正辛酸-肉豆蔻酸低温相变材料的制备和循环性能

doi:10.16085/j.issn.1000-6613.2017-0802

化工进展 ›› 2018, Vol. 37 ›› Issue (02): 689-693.DOI: 10.16085/j.issn.1000-6613.2017-0802

正辛酸-肉豆蔻酸低温相变材料的制备和循环性能

李玉洋, 章学来, 徐笑锋, MUNYALO Jotham Muthoka, 陈跃, 陈启杨

上海海事大学蓄冷技术研究所, 上海 201306

收稿日期:2017-05-02 修回日期:2017-06-05 出版日期:2018-02-05 发布日期:2018-02-05
通讯作者: 章学来,教授,博士生导师,研究方向为蓄能技术。
作者简介:李玉洋(1993-),男,硕士研究生。
基金资助:
上海市科委项目（16040501600）。

Preparation and cyclic properties of low temperature phase change materials of n-caprylic acid and myristic acid

LI Yuyang, ZHANG Xuelai, XU Xiaofeng, MUNYALO Jotham Muthoka, CHEN Yue, CHEN Qiyang

Cool Storage Technology Institute, Shanghai Maritime University, Shanghai 201316, China

Received:2017-05-02 Revised:2017-06-05 Online:2018-02-05 Published:2018-02-05

摘要/Abstract

摘要： 研制了一种用于相变温度在2~8℃的医药冷藏运输系统的二元有机复合相变材料，该材料由正辛酸与肉豆蔻酸按比例混合而成。首先通过理论计算预测二元混合物的共晶点，确定它的低共熔混合物的比例、相变温度以及潜热值，然后围绕共晶点比例配制了6种不同比例的混合物。使用步冷曲线法测得正辛酸与肉豆蔻酸的低共熔点温度为6.2℃，过冷度为0.5℃，其质量比为87：13。经过差示扫描量热仪（DSC）测得复合相变材料的相变温度为7.13℃，相变潜热为146.1J/g，热导率为0.2832W/（m·K）。对正辛酸-肉豆蔻酸复合相变材料进行40次、80次的循环充放冷实验，发现其相变温度和潜热值均未发生明显变化。实验结果表明，该材料在蓄冷系统尤其是医药冷藏运输系统中有着很大的应用潜力。

关键词: 二元混合物, 相变, 热力学性质, 稳定性

Abstract: This paper developed a binary organic composite phase change material that is used for pharmaceutical refrigerating transportation system with the phase change temperature of 2-8℃. The material was mixed with a mixture of n-caprylic acid and myristic acid. First two binary eutectic points were determined through the theoretical calculation method to calculate the eutectic mixture ratio, phase transition temperature and latent heat value. Then six different proportion of mixtures around the eutectic point were made. The low melting point temperature of n-caprylic acid and myristic acid was found to be 6.2℃, the sub-cooled temperature by 0.5℃. The mass ratio was found to be 87:13. The phase transition temperature of the composite phase change materials was 7.13℃ and the latent heat of phase change measured by differential scanning calorimeter (DSC)was found to be 146.1J/g. The thermal conductivity of eutectic liquid was measured by Hot Disk and was found to be 0.232 W/(m·K). It was found that the phase transition temperature and latent heat value of the composite phase change materials of n-caprylic acid and myristic acid were 40 times and 80 times more respectively. However, it was found that the phase change temperature and latent heat value were not altered. The results showed that the composite had great potential in the cold storage system, especially in medicine cold storage transportation system.

Key words: binary mixture, phase change, thermodynamic properties, stability

中图分类号:

TK02

李玉洋, 章学来, 徐笑锋, MUNYALO Jotham Muthoka, 陈跃, 陈启杨. 正辛酸-肉豆蔻酸低温相变材料的制备和循环性能[J]. 化工进展, 2018, 37(02): 689-693.

LI Yuyang, ZHANG Xuelai, XU Xiaofeng, MUNYALO Jotham Muthoka, CHEN Yue, CHEN Qiyang. Preparation and cyclic properties of low temperature phase change materials of n-caprylic acid and myristic acid[J]. Chemical Industry and Engineering Progress, 2018, 37(02): 689-693.

参考文献

[1] 朱明贵,孙志高,杨明明,等. 有机相变材料促进HCFC-141b水合物生成实验[J]. 化工进展, 2017, 36(4):1265-1269. ZHU G G, SUN Z G, YANG M M, et al. Experiment of organic phase change materials to promote the formation of HCFC-141b hydrate[J]. Chemical Industry and Engineering Progress, 2017, 36(4):1265-1269.
[2] 黄艳,章学来. 十二醇-癸酸纳米粒子复合相变材料传热性能[J]. 化工学报, 2016, 67(6):2271-2276. HUANG Y, ZHANG X L. Heat transfer performance of lauryl alcohol land capric acid composite phase change material[J]. CIESC Journal, 2016, 67(6):2271-2276.
[3] TAGUCHI Y, YOKOYAMA H, KADO H, et al. Preparation of PCM-microcapsules by using oil absorbable polymer particles[J]. Colloids Surf. A:Phys. Eng. Aspects, 2007, 301(1/2/3):41-47.
[4] 于永生,井强山,孙雅倩. 低温相变储能材料研究进展[J]. 化工进展, 2010, 29(5):896-900, 913. YU Y S, JING Q S, SUN Y Q. Research progress of low temperature phase change energy storage materials[J]. Chemical Industry and Engineering Progress, 2010, 29(5):896-900, 913.
[5] 袁艳平,白力,牛犇. 脂肪酸二元低共熔混合物相变温度和潜热的理论预测[J]. 材料导报, 2010, 24(1):111-113. YUAN Y P, BAI L, NIU B.Fatty acid binary eutectic phase change temperature and latent heat of the theoretical predictions[J]. Material Review, 2010, 24(1):111-113.
[6] ZHANG N, YUAN Y P, YUAN Y G, et al. Effect of carbon nanotubes on the thermal behavior of palmitic-stearic acid eutectic mixtures as phase change materials for energy storage[J]. Sol. Energy, 2014, 110:64-70.
[7] LIU C, YUAN Y P, ZHANG N, et al. A novel PCM of lauric-myristic-stearic acid/expanded graphite composite for thermal energy storage[J]. Mater. Lett., 2014, 120:43-46..
[8] YUAN Y G, YUAN Y P, ZHANG N. Preparation and thermal characterization of capric-myristic-palmitic acid/expanded graphite composite as phase change material for energy storage[J]. Mater. Lett., 2014, 125:154-157.
[9] ZHANG N, YUAN Y P, YUAN Y G. Lauric-palmitic-stearic acid/expanded perlite composite as form-stable phase change material:preparation and thermal properties[J]. Energ. Buildings, 2014, 82:505-511.
[10] YUAN Y P, ZHANG N, TAO W Q, et al. Fatty acids as phase changematerials:a review[J]. Renew. Sust. Energ. Rev., 2014, 29:482-498.
[11] ZHANG N, YUAN Y P, WANG X, et al. Preparation and characterization of lauric-myristic-palmitic acid ternary eutectic mixtures/expanded graphite composite phase change material for thermal energy storage[J]. Chemical Engineering Journal, 2013, 231:214-219.
[12] 袁艳平,白力,牛犇. 癸酸与棕榈酸低共熔混合物的制备与热特性分析[J]. 材料导报, 2010, 24(4):113-115. YUAN Y P, BAI L, NIU B. Study on Preparation and thermal properties of the eutectic mixture of capric acid and palmitic acid[J]. Material Review, 2010, 24(4):113-115.
[13] 刘程,袁艳平,张楠,等. 脂肪酸三元低共熔混合物相变温度和潜热的理论预测[J]. 材料导报, 2014, 28(2):165-168. LIU C, YUAN Y P, ZHANG N, et al. Theoretical prediction of the phase transition temperature and latent heat of three low eutectic mixture of fatty acids[J]. Material Review, 2014, 28(2):165-168.
[14] 陈文朴,章学来,丁锦宏,等. 癸酸-正辛酸低温相变材料的制备和循环性能[J]. 制冷学报, 2016, 37(3):12-16. CHEN W P, ZHANG X L, DING J H, et al.Capric acid-caprylic acid preparation and cycle performance of phase change materials at low temperature[J].Journal of Refrigeration, 2016, 37(3):12-16.
[15] 张寅平,苏跃红,葛新石. (准)共晶系相变材料融点及融解热的理论预测[J]. 中国科学技术大学学报, 1995, 25(4):475-476. ZHANG Y P, SU Y H, GE X S.(quasi) Eutectic phase change material melting point and the prediction of the heat of fusion theory[J].Journal of University of Science and Technology of China, 1995, 25(4):475-476.
[16] 胡孝才,吴会君,周孝清. 十二醇/辛酸二元混合工质相变蓄冷过程结晶特性[J]. 广州大学学报(自然科学版), 2011, 10(2):60-62. HU X C, WU W J, ZHOU X Q.Crystallization properties of lauryl alcohol/caprylic acid Binary mixed working medium phase change storage process[J].Journal of Guangzhou University(Natural Science Edition), 2011, 10(2):60-62.

正辛酸-肉豆蔻酸低温相变材料的制备和循环性能

Preparation and cyclic properties of low temperature phase change materials of n-caprylic acid and myristic acid

PDF (PC)

可视化

被引次数

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价

[1]	时雨, 赵运超, 樊智轩, 蒋达华. 夏热冬冷地区相变屋面最佳相变温度的实验研究[J]. 化工进展, 2023, 42(9): 4828-4836.
[2]	卜治丞, 焦波, 林海花, 孙洪源. 脉动热管计算流体力学模型与研究进展[J]. 化工进展, 2023, 42(8): 4167-4181.
[3]	张超, 杨鹏, 刘广林, 赵伟, 杨绪飞, 张伟, 宇波. 表面微结构对阵列微射流沸腾换热的影响[J]. 化工进展, 2023, 42(8): 4193-4203.
[4]	王鑫, 王兵兵, 杨威, 徐志明. 金属表面PDA/PTFE超疏水涂层抑垢与耐腐蚀性能[J]. 化工进展, 2023, 42(8): 4315-4321.
[5]	汤磊, 曾德森, 凌子夜, 张正国, 方晓明. 相变蓄冷材料及系统应用研究进展[J]. 化工进展, 2023, 42(8): 4322-4339.
[6]	陆洋, 周劲松, 周启昕, 王瑭, 刘壮, 李博昊, 周灵涛. CeO₂/TiO₂吸附剂煤气脱汞产物的浸出规律[J]. 化工进展, 2023, 42(7): 3875-3883.
[7]	吴展华, 盛敏. 绝热加速量热仪在反应安全风险评估应用中的常见问题[J]. 化工进展, 2023, 42(7): 3374-3382.
[8]	谢志伟, 吴张永, 朱启晨, 蒋佳骏, 梁天祥, 刘振阳. 植物油基Ni_0.5Zn_0.5Fe₂O₄磁流体的黏度特性及磁黏特性[J]. 化工进展, 2023, 42(7): 3623-3633.
[9]	杨竞莹, 施万胜, 黄振兴, 谢利娟, 赵明星, 阮文权. 改性纳米零价铁材料制备的研究进展[J]. 化工进展, 2023, 42(6): 2975-2986.
[10]	董晓珊, 王建, 林法伟, 颜蓓蓓, 陈冠益. 基于钙钛矿氧化物的金属纳米粒子溶出策略：溶出过程、驱动力及控制策略[J]. 化工进展, 2023, 42(6): 3049-3065.
[11]	杨许召, 李庆, 袁康康, 张盈盈, 韩敬莉, 吴诗德. 含Gemini离子液体低共熔溶剂热力学性质[J]. 化工进展, 2023, 42(6): 3123-3129.
[12]	杨扬, 孙志高, 李翠敏, 李娟, 黄海峰. 静态条件下表面活性剂OP-13促进HCFC-141b水合物生成[J]. 化工进展, 2023, 42(6): 2854-2859.
[13]	刘厚励, 顾中浩, 阳康, 张莉. 3D打印槽道结构槽宽对池沸腾传热特性的影响[J]. 化工进展, 2023, 42(5): 2282-2288.
[14]	张晨宇, 王宁, 徐洪涛, 罗祝清. 纳米颗粒强化传热的多级潜热储热器性能评价[J]. 化工进展, 2023, 42(5): 2332-2342.
[15]	徐玉珍, 蒋达华, 刘景滔, 陈璞. 粉煤灰基相变储能材料的制备及性能[J]. 化工进展, 2023, 42(5): 2595-2605.