木粉疏水改性对HDPE基木塑复合材料性能的影响

doi:10.16085/j.issn.1000-6613.2019-1873

化工进展 ›› 2020, Vol. 39 ›› Issue (9): 3487-3493.DOI: 10.16085/j.issn.1000-6613.2019-1873

• 专栏：材料科学与技术 • 上一篇下一篇

木粉疏水改性对HDPE基木塑复合材料性能的影响

张璐¹(), 孙金鹏², 俞青源¹, 李如燕³, 张云浩³, 王文俊¹()

^1.北京理工大学材料学院，北京 0008
^2.北华航天工业学院材料工程学院，河北廊坊 065000
^3.昆明理工大学固体废弃物资源化国家工程研究中心，云南昆明 65009

出版日期:2020-09-05 发布日期:2020-09-11
通讯作者: 王文俊
作者简介:张璐（1993—），女，硕士研究生，研究方向为纳米纤维素、聚合物基复合材料。E-mail：zhanglu1823@163.com。

Effect of hydrophobic modification of wood flour on properties of HDPE based wood plastic composites

Lu ZHANG¹(), Jinpeng SUN², Qingyuan YU¹, Ruyan LI³, Yunhao ZHANG³, Wenjun WANG¹()

^1.School of Materials Science and Engineering, Beijing Institute of Technology, Beijing 100081, China
^2.College of Material and Engineering, North China Institute of Aerospace Engineering, Langfang 065000, Hebei, China
^3.National Engineering Research Center of Waste Resource Recovery, Kunming University of Science and Technology, Kunming 650033, Yunnan, China

Online:2020-09-05 Published:2020-09-11
Contact: Wenjun WANG

摘要/Abstract

摘要：

采用一种操作简便且易于工业推广的方法对木粉进行疏水改性，具体过程为：将3种可热聚合的单体，即甲基丙烯酸甲酯（MMA）、甲基丙烯酸丁酯（BMA）和苯乙烯（St）均匀喷洒在木粉上，经过预热处理后，与配方中其他组分，如高密度聚乙烯（HDPE）和马来酸酐接枝聚乙烯（MAPE）等通过高速混合机混合均匀，采用双螺杆挤出机造粒后，注射制备木塑复合材料（WPC）样条，测试其力学性能。另外，考察了疏水改性对WPC接触角、维卡软化温度、洛氏硬度、吸水性能、热性能的影响规律。结果表明：疏水改性后WPC的接触角增大，木粉和HDPE的界面相容性改善，力学性能得到明显提高。其中，当MMA、BMA和St的添加量为3%时，WPC的力学性能最好，与疏水改性前相比，弯曲强度分别提高了17.3%、26.3%和27.5%，弯曲模量分别提高了24.4%、24.4%和26.0%，冲击强度分别提高了54.7%、57.7%和60.5%。此外，疏水改性后WPC的维卡软化温度、洛氏硬度、耐水性和耐热性也得到改善。

关键词: 木塑复合材料, 木粉疏水改性, 力学性能, 吸水性能

Abstract:

The wood flour was hydrophobic modified in a simple and scalable way. The specific process was as follows. The three kinds of thermal polymerization monomers, namely methyl methacrylate (MMA), butyl methacrylate (BMA) and styrene (St) were evenly sprayed on the wood flour, respectively. After preheating treatment, the wood flour was throughly mixed with other components in formula such as high density polyethylene (HDPE) and maleic anhydride grafted polyethylene (MAPE) by high-speed mixers, followed granulation by twin-screw extruder and injection molding to obtain testing samples of the wood plastic composites (WPC). The mechanical properties of WPC were tested. In addition, the effects of hydrophobic modification on the contact angle, Vica softening temperature, Rockwell hardness, water absorption and thermal properties of WPC were investigated. The results showed that the contact angle of WPC increased after hydrophobic modification. The interfacial compatibility between wood flour and HDPE was improved and the mechanical properties of WPC were obviously improved. When the addition of MMA, BMA and St was 3%, the mechanical properties of WPC reached their peaks. Compared with those before hydrophobic modification, the flexural strength increased by 17.3%, 26.3% and 27.5%, the flexural modulus by 24.4%, 24.4% and 26.0%, and the impact strength by 54.7%, 57.7% and 60.5%, respectively, corresponding to MMA, BMA and St. In addition, Vica softening temperature, Rockwell hardness, water resistance and heat resistance of WPC were also improved.

Key words: wood plastic composites, hydrophobic modification of wood flour, mechanical properties, water absorption

中图分类号:

TB332

张璐, 孙金鹏, 俞青源, 李如燕, 张云浩, 王文俊. 木粉疏水改性对HDPE基木塑复合材料性能的影响[J]. 化工进展, 2020, 39(9): 3487-3493.

Lu ZHANG, Jinpeng SUN, Qingyuan YU, Ruyan LI, Yunhao ZHANG, Wenjun WANG. Effect of hydrophobic modification of wood flour on properties of HDPE based wood plastic composites[J]. Chemical Industry and Engineering Progress, 2020, 39(9): 3487-3493.

参考文献

1	LI L, HAO T T, CHI T. Evaluation on China’s forestry resources efficiency based on big data[J]. Journal of Cleaner Production, 2017, 142(2): 513-523.
2	BORAH J S, KIM D S. Recent development in thermoplastic/wood composites and nanocomposites: a review[J]. Korean Journal of Chemical Engineering, 2016, 33(11): 3035-3049.
3	KASEEM M, HAMAD K, DERI F, et al. Material properties of polyethylene/wood composites: a review of recent works[J]. Polymer Science Series A, 2015, 57(6): 689-703.
4	LI D, LIU L, WANG K Q. Applications of wood-plastic composites (WPC) in the design of multimedia speaker box[J]. Advanced Materials Research, 2014, 842:100-103.
5	ASHORI A. Wood-plastic composites as promising green-composites for automotive industries![J]. Bioresource Technology, 2008, 99(11): 4661-4667.
6	SMITH P M, WOLCOTT M P. Opportunities for wood/natural fiber-plastic composites in residential and industrial applications[J]. Forest Products Journal, 2006, 56(3): 4-11.
7	ABDELMOULEH M, BOUFI S, BELGACEM M N, et al. Short natural-fibre reinforced polyethylene and natural rubber composites: effect of silane coupling agents and fibres loading[J]. Composites Science and Technology, 2007, 67(7/8): 1627-1639.
8	QIANG T, YU D, GAO H H. Wood flour/polylactide biocomposites toughened with polyhydroxyalkanoates[J]. Journal of Applied Polymer Science, 2012, 124(3): 1831-1839.
9	SHAH H L, MATUANA L M. Novel coupling agents for PVC/wood-flour composites[J]. Journal of Vinyl & Additive Technology, 2005, 11(4): 160-165.
10	XU K M, ZHENG Z F, HUANG S Y, et al. Influence of glycidyl methacrylate grafting on the mechanical, water absorption, and thermal properties of recycled high-density polyethylene/rubber seed shell particle composites[J]. Bioresources, 2016, 11(1): 2617-2628.
11	FANG Y Q, WANG Q W, GUO C G, et al. Effect of zinc borate andwood flour on thermal degradation and fire retardancy of polyvinyl chloride (PVC) composites[J]. Analytical and Applied Pyrolysis, 2013, 100: 230-236.
12	OU R X, WANG Q W, WOLCOTT M P, et al. Effects of chemical modification of wood flour on the rheological properties of high-density polyethylene blends[J]. Journal of Applied Polymer Science, 2014, 131: 4120023.
13	CHEN J X, WANG Y, GU C L, et al. Enhancement of the mechanical properties of basalt fiber-wood-plastic composites via maleic anhydride grafted high-density polyethylene (MAPE) addition[J]. Materials, 2013, 6(6): 2483-2496.
14	CUI Y H, LEE S, TAO J. Effects of alkaline and silane treatments on the water-resistance properties of wood-fiber-reinforced recycled plastic composites[J]. Journal of Vinyl & Additive Technology, 2008, 14(4): 211-220.
15	LIU H, WU Q, HAN G, et al. Compatibilizing and toughening bamboo flour-filled HDPE composites: mechanical properties and morphologies[J]. Composites A: Applied Science and Manufacturing, 2008, 39(12): 1891-1900.
16	WANG Q W, XIAO Z F, WANG W H, et al. Coupling pattern and efficacy of organofunctional silanes in wood flour-filled polypropylene or polyethylene composites[J]. Journal of Composite Materials, 2015, 49(6): 677-684.
17	赵爽，刘振国，高天正，等. 自聚甲基丙烯酸甲酯的结构及性能[J]. 中国塑料, 2016, 30(10): 20-24.
17	ZHAO Shuang, LIU Zhenguo, GAO Tianzheng, et al. Structure and properties of spontaneously poly(methyl methacrylate)[J]. China Plastics, 2016, 30(10): 20-24.
18	秦霁光，郭文平，张政. 苯乙烯热引发本体聚合的动力学研究 1: 转化率与时间的关系[J]. 化学反应工程与工艺, 2001, 4(17): 308-315.
18	QIN Qiguang, GUO Wenping, ZHANG Zheng. A study on kinetics of bulk thermal polymeriza-tion of styrene 1: Relation between conversion and time[J]. Chemical Reaction Engineering and Technology, 2001, 4(17): 308-315
19	杨景辉，陈超，栾英豪. 甲基丙烯酸丁酯过氧化物低聚物的制备及其引发作用[J]. 华东理工大学学报(自然科学版), 2013, 39(5): 549-553.
19	YANG Jinghun, CHEN Chao, LUAN Yinghao. Preparation and initiation of performance poly (butyl methacrylate)[J]. Journal of East China University of Science and Technology (Natural Science Edition), 2013, 39(5): 549-553.
20	YEH S K, KIM K J, GUPTA R K. Synergistic effect of coupling agents on polypropylene-based wood-plastic composites[J]. Journal of Applied Polymer Science, 2013, 127(S2): 1047-1053.
21	LI H B, LI Q, YAN M L. Influence of operation procedures on vicat softening temperature of thermoplastic materials[J]. Advanced Materials Research, 2011, 291/292/293/294: 1820-1824.

[1]	王家庆, 宋广伟, 李强, 郭帅成, DAI Qingli. 橡胶混凝土界面改性方法及性能提升路径[J]. 化工进展, 2023, 42(S1): 328-343.
[2]	刘大晨, 杜明慧, 王衡. 交联型特辛基酚醛树脂酚羟基间位的溴化改性[J]. 化工进展, 2022, 41(S1): 382-388.
[3]	刘竞, 郑新国, 李铁军, 王财平, 赵彦旭, 李颖, 楼梁伟, 沈伟. 可再分散乳化沥青粉末改性水泥砂浆的力学性能和微观形貌[J]. 化工进展, 2022, 41(4): 2015-2021.
[4]	马星星, 冯亚凯. 偶联剂改性氧化铈提高硅凝胶的耐热氧性能[J]. 化工进展, 2022, 41(2): 874-880.
[5]	尹洪贺, 沈绍传, 齐亮, 姚克俭. 新型多降液管塔板的流体力学性能及其流场CFD模拟[J]. 化工进展, 2022, 41(2): 601-608.
[6]	杨立宁, 郑东昊, 王立新, 杨光. 基于蜻蜓翅脉结构的连续碳纤维增强树脂基复合材料仿生设计与增材制造[J]. 化工进展, 2022, 41(11): 5961-5967.
[7]	金浩, 刘杏, 林咏梅. 植酸改性的明胶复合膜制备及其结构与性能分析[J]. 化工进展, 2021, 40(7): 3847-3853.
[8]	王文玉, 董瑞宝, 李志波, 潘广勤. 液体低分子聚异戊二烯改性丁腈橡胶发泡材料[J]. 化工进展, 2020, 39(8): 3230-3235.
[9]	郑帼,苗同梦,吴波,周存. 高强高模维纶纤维的表面修饰及其在水泥中的分散性[J]. 化工进展, 2020, 39(1): 250-256.
[10]	杨世诚, 孙琦, 谌伦建, 张玉龙, 薛晓晓, 仪桂云. 赤泥改性及其对丁苯橡胶复合材料微观结构和力学性能的影响[J]. 化工进展, 2019, 38(07): 3297-3303.
[11]	李思漩, 夏蕾, 李靖宇, 刘晓刚, 孙巾茹, 迟姚玲, 王虹, 李翠清, 宋永吉. 成型条件对Co/ZSM-5催化剂催化分解N₂O性能影响[J]. 化工进展, 2019, 38(04): 1746-1752.
[12]	姚彬彬, 阚泽. 天然虾青素改性白炭黑/天然橡胶复合材料的制备与性能[J]. 化工进展, 2019, 38(04): 1872-1878.
[13]	张政和,杨卫民,谭晶,李好义. 碳纤维石墨化技术研究进展[J]. 化工进展, 2019, 38(03): 1434-1442.
[14]	迟长云, 李英杰. 钙基碳载体造粒的捕集CO特性及力学性能[J]. 化工进展, 2018, 37(12): 4908-4916.
[15]	戴姗姗, 寇子敏, 刘艳, 赵晓文. SiO₂/聚丙烯酰胺核壳结构复合材料的分子动力学模拟[J]. 化工进展, 2018, 37(09): 3547-3554.

木粉疏水改性对HDPE基木塑复合材料性能的影响

Effect of hydrophobic modification of wood flour on properties of HDPE based wood plastic composites

RichHTML

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价