Hong, KE Ming. Effect of precipitating agent on the performance of Co₃O₄-catalyzed decomposition of N₂O[J]. Chemical Industry and Engineering Progress, 2024, 43(4): 1823-1831.

孙巾茹, 宋傲磊, 赵明新, 赵田田, 王虹, 柯明. 沉淀剂对Co₃O₄催化分解N₂O的性能影响[J]. 化工进展, 2024, 43(4): 1823-1831.

Figures/Tables 11

References 49

1	RICHARDS N, CARTER J H, PARKER L A, et al. Lowering the operating temperature of perovskite catalysts for N₂O decomposition through control of preparation methods[J]. ACS Catalysis, 2020, 10(10): 5430-5442.
2	LIAN X, GUO W L, HE B, et al. Insights of the mechanisms for CO oxidation by N₂O over M@Cu₁₂(M=Cu, Pt, Ru, Pd, Rh) core-shell clusters[J]. Molecular Catalysis, 2020, 494: 111126.
3	SHEN Q, WU M F, WANG H, et al. The influence of desilication on high-silica MFI and its catalytic performance for N₂O decomposition[J]. Applied Surface Science, 2018, 441: 474-481.
4	XIONG S C, CHEN J J, HUANG N, et al. Balance between reducibility and N₂O adsorption capacity for the N₂O decomposition: Cu _x Co _y catalysts as an example[J]. Environmental Science & Technology, 2019, 53(17): 10379-10386.
5	ZHAN Y Y, LIU Y, PENG X B, et al. Molecular-level understanding of reaction path optimization as a function of shape concerning the metal-support interaction effect of Co/CeO₂ on water-gas shift catalysis[J]. Catalysis Science & Technology, 2019, 9(18): 4928-4937.
6	ZENKOVETS G A, SHUTILOV R A, SOBOLEV V I, et al. Catalysts Cu/ZSM-5 for N₂O decomposition obtained with copper complexes of various structures[J]. Catalysis Communications, 2020, 144: 106072.
7	HE G Z, ZHANG B, HE H, et al. Atomic-scale insights into zeolite-based catalysis in N₂O decomposition[J]. Science of the Total Environment, 2019, 673: 266-271.
8	ZHANG Y Y, GUO Y Q, LI N, et al. Catalytic N₂O decomposition over CeMeO _y /γ-Al₂O₃(Me=Mn,Cu,Zn) catalysts prepared by impregnation method[J]. Asia-Pacific Journal of Chemical Engineering, 2018, 13(5): e2233.
9	DAVIDSON E A, KANTER D. Inventories and scenarios of nitrous oxide emissions[J]. Environmental Research Letters, 2014, 9(10): 105012.
10	RICHARDS N, CARTER J H, NOWICKA E, et al. Structure-sensitivity of alumina supported palladium catalysts for N₂O decomposition[J]. Applied Catalysis B: Environmental, 2020, 264: 118501.
11	ZHU H Y, LI Y Z, ZHENG X L, et al. In-situ DRIFTS study of CeO₂ supported Rh catalysts for N₂O decomposition[J]. Applied Catalysis A: General, 2019, 571: 89-95.
12	KONSOLAKIS M. Recent advances on nitrous oxide (N₂O) decomposition over non-noble-metal oxide catalysts: Catalytic performance, mechanistic considerations, and surface chemistry aspects[J]. ACS Catalysis, 2015, 5(11): 6397-6421.
13	FENG X B, TIAN M J, HE C, et al. Yolk-shell-like mesoporous CoCrO _x with superior activity and chlorine resistance in dichloromethane destruction[J]. Applied Catalysis B: Environmental, 2020, 264: 118493.
14	KIM K, BAEK S, KIM J J, et al. Catalytic decomposition of N₂O on Pd _x Cu _y alloy catalysts: A density functional theory study[J]. Applied Surface Science, 2020, 510: 145349.
15	FRANKEN T, PALKOVITS R. Investigation of potassium doped mixed spinels Cu _x Co_3- _x O₄,as catalysts for an efficient N₂O decomposition in real reaction conditions[J]. Applied Catalysis B: Environmental, 2015, 176/177: 298-305.
16	黄可龙, 刘人生, 杨幼平, 等. 形貌可控的四氧化三钴溶剂热合成及反应机理[J]. 物理化学学报, 2007, 23(5): 655-658.
	HUANG Kelong, LIU Rensheng, YANG Youping, et al. Shape-controlled synthesis and formation mechanism of Co₃O₄ by solvothermal method[J]. Acta Physico-Chimica Sinica, 2007, 23(5): 655-658.
17	张英芳, 董清溪, 马春, 等. Co₃O₄-Bi₂O₂CO₃催化剂的制备及其光催化性能[J]. 化工进展, 2021, 40(S1): 238-244.
	ZHANG Yingfang, DONG Qingxi, MA Chun, et al. Preparation and photocatalytic properties of Co₃O₄-Bi₂O₂CO₃ catalyst[J]. Chemical Industry and Engineering Progress, 2021, 40(S1): 238-244.
18	范书琼, 孔令斌, 王儒涛, 等. Co₃O₄的制备及电化学性能[J]. 化工进展, 2013, 32(S1): 168-173.
	FAN Shuqiong, KONG Lingbin, WANG Rutao, et al. Electrochemical performance of prepared Co₃O₄ materials[J]. Chemical Industry and Engineering Progress, 2013, 32(S1): 168-173.
19	QIAN M, ZENG H C. Synthesis and characterization of Mg-Co catalytic oxide materials for low-temperature N₂O decomposition[J]. Journal of Materials Chemistry, 1997, 7(3): 493-499.
20	WÓJCIK S, GRZYBEK G, STELMACHOWSKI P, et al. Bulk, surface and interface promotion of Co₃O₄ for the low-temperature N₂O decomposition catalysis[J]. Catalysts, 2019, 10(1): 41.
21	OHNISHI C， ASANO K， IWAMOTO S，et al ．Alkali-doped Co₃O₄ catalysts for direct decomposition of N₂O in the presence of oxygen[J]. Catalysis Today, 2007, 120(2): 145-150.
22	黄草明, 教光辉, 肖发新, 等. 沉淀法制备微米四氧化三钴试验研究[J]. 湿法冶金, 2019, 38(3): 243-248.
	HUANG Caoming, JIAO Guanghui, XIAO Faxin, et al. Preparation of micron cobaltosic oxide by precipitation method[J]. Hydrometallurgy of China, 2019, 38(3): 243-248.
23	WANG Y Z, HU X B, ZHENG K, et al. Effect of precipitants on the catalytic activity of Co-Ce composite oxide for N₂O catalytic decomposition[J]. Reaction Kinetics, Mechanisms and Catalysis, 2018, 123(2): 707-721.
24	ZHANG Q L, TANG X S, NING P, et al. Enhancement of N₂O catalytic decomposition over Ca modified Co₃O₄ catalyst[J]. RSC Advances, 2015, 5(63): 51263-51270.
25	KIM M-J, LEE S-J, I-S RYU, et al. Catalytic decomposition of N₂O over cobalt based spinel oxides: The role of additives[J]. Molecular Catalysis, 2017, 442: 202-207.
26	魏旭晖, 刘晓丽, 武瑞芳, 等. 动物骨源羟磷灰石负载Co₃O₄用于N₂O催化分解[J]. 工业催化, 2019, 27(8): 109-114.
	WEI Xuhui, LIU Xiaoli, WU Ruifang, et al. N₂O catalytic decomposition over Co₃O₄ supported on bone-derived hydroxyapatite of different animals[J]. Industrial Catalysis, 2019, 27(8): 109-114.
27	INAYAT A, AYOUB M, ABDULLAH A Z, et al. Decomposition of N₂O at low temperature over Co₃O₄ prepared by different methods[J]. Environmental Progress & Sustainable Energy, 2019, 38(4): 13129.
28	LIU S, TANG N F, SHANG Q H, et al. Superior performance of iridium supported on rutile titania for the catalytic decomposition of N₂O propellants[J]. Chinese Journal of Catalysis, 2018, 39(7): 1189-1193.
29	ARMANDI M, ANDANA T, BENSAID S, et al. Effect of the preparation technique of Cu-ZSM-5 catalysts on the isothermal oscillatory behavior of nitrous oxide decomposition[J]. Catalysis Today, 2020, 345: 59-70.
30	李帅, 叶丽萍, 罗勇. 制备条件对CuO-Co₃O₄-ZnO-CeO₂催化剂CO脱除性能的影响[J]. 应用技术学报, 2018, 18(1): 19-25.
	LI Shuai, YE Liping, LUO Yong. The influences of preparation conditions on CuO-Co₃O₄-ZnO-CeO₂ catalysts of CO removal[J]. Journal of Technology, 2018, 18(1): 19-25.
31	陶炎鑫, 於俊杰, 刘长春, 等. Co-Mg/Al类水滑石衍生复合氧化物上N₂O催化分解[J]. 物理化学学报, 2007, 23(2): 162-168.
	TAO Yanxin, YU Junjie, LIU Changchun, et al. N₂O catalytic decomposition over mixed oxides derived from Co-Mg/Al hydrotalcite-like compounds[J]. Acta Physico-Chimica Sinica, 2007, 23(2): 162-168.
32	YANG Q, DU L Y, WANG X, et al. CO oxidation over Au/ZrLa-doped CeO₂ catalysts: Synergistic effect of zirconium and lanthanum[J]. Chinese Journal of Catalysis, 2016, 37(8): 1331-1339.
33	YU H B, WANG X P, WU X X, et al. Promotion of Ag for Co₃O₄ catalyzing N₂O decomposition under simulated real reaction conditions[J]. Chemical Engineering Journal, 2018, 334: 800-806.
34	LYKAKI M, PAPISTA E, CARABINEIRO S A C, et al. Optimization of N₂O decomposition activity of CuO-CeO₂ mixed oxides by means of synthesis procedure and alkali (Cs) promotion[J]. Catalysis Science & Technology, 2018, 8(9): 2312-2322.
35	ZHANG T, QIN X, PENG Y, et al. Effect of Fe precursors on the catalytic activity of Fe/SAPO-34 catalysts for N₂O decomposition[J]. Catalysis Communications, 2019, 128: 105706.
36	WANG Y Z, HU X B, ZHENG K, et al. Effect of SnO₂ on the structure and catalytic performance of Co₃O₄ for N₂O decomposition[J]. Catalysis Communications, 2018, 111: 70-74.
37	LYKAKI M, PAPISTA E, KAKLIDIS N, et al. Ceria nanoparticles’ morphological effects on the N₂O decomposition performance of Co₃O₄/CeO₂ mixed oxides[J]. Catalysts, 2019, 9(3): 233.
38	GRZYBEK G, WÓJCIK S, CIURA K, et al. Influence of preparation method on dispersion of cobalt spinel over alumina extrudates and the catalyst deN₂O activity[J]. Applied Catalysis B: Environmental, 2017, 210: 34-44.
39	ZHAO T Q, GAO Q, LIAO W P, et al. Effect of Nd-incorporation and K-modification on catalytic performance of Co₃O₄ for N₂O decomposition[J]. Journal of Fuel Chemistry and Technology, 2019, 47(9): 1120-1128.
40	CHEN J H, SHI W B, LI J H. Catalytic combustion of methane over cerium-doped cobalt chromite catalysts[J]. Catalysis Today, 2011, 175(1): 216-222.
41	LIU Q, WANG L C, CHEN M, et al. Dry citrate-precursor synthesized nanocrystalline cobalt oxide as highly active catalyst for total oxidation of propane[J]. Journal of Catalysis, 2009, 263(1): 104-113.
42	ABU-ZIED B M, OBALOVÁ L, PACULTOVÁ K, et al. An investigation on the N₂O decomposition activity of Mn _x Co_1- _x Co₂O₄ nanorods prepared by the thermal decomposition of their oxalate precursors[J]. Journal of Industrial and Engineering Chemistry, 2021, 93: 279-289.
43	LIU F D, HE H, DING Y, et al. Effect of manganese substitution on the structure and activity of iron titanate catalyst for the selective catalytic reduction of NO with NH₃ [J]. Applied Catalysis B: Environmental, 2009, 93(1/2): 194-204.
44	WU L N, QIN W, HU X Y, et al. Decomposition and reduction of N₂O on CaS (100) surface: A theoretical account[J]. Surface Science, 2015, 632: 83-87.
45	TANG W X, WENG J F, LU X X, et al. Alkali-metal poisoning effect of total CO and propane oxidation over Co₃O₄ nanocatalysts[J]. Applied Catalysis B: Environmental, 2019, 256: 117859.
46	KALE G M, PANDIT S S, JACOB K T. Thermodynamics of cobalt (Ⅱ, Ⅲ) oxide (Co₃O₄): Evidence of phase transition[J]. Transactions of the Japan Institute of Metals, 1988, 29(2): 125-132.
47	TANG W X, XIAO W, WANG S B, et al. Boosting catalytic propane oxidation over PGM-free Co₃O₄nanocrystal aggregates through chemical leaching: A comparative study with Pt and Pd based catalysts[J]. Applied Catalysis B: Environmental, 2018, 226: 585-595.
48	WANG Y Z, ZHENG K, HU X B, et al. Y₂O₃ promoted Co₃O₄ catalyst for catalytic decomposition of N₂O[J]. Molecular Catalysis, 2019, 470: 104-111.
49	DEL R L, MARBAN G. Stainless steel wire mesh-supported potassium-doped cobalt oxide catalysts for the catalytic decomposition of nitrous oxide[J]. Applied Catalysis B: Environmental, 2012, 126: 39-46.

催化剂	2θ/(°)	a₀/Å	V/nm³	FWHM /(°)	D_XRD/nm	比表面积 /m²∙g^-1
Co₃O₄-NaOH	37.095	8.027	517.1	0.186	46.52	25.2
Co₃O₄-Na₂CO₃	37.154	8.014	514.8	0.179	47.96	17.4
Co₃O₄-NaHCO₃	37.057	8.035	518.7	0.148	58.79	25.9
Co₃O₄-尿素	37.002	8.046	520.9	0.149	58.90	21.4
Co₃O₄-碳酸铵	37.040	8.038	519.3	0.148	58.94	18.6
Co₃O₄-氨水	37.036	8.039	519.5	0.147	59.38	15.7

催化剂	2θ/(°)	a₀/Å	V/nm³	FWHM /(°)	D_XRD/nm	比表面积 /m²∙g^-1
Co₃O₄-NaOH	37.095	8.027	517.1	0.186	46.52	25.2
Co₃O₄-Na₂CO₃	37.154	8.014	514.8	0.179	47.96	17.4
Co₃O₄-NaHCO₃	37.057	8.035	518.7	0.148	58.79	25.9
Co₃O₄-尿素	37.002	8.046	520.9	0.149	58.90	21.4
Co₃O₄-碳酸铵	37.040	8.038	519.3	0.148	58.94	18.6
Co₃O₄-氨水	37.036	8.039	519.5	0.147	59.38	15.7

催化剂	原子含量/%
催化剂	Na	O	Co
Co₃O₄-NaOH	0.4	53.1	46.5
Co₃O₄-Na₂CO₃	9.1	48.9	42.0
Co₃O₄-NaHCO₃	6.5	53.4	40.1

催化剂	原子含量/%
催化剂	Na	O	Co
Co₃O₄-NaOH	0.4	53.1	46.5
Co₃O₄-Na₂CO₃	9.1	48.9	42.0
Co₃O₄-NaHCO₃	6.5	53.4	40.1

催化剂	α		β		总面积 /10^-6	面积比(β/α)
催化剂	峰位 /℃	面积 /10^-6	峰位 /℃	面积 /10^-6	总面积 /10^-6	面积比(β/α)
Co₃O₄-NaOH	350	1.61	397	5.10	6.71	3.2
Co₃O₄-Na₂CO₃	337	1.83	441	5.72	7.55	3.1
Co₃O₄-NaHCO₃	353	1.52	441	4.69	6.21	3.1
Co₃O₄-尿素	352	1.16	402	3.48	4.64	3.0
Co₃O₄-碳酸铵	358	1.08	405	3.26	4.34	3.0
Co₃O₄-氨水	359	0.68	408	2.10	2.78	3.1

Effect of precipitating agent on the performance of Co₃O₄-catalyzed decomposition of N₂O

沉淀剂对Co₃O₄催化分解N₂O的性能影响

RichHTML

PDF (PC)

Knowledge

Abstract

Cite this article

share this article

Figures/Tables 11

References 49

Related Articles 13

Recommended Articles

Metrics

Comments

催化剂	Co 2p_3/2结合能/eV		Co²⁺/Co³⁺	O 1s结合能/eV		O_ads/O_latt
催化剂	Co²⁺	Co³⁺	Co²⁺/Co³⁺	O_ads	O_latt	O_ads/O_latt
Co₃O₄-NaOH	780.59	778.89	0.53	531.01	529.71	0.68
Co₃O₄-Na₂CO₃	780.61	778.91	0.53	531.02	529.52	0.79
Co₃O₄-NaHCO₃	780.63	778.93	0.52	531.02	529.52	0.62
Co₃O₄-尿素	780.71	779.01	0.49	531.12	529.82	0.59
Co₃O₄-碳酸铵	780.71	779.01	0.47	531.12	529.82	0.55
Co₃O₄-氨水	780.72	779.02	0.46	531.12	529.82	0.45

[1]	DONG Xiaoshan, WANG Jian, LIN Fawei, YAN Beibei, CHEN Guanyi. Exsolved metal nanoparticles on perovskite oxides: exsolution, driving force and control strategy [J]. Chemical Industry and Engineering Progress, 2023, 42(6): 3049-3065.
[2]	ZHANG Peng, MENG Fanhui, YANG Guinan, LI Zhong. Progress of metal oxide in OX-ZEO catalyst for CO _x hydrogenation to light olefins [J]. Chemical Industry and Engineering Progress, 2022, 41(8): 4159-4172.
[3]	ZHAO Yu, ZHOU Fei, ZHANG Weiwei, LI Ning, LI Shiyou, LI Guixian. Research progress of cobalt phosphide materials in the field of electrochemical energy [J]. Chemical Industry and Engineering Progress, 2021, 40(4): 2188-2205.
[4]	LIU Haihua, LI Yanchun, DING Chuanmin, GE Hui, LI Xuekuan, ZHANG Wei. Catalytic performance of ZnZr/HZSM-5 bifunctional catalyst for the alkylation of syngas with benzene [J]. Chemical Industry and Engineering Progress, 2021, 40(12): 6696-6704.
[5]	Runhong WEI, Ruhui XU, Xuejun HU, Keyu ZHANG, Yenan ZHANG, Feng LIANG, Yaochun YAO. Dimensional design of SnO₂-C composite anode material for lithium and sodium ion batteries [J]. Chemical Industry and Engineering Progress, 2020, 39(7): 2677-2686.
[6]	Tingting ZHENG, Guodong WANG, Shaojing GU, Chengxiong WANG, Dongxia YANG, Bing LU, Yunshan GE, Yunkun ZHAO. Research progress on the formation and control of N₂O and NH₃ in automotive three-way catalyst [J]. Chemical Industry and Engineering Progress, 2020, 39(6): 2399-2410.
[7]	GAN Rongli, LUO Guangqian, XU Yang, MEI Ruidong, ZHU Hailu, ZHOU Mengli. Removal of toluene by non-thermal plasma coupled with Cu-Ce catalysts [J]. Chemical Industry and Engineering Progress, 2018, 37(09): 3416-3423.
[8]	ZHANG Yingjie, ZHU Ziyi, DONG Peng, ZHAO Shaobo, ZHANG Yanjia, YANG Chengyun, YANG Chengfeng, WEI Keyi, LI Xue. Research progress of carbon-based anode materials for sodium ion batteries [J]. Chemical Industry and Engineering Progress, 2017, 36(11): 4106-4115.
[9]	SHI Wenjing, YAN Yongwang, XU Shoudong, CHEN Liang, LIU Shibin, ZHANG Ding. Research progress of sodium manganate oxide Na_0.44MnO₂ as cathode for sodium-ion batteries [J]. Chemical Industry and Engineering Progress, 2017, 36(09): 3343-3352.
[10]	ZHOU Chen, PAN Yuting, LIU Min, CHEN Ying. Advance of mechanism on N₂O emissions from biological denitrification [J]. Chemical Industry and Engineering Progress, 2017, 36(08): 3074-3084.
[11]	CHEN Hu, WANG Ying, LÜ Yongkang. Progress on mechanisms and influence factors of N₂O production in microbial nitrogen removal process from wastewater [J]. Chemical Industry and Engineering Progree, 2016, 35(12): 4020-4025.
[12]	DING Lin, CAO Yulai, SONG Yongji, LI Cuiqing, REN Xiaoguang, WANG Hong. The study of catalytic decomposition of N₂O over Cu-Co-M(M=Fe, Mn, Ni, Zn, Ce) [J]. Chemical Industry and Engineering Progress, 2016, 35(11): 3519-3523.
[13]	ZHAO Xiaoxu，CHENG Dangguo，CHEN Fengqiu，ZHAN Xiaoli. Review of catalysts for catalytic decomposition of N2O [J]. Chemical Industry and Engineering Progree, 2009, 28(9): 1562-.

催化剂	T₁₀/℃	T₉₅/℃
Co₃O₄-NaOH	330	470
Co₃O₄-Na₂CO₃	398	462
Co₃O₄-NaHCO₃	418	491
Co₃O₄-尿素	378	561
Co₃O₄-碳酸铵	400	580
Co₃O₄-氨水	411	630

催化剂	T₁₀/℃	T₉₅/℃
Co₃O₄-NaOH	330	470
Co₃O₄-Na₂CO₃	398	462
Co₃O₄-NaHCO₃	418	491
Co₃O₄-尿素	378	561
Co₃O₄-碳酸铵	400	580
Co₃O₄-氨水	411	630