Preparation of rutile TiO2 dispersion slurry and its rheological properties

doi:10.16085/j.issn.1000-6613.2019-0490

Chemical Industry and Engineering Progress ›› 2019, Vol. 38 ›› Issue (12): 5465-5470.DOI: 10.16085/j.issn.1000-6613.2019-0490

• Materials science and technology • Previous Articles Next Articles

Preparation of rutile TiO₂ dispersion slurry and its rheological properties

You WANG¹(),Qiang LI²,Shixiang ZUO¹,Xiazhang LI¹,Wenjie LIU¹,Fengqin WU¹,Chao YAO¹()

1. School of Petrochemical Engineering, Changzhou University, Changzhou 213164, Jiangsu, China
2. Sinopec Taizhou Petrochemical Company Limited, Taizhou 225300, Jiangsu, China

Received:2019-04-01 Online:2019-12-05 Published:2019-12-05
Contact: Chao YAO

金红石型TiO₂分散浆的制备及其流变特性

王优¹(),李强²,左士祥¹,李霞章¹,刘文杰¹,吴凤芹¹,姚超¹()

1. 常州大学石油化工学院，江苏常州 213164
2. 中国石化泰州石油化工有限责任公司，江苏泰州 225300

通讯作者: 姚超
作者简介:王优（1995—），男，硕士研究生，研究方向为纳米TiO2在防晒化妆品中的应用。E-mail: 1163742332@qq.com。
基金资助:
江苏省重点研发计划(BE2018649);江苏省六大人才高峰”第十三批创新人才团队项目(XCL-CXTD-029)

Abstract

Abstract:

The dispersibility and rheological properties of rutile TiO₂ dispersion slurry were studied in this paper. The dispersion of slurry was characterized by zeta potential, viscosity and so on. The suitable dispersant was sodium polyacrylate with the appropriate dosage of 4% (mass ratio to TiO₂), and the suitable solid content of TiO₂ in the dispersion slurry was 20%. Through steady shear measurements, it was found that the solids content, pH and salt in the dispersed slurry had strong influence on the rheological properties. The dispersed slurry had shear thinning phenomenon, which was consistent with the power-law model. And it exhibited pseudoplastic fluid behavior without thixotropy. NaCl decreased the viscosity of the dispersion slurry, and the higher the Na⁺ ion concentration, the lower the viscosity of the slurry. The presence of CaCl₂ caused the dispersion to flocculate. The suitable pH of the dispersion slurry was 12, and the viscosity of the slurry decreased while the pH of the system increased or decreased. The viscosity of the dispersion was slightly reduced when the temperature was raised from 25℃ to 50℃. The effect of temperature on the viscosity could be well described by the Arrhenius equation. The frequency sweep showed that the dispersed slurry took a state of gels at low frequencies and it didn’t at high frequencies. The dispersion cross frequency value decreased with the decreasing solid content.

Key words: TiO₂ dispersion slurry, sodium polyacrylate, viscosity, rheology

摘要：

研究了金红石型TiO₂颗粒在水相体系的分散性及其流变特性，通过zeta电位、黏度等参数表征浆体的分散状况，确定了合适的分散剂为聚丙烯酸钠、其用量为4%（与TiO₂质量比），分散浆中TiO₂合适的固含量为20%。通过稳态剪切测量法，发现分散浆中的固含量、pH和盐强烈影响其流变特性。分散浆存在剪切稀化现象，符合幂律模型，并呈现假塑性流体行为且无触变性。NaCl导致分散浆黏度降低， Na⁺离子浓度越大，浆体黏度越小；而CaCl₂的存在会使分散浆出现絮凝现象。分散浆合适的pH为12，增大或减小体系pH，浆体黏度均降低。当温度从25℃提升到50℃时，分散浆黏度略微降低，通过阿伦尼乌斯方程可以很好地描述温度对黏度的影响。频率扫描结果显示，分散浆在低频下呈凝胶状态，在高频下表现得更像是溶液。随着固含量的下降，分散浆交叉频率值降低。

关键词: TiO₂分散浆, 聚丙烯酸钠, 黏度, 流变特性

CLC Number:

O643.36

You WANG,Qiang LI,Shixiang ZUO,Xiazhang LI,Wenjie LIU,Fengqin WU,Chao YAO. Preparation of rutile TiO₂ dispersion slurry and its rheological properties[J]. Chemical Industry and Engineering Progress, 2019, 38(12): 5465-5470.

王优,李强,左士祥,李霞章,刘文杰,吴凤芹,姚超. 金红石型TiO₂分散浆的制备及其流变特性[J]. 化工进展, 2019, 38(12): 5465-5470.

Figures/Tables 13

References 10

1	PANG C L, LINDSAY R, THORNTON G. Structure of clean and adsorbate-covered single-crystal rutile TiO₂ surfaces[J]. Chemical Reviews, 2013, 113(6): 3887-3948.
2	陈新红, 郑少华, 李春. 二氧化钛分散技术研究[J]. 钢铁钒钛, 2016, 37(1): 16-20.
	CHEN Xinhong, ZHENG Shaohua, LI Chun. Technology research on dispersity of titanium dioxide[J]. Iron Steel Vanadium Titanium, 2016, 37(1): 16-20.
3	PERRET D, LOCAT J, MARTIGNONI P. Thixotropic behavior during shear of a fine-grained mud from Eastern Canada[J]. Engineering Geology, 1996, 43(1): 31-44.
4	林嵩, 徐宏, 古宏晨. 纳米TiO₂表面电位特性的研究[J]. 材料科学与工程学报, 2004, 22(4): 544-546.
	LIN Song, XU Hong, GU Hongchen. Surface charge properties of nano-titanium dioxide[J]. Journal of Materials Science and Engineering, 2004, 22(4): 544-546.
5	秦伟庭, 沈勇, 张惠芳, 等. 纳米TiO₂在水分散体系中的稳定性[J]. 印染, 2006, 32(7): 4-6.
	QIN Weiting, SHEN Yong, ZHANG Huifang, et al. Stability of nano TiO₂ in water-based disperse system[J]. Dyeing and Finishing, 2006, 32(7): 4-6.
6	李玲. 表面活性剂与纳米技术[M]. 北京: 化学工业出版社, 2005: 42.
	LI L. Surfactants and nanotechnology[M]. Beijing: Chemical Industry Press, 2005: 42
7	李志军, 王红英. 纳米二氧化钛分散性的实验研究[J]. 广州化工, 2005, 33(6): 26-29.
	LI Zhijun, WANG Hongying. Study on the dispersion behavior of nano-titania powders[J]. Guangzhou Chemical Industry, 2005, 33(6): 26-29.
8	王琴, 白卫东, 魏炎雄, 等. 低浓度聚丙烯酸钠的流变特性研究[J]. 食品工业科技, 2004, 25(5): 108-109.
	WANG Qin, BAI Weidong, WEI Yanxiong, et al. Study on the rheological property of low concentration polyacrylate acid sodium[J]. Science and Technology of Food Industry, 2004, 25(5): 108-109.
9	KIM W W, YOO B. Rheological behaviour of acorn starch dispersions: effects of concentration and temperature[J]. International Journal of Food Science & Technology, 2008, 44(3): 503-509.
10	KOOCHEKI A, TAHERIAN A R, BOSTAN A. Studies on the steady shear flow behavior and functional properties of Lepidium perfoliatum seed gum[J]. Food Research International, 2013, 50(1): 446-456.

固含量/%	K/Pa·sⁿ	n
16	4.26	0.29
18	4.99	0.30
20	4.89	0.29
21	8.25	0.27
22	9.45	0.25

固含量/%	K/Pa·sⁿ	n
16	4.26	0.29
18	4.99	0.30
20	4.89	0.29
21	8.25	0.27
22	9.45	0.25

固含量/%	A	E_a/J?mol^-1
16	0.08	3127
18	0.09	3161
20	0.11	2527
21	0.23	1881
22	0.31	1076

固含量/%	A	E_a/J?mol^-1
16	0.08	3127
18	0.09	3161
20	0.11	2527
21	0.23	1881
22	0.31	1076

[1]	ZHAO Jian, ZHUO Zewen, DONG Hang, GAO Wenjian. A new method for observation of microstructure of waxy crude oil and its emulsion system [J]. Chemical Industry and Engineering Progress, 2023, 42(8): 4372-4384.
[2]	CHEN Weiyang, SONG Xin, YIN Yaran, ZHANG Xianming, ZHU Chunying, FU Taotao, MA Youguang. Effect of liquid viscosity on bubble interface in the rectangular microchannel [J]. Chemical Industry and Engineering Progress, 2023, 42(7): 3468-3477.
[3]	XIE Zhiwei, WU Zhangyong, ZHU Qichen, JIANG Jiajun, LIANG Tianxiang, LIU Zhenyang. Viscosity properties and magnetoviscous effects of Ni_0.5Zn_0.5Fe₂O₄ vegetable oil-based magnetic fluid [J]. Chemical Industry and Engineering Progress, 2023, 42(7): 3623-3633.
[4]	SUN Zhengnan, LI Hongjing, JING Guolin, ZHANG Funing, YAN Biao, LIU Xiaoyan. Application of EVA and its modified polymer in crude oil pour point depressant field [J]. Chemical Industry and Engineering Progress, 2023, 42(6): 2987-2998.
[5]	LI Guangwen, HUA Qucheng, HUANG Zuoxin, DA Zhijian. Progress on polymethacrylate as viscosity index improvers for lube oil [J]. Chemical Industry and Engineering Progress, 2023, 42(3): 1562-1571.
[6]	YANG Juanjuan, HE Lin, HE Changqing, LI Xingang, SUI Hong. Treatment of oily sludge through multiphase compound conditioning and demulsification separation process [J]. Chemical Industry and Engineering Progress, 2023, 42(2): 614-623.
[7]	ZHU Qichen, WU Zhangyong, WANG Zhiqiang, JIANG Jiajun, LI Xiang. Sedimentation stability and viscosity properties of silicone oil-based magnetic nanofluid at low temperature [J]. Chemical Industry and Engineering Progress, 2023, 42(10): 5101-5110.
[8]	LI Lu, BAO Sui, ZHANG Liming, WANG Ran, TAO Zhenghong, YANG Xingxiang. Preparation and characterization of carrageenan-konjac gum hybrid gel for encapsulating fragrance [J]. Chemical Industry and Engineering Progress, 2022, 41(S1): 376-381.
[9]	CHEN Zhekun, PAN Weitong, YAO Dingsong, DING Lu, WANG Fuchen. Microstructure and rheology of microporous layer ink for proton exchange membrane fuel cells [J]. Chemical Industry and Engineering Progress, 2022, 41(7): 3808-3815.
[10]	ZHANG Xincheng, HE Lin, SUI Hong, LI Xingang. Demulsification process and enhancement by viscosity reduction for water-in-heavy oil emulsions [J]. Chemical Industry and Engineering Progress, 2022, 41(7): 3534-3544.
[11]	CUI Kun, HUANG Jin, ZHAO Qiaoling, MA Zhi. New progress in analysis and characterization of long chain branched structure in high melt strength polypropylene [J]. Chemical Industry and Engineering Progress, 2022, 41(10): 5425-5440.
[12]	FENG Jianghui, HU Miaomiao, ZHAO Jiaqi, XIONG Xiangyu, GUO Jintang. Preparation of highly dispersible SSBR latex and modification of cement [J]. Chemical Industry and Engineering Progress, 2022, 41(1): 359-364.
[13]	YANG Xiaofang, WEI Ming, SUN Li. Preparation and research of PAM/CQDs/GO composite hydrogel [J]. Chemical Industry and Engineering Progress, 2021, 40(S2): 301-308.
[14]	WANG Shuai, ZHAO Jinzhu, WANG Rongyuan, CUI Kaixiang, JING Jiaqiang. New ideas of heavy oil flow drag reduction by emulsification and wetting coupling action [J]. Chemical Industry and Engineering Progress, 2021, 40(S2): 126-139.
[15]	FAN Kaifeng, LI Si, HUANG Qiyu, WAN Yufei. Research progress on radial properties of wax deposits in crude oil pipelines [J]. Chemical Industry and Engineering Progress, 2021, 40(7): 3679-3692.