N,N-双十二烷基-3,6-O - 磺丙基壳聚糖对紫杉醇的增溶作用

化工进展

N,N-双十二烷基-3,6-O - 磺丙基壳聚糖对紫杉醇的增溶作用

张晓林，李明春，辛梅华，王军

华侨大学材料科学与工程学院，环境友好功能材料教育部工程中心, 福建厦门 361021

出版日期:2012-12-05 发布日期:2012-12-05

Solubilization ability of N,N-dilauryl-3,6-O - sulfopropyl chitosan polymeric micelles on paclitaxel

ZHANG Xiaolin, LI Mingchun, XIN Meihua, WANG Jun

College of Material Science and Engineering, Huaqiao University，Engineering Research Center of Environment-Friendly Functional Materials, Ministry of Education, Xiamen 361021，Fujian，China

Online:2012-12-05 Published:2012-12-05

摘要/Abstract

摘要： 合成高取代度的N,N-双十二烷基-3,6-O-磺丙基壳聚糖（SPDLCS）双亲性衍生物，通过透析法制备了SPDLCS载紫杉醇（PTX）胶束，考察了投料比对载药量、包封率、胶束粒径和Zeta电位的影响，并对胶束形态及其稳定性进行了研究。结果表明，紫杉醇以无定形态包载于胶束的疏水内核中，最优投料比为SPDLCS∶PTX=1∶1.1，载药量为50.36 %，包封率为92.2 %，对紫杉醇的增溶能力达6.08 mg/mL。载药胶束呈现分散性良好的球形颗粒，平均粒径为141.1 nm，Zeta电位为?34.1 mV。稳定性实验表明SPDLCS载紫杉醇胶束具有良好的稳定性，SPDLCS是潜在的疏水药物高增溶载体材料。

关键词: 双亲性壳聚糖衍生物, 聚合物胶束, 紫杉醇, 增溶

Abstract: A novel chitosan amphiphilic derivative with high degree of substitution, N,N-dilauryl-3,6-O-sulfopropyl chitosan (SPDLCS), was synthesized. PTX-loaded SPDLCS micelles were prepared by a dialysis method. The impact of the feed ratio of SPDLCS to PTX on drug-loading concentration and its efficiency, together with the mean diameter and Zeta potential were investigated. The morphology and stability of micelles were further studied. The results show that SPDLCS self-assembled nanomicelle with amorphous PTX inside was successfully prepared. The drug loading concentration (DLC) and drug loading efficiency(DLE) of PTX-loaded SPDLCS micelles with the average size of 141.1 nm, zeta potential of -34.1 mV and spherical shape were as high as 50.36 % and 92.2 % respectively under the optimal feed ratio of SPDLCS∶PTX = 1∶1.1. The results of stability test show that the micelles system with the DLC of 50.36 % displays good stability and the PTX concentration of 6.08 mg/mL was found in this aqueous solution, which has not been reported yet. It suggests that the product SPDLCS may be used as a carrier material with a high solubilization capacity for hydrophobic drug.

Key words: amphiphilic chitosan, polymeric micelles, paclitexel, solubilization

张晓林，李明春，辛梅华，王军. N,N-双十二烷基-3,6-O - 磺丙基壳聚糖对紫杉醇的增溶作用[J]. 化工进展.

ZHANG Xiaolin, LI Mingchun, XIN Meihua, WANG Jun. Solubilization ability of N,N-dilauryl-3,6-O - sulfopropyl chitosan polymeric micelles on paclitaxel[J]. Chemical Industry and Engineering Progree.

[1]	徐波, 蒋国斌, 于劲磊, 胡金燕, 赵靓, 徐炳科. 不同表面活性剂对单相微乳液特性的影响[J]. 化工进展, 2021, 40(S1): 350-356.
[2]	尚泽仁, 胡卫国, 汤伟伟, 贾丽娜, 李鸣晨, 赵燕晓, 魏宁, 龚俊波. 离子液体在药物晶体工程中的应用[J]. 化工进展, 2019, 38(05): 2389-2401.
[3]	周平平, 刘会娥, 陈爽, 于文赫, 张秀霞. 无机盐对十六烷基三甲基溴化铵（CTAB）微乳液相行为的影响[J]. 化工进展, 2018, 37(08): 2942-2947.
[4]	朱梦琴, 葛璐, 邱立朋. 透明质酸自组装聚合物胶束的制备及表征[J]. 化工进展, 2016, 35(S2): 283-286.
[5]	张昕欣1，吴翰桂1，奚立民1，王玲萍2 . 微生物发酵法生产紫杉醇的研究进展[J]. 化工进展, 2012, 31(02 ): 392-396.
[6]	胡印滔，辛梅华，李明春. 壳聚糖衍生物的表面活性及其药物增溶性研究进展[J]. 化工进展, 2011, 30(10): 2228-.
[7]	裘迪，朱宏. 聚乳酸类载紫杉醇纳米粒表面修饰的研究进展 [J]. 化工进展, 2009, 28(7): 1198-.
[8]	代文亮，陶文沂. 一株紫杉醇产生菌发酵条件的初步研究 [J]. 化工进展, 2008, 27(6): 883-.