燃煤电站锅炉水冷壁壁面高温腐蚀问题分析与对策

doi:10.16085/j.issn.1000-6613.2020-0302

摘要/Abstract

摘要：

以对冲燃烧方式的电站锅炉水冷壁壁面高温腐蚀问题为研究对象，从腐蚀机理与燃烧特性角度对水冷壁燃烧区域进行腐蚀特性建模分析，研究水冷壁近壁区域还原性和腐蚀性气氛作用下的硫化物型熔盐腐蚀部位分布规律，腐蚀发生严重的区域将集中在两侧墙的燃烧器周围区域、下层冷灰斗区域、上层燃烧器与顶层燃尽风喷口之间的两侧墙中间区域。现场实测数据验证可知，燃煤电站锅炉水冷壁近壁区域在氧浓度极低情况下，H₂S、CO等物质浓度严重超出腐蚀判定指标要求，水冷壁壁面腐蚀严重，腐蚀发生部位与数值模型结果吻合。结合工程经验，给出了水冷壁壁面高温腐蚀防治的具体措施。

关键词: 燃煤电站锅炉, 水冷壁, 高温腐蚀, 分析, 对策

Abstract:

The object of research is the high-temperature corrosion of the water-cooled wall of the utility boiler in the form of hedge combustion. The corrosion characteristics of the water-cooled wall combustion area are modeled and analyzed from the perspective of corrosion mechanism and combustion characteristics. The distribution of sulfide-type molten salt corrosion parts is distributed. The areas where severe corrosion occurs will be concentrated in the area around the burners on both sides of the wall, the area of the lower cold ash hopper, and the middle of the sides of the wall between the upper burner and the top burnout vent region.The verification of field measured data shows that when the oxygen concentration in the near wall of the water-cooled wall of a coal-fired power plant boiler is extremely low, the concentration of H₂S, CO and other substances exceeds the requirements of the corrosion judgment index.Combined with engineering experience, specific measures for high temperature corrosion prevention of water-cooled walls are given.

Key words: coal-fired power plant boiler, water wall, high temperature corrosion, analysis, countermeasures

中图分类号:

TK224.9

于英利, 付旭晨, 戴莹莹, 荣俊, 高正平, 蔡斌, 胡俊虎. 燃煤电站锅炉水冷壁壁面高温腐蚀问题分析与对策[J]. 化工进展, 2020, 39(S1): 90-96.

Yingli YU, Xuchen FU, Yingying DAI, Jun RONG, Zhengping GAO, Bin CAI, Junhu HU. Analysis and countermeasure of high temperature corrosion on water wall of coal-fired power plant boiler[J]. Chemical Industry and Engineering Progress, 2020, 39(S1): 90-96.

图/表 10

参考文献 10

1	赵虹, 魏勇. 燃煤锅炉水冷壁烟侧高温腐蚀的机理及影响因素[J]. 动力工程, 2002, 22(2): 1700-1704.
	ZHAO Hong, WEI Yong. Discussion on the mechanisms and factors of the gas side hign temperature corrosion in water wall tubes for coal fired boilers[J]. Power Engineering, 2002, 22(2): 1700-1704.
2	李永生,刘建民,陈国庆,等.对冲旋流燃烧锅炉侧墙水冷壁近壁区还原性气氛分布特性[J]. 动力工程学报, 2017, 37(7): 513-519.
	LI Yongsheng, LIU Jianmin, CHEN Guoqing, et al. Distribution characteristics of reductive atmosphere close to the water wall of an opposed firing boiler[J].Journal of Chinese Society of Power Engineering, 2017, 37(7): 513-519.
3	姚斌,曾汉才,焦庆丰.大型锅炉水冷壁高温腐蚀分析及改进措施[J].华中科技大学学报(自然科学版), 2004, 32(3): 20-22.
	YAO Bin, ZENG Hancai, JIAO Qingfeng. The high temperature corrosion on water cooled wall in large-scale boiler and its improvement[J].Journal of Huazhong University of Sci. & Tech.(Nature Science Edition), 2004, 32(3): 20-22.
4	刘鸿国,蔡晖,唐丽英.超超临界机组水冷壁高温腐蚀问题的探讨[J].腐蚀与防护, 2009, 30(8): 577-579.
	LIU Hongguo, CAI Hui, TANG Liying. High temperature corrosion of water cooling wall of extra-super-critical units[J].Corrosion & Protection, 2009, 30(8): 577-579.
5	孟凡冉, 高畅, 金保曻, 等. 异距贴壁风喷口布置方案的数值模拟[J].化工进展, 2017, 36(9): 3237-3242.
	MENG Fanran, GAO Chang, JIN Baosheng, et al. Numerical simulation of near-wall air scheme combined with different jet position[J]. Chemical Industry and Engineering Progress, 2017, 36(9): 3237-3242.
6	李春曦, 许涛, 李敏, 等. 对冲燃烧锅炉防高温硫腐蚀改造的数值研究[J].动力工程学报, 2016, 36(11): 853-861.
	LI Chunxi, XU Tao, LI Min, et al. Retrofit of an opposed firing boiler to prevent high-temperature sulfur corrosion[J]. Journal of Chinese Society of Power Engineering, 2016, 36(11): 853-861.
7	石荣雪, 张适宜, 张胜寒. 基于大数据分析的电厂锅炉水冷壁失效研究[J].化工进展, 2016, 35(9): 2640-2646.
	SHI Rongxue, ZHANG Shiyi, ZHANG Shenghan. Failure investigation on boiler water wall tubes in power plant by large data analysis[J]. Chemical Industry and Engineering Progress, 2016, 35(9): 2640-2646.
8	肖海平, 陈裕辉, 葛金林, 等.电站锅炉省煤器受热面的积灰监测[J].化工进展, 2019, 38(3): 1573-1578.
	XIAO Haiping, CHEN Yuhui, GE Jinlin, et al. Online monitoring heating surface pollution of a boiler economizer in coal-fired power plant[J]. Chemical Industry and Engineering Progress, 2019, 38(3): 1573-1578.
9	陈天杰, 姚露, 刘建民, 等.某660MW前后墙对冲燃煤锅炉贴壁风优化方案的数值模拟[J]. 中国电机工程学报, 2015, 35(20): 5265-5271.
	CHEN Tianjie, YAO Lu, LIU Jianmin, et al. Numerical simulation on the optimization of closing-to-wall air in a 660MW front and rear wall opposed coal-fired boiler[J]. Proceedings of the CSEE, 2015, 35(20): 5265-5271.
10	柳宏刚, 张广才, 王志刚, 等.墙式对冲燃烧锅炉高温腐蚀原因分析与治理[J]. 热力发电, 2013, 42(12): 129-131.
	LIU Honggang, ZHANG Guangcai, WANG Zhigang, et al. High temperature corrosion in wall-firing boiler: reason analysis and treatment[J]. Thermal Power Generation,2013, 42(12): 129-131.

项目名称	数值
一次风温/℃	70
二次风温/℃	354
磨煤机入口风温/℃	234
一次风速/m·s^-1	17.3
二次风速（内环）/m·s^-1	20.4
二次风速（外环）/m·s^-1	40.7
一次风比/%	24.6
煤粉细度R₉₀/%	20

项目名称	数值
一次风温/℃	70
二次风温/℃	354
磨煤机入口风温/℃	234
一次风速/m·s^-1	17.3
二次风速（内环）/m·s^-1	20.4
二次风速（外环）/m·s^-1	40.7
一次风比/%	24.6
煤粉细度R₉₀/%	20

位置	各成分浓度
位置	O₂体积分数/%	CO /μL·L^-1	H₂S /μL·L^-1	NO /μL·L^-1	SO₂ /μL·L^-1	CO₂体积分数/%
上层测孔
甲侧墙前孔	0.5	1570	978	79	88	18.6
甲侧墙中孔	0.2	18753	1486	37	659	18.3
甲侧墙后孔	0.7	1422	71	211	69	18.6
乙侧墙前孔	0.2	23125	738	44	295	17.9
乙侧墙中孔	0.2	19895	1633	59	732	18.2
乙侧墙后孔	0.9	7783	164	260	233	17.6
中层测孔
甲侧墙前孔	0.3	2384	760	45	117	18.3
甲侧墙中孔	0.6	8590	1396	25	176	18.2
甲侧墙后孔	0.4	6211	1288	137	103	18.8
乙侧墙前孔	0.3	9782	1162	32	279	18.1
乙侧墙中孔	0.4	13793	1346	31	292	18.0
乙侧墙后孔	0.6	9159	894	380	244	17.9
下层测孔
甲侧墙前孔	0.4	646	891	24	476	18.9
甲侧墙中孔	0.5	10962	745	19	134	18.6
甲侧墙后孔	0.3	679	697	332	645	18.8
乙侧墙前孔	0.4	4880	943	17	460	18.6
乙侧墙中孔	0.5	14658	492	63	1398	17.8
乙侧墙后孔	0.2	13722	327	261	348	17.8

位置	各成分浓度
位置	O₂体积分数/%	CO /μL·L^-1	H₂S /μL·L^-1	NO /μL·L^-1	SO₂ /μL·L^-1	CO₂体积分数/%
上层测孔
甲侧墙前孔	0.5	1570	978	79	88	18.6
甲侧墙中孔	0.2	18753	1486	37	659	18.3
甲侧墙后孔	0.7	1422	71	211	69	18.6
乙侧墙前孔	0.2	23125	738	44	295	17.9
乙侧墙中孔	0.2	19895	1633	59	732	18.2
乙侧墙后孔	0.9	7783	164	260	233	17.6
中层测孔
甲侧墙前孔	0.3	2384	760	45	117	18.3
甲侧墙中孔	0.6	8590	1396	25	176	18.2
甲侧墙后孔	0.4	6211	1288	137	103	18.8
乙侧墙前孔	0.3	9782	1162	32	279	18.1
乙侧墙中孔	0.4	13793	1346	31	292	18.0
乙侧墙后孔	0.6	9159	894	380	244	17.9
下层测孔
甲侧墙前孔	0.4	646	891	24	476	18.9
甲侧墙中孔	0.5	10962	745	19	134	18.6
甲侧墙后孔	0.3	679	697	332	645	18.8
乙侧墙前孔	0.4	4880	943	17	460	18.6
乙侧墙中孔	0.5	14658	492	63	1398	17.8
乙侧墙后孔	0.2	13722	327	261	348	17.8

[1]	王乐乐, 杨万荣, 姚燕, 刘涛, 何川, 刘逍, 苏胜, 孔凡海, 朱仓海, 向军. SCR脱硝催化剂掺废特性及性能影响[J]. 化工进展, 2023, 42(S1): 489-497.
[2]	李宁, 李金科, 董金善. 乙烯裂解炉多孔介质燃烧器的研究与开发[J]. 化工进展, 2023, 42(S1): 73-83.
[3]	刘阳, 王云刚, 修浩然, 邹立, 白彦渊. 基于动力学分析的核桃壳最佳炭化工艺[J]. 化工进展, 2023, 42(S1): 94-103.
[4]	王胜岩, 邓帅, 赵睿恺. 变电吸附二氧化碳捕集技术研究进展[J]. 化工进展, 2023, 42(S1): 233-245.
[5]	邵志国, 任雯, 许世佩, 聂凡, 许毓, 刘龙杰, 谢水祥, 李兴春, 王庆吉, 谢加才. 终温对油基钻屑热解产物分布和特性影响[J]. 化工进展, 2023, 42(9): 4929-4938.
[6]	白亚迪, 邓帅, 赵睿恺, 赵力, 杨英霞. 变温吸附碳捕集机组标准化测试方案探讨及性能实验[J]. 化工进展, 2023, 42(7): 3834-3846.
[7]	孙旭东, 赵玉莹, 李诗睿, 王琦, 李晓健, 张博. 我国地方性氢能发展政策的文本量化分析[J]. 化工进展, 2023, 42(7): 3478-3488.
[8]	庄捷, 薛锦辉, 赵斌成, 张文艺. 猪粪厌氧消化进程中重金属与腐殖质的有机结合机制[J]. 化工进展, 2023, 42(6): 3281-3291.
[9]	赵尧, 周志辉, 吴红丹, 胡传智, 张国春, 吴睿鹏. Silicalite-1分子筛膜渗透蒸发条件的响应面分析与优化[J]. 化工进展, 2023, 42(5): 2586-2594.
[10]	郭文杰, 翟玉玲, 陈文哲, 申鑫, 邢明. Al₂O₃-CuO/水混合纳米流体对流传热性能及热经济性分析[J]. 化工进展, 2023, 42(5): 2315-2324.
[11]	庞力平, 袁虎, 丘文生, 段立强, 李文学. 深度调峰锅炉水动力特性分析[J]. 化工进展, 2023, 42(4): 1708-1718.
[12]	张成松, 张静, 龚斌, 李明洋, 袁佳新, 李宏业. 自吸射流柔性搅拌桨振动特性[J]. 化工进展, 2023, 42(4): 1728-1738.
[13]	贺山明, 潘界昌, 徐国钻, 李文君, 梁勇. 粗钨酸钠溶液亚铁盐沉淀法除铬、钒的热力学分析及实验验证[J]. 化工进展, 2023, 42(4): 2171-2179.
[14]	刘洪茹, 林文胜. 基于液氢和氨的氢运输链能效和碳排放分析[J]. 化工进展, 2023, 42(3): 1291-1298.
[15]	陈佳昆, 汤健, 夏恒, 乔俊飞. 城市固废炉排炉焚烧过程二𫫇英排放浓度数值仿真[J]. 化工进展, 2023, 42(2): 1061-1072.