Preparation and flocculation performance of ionic polyacrylamide initiated by acetone-EG under UV excitation

doi:10.16085/j.issn.1000-6613.2017.02.040

Abstract

Abstract: With acetone and ethylene glycol (acetone-EG) as new initiator,high molecular weight ionic polyacrylamide was polymerized under UV excitation,and the flocculation effect on primary coal slurry water was studied. Anionic polyacrylamide (HPAM),cationic polyacrylamide (CPAM),and amphiprotic polyacrylamide (APAM) were synthesized by copolymerizing acrylamide (AM) with 2-acrylamido-2-methylpropane sulfonic acid (AMPS) and dimethyl diallyl ammonium chloride (DDAC),respectively or at the same time. Limiting viscosity number ([η]) of the ionic polyacrylamide was taken as main factor to evaluate the optimal synthesis process parameters for each type of polyacrylamide. Three type ionic polyacrylamide maximum limiting viscosity numbers can be reached:[η]_HPAM=1760mL/g;[η]_CPAM=980mL/g;[η]_APAM=1120mL/g. When one of HPAM,CPAM and APAM was added to the primary coal slurry water as a flocculant agent and with the dosages of 3-4mg/L, 4-5mg/L and 4-5mg/L,respectively,the lowest coal slurry turbidity could be reduced to 0.9FTU, 1.3FTU and 0.9FTU,the maximum flocculation settling velocity was reached at 61.6cm/min,51.8cm/min and 58.2cm/min,respectively.

Key words: polyacrylamide, photo polymerization, acetone, ethylene glycol, limiting viscosity number, flocculant

摘要： 以丙酮-乙二醇（acetone-EG）作为新型引发剂，紫外激发引发单体共聚制备高分子量离子型聚丙烯酰胺，并研究聚合物对原生煤泥水的絮凝效果。将2-丙烯酰胺基-2-甲基丙磺酸（AMPS）阴离子功能单体和二甲基二烯丙基氯化铵（DDAC）阳离子功能单体分别或同时与丙烯酰胺（AM）共聚合成阴离子型聚丙烯酰胺（HPAM）、阳离子型聚丙烯酰胺（CPAM）以及两性型聚丙烯酰胺（APAM）。以离子型聚丙烯酰胺的特性黏数[η]作为指标，获取了该引发体系下每种类型聚丙烯酰胺的最优合成工艺参数，所制备的各类离子型聚丙烯酰胺的特性黏数可分别达到：[η]_HPAM=1760mL/g；[η]_CPAM=980mL/g；[η]_APAM=1120mL/g。用所制备的聚合物对煤泥水进行絮凝，结果表明HPAM用量3~4mg/L时，煤泥水浊度最低降到0.9FTU，絮凝沉降最大速度为61.6cm/min，APAM和CPAM用量4~5mg/L时有较好的絮凝效果，CPAM使煤泥水浊度最低降到1.3FTU，絮凝沉降最大为51.8cm/min，APAM使煤泥水浊度最低降到0.9FTU，絮凝沉降速度最大为58.2cm/min。

关键词: 聚丙烯酰胺, 光聚合, 丙酮, 乙二醇, 特性黏数, 絮凝剂

CLC Number:

TQ326.4

LI Dagang, CHEN Chongcheng, CHEN Xiaoling, LI Yunlong, HUANG Maokun. Preparation and flocculation performance of ionic polyacrylamide initiated by acetone-EG under UV excitation[J]. Chemical Industry and Engineering Progree, 2017, 36(02): 689-694.

李大刚, 陈崇城, 陈晓玲, 李云龙, 黄茂坤. 紫外激发丙酮-乙二醇引发制备离子型聚丙烯酰胺及其絮凝性能[J]. 化工进展, 2017, 36(02): 689-694.

References

[1] 严瑞瑄. 水溶性高分子[M].2版.北京:化学工业出版社,2010:78. YAN R X.Water-soluble polymer[M].2nd ed.Beijing:Chemical Industry Press,2010:78.
[2] ZHANG L G,JIN W Q,QUAN F A,et al. Synthesis,characterization and flocculation performance of zwitterionic copolymer of acrylamide and 4-vinylpyridine propylsulfobetaine[J]. European Polymer Journal,2009,45(5):1403-1411.
[3] OVENDEN C,XIAO H. Flocculation behaviour and mechanisms of cationic inorganic microparticle/polymer systems[J].Colloids and Surfaces A:Physicochemical and Engineering Aspects,2002,197(1-3):225-234.
[4] LIU H,YANG X,ZHANG Y,et al. Flocculation characteristics of polyacrylamide grafted cellulose from phyllostachys heterocycla:an efficient and eco-friendly flocculant[J]. Water Research,2014,59(4):165-171.
[5] AGUILAR M I,SÁEZ J,LLORÉNS M,et al. Improvement of coagulation-flocculation process using anionic polyacrylamide as coagulant aid[J]. Chemosphere,2005,58(1):47-56.
[6] MA J Y,ZHENG H L,TANG X M,et al. Research on flocculation behavior in diethyl phthalate removal from water by using anionic flocculants P(AM-AA-AMPS)[J]. Applied Mechanics & Materials,2013,361/362/363:726-729.
[7] PENG P,GAMIER G. Effect of cationic polyacrylamide adsorption kinetics and ionic strength on precipitated calcium carbonate flocculation[J]. Langmuir,2010,26(22):16949-16957.
[8] RASTEIRO M G,PINHEIRO I,AHMADLOO H,et al. Correlation between flocculation and adsorption of cationic polyacrylamides on precipitated calcium carbonate[J]. Chemical Engineering Research & Design,2014,95:298-306.
[9] ZHU J,ZHANG G,LI J. Preparation of amphoteric polyacrylamide flocculant and its application in the treatment of tannery waste water[J]. Petroleum Exploration & Development,2014,41(1):135-143.
[10] ZHENG H L,LIAO Y,ZHENG M Z,et al. Photoinitiated polymerization of cationic acrylamide in aqueous solution:synthesis,characterization,and sludge dewatering performance[J]. Scientific World Journal,2014(11):1-11.
[11] KAHVECI M U,BEYAZKILIC Z,YAGCI Y. Polyacrylamide cryogels by photoinitiated free radical polymerization[J]. Journal of Polymer Science Part A:Polymer Chemistry,2010,48(22):4989-4994.
[12] LOUGNOT D J,FOUASSIER J P. Comparative reactivity of water soluble photoinitiators as viewed in terms of excited states processes[J]. Journal of Polymer Science & Technology General Part A:Polymer Chemistry,1988,26(4):1021-1033.
[13] ALLEN N S,PULLEN G,SHAH M,et al. Photochemistry and photoinitiator properties of 2-substituted anthraquinones 1.Absorption and luminescence characteristics[J].Journal of Photochemistry and Photobiology A:Chemistry,1995,91(1):73-79.
[14] CASTELVETRO V,MOLESTI M,ROLLA P. UV-curing of acrylic formulations by means of polymeric photoinitiators with the active 2,6-dimethylbenzoylphosphine oxide moieties pendant from a tetramethylene side chain[J].Macromolecular Chemistry and Physics,2002,203(10/11):1486-1496.
[15] WANG H L,BROWN H R. Aliphatic ketones/water/alcohol as a new photoinitiating system for the photografting of methacrylic acid onto high-density polyethylene[J]. Polymer,2007,48(4):939-948.
[16] 朱光来,许新胜,洪新,等. 光解丙酮/乙二醇体系的CIDEP实验研究[J].原子与分子物理学报,2006,23(6):1025-1028. ZHU G L,XU X S,HONG X,et al.An experimental investigation on the CIDEP of acetone/EG system[J].Journal of Atomic and Molecular Physics,2006,23(6):1025-1028.
[17] 李大刚,袁淑芳,李云龙,等. 紫外激发丙酮-乙二醇引发丙烯酰胺聚合[J].化工进展,2012,31(11):2553-2557. LI D G,YUAN S F,LI Y L,et al.UV photoinitiation of acylamide polymerization by acetone-ethylene glycol[J].Chemical Industry and Engineering Progress,2012,31(11):2553-2557.
[18] 全国塑料标准化技术委员会物理力学方法分会.聚丙烯酰胺分子量测定粘度法:GB/T 12005.10-1992[S].北京:中国标准出版社,1993. Physical Mechanics Method Chapter of National Plastics Standardization Technical Committee. Determination for molecular weight of polyacrylamide by viscometry:GB/T 12005.10-1992[S].Beijing:Standards Press of China,1993.