氨基修饰片状氮化碳的制备及光催化性能

doi:10.16085/j.issn.1000-6613.2019-1336

摘要/Abstract

摘要：

石墨相氮化碳是一种低成本易获得的可见光响应光催化剂，但由于比表面积小、光生载流子易复合等缺点限制了其应用。为克服传统氮化碳的缺陷，本实验以尿素和三聚氰胺为原料，通过水热预处理改性前体，再用高温煅烧法成功制备出氨基修饰片状氮化碳光催化材料。并通过X射线衍射（XRD）、扫描电子显微镜（SEM）和X射线光电子能谱仪（XPS）等手段对样品的晶格结构和形貌特征等进行表征。结果表明，成功引入氨基基团的片状氮化碳，比表面积增加且光生载流子复合率显著降低。以罗丹明B和壬基酚溶液的光降解考察材料光催化性能，发现氨基修饰片状氮化碳对其去除率分别为80.69%和50.7%，分别是传统块状氮化碳的2.45倍和2.19倍，是未修饰片状氮化碳的1.26倍和1.21倍。且氨基修饰片状氮化碳材料重复使用5次后仍具有较高光催化活性，光催化性能显著提高。

关键词: 氨基修饰, 片状氮化碳, 光催化, 氧化降解, 稳定性

Abstract:

Graphitic carbon nitride is a low-cost and accessible photocatalyst with visible light-responsive region. However, low specific surface area and fast recombination of photogenerated carriers limit its practical application. To overcome the above defects of traditional carbon nitride, the urea and melamine were employed to prepare precursors by hydrothermal pretreatment. After that, amino-modified sheet-like carbon nitride was successfully synthesized by calcinating the precursors with high-temperature. The crystal lattice structure, morphology and other properties of the sample were characterized by X-ray diffraction(XRD), scanning electron microscopy(SEM) and X-ray photoelectron spectroscopy(XPS) and so on. The results showed that the specific surface area was increased and the photocarrier recombination rate was decreased significantly after the introduction of amino groups into the sheet-like carbon nitride. In order to test the performance of the photocatalytic materials, Rhodamine B and nonylphenol were identified as the target pollutants. The removal rates of Rhodamine B and nonylphenol with amino-modified sheet-like carbon nitride were 80.69% and 50.7%, respectively, which was 2.5 and 2.2 times higher than that of traditional bulk carbon nitride, and 1.3 and 1.2 times higher than that of unmodified sheet-like carbon nitride, respectively. In addition, after five times cycle, the amino-modified sheet-like carbon nitride still possessed high photocatalytic activity. In summary, the photocatalytic performance of amino-modified sheet-like carbon nitride was significantly improved.

Key words: amino-modified, sheet-like carbon nitride, photocatalyst, oxidative degradation, stability

中图分类号:

X703

焦莉, 徐金妹, 张秋亚, 彭慧, 许霞, 王利平. 氨基修饰片状氮化碳的制备及光催化性能[J]. 化工进展, 2020, 39(5): 1866-1874.

Li JIAO, Jinmei XU, Qiuya ZHANG, Hui PENG, Xia XU, Liping WANG. Preparation and photocatalytic activity of amino-modified sheet-like carbon nitride[J]. Chemical Industry and Engineering Progress, 2020, 39(5): 1866-1874.

参考文献

1	CUI L F, XIANG D, WANG Y G, et al. Facile preparation of Z-scheme WO₃/g-C₃N₄ composite photocatalyst with enhanced photocatalytic performance under visible light[J]. Applied Surface Science, 2017, 391: 202-210.
2	PRASAD C, TANG H, BAHADUR I. Graphitic carbon nitride based ternary nanocomposites: from synthesis to their applications in photocatalysis: a recent review[J]. Journal of Molecular Liquids, 2019, 281: 634-654.
3	DONG F, ZHAO Z, XIONG T, et al. In situ construction of g-C₃N₄/g-C₃N₄ metal-free heterojunction for enhanced visible-light photocatalysis[J]. Applied Materials & Interfaces, 2013, 5(21): 11392-11401.
4	WEN J Q, XIE J, CHEN X B, et al. A review on g-C₃N_4s-based photocatalysts[J]. Applied Surface Science, 2017, 391: 72-123.
5	ONG W J, TAN L L, NG Y H, et al. Graphitic carbon nitride (g-C₃N₄)-based photocatalysts for artificial photosynthesis and environmental remediation: are we a step closer to achieving sustainability?[J]. Chemical Reviews, 2016, 116(12): 7159-7329.
6	范乾靖, 刘建军, 于迎春, 等. 新型非金属光催化剂——石墨型氮化碳的研究进展[J]. 化工进展, 2014, 33(5): 1185-1194.
6	FAN Q J, LIU J J, YU Y C, et al. Research progress in a new metal-free photocatalyst-graphitic carbon nitride[J]. Chemical Industry and Engineering Progress, 2014, 33(5): 1185-1194.
7	郭雅容, 陈志鸿, 刘琼, 等.石墨相氮化碳光催化剂研究进展[J]. 化工进展, 2016, 35(7): 2063-2070.
7	GUO Y R, CHEN Z H, LIU Q, et al. Research progress of graphitic carbon nitride in photocatalysis[J]. Chemical Industry and Engineering Progress, 2016, 35(7): 2063-2070.
8	SUN L L, LIU C Y, LI J Z, et al. Fast electron transfer and enhanced visible light photocatalytic activity by using poly-o-phenylenediamine modified AgCl/g-C₃N₄ nanosheets[J]. Chinese Journal of Catalysis, 2019, 40(1): 80-94.
9	GAO D, XU Q, ZHANG J, et al. Defect-related ferromagnetism in ultrathin metal-free g-C₃N₄ nanosheets[J]. Nanoscale, 2014, 6(5): 2577-2581.
10	LIANG Q H, LI Z, HUANG Z H, et al. Holey graphitic carbon nitride nanosheets with carbon vacancies for highly improved photocatalytic hydrogen production[J]. Advanced Functional Materials, 2015, 25(44): 6885-6892.
11	DONG G H, AI Z H, ZHANG L Z. Efficient anoxic pollutant removal with oxygen functionalized graphitic carbon nitride under visible light[J]. RSC Advances, 2014, 4(11): 5553-5560.
12	LAU W H, YU W Z, EHRAT F, et al. Urea-modified carbon nitrides: enhancing photocatalytic hydrogen evolution by rational defect engineering[J]. Advanced Energy Materials, 2017, 7(12): 1602251.
13	MENG N N, REN J, LIU Y, et al. Engineering oxygen-containing and amino groups into two-dimensional atomically-thin porous polymeric carbon nitrogen for enhanced photocatalytic hydrogen production[J]. Energy & Environmental Science, 2018, 11(3): 566-571.
14	SANTACLARA J G, NASALEVICH M A, CATELLANONS S, et al. Organic linker defines the excited-state decay of photocatalytic MIL-125(Ti)-type materials[J]. ChemSusChem, 2016, 9(4): 388-395.
15	MATTHEN B C, WANG X, LAURA E, et al. Maximizing the photocatalytic activity of meta-organic frameworks with aminated-functionalized linkers: substoichiometric effects in MIL-125-NH₂[J]. Journal of the American Chemical Society, 2017, 139(24): 8222-8228.
16	ZHANG Z Y, HUANG J D, ZHANG M Y, et al. Ultrathin hexagonal SnS₂ nanosheets coupled with g-C₃N₄ nanosheets as 2D/2D heterojunction photocatalysts toward high photocatalytic activity[J]. Applied Catalysis B: Environmental, 2015, 163: 298-305.
17	NEAM U M, FRIMMEL F H. Photodegradation of endocrine disrupting chemical nonylphenol by simulated solar UV-irradiation[J]. Science of the Total Environment, 2006, 369(1/2/3): 295-306.
18	INUMARU K, KASAHARA T, YAMANAKA S. Enhanced photocatalytic decomposition of 4-nonylphenol by surface-organografted TiO₂: a combination of molecular selective adsorption and photocatalysis[J]. Applied Catalysis B: Environmental, 2004, 52(4): 275-280.
19	LI H T, LI N, WANG M, et al. Synthesis of novel and stable g-C₃N₄-Bi₂WO₆ hybrid nanocomposites and their enhanced photocatalytic activity under visible light irradiation[J]. Royal Society Open Science, 2018, 5(3): 171419.
20	WANG X W, ZHANG S H, GAO H S, et al. Ultrathin g-C₃N₄ nanosheets coupled with amorphous Cu doped FeOOH nanoclusters as 2D/0D heterogeneous catalysts for water remediation[J]. Environmental Science: Nano, 2018, 5: 1179-1190.
21	WU S Z, CHEN C H, ZHANG W D. Etching graphitic carbon nitride by acid for enhanced photocatalytic activity toward degradation of 4-nitrophenol[J]. Chinese Chemical Letters, 2014, 25(9): 1247-1251.
22	OU H, LIN L, ZHENG Y, et al. Tri‐s‐triazine‐based crystalline carbon nitride nanosheets for an improved hydrogen evolution[J]. Advanced Materials, 2017, 29(22): 1700008.
23	WAN Y L, YANG M, RONG J F, et al. Hybrid 0D-2D black phosphorus quantum dots-graphitic carbon nitride nanosheets for efficient hydrogen evolution[J]. Nano Energy, 2018, 50: 552-561.
24	ZHENG Y, JIAO Y, ZHU Y H, et al. Molecule-level g-C₃N₄ coordinated transition metals as a new class of electrocatalysts for oxygen electrode reactions[J]. Journal of the American Chemical Society, 2017, 139(9): 3336.
25	ZHAO C C, YAN Q Y, WANG S J, et al. Regenerable g-C₃N₄-chitosan beads with enhanced photocatalytic activity and stability[J]. RSC Advances, 2018, 8(48): 27516-27524.
26	MASIH D, MA Y Y, ROHANI S. Graphitic C₃N₄ based noble-metal-free photocatalyst systems: a review[J]. Applied Catalysis B:Environmental, 2017, 206: 556-588.
27	SOHEILA A K, AZIZ H Y, KUNIO Y. Novel g-C₃N₄ nanosheets/CDs/BiOCl photocatalysts with exceptional activity under visible light[J]. Journal of the American Ceramic Society, 2018, 102(3): 1435-1453.
28	LIU X, ZHANG J, DONG Y M, et al. A facile approach for the synthesis of Z-scheme photocatalyst ZIF-8/g-C₃N₄ with highly enhanced photocatalytic activity under simulated sunlight[J]. New Journal of Chemistry, 2018, 42(14): 202-210.
29	LI Y F, JIN R X, YAN X, et al. Macroscopic foam‐like holey ultrathin g-C₃N₄ nanosheets for drastic improvement of visible‐light photocatalytic activity[J]. Advanced Energy Materials, 2016, 6(24): 1601273.
30	梁庆华. 石墨相氮化碳的结构调控及增强光催化性能研究[D]. 北京: 清华大学, 2016. LIANG Q H. Structural tuning of graphitic carbon nitrides with highly improved photocatalytic performance[D]. Beijing: Tsinghua University, 2016.
31	TENG Z Y, YANG N L, Lü H Y, et al. Edge-functionalized g-C₃N₄ nanosheets as a highly efficient metal-free photocatalyst for safe drinking water[J]. Chem., 2019, 5(3): 664-680.
32	ZHANG H. Ultrathin two-dimensional nanomaterials[J]. ACS Nano, 2015, 9(10): 51-69.
33	QIU J H, YI F, ZHANG X F, et al. Facile stir-dried preparation of g-C₃N₄/TiO₂ homogeneous composites with enhanced photocatalytic activity[J]. RSC Advances, 2017, 7(18): 10668-10674.
34	VU M H, SAKAR M, NGUYEN C C, et al. Chemically bonded Ni cocatalyst onto the S doped g-C₃N₄ nanosheets and their synergistic enhancement in H₂ production under sunlight irradiation[J]. ACS Sustainable Chemistry & Engineering, 2018, 6(3): 4194-4203.
35	陈鹏, 董帆, 冉茂希, 等. MnO_x/g-C₃N₄光热协同催化净化NO的性能增强和反应机理[J]. 催化学报, 2018, 39(4): 619-629.
35	CHEN P, DONG F, RAN M X,et al. Synergistic photo-thermal catalytic NO purification of MnO_x/g-C₃N₄: enhanced performance and reaction mechanism[J] Chinese Journal of Catalysis, 2018, 39(4): 619-629.
36	TIAN N, ZHANG Y H, LI X W, et al. Precursor-reforming protocol to 3D mesoporous g-C₃N₄ established by ultrathin self-doped nanosheets for superior hydrogen evolution[J]. Nano Energy, 2017, 38(5): 72-81.
37	陈峰, 杨慧, 王雪飞, 等. NiS₂助剂修饰g-C₃N₄光催化剂的简易合成及光催化制氢性能增强研究[J]. 催化学报, 2017, 38(2): 296-304.
37	CHEN F, YANG H, WANG X F, et al. Facile synthesis and enhanced photocatalytic H₂-evolution performance of NiS₂-modified g-C₃N₄ photocatalysts[J]. Chinese Journal of Catalysis, 2017, 38(2): 296-304.
38	KIM J Y, KIM D Y, LEE W S, et al. Impact of total organic carbon and specific surface area on the adsorption capacity in Horn River shale[J]. Journal of Petroleum Science & Engineering, 2017, 149: 331-339.
39	曹丽丽, 蒋善庆, 凌泽玉, 等.水热合成Ag⁺掺杂SrTiO₃可见光催化降解四环素性能和机制[J]. 化工进展, 2018, 37(11): 4500-4508.
39	CAO L L, JIANG S Q, LING Z Y, et al. Properties and mechanisms of tetracycline photocatalytic degradation by hydrothermal synthesis Ag-SrTiO₃ in visible-light[J] Chemical Industry and Engineering Progress, 2018, 37(11): 4500-4508.

[1]	王晨, 白浩良, 康雪. 大功率UV-LED散热与纳米TiO₂光催化酸性红26耦合系统性能[J]. 化工进展, 2023, 42(9): 4905-4916.
[2]	黄玉飞, 李子怡, 黄杨强, 金波, 罗潇, 梁志武. 光催化CO₂和CH₄重整催化剂研究进展[J]. 化工进展, 2023, 42(8): 4247-4263.
[3]	王鑫, 王兵兵, 杨威, 徐志明. 金属表面PDA/PTFE超疏水涂层抑垢与耐腐蚀性能[J]. 化工进展, 2023, 42(8): 4315-4321.
[4]	郭立行, 庞蔚莹, 马克遥, 杨镓涵, 孙泽辉, 张盼, 付东, 赵昆. 层序空间多孔结构TiO₂实现高效光催化CO₂还原[J]. 化工进展, 2023, 42(7): 3643-3651.
[5]	陆洋, 周劲松, 周启昕, 王瑭, 刘壮, 李博昊, 周灵涛. CeO₂/TiO₂吸附剂煤气脱汞产物的浸出规律[J]. 化工进展, 2023, 42(7): 3875-3883.
[6]	吴展华, 盛敏. 绝热加速量热仪在反应安全风险评估应用中的常见问题[J]. 化工进展, 2023, 42(7): 3374-3382.
[7]	谢志伟, 吴张永, 朱启晨, 蒋佳骏, 梁天祥, 刘振阳. 植物油基Ni_0.5Zn_0.5Fe₂O₄磁流体的黏度特性及磁黏特性[J]. 化工进展, 2023, 42(7): 3623-3633.
[8]	杨竞莹, 施万胜, 黄振兴, 谢利娟, 赵明星, 阮文权. 改性纳米零价铁材料制备的研究进展[J]. 化工进展, 2023, 42(6): 2975-2986.
[9]	杨扬, 孙志高, 李翠敏, 李娟, 黄海峰. 静态条件下表面活性剂OP-13促进HCFC-141b水合物生成[J]. 化工进展, 2023, 42(6): 2854-2859.
[10]	张宁, 吴海滨, 李钰, 李剑锋, 程芳琴. 漂浮型光催化材料的制备及其在水处理领域的应用研究进展[J]. 化工进展, 2023, 42(5): 2475-2485.
[11]	李玲, 马超峰, 卢春山, 于万金, 石能富, 金佳敏, 张建君, 刘武灿, 李小年. 新型含氟替代品1,1,2-三氟乙烯的合成工艺与催化剂研究进展[J]. 化工进展, 2023, 42(4): 1822-1831.
[12]	殷铭, 郭晋, 庞纪峰, 吴鹏飞, 郑明远. 铜催化剂在涉氢反应中的失活机制和稳定策略[J]. 化工进展, 2023, 42(4): 1860-1868.
[13]	李云闯, 谢方明, 席亚男, 万新月, 孙玉虎, 赵永峰, 李根, 刘宏海, 高雄厚, 刘洪涛. 高水热稳定性介孔分子筛的低成本合成研究进展[J]. 化工进展, 2023, 42(4): 1877-1884.
[14]	王钰琢, 李刚. 硫、氮共掺杂三维石墨烯的全固态超级电容器[J]. 化工进展, 2023, 42(4): 1974-1982.
[15]	谭德新, 曾佳欣, 梁莉敏, 申思慧, 曾子倩, 王艳丽. 取代烷基变化对芳炔单体及其聚合物性能影响[J]. 化工进展, 2023, 42(4): 2031-2037.