Preparation and properties of GPs-PVA/MCE multifunctional hybrid membrane

doi:10.16085/j.issn.1000-6613.2020-2460

Abstract

Abstract:

A multifunctional hybrid membrane was obtained by assembling of geopolymer nanoparticles (GPs) and polyvinyl alcohol (PVA) on the surface of mixed cellulose membrane (MCE) through vacuum filtration. The effects of particle size and amount of GPs on the performance of hybrid membrane were investigated. The results showed that the performance of the hybrid membrane was the best with water flux of 11293L/(m²·h·MPa) when the content of GPs was 0.15g. The structure of the hybrid membrane was characterized by SEM, FTIR, AFM and XRD, and the removal performance of the hybrid membrane for different pollutants was investigated. The results indicated that the removal rate of 50nm polystyrene microspheres and emulsified oil in water could reach 100% and 99.87%, respectively by pore interception. The removal rate of cationic dyes in water could also reach 100% by adsorption. Compared to the original MCE, the removal rate was increased by 528.54%, 25.78% and 90.96%, respectively. When the hybrid membrane was used to filter the oil emulsion in a continuous mode, the fluxes decreased only by 21.70% after 1h operation, while the flux of MCE decreased by 95.70%. The results implied the good antifouling performance of the hybrid membrane, which accordingly had a great potential for practical application in water purification.

Key words: geopolymer nanoparticles, polyvinyl alcohol, hybrid membrane, dye

摘要：

地聚物微纳米粒子（GPs）经聚乙烯醇（PVA）修饰后，采用真空抽滤法将其组装在混合纤维素基膜（MCE）表面，得到多功能地聚物颗粒-聚乙烯醇/混合纤维素杂化膜（GPs-PVA/MCE）。本文考察了GPs的添加量对杂化膜结构和性能的影响，通过SEM、FTIR、AFM、XRD等表征杂化膜的结构。结果表明GPs添加量为0.15g时制备的杂化膜性能最佳，水通量为11293L/(m²·h·MPa)。该多功能杂化膜对不同污染物均表现出优异的去除性能：通过孔道截留作用可去除水中100%的50nm聚苯乙烯微球和99.87%的乳化油；通过吸附作用亦可去除水中100%的阳离子型染料；比原始MCE膜分别提升了528.54%、25.78%、90.96%。特别是在连续处理含油乳液时，该杂化膜使用1h后通量仅降低了21.70%，远低于MCE膜的95.70%，说明其抗污染性能得到显著提升，显示出良好的应用潜力。

关键词: 地聚物微纳米颗粒, 聚乙烯醇, 杂化膜, 染料

CLC Number:

TQ352

SONG Ying, GE Yuanyuan, HAN Yurong, ZHOU Qinyi, HUANG Laitao, ZHOU Jian. Preparation and properties of GPs-PVA/MCE multifunctional hybrid membrane[J]. Chemical Industry and Engineering Progress, 2021, 40(11): 6287-6294.

宋颖, 葛圆圆, 韩玉蓉, 周覃艺, 黄来涛, 周剑. GPs-PVA/MCE多功能杂化膜的制备及性能[J]. 化工进展, 2021, 40(11): 6287-6294.

Figures/Tables 7

References 35

1	ALBERGAMO V, BLANKERT B, CORNELISSE E R, et al. Removal of polar organic micropollutants by pilot-scale reverse osmosis drinking water treatment[J]. Water Research, 2019, 148: 535-545.
2	TANG Y Y, XU J, GAO C J. Ultrafiltration membranes with ultrafast water transport tuned via different substrates[J]. Chemical Engineering Journal, 2016, 303: 322-330.
3	HAMOUDA R A, EL-NAGGAR N E, DOLEIB N M, et al. Bioprocessing strategies for cost-effective simultaneous removal of chromium and malachite green by marine alga Enteromorpha intestinalis[J]. Scientific Reports, 2020, 10: 13479.
4	MA J, GUO X, YING Y, et al. Composite ultrafiltration membrane tailored by MOF@GO with highly improved water purification performance[J]. Chemical Engineering Journal, 2017, 313: 890-898.
5	HASANZADEH M, SIMCHI A, SHAHRIYARI FAR H. Nanoporous composites of activated carbon-metal organic frameworks for organic dye adsorption: synthesis, adsorption mechanism and kinetics studies[J]. Journal of Industrial and Engineering Chemistry, 2020, 81: 405-414.
6	ZIA Q, TABASSUM M, LU Z H, et al. Porous poly(L-lactic acid)/chitosan nanofibres for copper ion adsorption[J]. Carbohydrate Polymers, 2020, 227: 115343.
7	GE Y Y, CUI X M, LIAO C L, et al. Facile fabrication of green geopolymer/alginate hybrid spheres for efficient removal of Cu(‍Ⅱ) in water: batch and column studies[J]. Chemical Engineering Journal, 2017, 311: 126-134.
8	HUANG J Q, LI Z L, ZHANG J B, et al. In-situ synchronous carbonation and self-activation of biochar/geopolymer composite membrane: enhanced catalyst for oxidative degradation of tetracycline in water[J]. Chemical Engineering Journal, 2020, 397: 125528.
9	ZINADINI S, ZINATIZADEH A A, RAHIMI M, et al. Novel high flux antifouling nanofiltration membranes for dye removal containing carboxymethyl chitosan coated Fe₃O₄ nanoparticles[J]. Desalination, 2014, 349: 145-154.
10	刘超, 董岸杰, 张建华. 改性聚乙烯醇膜的研究进展[J]. 化工进展, 2021, 40(6): 3258-3269.
	LIU C, DONG A J, ZHANG J H. Research progress of modified polyvinyl alcohol membrane[J]. Chemical Industry and Engineering Progress, 2021, 40(6): 3258-3269.
11	WALTHER A, BJURHAGER I, MALHO J M, et al. Large-area, lightweight and thick biomimetic composites with superior material properties via fast, economic, and green pathways[J]. Nano Letters, 2010, 10(8): 2742-2748.
12	WANG J F, CHENG Q F, LIN L, et al. Understanding the relationship of performance with nanofiller content in the biomimetic layered nanocomposites[J]. Nanoscale, 2013, 5(14): 6356.
13	E S F, NING D D, WANG Y F, et al. Ternary synergistic strengthening and toughening of bio-inspired TEMPO-oxidized cellulose nanofibers/borax/polyvinyl alcohol composite film with high transparency[J]. ACS Sustainable Chemistry & Engineering, 2020, 8(41): 15661-15669.
14	YANG W J, QI G C, KENNY J M, et al. Effect of cellulose nanocrystals and lignin nanoparticles on mechanical, antioxidant and water vapour barrier properties of glutaraldehyde crosslinked PVA films[J]. Polymers, 2020, 12(6): 1364.
15	RAMEZAN ZADEH M H, SEIFI M. Synthesis and physical investigation of PVA-based cast films reinforced with non-covalently functionalized magnetite-deposited carbon nanotubes[J]. Materials Research Express, 2019, 6(6): 066113.
16	JI T T, ZHANG R, DONG X R, et al. Effects of ultrasonication time on the properties of polyvinyl alcohol/sodium carboxymethyl cellulose/nano-ZnO/multilayer graphene nanoplatelet composite films[J]. Nanomaterials, 2020, 10(9): 1797.
17	LYU D, WANG R X, TANG G S, et al. Ecofriendly electrospun membranes loaded with visible-light-responding nanoparticles for multifunctional usages: highly efficient air filtration, dye scavenging, and bactericidal activity[J]. ACS Applied Materials & Interfaces, 2019, 11(13): 12880-12889.
18	LUUKKONEN T, YLINIEMI J, SREENIVASAN H, et al. Ag- or Cu-modified geopolymer filters for water treatment manufactured by 3D printing, direct foaming, or granulation[J]. Scientific Reports, 2020, 10: 7233.
19	蒋旭光, 龙凌, 赵晓利, 等. 固化材料在生活垃圾焚烧飞灰处置中的应用概况及前景[J]. 化工进展, 2019, 38(S1): 216-225.
	JIANG Xuguang, LONG Ling, ZHAO Xiaoli, et al. Application of solidified materials in disposal of MSWI fly ash[J]. Chemical Industry and Engineering Progress, 2019, 38(S1): 216-225.
20	SONG Y, LI Z L, ZHANG J B, et al. A low-cost biomimetic heterostructured multilayer membrane with geopolymer microparticles for broad-spectrum water purification[J]. ACS Applied Materials & Interfaces, 2020, 12(10): 12133-12142.
21	WEN G, GAO X Y, GUO Z G. Simple fabrication of a multifunctional inorganic paper with high efficiency separations for both liquids and particles[J]. Journal of Materials Chemistry A, 2018, 6(43): 21524-21531.
22	CHONG J Y, WANG B, MATTEVI C, et al. Dynamic microstructure of graphene oxide membranes and the permeation flux[J]. Journal of Membrane Science, 2018, 549: 385-392.
23	ZHU X W, CHENG X X, XING J J, et al. In-situ covalently bonded supramolecular-based protective layer for improving chlorine resistance of thin-film composite nanofiltration membranes[J]. Desalination, 2020, 474: 114197.
24	ZHAO B, MA W Z, ZHANG P, et al. Permeation and diffusion of nutrient ions in poly (vinyl alcohol) hydrogel membrane[J]. Chemical Papers, 2020, 74(11): 3913-3923.
25	王司雯, 李秋莹, 张东栋, 等. 聚乙烯醇/普鲁兰多糖纳米纤维膜的制备及表征[J]. 包装与食品机械, 2019, 37(6): 8-13.
	WANG Siwen, LI Qiuying, ZHANG Dongdong, et al. Preparation and characterization of polyvinyl alcohol/pullulan nanofibers[J]. Packaging and Food Machinery, 2019, 37(6): 8-13.
26	QING W H, LI X H, WU Y F, et al. In situ silica growth for superhydrophilic-underwater superoleophobic Silica/PVA nanofibrous membrane for gravity-driven oil-in-water emulsion separation[J]. Journal of Membrane Science, 2020, 612: 118476.
27	GAO S J, ZHU Y Z, WANG J L, et al. Layer-by-layer construction of Cu²⁺/alginate multilayer modified ultrafiltration membrane with bioinspired superwetting property for high-efficient crude-oil-in-water emulsion separation[J]. Advanced Functional Materials, 2018, 28(49): 1801944.
28	LIU H L, YU H, YUAN X, et al. Amino-functionalized mesoporous PVA/SiO₂ hybrids coated membrane for simultaneous removal of oils and water-soluble contaminants from emulsion[J]. Chemical Engineering Journal, 2019, 374: 1394-1402.
29	GHAFFAR A, CHEN C, ZHU X Y, et al. Underwater superoleophobic PVA GO nanofibrous membranes for emulsified oily water purification[J]. Environmental Science: Nano, 2019, 6(12): 3723-3733.
30	XU X, LONG Y W, LI Q, et al. Modified cellulose membrane with good durability for effective oil-in-water emulsion treatment[J]. Journal of Cleaner Production, 2019, 211: 1463-1470.
31	TIAN M, LIAO Y, WANG R. Engineering a superwetting thin film nanofibrous composite membrane with excellent antifouling and self-cleaning properties to separate surfactant-stabilized oil-in-water emulsions[J]. Journal of Membrane Science, 2020, 596: 117721.
32	VENKATESH K, ARTHANAREESWARAN G, CHANDRA BOSE A, et al. Diethylenetriaminepentaacetic acid-functionalized multi-walled carbon nanotubes/titanium oxide-PVDF nanofiber membrane for effective separation of oil/water emulsion[J]. Separation and Purification Technology, 2021, 257: 117926.
33	WU J D, HOU Z Q, YU Z X, et al. Facile preparation of metal-polyphenol coordination complex coated PVDF membrane for oil/water emulsion separation[J]. Separation and Purification Technology, 2021, 258: 118022.
34	ZHANG L Y, XUE W, GU L M. Modification of hyperbranched hemicellulose polymer and its application in adsorbing acid dyes[J]. Cellulose, 2019, 26(9): 5583-5601.
35	SIYAL A A, SHAMSUDDIN M R, KHAN M I, et al. A review on geopolymers as emerging materials for the adsorption of heavy metals and dyes[J]. Journal of Environmental Management, 2018, 224: 327-339.

样品名称	油类型	压力/MPa	分离效率/%	通量/L·m^-2·h^-1·MPa^-1	参考文献
二氧化硅/PVA纳米纤维膜	正庚烷	0	≥95%	1500	［26］
介孔PVA/SiO₂杂化涂层膜	环己烷	0.09	—	5442.6	［28］
PVA-GO纳米纤维膜	己烷	0	99	45	［29］
纤维素-PVA膜	己烷	0	99.99	37	［30］
PVA/CNTs-PAN	菜籽油	0.02	93	48	［31］
多壁碳纳米管/TiO₂-PVDF纳米纤维膜	己烷	0.1	97.4	8253	［32］
金属-多酚配位复合涂层PVDF膜	正己烷	0.01	98.53	4968	［33］
GPs-PVA/MCE	正十六烷	0.09	99.87	2814	本文

样品名称	油类型	压力/MPa	分离效率/%	通量/L·m^-2·h^-1·MPa^-1	参考文献
二氧化硅/PVA纳米纤维膜	正庚烷	0	≥95%	1500	［26］
介孔PVA/SiO₂杂化涂层膜	环己烷	0.09	—	5442.6	［28］
PVA-GO纳米纤维膜	己烷	0	99	45	［29］
纤维素-PVA膜	己烷	0	99.99	37	［30］
PVA/CNTs-PAN	菜籽油	0.02	93	48	［31］
多壁碳纳米管/TiO₂-PVDF纳米纤维膜	己烷	0.1	97.4	8253	［32］
金属-多酚配位复合涂层PVDF膜	正己烷	0.01	98.53	4968	［33］
GPs-PVA/MCE	正十六烷	0.09	99.87	2814	本文

[1]	WU Fengzhen, LIU Zhiwei, XIE Wenjie, YOU Yating, LAI Rouqiong, CHEN Yandan, LIN Guanfeng, LU Beili. Preparation of biomass derived Fe/N co-doped porous carbon and its application for catalytic degradation of Rhodamine B via peroxymonosulfate activation [J]. Chemical Industry and Engineering Progress, 2023, 42(6): 3292-3301.
[2]	TIAN Fang, GUO Guang, DING Keqiang, YANG Feng, LIU Chong, WANG Huiya. Isolation of halophilic bacterium and their decolorization characteristics and mechanism of azo dyes [J]. Chemical Industry and Engineering Progress, 2023, 42(4): 2115-2121.
[3]	WANG Yan, QIN Zhenping, LIU Yue, ZHANG Wenhai, GUO Hongxia. Preparation and properties of β-cyclodextrin in-situ modified MoS₂ tubular ceramic composite membrane [J]. Chemical Industry and Engineering Progress, 2023, 42(10): 5373-5380.
[4]	XU Chunshu, YAO Qingda, LIANG Yongxian, ZHOU Hualong. Structural design of metal-organic framework materials and its adsorption performance on synthetic dyes [J]. Chemical Industry and Engineering Progress, 2023, 42(10): 5322-5338.
[5]	SUN Guoqi, WANG Wei, SONG Bing, WANG Liang, SHAO Ruiqi, XU Zhiwei, LUO Shigang, YAN Minjie, WANG Lijing, QIAN Xiaoming. Research progress of thermoplastic modification of polyvinyl alcohol [J]. Chemical Industry and Engineering Progress, 2022, 41(S1): 293-306.
[6]	FAN Jiao, XIE Xuehui, QIN Yan, CHEN Xiaoguang, FANG Yingrong, YANG Shanshan, ZHAO Jianggui, MO Haonan, ZHENG Hangmi, LIU Na, ZHANG Qingyun, SONG Xinshan. Differential effect of DDMZ1 cometabolic decolorization on the degradation of dyes with different structures [J]. Chemical Industry and Engineering Progress, 2022, 41(8): 4449-4463.
[7]	PAN Wenzheng, JI Zhiyong, WANG Jing, LI Shuming, HUANG Zhihui, GUO Xiaofu, LIU Jie, ZHAO Yingying, YUAN Junsheng. Research on the electricity production performance and degradation process of microbial fuel cell treating azo-dye saline wastewater [J]. Chemical Industry and Engineering Progress, 2022, 41(6): 3306-3313.
[8]	MA Hongpeng, ZHANG Xin, QIN Wenbo, GUO Bin, LI Panxin. Research progress of different modification methods of polyvinyl alcohol fiber before and after fiber formation [J]. Chemical Industry and Engineering Progress, 2022, 41(6): 3063-3076.
[9]	CHANG Xian, YANG Wenjie, LI Shiyang, ZHANG Xiumin, WU Tao, XUE Lixin. Polyvinyl alcohol (PVA) based ternary mixed matrix total heat exchange membranes (THEM) comprising montmorillonite (MMT) and CaCl₂: preparation and characterization [J]. Chemical Industry and Engineering Progress, 2022, 41(2): 911-919.
[10]	CHEN Yu, WANG Jiajia, TANG Lin. Preparation and performance of floating carbon nitride photocatalyst CNx@mEP [J]. Chemical Industry and Engineering Progress, 2022, 41(12): 6477-6488.
[11]	LI Zehui, CUI Heng, WANG Jun. Preparation of CPVC composite nanofiltration membrane and its application in simulated RB5 dye wastewater treatment [J]. Chemical Industry and Engineering Progress, 2021, 40(S1): 456-465.
[12]	LIU Chao, DONG Anjie, ZHANG Jianhua. Research progress of modified polyvinyl alcohol membrane [J]. Chemical Industry and Engineering Progress, 2021, 40(6): 3258-3269.
[13]	LI Siyuan, LI Ruisong, CHENG Jun, GAO Mengmeng, ZHANG Yucang, SONG Hui. Preparation and characterization of acrylamide modified corn starch/PVA composite film [J]. Chemical Industry and Engineering Progress, 2021, 40(6): 3374-3379.
[14]	HUANG Congxin, WANG Shunteng, FAN Yuying, JIAN Meipeng, TANG Chaochun, LIU Ruiping. Advance of ultrathin 2D porous nanosheets in water treatment [J]. Chemical Industry and Engineering Progress, 2021, 40(12): 6859-6875.
[15]	Si CHEN, Tengfei HU, Yongbo YU, Bingxin WANG, Junming HONG, Qian ZHANG. Electrocatalytic degradation of organic dye methyl orange by sulfur-doped graphene [J]. Chemical Industry and Engineering Progress, 2021, 40(1): 550-558.