Analysis of theswelling properties of sealing rubber in isopropyl nitrate(IPN)

doi:10.16085/j.issn.1000-6613.2017-1021

Abstract

Abstract: Nitrile rubber is used as the sealing material of isopropyl nitrate but the leakage or vaporization of isopropyl nitrate frequently occurs. In order to select new rubber to replace nitrile rubber to seal isopropyl nitrate,nitrile rubber and EPDM rubber samples were prepared. The mass and volume change rate,structure,surface morphology and mechanical properties of nitrile rubber and EPDM rubber were measured,after which the swelling property were also tested. The results show that the properties of both nitrile rubber and EPDM rubber are decreased after swelling,but the performance of EPDM rubber is better than that of nitrile rubber. The isopropyl nitrate-resistant properties of EPDM are beter than that of nitrile rubber. Finally it recommends to use EPDM rubber and sprayed phenolic resin liquid sealant to seal isopropyl nitrate.

Key words: polymer, diffusion, dissolution

摘要： 丁腈橡胶作为硝酸异丙酯的密封材料，常常会发生硝酸异丙酯的渗漏挥发现象。为选择新的橡胶代替丁腈橡胶密封硝酸异丙酯，本文制备了丁腈橡胶与三元乙丙橡胶试样，测试经溶胀后丁腈橡胶与三元乙丙橡胶的质量与体积变化率、组织结构、表面形貌、力学性能，并对比了丁腈橡胶与三元乙丙橡胶溶胀后的性能。结果表明：丁腈橡胶与三元乙丙橡胶在硝酸异丙酯中溶胀后各方面性能均有所下降，但是三元乙丙橡胶溶胀后的性能要强于丁腈橡胶，显示出更好的耐硝酸异丙酯性能，建议使用三元乙丙橡胶并喷涂酚醛树脂液体密封胶密封硝酸异丙酯。

关键词: 聚合物, 扩散, 溶解

CLC Number:

TM411

WU Lili, DING Yukui, ZHEN Jianwei, CHEN Siyang. Analysis of theswelling properties of sealing rubber in isopropyl nitrate(IPN)[J]. Chemical Industry and Engineering Progress, 2018, 37(05): 1896-1901.

吴力力, 丁玉奎, 甄建伟, 陈思扬. 密封橡胶在硝酸异丙酯中的溶胀性能分析[J]. 化工进展, 2018, 37(05): 1896-1901.

References

[1] 王志军,尹建平. 弹药学[M]. 北京:北京理工大学出版社,2012. WANG Zhijun,YIN Jianping. Ammunition[M]. Beijing:Beijing Polytechnic University Press,2012.
[2] 阚金玲. 液固复合云爆剂的爆炸和毁伤特性研究[D]. 南京:南京理工大学,2008. KAN Jinling. Study on the explosive and damage characteristics of liquid-solid composite cloud coatings[J]. Nanjing:Nanjing University of Science and Technology,2008.
[3] 陈永康,陈明华,张力. 硝酸异丙酯对单基发射药燃烧性能的影响[J].火炸药学报,2014,37(4):84-87. CHEN Yongkang,CHEN Minghua,ZHANG Li.Effects of isopropyl nitrate on combustion performance of single-base propellant[J]. Journal of Explosives & Propellants,2014,37(4):84-87.
[4] 王阵,李海广,贲旭东. 储存条件下云爆火箭弹云爆剂质量变化研究[J]. 装备环境工程,2012,9(6):82-86. WANG Zhen,LI Haiguang,BEN Xudong. Study on quality change of cloud explosion of cloud fire rocket[J]. Equipment Environmental Engineering,2012,9(6):82-86.
[5] 张涛,邹云峰,车浩,等. 乙丙橡胶生产工艺与技术[J]. 化工进展,2016,35(8):2317-2322. ZHANG Tao,ZOU Yunfeng,CHE Hao,et al. Production technology and technology of ethylene-propylene rubber[J]. Chemical Industry and Engineering Progress,2016,35(8):2317-2322.
[6] 李建芳. EPDM为基体制备高性能的研究[D]. 青岛:青岛科技大学,2013. LI Jianfang. Study on high performance of EPDM as matrix[D]. Qingdao:Qingdao University of Science and Technology,2013.
[7] 程超. 离子化热塑性弹性体的制备及改性EPDM性能研究[D]. 青岛:青岛科技大学,2016. CHENG Chao.Study on preparation and modified EPDM properties of ionized thermoplastic elastomer[D]. Qingdao:Qingdao University of Science and Technology,2016.
[8] 中华人民共和国国家质量监督检验检疫总局,中国国家标准化管理委员会.硫化橡胶或热塑性橡胶耐液体试验方法:GB/T1690-2010[S]. 北京:中国标准出版社,2010. General Administration of Quality Supervision,Inspection and Quarantine of the People's Republic of China,Standardization Administration of the People's Republic of China. Test method for liquid resistance of vulcanized rubber or thermoplastic rubber:GB/T1690-2010[S]. Beijing:Standards Press of China,2010.
[9] 中华人民共和国国家质量监督检验检疫总局,中国国家标准化管理委员会.胶粘剂180°剥离强度试验方法:GB/T 2790-1995[S]. 北京:中国标准出版社,1995. General Administration of Quality Supervision,Inspection and Quarantine of the People's Republic of China,Standardization Administration of the People's Republic of China. Test method for 180°peel strength of adhesives:GB/T 2790-1995[S]. Beijing:Standards Press of China,1995.
[10] 中华人民共和国国家质量监督检验检疫总局,中国国家标准化管理委员会. 硫化橡胶或热塑性橡胶压入硬度试验方法:GB/T 531.1-2008[S]. 北京:中国标准出版社,2008. General Administration of Quality Supervision,Inspection and Quarantine of the People's Republic of China,Standardization Administration of the People's Republic of China. Vulcanized rubber or thermoplastic rubber press hardness test method:GB/T 531.1-2008[S]. Beijing:Standards Press of China,2008.
[11] 董炎明,朱平平,徐世爱.高分子结构与性能[M]. 上海:华东理工大学出版社,2010. DONG Yanming,ZHU Pingping,XU Shiai.Molecular structure and properties[M]. Shanghai:East China University of Science and Technology Press,2010.
[12] 天华化工机械及自动化研究设计院. 腐蚀与防护手册[M].北京:化学工业出版社,2009. Tianhua Institute of Chemical Machinery and Automation Co.,Ltd. Corrosion and protection manual[M]. Beijing:Chemical Industry Press,2009.
[13] 王云飞. EPDM橡胶的性能影响材料分析[J]. 橡塑技术与制备,2016,42(6):30-31. WANG Yufei. Effects of EPDM rubber on material impact analysis[J]. Rubber & Plastics Technology and Preparation,2016,42(6): 30-31.
[14] 徐志强. 三元乙丙橡胶拉伸取向和应变诱导结晶行为[D]. 北京:北京化工大学,2012. XU Zhijiang. Tensile orientation and strain-induced crystallization behavior of EPDM rubber[D]. Beijing:Beijing University of Chemical Technology,2012.
[15] 孙翀,张萍,赵树高.炭黑填充顺丁橡胶(BR)复合材料中多重相互作用的研究[J].高分子学报,2015(2):204-212. SUN Chong,ZHANG Ping,ZHAO Shugao. Study on multiple interactions of carbon black filled butadiene rubber(BR)composites[J]. Acta Polymerica Sinica,2015(2):204-212.
[16] 胡宗杰,周映,邓俊,等. 生物柴油混合燃料对橡胶溶胀性和机械性能的影响[J]. 内燃机学报,2010,28(4):357-361. HU Zongjie,ZHOU Ying,DENG Jun,et al. Effects of biodiesel blend fuel on rubber swelling and mechanical properties[J]. Journal of Internal Combustion Engineering,2010,28(4):357-361.