The synthesis and properties of industrial-grade zinc oxide

doi:10.16085/j.issn.1000-6613.2016.s1.042

Abstract

Abstract: In this paper, the precursor of nano zinc oxide was prepared by precipitation method used by zinc sulfate heptahydrate, ammonium bicarbonate, zinc oxide was obtained by calcining the precursor.Nano zinc oxide and its precursors were characterized by XRD, TG-DSC, TEM, BET and other testing methods, investigated the effects of different calcination temperature on the zinc oxide morphology, crystal phase and desulfurization activity by changing calcination temperature of the precursor.the results showed that:the microstructure of obtained basic zinc carbonate appears irregular nanocrystalline with the grain size of about 2-10nm.under different firing temperature, the presence of obtained zinc oxide exists large performance differences, where a higher degree of heat treatment at 300℃ nano zinc oxide showed the best performance, the grain size of which is between 5-10nm with specific surface area of 41.41m²/g and high desulfurization activity that penetration of the sulfur content was over 25% at 220℃.With the increase of calcination temperature, the degree of crystallization of zinc oxide was increased, the surface properties were destroyed, the grain size became larger with the more complete degree of crystallinity, agglomeration was serious.When calcination temperature was too low, the nano-zinc oxide precursor decomposition was incomplete, affecting its purity.

Key words: zinc subcarbonate, nano zinc oxide, calcination, material synthesis, desulfurization activity

摘要： 以七水硫酸锌、碳酸氢铵为原料,通过液相沉淀法合成纳米氧化锌前体,并焙烧获得纳米氧化锌。本文采用XRD、TG-DSC、TEM、BET等测试手段对纳米氧化锌及其前体进行表征,研究了焙烧温度对所制备氧化锌形貌、晶型及脱硫活性的影响,结果表明:所获得的碱式碳酸锌为不规则纳米晶,晶粒尺寸约为2~10nm;在不同的焙烧温度下所获得的纳米氧化锌的综合性能存在较大差异,其中在焙烧温度300℃处理所得纳米氧化锌综合性能较高,其晶粒尺寸为5~10nm之间,结晶度较完整,比表面积为41.41m²/g,在220℃脱硫活性较高,穿透硫容>25%;随着焙烧温度的提高,纳米氧化锌的晶化程度加大,表面性质被破坏,比表面积急剧下降,颗粒团聚严重;焙烧温度太低,则纳米氧化锌前体分解不完全,影响其纯度。

关键词: 碱式碳酸锌, 纳米氧化锌, 焙烧, 材料合成, 脱硫活性

CLC Number:

O611.6

WANG Lixian, ZHAO Wentao, WANG Lulu, LI Haiying. The synthesis and properties of industrial-grade zinc oxide[J]. Chemical Industry and Engineering Progree, 2016, 35(S1): 259-264.

王立贤, 赵文涛, 王鲁璐, 李海英. 工业级纳米氧化锌的合成及性能[J]. 化工进展, 2016, 35(S1): 259-264.

References

[1] 冯续.国内氧化锌脱硫剂研究现状和需求预测[J].化工进展,2002,21(10):773.
[2] 丁明雷,刘建周,段利叶,等.中温氧化锌脱硫剂再生及其织构研究[J].天然气化工,2013,38(5):67.
[3] 王安友,郭曙强,潘晋波,等.负载型氧化锌脱硫剂的实验研究[J].煤炭转化,2010,33(1):16.
[4] 李赫,雷姣,岳海荣,等.氧化锌脱除H₂S穿透时间的理论预测和实验研究[J].化学反应工程与工艺,2014(2):156.
[5] ZHANG Q,YANG H,WEI Y G,et al.Selection of destination ports of inland-port-transferring RHCTS based on sea-rail combined container transportation[C]//Innovation and Sustainability of Modern Railway:Third International Symposium on Innovation and Sustainability of Modern Railway(ISMR 2012),Nanchang.2012:675.
[6] 曹智,苏小莉,李庆华,等.纳米氧化锌的气流粉碎改性及应用研究[J].功能材料,2010,41(3):537.
[7] 鲍艳,张永辉,马建中,等.一维纳米氧化锌的制备及应用研究进展[J].材料工程,2015,43(2):103.
[8] 张晓丽,王瑶,赵璐,等.微乳液法制备纳米氧化锌及微乳体系相行为研究[J].大连理工大学学报,2014(3):267.
[9] Kumarjyoti Roy,Md.Najib Alam,Swapan Kumar Mandal,et al.Sol-gel derived nano zinc oxide for the reduction of zinc oxide level in natural rubber compounds[J].Journal of Sol-Gel Science and Technology,2014,70(3):378..
[10] 曹渊,王亚涛,徐彦芹,等.微波诱导燃烧法制备稀土离子掺杂氧化锌纳米材料[J].硅酸盐通报,2012,31(5):1317.
[11] 陈先梅.ZnO及ZnO:Ag纳米棒的两步法制备研究[D].郑州:郑州大学,2013.
[12] 陈先梅,王晓霞,郜小勇,等.掺银氧化锌纳米棒的水热法制备研究[J].物理学报,2013(5):300.
[13] 黄玉娟.介孔/大孔复合催化材料的合成及应用研究[D].长沙:长沙理工大学,2013.
[14] 骆英民,支壮志,葛贝尔,等.水热合成法制备杯状氧化锌微晶及其光学性质研究[J].功能材料,2011,42(2):302.
[15] 王真真.氧化锌多级微纳米结构的构建及其光催化性能研究[D].河南:河南师范大学,2013.
[16] 韩艳丽.低温溶液法制备氧化锌微纳米结构及其性能表征[D].郑州:郑州大学,2013.
[17] 董乾英,张保林,程亮,等.纳米氧化锌的制备及光催化应用[J].无机盐工业,2013,45(5):52.
[18] 熊静芳,肖佩,吴强,等.氧化锌多孔微米花的制备及其气敏性能研究[J].化学学报,2014,72(4):433.
[19] 董乾英.纳米氧化锌的制备及应用研究[D].郑州:郑州大学,2013.
[20] 王玲玲.改性纳米氧化锌的制备及其在路用煤沥青中的应用[D].太原:中国日用化学工业研究院,2012.
[21] 刘文魁.氧化锌纳米结构的制备、表征及性能研究[D].长沙:湖南大学,2013.
[22] 刘萍,陈长春,陆春华.纳米氧化锌制备所需碱式碳酸锌的实验研究[J].材料导报,2008(3):49.
[23] 侯新刚,郝亚莉,王玉棉,等.纳米微晶碱式碳酸锌的制备[J].兰州理工大学学报,2008(6):34.