二氧化硅溶胶体系的电导行为

黎珊^1,2, 戴红旗¹, 姜兴茂², 陈龙龙²

1 南京林业大学江苏省制浆造纸科学与技术重点实验室, 江苏南京 210037;
2 常州大学石油化工学院, 江苏常州 213164

收稿日期:2014-11-04 修回日期:2015-01-14 出版日期:2015-08-05 发布日期:2015-08-05
通讯作者: 戴红旗,教授,博士生导师,主要从事精细化学品的开发及造纸湿部化学的研究。E-mail hgdhq@njfu.edu.cn;姜兴茂,教授。E-mail jxm@cczu.edu.cn。
作者简介:黎珊(1979—),女,博士研究生,讲师。
基金资助:
国家自然科学基金(21373034, 31470599)及江苏省高校优势学科建设工程(PAPD)项目。

Study on the electric conductivity of silica sol system

LI Shan^1,2, DAI Hongqi¹, JIANG Xingmao², CHEN Longlong²

1 Jiangsu Province Key Lab of Pulp and Paper Science and Technology, Nanjing Forestry University, Nanjing 210037, Jiangsu, China;
2 School of Petrochemical Engineering, Changzhou University, Changzhou 213164, Jiangsu, China

Received:2014-11-04 Revised:2015-01-14 Online:2015-08-05 Published:2015-08-05

摘要/Abstract

摘要： 二氧化硅溶胶的导电性与其储存稳定性及纳米材料的制备和应用密切相关。本文通过Stöber法制备了分散性较好的非晶型二氧化硅纳米微球,用激光粒度分析仪、高分辨透射电子显微镜和X射线衍射仪对微粒进行了表征。通过电导率的变化监测了不同条件下的溶胶-凝胶动力学过程,并详细地研究了影响二氧化硅溶胶体系电导行为的各个因素。实验结果表明,氨水用量对溶胶-凝胶过程的平衡时间有很大影响,氨水用量少,体系平衡时间短,反之亦然。二氧化硅的浓度、粒径、分散介质的温度、pH值和电解质浓度对溶胶体系的电导率都有显著的影响,并得出了二氧化硅的浓度和体系温度与电导率之间呈线性关系,同时发现,硅溶胶体系的电导率与胶体粒子总的比表面积成正比,与颗粒表面的ζ电位也密切相关。

关键词: 二氧化硅, 胶体, 粒度分布, 电导率, 比表面积, ζ电位

Abstract: Electric conductivity of silica sol is closely related to its storage stability and preparation and application of nanomaterials. Mono-dispersed non-crystalline silica nanospheres were fabricated by Stöber process and the resulted microparticles were characterized by laser particle size analyzer, high-resolution transmission electron microscope and X-ray diffractometer. The sol-gel dynamic processes at various conditions were monitored by conductivity variation, and factors affecting the electric conductivity of silica sol system were discussed. The experimental results indicate that the dose of aqueous ammonia has a large impact on the equilibration time of sol-gel process and it decreases with the decrement of the dose of aqueous ammonia, vice versa. The electric conductivity of silica sol system is apparently influenced by the concentration and diameter of SiO₂microparticles, system temperature, pH value and the electrolyte concentration of dispersion medium. It is concluded that the electric conductivity shows a good linear relationship with SiO₂ concentration and system temperature. Meanwhile, it is found that the electric conductivity is proportional with the total surface area of the microparticles of silica sol system, and is closely related to the zeta potential of SiO₂ particle surface.

Key words: silica, colloid, particle size distribution, electric conductivity, specific surface area, zeta potential

中图分类号:

TQ170.2

黎珊, 戴红旗, 姜兴茂, 陈龙龙. 二氧化硅溶胶体系的电导行为[J]. 化工进展, 2015, 34(08): 3093-3098.

LI Shan, DAI Hongqi, JIANG Xingmao, CHEN Longlong. Study on the electric conductivity of silica sol system[J]. Chemical Industry and Engineering Progree, 2015, 34(08): 3093-3098.

参考文献

[1] 李良, 梁汉东, 张海军, 等. 硅溶胶应用评述[J]. 无机盐工业, 2006, 38(8): 8-10.
[2] Snyder K L, Holmes H R, van Wagner M J, et al. Development of vapor deposited silica sol-gel particles for use as a bioactive materials system[J]. Journal of Biomedical Materials Research Part A, 2013, 101(6): 1682-1693.
[3] 廖婵娟, 赵健全, 于萍, 等. 不同结构二氧化硅对聚偏氟乙烯超滤膜的性能影响[J]. 化工进展, 2011, 30(s1): 277-281.
[4] Atalay S, Ma Y, Qian S Z. Analytical model for charge properties of silica particles[J]. Journal of Colloid and Interface Science, 2014, 425: 128-130.
[5] Lu F, Wu S H, Hung Y, et al. Size effect on cell uptake in well-suspended, uniform mesoporous silica nanoparticles[J]. Small, 2009, 5(12): 1408-1413.
[6] Leroy P, Devau N, Revil A, et al. Influence of surface conductivity on the apparent zeta potential of amorphous silica nanoparticles[J]. Journal of Colloid and Interface Science, 2013, 410: 81-93.
[7] Barisik M, Atalay S, Beskok A, et al. Size dependent surface charge properties of silica nanoparticles[J]. Journal of Physical Chemistry C, 2014, 118(4): 1836-1842.
[8] Abbas Z, Labbez C, Nordholm S, et al. Size-dependent surface charging of nanoparticles[J]. Journal of Physical Chemistry C, 2008, 112(15): 5715-5723.
[9] Leroy P, Tournassat C, Bizi M. Influence of surface conductivity on the apparent zeta potential of TiO₂ nanoparticles[J]. Journal of Colloid and Interface Science, 2011, 356(2): 442-453.
[10] Crespy A, Bolèveb A, Revil A. Influence of the Dukhin and Reynolds numbers on the apparent zeta potential of granular porous media[J]. Journal of Colloid and Interface Science, 2007, 305(1): 188-194.
[11] Lyklema J, Minor M. On surface conduction and its role in electrokinetics[J]. Colloids and Surfaces A: Physicochemical and Engineering Aspects, 1998, 140(1): 33-41.
[12] 董鹏. 单分散二氧化硅颗粒的研究进展[J]. 自然科学进展, 2000, 10(3): 201-207.
[13] 王金忠, 赵岩, 张彩碚. 单分散球形SiO₂形成过程的电导率和粘度变化[J]. 硅酸盐通报, 2003(1): 88-91.
[14] Stöber W, Fink A, Bohn E. Controlled growth of monodisperse silica spheres in the micron size range[J]. Journal of Colloid and Interface Science, 1968, 26(1): 62-69.
[15] Giesche H. Synthesis of monodispersed silica powders I. Particle properties and reaction kinetics[J]. Journal of the European Ceramic Society, 1994, 14(3): 189-204.
[16] Razo D A S, Pallavidino L, Garrone E, et al. A version of Stöber synthesis enabling the facile prediction of silica nanospheres size for the fabrication of opal photonic crystals[J]. Journal of Nanoparticle Research, 2008, 10(7): 1225-1229.
[17] Kim J, Lawler D F. Characteristics of zeta potential distribution in silica particles[J]. Bulletin of the Korean Chemical Society, 2005, 26(7): 1083-1089.
[18] Ceram Research Ltd. Zeta potential[J/OL].[2001-10-09]. http: //www. azom. com/article. aspx?ArticleID=935.
[19] Elimelech M, Jia X D, Gregory J, et al. Particle Deposition and Aggregation: Measurement, Modelling and Simulation[M]. U. K., Oxford: Butterworth-Heinemann Ltd., 1998: 23-32.

二氧化硅溶胶体系的电导行为

Study on the electric conductivity of silica sol system

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价

[1]	王尚彬, 欧红香, 薛洪来, 曹海珍, 王钧奇, 毕海普. 黄原胶和纳米二氧化硅对无氟泡沫性能的影响[J]. 化工进展, 2023, 42(9): 4856-4862.
[2]	王兰江, 梁瑜, 汤琼, 唐明兴, 李学宽, 刘雷, 董晋湘. 快速热解铂前体合成高分散的Pt/HY催化剂及其萘深度加氢性能[J]. 化工进展, 2023, 42(8): 4159-4166.
[3]	吴霞, 蒋勋涛, 张余晓, 吕慧园, 黄方, 于筱溪. 基于液滴微流控技术的蛋白质结晶[J]. 化工进展, 2023, 42(4): 2024-2030.
[4]	杨程瑞雪, 黄琪媛, 冉建速, 崔耘通, 王健健. 磷酸修饰二氧化硅负载钯催化剂用于木质素衍生物高效水相低温加氢脱氧[J]. 化工进展, 2023, 42(10): 5179-5190.
[5]	潘月磊, 程旭东, 闫明远, 何盼, 张和平. 二氧化硅气凝胶及其在保温隔热领域应用进展[J]. 化工进展, 2023, 42(1): 297-309.
[6]	王一茹, 宋小三, 水博阳, 王三反. 胺功能化介孔二氧化硅捕集CO₂的研究进展[J]. 化工进展, 2022, 41(S1): 536-544.
[7]	郭振雪, 于海斌, 张国辉, 张景成, 卢雁飞, 何艳贞, 孙彦民, 韩恩山. Si改性对NiMo/Al₂O₃催化剂加氢脱硫性能的影响[J]. 化工进展, 2022, 41(S1): 210-220.
[8]	张洪铭, 卢炯元, 王三反. 燃料电池用阴离子交换膜分子结构研究进展[J]. 化工进展, 2022, 41(S1): 318-330.
[9]	王光绪, 金晶, 张云鹏, 刘薄鉴治, 梁诗雨, 翟中媛. 硅钙摩尔比对准东煤燃烧过程中矿物演变及灰熔融特性的影响[J]. 化工进展, 2022, 41(8): 4140-4146.
[10]	单清雯, 张娟, 王亚娟, 刘文强. 聚合离子液体的合成及其吸附脱硫性能[J]. 化工进展, 2022, 41(8): 4571-4579.
[11]	李娟娟, 张天永, 李祥高. 电泳显示用高质量铁锰黑纳米分散系的构建[J]. 化工进展, 2022, 41(6): 3178-3185.
[12]	章雪莹, 马俊, 何林, 隋红, 李鑫钢. 沥青岩中界面活性沥青质分子结构及其在矿物表面吸附特征[J]. 化工进展, 2022, 41(2): 628-636.
[13]	武晨浩, 李昆锋, 李肖华, 费志方, 张震, 杨自春. 二氧化硅气凝胶常压干燥工艺的研究进展[J]. 化工进展, 2022, 41(2): 837-847.
[14]	韩芬, 杨娜, 孙永利, 姜斌, 肖晓明, 张吕鸿. 玻璃纤维聚结器脱除油中乳化水[J]. 化工进展, 2022, 41(12): 6723-6732.
[15]	李群艳, 孙路瑶, 常其飞, 周运炉. 磁性Fe₃O₄@SiO₂@介孔SiO₂空心微球的制备及漆酶固定化[J]. 化工进展, 2022, 41(10): 5494-5500.