Preparation of sulfydryl functionalized magnetic SBA-15 by an assembling process

doi:10.16085/j.issn.1000-6613.2017-1294

Abstract

Abstract: Monodisperse and magnetic manganese ferrite nanoparticles with average diameter of 15nm were synthesized by a thermal decomposition method. The obtained magnetic nanoparticles were anchored onto the surface of SBA-15 through ligand exchange reaction of oleic acid and tetraethylorthosilicate. Meanwhile,sulfydryl functionalized magnetic SBA-15 was prepared by combining the anchoring process and surface modification of SBA-15. The influence of drying methods used during the synthesis of SBA-15 on its structure and properties was investigated. Effect of execution sequence of the anchoring and modification process on the structure and properties of sulfydryl functionalized magnetic SBA-15 was discussed. The result showed that SBA-15 prepared by spray drying showed thinner pore wall,higher specific surface area,pore volume and larger pore diameter,and could support more magnetic nanoparticles and thus exhibited stronger saturation magnetization. When the anchoring of the magnetic nanoparticles occurred on surface of the modified SBA-15,more nanoparticles were anchored on the surface of the SBA-15 due to a compatible hydrophobic chemical environment. Magnetic nanoparticles were mainly anchored onto the outside surface of SBA-15 because the pore diameters of the SBA-15 were smaller,which conserved the mesopores of SBA-15 unblocked. The obtained sulfydryl functionalized magnetic SBA-15 had pore volumes between 0.56cm³/g and 0.6cm³/g,specific surface area between 353m²/g and 432m²/g,and saturation magnetization of 0.91emu/g,which make it a high-capacity adsorbent for separation and drug release.

Key words: molecular sieve, silica, composites, magnetism, surface modification

摘要： 采用热分解法制备了单分散、平均粒径约15nm的锰铁氧体磁性纳米粒子。通过正硅酸乙酯与磁性纳米粒子表面油酸盐的配体交换将磁性纳米粒子锚定在SBA-15表面。并且将负载过程与巯基改性过程耦合制备了巯基改性的磁性SBA-15。考察了合成SBA-15过程中干燥方式对其结构和性质的影响，研究了负载磁性纳米粒子和巯基改性顺序对巯基改性磁性SBA-15的结构和性能的影响。结果表明，喷雾干燥法合成的SBA-15介孔孔壁较薄，但具有更大的比表面积、孔体积和平均孔径。以其为载体时磁性纳米粒子负载量更大，所得磁性SBA-15的饱和磁强度更高。当将巯基改性和负载磁性纳米粒子分为前后两步时，巯基改性SBA-15的表面疏水环境有利于吸附疏水磁性纳米粒子，所得磁性SBA-15负载磁性纳米粒子量更大，饱和磁强度更高。磁性纳米粒子粒径大于SBA-15孔径，其主要负载于SBA-15外表面，有利于得到介孔孔道通畅的磁性SBA-15。巯基改性的磁性SBA-15的孔体积介于0.56~0.6cm³/g，比表面积介于353~432m²/g，饱和磁强度最高达到0.91emu/g，可作为一种大容量的吸附材料用于吸附分离、药物缓释等领域。

关键词: 分子筛, 二氧化硅, 复合材料, 磁性能, 表面改性

CLC Number:

TB332

ZHANG Yaping, ZHEN Bin, LI Hansheng, FENG Yaqing. Preparation of sulfydryl functionalized magnetic SBA-15 by an assembling process[J]. Chemical Industry and Engineering Progress, 2018, 37(04): 1501-1508.

张亚平, 甄彬, 黎汉生, 冯亚青. 组装法制备巯基改性磁性SBA-15[J]. 化工进展, 2018, 37(04): 1501-1508.

References

[1] KRESGE C T,LEONOWICZ M E,ROTH W J,et al. Ordered mesoporous molecular sieves synthesized by a liquid-crystal template mechanism[J]. Nature,1992,359(22):710-712.
[2] BECK J S,VARTULI J C,ROTH W J,et al. A new family of mesoporous molecular sieves prepared with liquid crystal templates[J]. Journal of the American Chemical Society,1992,114(27):10834-10843.
[3] ATASHIN H,MALAKOOTI R. Magnetic iron oxide nanoparticles embedded in SBA-15 silica wall as a green and recoverable catalyst for the oxidation of alcohols and sulfides[J]. Journal of Saudi Chemical Society,2017,21(s1):S17-S24.
[4] OSORIO Z V,PINEIRO Y,VAZQUEZ C,et al. Magnetic nanocomposites based on mesoporous silica for biomedical applications[J]. International Journal of Nanotechnology,2016,13(8/9):648-658.
[5] ZHAO D Y,FENG J L,HUO Q S,et al. Triblock copolymer syntheses of mesoporous silica with periodic 50 to 300 angstrom pores[J]. Science,1998,279(5350):548-552.
[6] 李瑞丽,吕本震,蒋善良,等. 磷钨酸/SBA-15催化氧化-萃取柴油脱硫[J]. 化工进展,2016,35(9):2790-2795. LI Ruili,LV Benzhen,JIANG Shanliang,et al. Diesel desulfurization by phosphotungstic acid/SBA-15 catalytic oxidation-extraction[J]. Chemical Industry and Engineering Progress,2016,35(9):2790-2795.
[7] WONDRACEK W H P,JORGETTO A O,SILVA A C P,et al. Synthesis of mesoporous silica-coated magnetic nanoparticles modified with 4-amino-3-hydrazino-5-mercapto-1,2,4-triazole and its application as Cu(Ⅱ) adsorbent from aqueous samples[J]. Applied Surface Science,2016,367:533-541.
[8] YAO J,SUN N,WANG J,et al. New targeted approaches for the quantification of data-independent acquisition mass spectrometry[J]. Proteomics,2017,17(9):1700021
[9] ROSTAMIZADEH S,ESTIRI H,AZAD M. Ullmann homocoupling of aryl iodides catalyzed by gold nanoparticles stabilized on magnetic mesoporous silica[J]. Journal of the Iranian Chemical Society,2017,14(5):1005-1010
[10] MAI Z,HU Y,HUANG P,et al. Outside-in stepwise bi-functionalization of magnetic mesoporous silica incorporated with Pt nanoparticles for effective removal of hexavalent chromium[J]. Powder Technology,2017,312:48-57.
[11] 朱慎林,赵俊琦,刁香,等. 磁性介孔氧化硅材料的制备与应用[J]. 石油化工,2009,38(8):811-817. ZHU Shenlin,ZHAO Junqi,DIAO Xiang,et al. Preparation and application of magnetic mesoporous silica[J]. Petrochemical Technology,2009,38(8):811-817.
[12] LU A H,LI W C,KIEFER A,et al. Fabrication of magnetically separable mesostructured silica with an open pore system[J]. Journal of the American Chemical Society,2004,126(28):8616-8617.
[13] HODGKINS R P,AHNIYAZ A,PAREKH K,et al. Maghemite nanocrystal impregnation by hydrophobic surface modification of mesoporous silica[J]. Langmuir,2007,23(17):8838-8844.
[14] PALMA R D,PEETERS S,BAEL M J V,et al. Silane ligand exchange to make hydrophobic superparamagnetic nanoparticles water-dispersible[J]. Chemistry of Materials,2007,19(7):1821-1831.
[15] BAO N,SHEN L,AN W,et al. Formation mechanism and shape control of monodisperse magnetic CoFe₂O₄ nanocrystals[J]. Chemistry of Materials,2009,21(14):3458-3468.
[16] LI J J,MU Z,HE C,et al. Promoted and controllable self-assembly of hydrolyzed siloxane and triblock copolymer under organic polyhydroxy acids[J]. Industrial & Engineering Chemistry Research,2009,48(13):6308-6314.
[17] FU Y S,XIONG P,CHEN H Q,et al. High photocatalytic activity of magnetically separable manganese ferrite-graphene heteroarchitectures[J]. Industrial & Engineering Chemistry Research,2012,51(2):725-731.
[18] KANG E,PARK J,HWANG Y,et al. Direct synthesis of highly crystalline and monodisperse manganese ferrite nanocrystals[J]. The Journal of Physical Chemistry B,2004,108(37):13932-13935.
[19] JIANG L,KIM J. A new nonhydrolytic synthesis of magnetite nanocrystallites in the presence of ω-functionalized polystyrene matrix[J]. Journal of Applied Polymer Science,2006,101(1):186-191.
[20] CUI X,ZIN W C,CHO W J,et al. Nonionic triblock copolymer synthesis of SBA-15 above the isoelectric point of silica(pH=2-5)[J]. Materials Letters,2005,59(18):2257-2261.
[21] LIND A,HOHENESCHE C D F V,SMATT J H,et al. Spherical silica agglomerates possessing hierarchical porosity prepared by spray drying of MCM-41 and MCM-48 nanospheres[J]. Microporous and Mesoporous Materials,2003,66(2/3):219-227.
[22] BOISSIERE C,GROSSO D,AMENITSCH H,et al. First in-situ SAXS studies of the mesostructuration of spherical silica and titania particles during spray-drying process[J]. Chemical Communications,2003,9(22):2798-2799.
[23] WALDRON K,WU Z,ZHAO D,et al. On the improvement of pore accessibility through post-synthesis hydrothermal treatments of spray dried SBA-15 microspheres[J]. Chemical Engineering Science,2015,127:276-284.
[24] 龚占魁,谢进宁. 喷雾干燥技术在分子筛催化剂生产中的应用研究[J]. 辽宁化工,2016,45(7):924-926. GONG Zhankui,XIE Jinning. Study on application of spray drying technology in production of molecular sieve catalyst[J]. Liaoning Chemical Industry,2016,45(7):924-926.