HZSM-22的粒径调控及Pt/HZSM-22的正十二烷加氢异构催化性能

doi:10.16085/j.issn.1000-6613.2023-0447

化工进展 ›› 2024, Vol. 43 ›› Issue (3): 1309-1317.DOI: 10.16085/j.issn.1000-6613.2023-0447

• 工业催化 • 上一篇

HZSM-22的粒径调控及Pt/HZSM-22的正十二烷加氢异构催化性能

陈风¹(), 王宣德³, 黄伟¹, 王晓东¹(), 王琰²()

^1.太原理工大学省部共建煤基能源清洁高效利用国家重点实验室，山西太原 030024
^2.太原理工大学化学工程与技术学院，山西太原 030024
^3.国能寿光发电有限责任公司，山东潍坊 262714

收稿日期:2023-03-23 修回日期:2023-07-01 出版日期:2024-03-10 发布日期:2024-04-11
通讯作者: 王晓东,王琰
作者简介:陈风（1997—）女，硕士研究生，研究方向为分子筛的制备及催化。E-mail：1227679716@qq.com。
基金资助:
国家重点研发计划(2020YFB0606405);山西省基础研究计划(20210302123197);山西省重点研发计划(201803D121043)

Particle size regulation of HZSM-22 and Pt/HZSM-22 for n-dodecane hydroisomerization

CHEN Feng¹(), WANG Xuande³, HUANG Wei¹, WANG Xiaodong¹(), WANG Yan²()

^1.State Key Laboratory of Clean and Efficient Coal Utilization, Taiyuan University of Technology, Taiyuan 030024, Shanxi, China
^2.College of Chemical Engineering and Technology, Taiyuan University of Technology, Taiyuan 030024, Shanxi, China
^3.Guoneng Shouguang Power Generation Co. , Ltd. , Weifang 262714, Shandong, China

Received:2023-03-23 Revised:2023-07-01 Online:2024-03-10 Published:2024-04-11
Contact: WANG Xiaodong, WANG Yan

摘要/Abstract

摘要：

通过调控合成液中的水含量，采用过饱和溶液法，在静态水热条件下合成了三种不同c轴长度的ZSM-22分子筛，对其进行了X射线衍射、扫描电子显微镜、N₂物理吸附、NH₃-程序升温脱附和吡啶吸附傅里叶变换红外光谱（Py-FTIR）表征。并以所制备的ZSM-22分子筛为酸性载体，在其上负载0.5%（质量分数）的金属Pt作为加（脱）氢活性位点，制备成Pt/ZSM-22双功能催化剂。以正十二烷为探针分子，进行正构烷烃加氢异构化反应，考察了分子筛合成液中水含量对Pt/ZSM-22催化剂加氢异构化性能的影响。结果表明，随着合成液中水含量减少，ZSM-22分子筛粒径减小。但是当水含量低到一定值时，会有方英石和ZSM-5杂晶生成。当分子筛合成液摩尔组成为SiO₂∶Al₂O₃∶K₂O∶DEA∶H₂O=1∶0.01∶0.08∶0.29∶28时，获得的HZSM-22在所合成的三种分子筛中拥有最多的中、强Brønsted酸量以及较短的c轴长度，对应的双功能催化剂Pt/HZSM-22表现出最佳催化性能。在320℃时，正十二烷转化率为73.24%，异构烷烃收率为57.92%，异构烷烃选择性为79.09%，尤其是中心位置甲基异构体5-甲基十一烷的选择性达到了17.66%。

关键词: 过饱和溶液法, ZSM-22分子筛, c轴长度, 正十二烷, 加氢异构化

Abstract:

ZSM-22 zeolite crystals with different c-axis lengths were synthesized by using supersaturated solution method under static hydrothermal conditions and adjusting the water content in the synthetic solution. The as-synthesized ZSM-22 zeolite crystals were characterized by XRD, SEM, N₂ physical adsorption, NH₃-TPD and Fourier transformed infra-red spectroscopy of pyridine adsorption(Py-FTIR). By loading Pt on the ZSM-22 zeolite crystals, the Pt/ZSM-22 bifunctional catalysts were prepared, in which ZSM-22 zeolite crystals played the role of acid supports and the 0.5% Pt acts as (de)hydrogenation active sites. The hydroisomerization of n-alkanes was carried out with n-dodecane as the probe molecules. The effect of water content in the zeolite synthesis solution on the hydroisomerization performance of Pt/ZSM-22 catalyst was investigated. The results indicated that the less the water, the smaller the ZSM-22 crystals. However, a few cristobalite and ZSM-5 crystals were formed when the content of water in the synthetic solution was reduced to a certain value. HZSM-22 synthesized in the solution with the molar composition of SiO₂∶Al₂O₃∶K₂O∶DEA∶H₂O=1∶0.01∶0.08∶0.29∶28 showed the highest medium and strong Brønsted acid amount in the three HZSM-22 samples, and shorter c-axis length. The bifunctional catalyst Pt/HZSM-22 prepared with this kind of HZSM-22 crystals showed the best catalytic performance. The conversion of n-dodecane was 73.24%, the yield of iso-alkanes was 57.92%, and the selectivity of iso-alkanes was 79.09%.Moreover, the selectivity of mono-branched iso-dodecane with methyl branching positioned in the center of the chain, 5-methylundecane, was up to 17.66% at 320℃.

Key words: supersaturated solution method, ZSM-22 molecular sieve, c-axis length, n-dodecane, hydroisomerization

中图分类号:

TQ032.4

陈风, 王宣德, 黄伟, 王晓东, 王琰. HZSM-22的粒径调控及Pt/HZSM-22的正十二烷加氢异构催化性能[J]. 化工进展, 2024, 43(3): 1309-1317.

CHEN Feng, WANG Xuande, HUANG Wei, WANG Xiaodong, WANG Yan. Particle size regulation of HZSM-22 and Pt/HZSM-22 for n-dodecane hydroisomerization[J]. Chemical Industry and Engineering Progress, 2024, 43(3): 1309-1317.

图/表 9

参考文献 28

1	BATALHA N, MORISSET S, PINARD L, et al. BEA zeolite nanocrystals dispersed over alumina for n-hexadecane hydroisomerization[J]. Microporous and Mesoporous Materials, 2013, 166: 161-166.
2	ZHANG Yadong, LIU Dong, LOU Bin, et al. Hydroisomerization of n-decane over micro/mesoporous Pt-containing bifunctional catalysts: Effects of the MCM-41 incorporation with Y zeolite[J]. Fuel, 2018, 226: 204-212.
3	WANG Yudan, TAO Zhichao, WU Baoshan, et al. Effect of metal precursors on the performance of Pt/ZSM-22 catalysts for n-hexadecane hydroisomerization[J]. Journal of Catalysis, 2015, 322: 1-13.
4	CHAI Zhibo, Enjing LYU, ZHANG Huaike, et al. Effect of ethanol on the isomerization of n-heptane over Pt/SAPO-11 and Pt/ZSM-22 catalysts[J]. Journal of Fuel Chemistry and Technology, 2014, 42(2): 207-211.
5	LEE Eunok, YUN Soyoung, PARK Young-Kwon, et al. Selective hydroisomerization of n-dodecane over platinum supported on SAPO-11[J]. Journal of Industrial and Engineering Chemistry, 2014, 20(3): 775-780.
6	WANG Xiangyu, ZHANG Xiangwen, WANG Qingfa. N-dodecane hydroisomerization over Pt/ZSM-22: Controllable microporous Brϕnsted acidity distribution and shape-selectivity[J]. Applied Catalysis A: General, 2020, 590: 117335.
7	Guang LYU, WANG Congxin, WANG Ping, et al. Pt/ZSM-22 with partially filled micropore channels as excellent shape-selective hydroisomerization catalyst[J]. ChemCatChem, 2019, 11(5): 1431-1436.
8	JAMIL Anas Karrar, MURAZA Oki. Facile control of nanosized ZSM-22 crystals using dynamic crystallization technique[J]. Microporous and Mesoporous Materials, 2016, 227: 16-22.
9	ZHANG Lei, FU Wenqian, HE Liwen, et al. Design and synthesis of Pt catalyst supported on ZSM-22 nanocrystals with increased accessible 10-MR pore mouths and acidic sites for long-chain n-alkane hydroisomerization[J]. Microporous and Mesoporous Materials, 2021, 313: 110834.
10	OKAMOTO Masaki, NISHIMURA Yohei, TAKAHASHI Miyuki, et al. Synthesis of short, needle-shaped crystals of TON-type zeolite by addition of inhibitors of crystal growth along the [001] direction[J]. Crystal Growth & Design, 2018, 18(11): 6573-6580.
11	ZHAI Miao, WU Wenxue, XING Enhui, et al. Generating TON zeolites with reduced [001] length through combined mechanochemical bead-milling and porogen-directed recrystallization with enhanced catalytic property in hydroisomerization[J]. Chemical Engineering Journal, 2022, 440: 135874.
12	高晓霞. 纳米梯度孔ZSM-5和Zn/ZSM-5分子筛催化剂的制备及其在甲醇制汽油中催化性能的研究[D]. 太原: 太原理工大学, 2013.
	GAO Xiaoxia. Preparation of ZSM-5 and Zn/ZSM-5 zeolite catalysts with nanometer gradient pores and their catalytic performance in methanol to gasoline[D]. Taiyuan: Taiyuan University of Technology, 2013.
13	吴卓. ZSM-22分子筛的合成及其催化性能的研究[D]. 大连: 大连理工大学, 2009.
	WU Zhuo. Synthesis and catalytic performance of ZSM-22 molecular sieve[D]. Dalian: Dalian University of Technology, 2009.
14	NIU Pengyu, XI Hongjuan, REN Jun, et al. Micropore blocked core-shell ZSM-22 designed via epitaxial growth with enhanced shape selectivity and high n-dodecane hydroisomerization performance[J]. Catalysis Science & Technology, 2018, 8(24): 6407-6419.
15	LIU Suyao, REN Jie, ZHU Shujin, et al. Synthesis and characterization of the Fe-substituted ZSM-22 zeolite catalyst with high n-dodecane isomerization performance[J]. Journal of Catalysis, 2015, 330: 485-496.
16	HE Liwen, FU Wenqian, LI Leyi, et al. Study of CA-treated ZSM-22 zeolite with enhanced catalytic performance in the hydroisomerization of long-chain n-dodecane[J]. New Journal of Chemistry, 2021, 45(5): 2820-2829.
17	WANG Yan, LIU Wei, ZHANG Wei, et al. Comparison of n-dodecane hydroisomerization performance over Pt supported ZSM-48 and ZSM-22[J]. Catalysis Letters, 2021, 151(12): 3492-3500.
18	史梦园. B-ZSM-22的合成和催化性能的研究[D]. 大连: 大连理工大学, 2014.
	SHI Mengyuan. Study on synthesis and catalytic performance of B-ZSM-22[D]. Dalian: Dalian University of Technology, 2014.
19	JAMIL Anas K, MURAZA Oki, AL-AMER Adnan M. Microwave-assisted solvothermal synthesis of ZSM-22 zeolite with controllable crystal lengths[J]. Particuology, 2016, 24: 138-141.
20	WANG Xiangyu, ZHANG Xiangwen, WANG Qingfa. n-dodecane hydroisomerization over hierarchical ZSM-22 prepared by a dual-protected alkali treatment[J]. Industrial & Engineering Chemistry Research, 2019, 58(19): 8495-8505.
21	LUO Yi, WANG Zhendong, JIN Shaoqing, et al. Synthesis and crystal growth mechanism of ZSM-22 zeolite nanosheets[J]. CrystEngComm, 2016, 18(30): 5611-5615.
22	NIU Pengyu, LIU Ping, XI Hongjuan, et al. Design and synthesis of Pt/ZSM-22 catalysts for selective formation of iso-Dodecane with branched chain at more central positions from n-dodecane hydroisomerization[J]. Applied Catalysis A: General, 2018, 562: 310-320.
23	NIEMINEN Ville, KUMAR Narendra, Teemu HEIKKILÄ, et al. Isomerization of 1-butene over SAPO-11 catalysts synthesized by varying synthesis time and silica sources[J]. Applied Catalysis A: General, 2004, 259(2): 227-234.
24	赵思梦, 林明桂, 郗宏娟, 等. 以SBA-15为硅源合成多级孔SAPO-11分子筛及其在正十二烷临氢异构化中的应用[J]. 燃料化学学报, 2018, 46(6): 700-709
	ZHAO Simeng, LIN Minggui, XI Hongjuan, et al. Hierarchical SAPO-11 prepared using SBA-15 as the silicon source and its application in n-dodecane hydroisomerization[J]. Journal of Fuel Chemistry and Technology, 2018, 46(6): 700-709
25	Yoshio ONO. A survey of the mechanism in catalytic isomerization of alkanes[J]. Catalysis Today, 2003, 81(1): 3-16.
26	LIU Suyao, REN Jie, ZHANG Huaike, et al. Synthesis, characterization and isomerization performance of micro/mesoporous materials based on H-ZSM-22 zeolite[J]. Journal of Catalysis, 2016, 335: 11-23.
27	TAO Shuo, LI Xiaolei, Guang LYU, et al. Highly mesoporous SAPO-11 molecular sieves with tunable acidity: Facile synthesis, formation mechanism and catalytic performance in hydroisomerization of n-dodecane[J]. Catalysis Science & Technology, 2017, 7(23): 5775-5784.
28	CLAUDE Marion C, MARTENS Johan A. Monomethyl-branching of long n-alkanes in the range from decane to tetracosane on Pt/H-ZSM-22 bifunctional catalyst[J]. Journal of Catalysis, 2000, 190(1): 39-48.

样品	相对结晶度/%	晶体平均长度/μm	比表面积/m²·g^-1	微孔比表面积/m²·g^-1	外比表面积/m²·g^-1	微孔孔容/cm³·g^-1	介孔孔容/cm³·g^-1
HZSM-22-38	87.7	9.22	52	47	5	0.02	0.04
HZSM-22-28	97.4	7.26	72	60	12	0.02	0.04
HZSM-22-23	100	5.99	92	77	15	0.03	0.05

样品	相对结晶度/%	晶体平均长度/μm	比表面积/m²·g^-1	微孔比表面积/m²·g^-1	外比表面积/m²·g^-1	微孔孔容/cm³·g^-1	介孔孔容/cm³·g^-1
HZSM-22-38	87.7	9.22	52	47	5	0.02	0.04
HZSM-22-28	97.4	7.26	72	60	12	0.02	0.04
HZSM-22-23	100	5.99	92	77	15	0.03	0.05

样品	酸度			酸类型
样品	总酸量	弱酸量	强酸量	总Brønsted酸量	中、强Brønsted酸量	总Lewis酸量	中、强Lewis酸量
HZSM-22-38	537	366.4（166.92℃）	170.6（412.67℃）	99.6	65.3	7.1	3.4
HZSM-22-28	540	366.9（160.07℃）	173.1（401.61℃）	109.3	100.6	37.1	11.9
HZSM-22-23	549	370.4（152.42℃）	178.6（399.06℃）	99.3	78.8	30.4	8.8

样品	酸度			酸类型
样品	总酸量	弱酸量	强酸量	总Brønsted酸量	中、强Brønsted酸量	总Lewis酸量	中、强Lewis酸量
HZSM-22-38	537	366.4（166.92℃）	170.6（412.67℃）	99.6	65.3	7.1	3.4
HZSM-22-28	540	366.9（160.07℃）	173.1（401.61℃）	109.3	100.6	37.1	11.9
HZSM-22-23	549	370.4（152.42℃）	178.6（399.06℃）	99.3	78.8	30.4	8.8

参数	Pt/HZSM-22-38	Pt/HZSM-22-28	Pt/HZSM-22-23
转化率/%	32.90	73.24	66.05
总选择性/%	81.93	79.09	64.52
总收率/%	26.96	57.92	42.62
单支链选择性/%	70.51	60.29	46.76
多支链选择性/%	13.52	18.79	17.75
单多选择性比	5.22	3.21	2.63
产物选择性/%
2-甲基十一烷	23.55	15.83	13.03
3-甲基十一烷	16.37	14.58	11.19
4-甲基十一烷	11.08	10.92	8.16
5-甲基十一烷	18.30	17.66	13.35
6-甲基十一烷	1.22	1.30	1.04
2,4-二甲基癸烷	1.18	0.29	0.31
2,5-二甲基癸烷	0.96	1.31	1.25
2,6-二甲基癸烷	0.76	4.30	4.25
2,7-二甲基癸烷	2.44	2.76	2.68
2,8-二甲基癸烷	0.43	3.23	2.96
2,9-二甲基癸烷	1.51	3.58	3.46
3,3-二甲基癸烷	1.85	0.34	0.37
3,7-二甲基癸烷	2.42	0.50	0.31
3,8-二甲基癸烷	0.41	0.87	0.91
甲基乙基壬烷	1.55	1.62	1.27
其他	0	0	0

HZSM-22的粒径调控及Pt/HZSM-22的正十二烷加氢异构催化性能

Particle size regulation of HZSM-22 and Pt/HZSM-22 for n-dodecane hydroisomerization

RichHTML

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

图/表 9

参考文献 28

相关文章 4

编辑推荐

Metrics

本文评价

[1]	张海鹏, 王树振, 马梦茜, 张巍, 向江南, 王玉婷, 王琰, 范彬彬, 郑家军, 李瑞丰. ZSM-22分子筛合成及其正十二烷烃临氢异构化性能：模板剂和动态晶化的影响[J]. 化工进展, 2024, 43(1): 414-421.
[2]	韩京京, 谭涓, 刘靖, 刘宇. 小晶粒ZSM-22的可控合成及其催化长链正构生物烷烃制航空煤油性能[J]. 化工进展, 2022, 41(4): 1916-1924.
[3]	代校军, 成艳, 王晓晗, 黄文斌, 魏强, 周亚松. 小粒径SAPO-11分子筛合成的研究进展[J]. 化工进展, 2021, 40(S1): 191-203.
[4]	迟克彬1，2，赵震2，田志坚3，胡胜1，阎立军1，孟祥彬1，李发永1. 正十二烷在Pt/ZSM-22和Pt/ZSM-23上的加氢异构反应性能[J]. 化工进展, 2012, 31(11): 2477-2482.