Research on pyrolysis process of high sulfur petroleum coke and the changes of sulfur species

doi:10.16085/j.issn.1000-6613.2016.08.18

Chemical Industry and Engineering Progree ›› 2016, Vol. 35 ›› Issue (08): 2420-2425.DOI: 10.16085/j.issn.1000-6613.2016.08.18

• Energy processes and technology • Previous Articles Next Articles

Research on pyrolysis process of high sulfur petroleum coke and the changes of sulfur species

DU Hongfei, DUAN Yufeng, SHE Min

Key Laboratory of Energy Thermal Conversion and Control of Ministry of Education, School of Energy and Environment, Southeast University, Nanjing 210096, Jiangsu, China

Received:2015-12-15 Revised:2016-01-24 Online:2016-08-05 Published:2016-08-05

高硫石油焦热解过程及硫形态的变化特性

杜鸿飞, 段钰锋, 佘敏

东南大学能源与环境学院, 能源热转换及其过程测控教育部重点实验室, 江苏南京 210096

通讯作者: 段钰锋,博士,教授,博士生导师。E-mail:yfduan@seu.
作者简介:杜鸿飞(1992—),男,硕士研究生。E-mail:duhongfei_seu@163.com。
基金资助:
国家自然科学基金（51376046）、中央高校基本科研业务费专项资金及江苏省普通高校研究生科研创新计划（KYLX15_0071）项目。

Abstract

Abstract: Pyrolysis experiments of high sulfur petroleum coke under N₂ atmosphere at different temperatures were conducted in a tube furnace. TG-FTIR test was carried out to analyze the pyrolysis process and the transformation of sulfur species during the pyrolysis process was characterized by XPS. TG/DTG resulted show that the pyrolysis process experienced dehydration,decomposition of long chain aliphatic hydrocarbon and fused ring aromatic hydrocarbon stages,with the maximum rate of weight loss at 430℃ and 635℃ respectively. The FTIR analysis showed that the gas-phase products from the pyrolysis process mainly included CO₂,CH₄,H₂O,SO₂,aromatic compounds,aliphatic compounds and so on. In addition,the gas components that released at different temperatures showed great difference. The XPS analysis showed that the total sulfur content and the species on the surface of high sulfur petroleum coke were associated with the pyrolysis temperature. To be specific,the total sulfur content on the surface increased with the temperature,reaching a maximum value at 700℃,and the mutual conversion among different sulfur species occurred during the pyrolysis process.

Key words: high sulfur petroleum coke, pyrolysis, sulfur species, XPS

摘要： 在管式炉实验装置上进行不同温度高硫石油焦N₂气氛热解实验，并利用X射线光电子能谱分析（XPS）技术进行表征，深入分析高硫石油焦热解过程中硫形态变化特性，同时采用热重-红外联用（TG-FTIR）技术深入分析热解过程。热重分析结果表明，高硫石油焦热解经历了干燥脱水阶段，长链脂肪烃、稠环芳香烃等组分分解阶段，在430℃和635℃失重速率达到最大形成失重峰。红外分析结果表明，高硫石油焦热解释放气体主要包括CO₂、CH₄、H₂O、SO₂、芳烃化合物和脂肪族化合物等，并且在不同温度区间释放气体组成有着巨大的差异。XPS分析结果表明，高硫石油焦表面硫含量及存在形态与热解温度紧密关联，随着热解温度的不断升高，高硫石油焦表面硫含量在700℃达到最大值，不同硫形态之间发生相互转化。

关键词: 高硫石油焦, 热解, 硫形态, X射线能谱分析

CLC Number:

X742

DU Hongfei, DUAN Yufeng, SHE Min. Research on pyrolysis process of high sulfur petroleum coke and the changes of sulfur species[J]. Chemical Industry and Engineering Progree, 2016, 35(08): 2420-2425.

杜鸿飞, 段钰锋, 佘敏. 高硫石油焦热解过程及硫形态的变化特性[J]. 化工进展, 2016, 35(08): 2420-2425.

References

[1] JIANG B C,ZHANG Y C,ZHOU J X,et al. Effects of chemical modification of petroleum cokes on the properties of the resulting activated carbon[J]. Fuel,2008,87(10):1844-1848.
[2] RAMBABU N,AZARGOHAR R,DALAI A K,et al. Evaluation and comparison of enrichment efficiency of physical/chemical activations and functionalized activated carbons derived from fluid petroleum coke for environmental applications[J]. Fuel Processing Technology,2013,106:501-510.
[3] RAMIREZ-MUNIZ K,SONG S X,BERBER-MENDOZA S,et al. Adsorption of the complex ion Au onto sulfur-impregnated activated carbon in aqueous solutions[J]. Journal of Colloid and Interface Science,2010,349(2):602-606.
[4] LEE S H,RHIM Y J,CHO S P,et al. Carbon-based novel sorbent for removing gas-phase mercury[J]. Fuel,2006,85(2):219-226.
[5] 吴诗勇,吴幼青,顾菁,等. 高温煅烧条件下石油焦和沥青焦的物理结构及其CO₂气化特性[J]. 石油学报(石油加工),2009,25(2):258-265.
[6] 顾晓利,马旭,李丽鲜,等. 基于 TG-FTIR 分析的木屑热解机理[J]. 石油学报(石油加工),2013(1):174-180.
[7] 王贵金,郭大亮,袁洪友,等. 黑液与石油焦共热解及其产物特性研究[J]. 燃料化学学报,2014,42(5):545-551.
[8] 李爽,陈静升,冯秀燕,等. 应用 TG-FTIR 技术研究黄土庙煤催化热解特性[J]. 燃料化学学报,2013,41(3):271-276.
[9] 何川. 高硫石油焦脱硫技术研究[D]. 长沙:中南大学,2013.
[10] WANG M J,HU Y F,WANG J C,et al. Transformation of sulfur during pyrolysis of inertinite-rich coals and correlation with their characteristics[J]. Journal of Analytical and Applied Pyrolysis,2013,104:585-592.
[11] 马玲玲,秦志宏,张露,等. 煤有机硫分析中 XPS 分峰拟合方法及参数设置[J]. 燃料化学学报,2014,42(3):277-283.
[12] LIU S,WEI M M,QIAO Y,et al. Release of organic sulfur as sulfur-containing gases during low temperature pyrolysis of sewage sludge[J]. Proceedings of the Combustion Institute,2015,35(3):2767-2775.
[13] 杨建丽,李允梅,刘振宇. 兖州煤热解预脱硫行为(Ⅰ)热解过程中硫的迁移[J]. 化工学报,2003,54(10):1430-1435.
[14] 李梅,杨俊和,张启锋,等. 高硫煤镜质组热解过程中结构变化及有机硫形态变迁规律研究[J]. 燃料化学学报,2014,42(2):138-145.
[15] TELFER M,ZHANG D K. The influence of water-soluble and acid-soluble inorganic matter on sulphur transformations during pyrolysis of low-rank coals[J]. Fuel,2001,80(14):2085-2098.

Research on pyrolysis process of high sulfur petroleum coke and the changes of sulfur species

高硫石油焦热解过程及硫形态的变化特性

PDF (PC)

Knowledge

Abstract

Cite this article

share this article

References

Related Articles 15

Recommended Articles

Metrics

Comments

[1]	LI Zhiyuan, HUANG Yaji, ZHAO Jiaqi, YU Mengzhu, ZHU Zhicheng, CHENG Haoqiang, SHI Hao, WANG Sheng. Characterization of heavy metals during co-pyrolysis of sludge with PVC [J]. Chemical Industry and Engineering Progress, 2023, 42(9): 4947-4956.
[2]	LI Haidong, YANG Yuankun, GUO Shushu, WANG Benjin, YUE Tingting, FU Kaibin, WANG Zhe, HE Shouqin, YAO Jun, CHEN Shu. Effect of carbonization and calcination temperature on As(Ⅲ) removal performance of plant-based Fe-C microelectrolytic materials [J]. Chemical Industry and Engineering Progress, 2023, 42(7): 3652-3663.
[3]	YAO Liming, WANG Yazhuo, FAN Honggang, GU Qing, YUAN Haoran, CHEN Yong. Treatment status of kitchen waste and its research progress of pyrolysis technology [J]. Chemical Industry and Engineering Progress, 2023, 42(7): 3791-3801.
[4]	ZHANG Shan, ZHONG Zhaoping, YANG Yuxuan, DU Haoran, LI Qian. Enrichment of heavy metals in pyrolysis of municipal solid waste by phosphate modified kaolin [J]. Chemical Industry and Engineering Progress, 2023, 42(7): 3893-3903.
[5]	LI Ruolin, HE Shaolin, YUAN Hongying, LIU Boyue, JI Dongli, SONG Yang, LIU Bo, YU Jiqing, XU Yingjun. Effect of in-situ pyrolysis on physical properties of oil shale and groundwater quality [J]. Chemical Industry and Engineering Progress, 2023, 42(6): 3309-3318.
[6]	LI Dongxian, WANG Jia, JIANG Jianchun. Producing biofuels from soapstock via pyrolysis and subsequent catalytic vapor-phase hydrotreating process [J]. Chemical Industry and Engineering Progress, 2023, 42(6): 2874-2883.
[7]	WANG Zhiwei, GUO Shuaihua, WU Mengge, CHEN Yan, ZHAO Junting, LI Hui, LEI Tingzhou. Recent advances on catalytic co-pyrolysis of biomass and plastic [J]. Chemical Industry and Engineering Progress, 2023, 42(5): 2655-2665.
[8]	ZHAO Jiaqi, HUANG Yaji, LI Zhiyuan, DING Xueyu, QI Shuaijie, ZHANG Yuyao, LIU Jun, GAO Jiawei. Characteristics of three-phase products from co-pyrolysis of sewage sludge and PVC [J]. Chemical Industry and Engineering Progress, 2023, 42(4): 2122-2129.
[9]	YANG Ziqiang, LI Fenghai, GUO Weijie, MA Mingjie, ZHAO Wei. Review on phosphorus migration and transformation during municipal sewage sludge heat treatment [J]. Chemical Industry and Engineering Progress, 2023, 42(4): 2081-2090.
[10]	LIU Jing, LIN Lin, ZHANG Jian, ZHAO Feng. Research progress in pore size regulation and electrochemical performance of biomass-based carbon materials [J]. Chemical Industry and Engineering Progress, 2023, 42(4): 1907-1916.
[11]	LIANG Yijing, MA Yan, LU Zhanfeng, QIN Fusheng, WAN Junjie, WANG Zhiyuan. Experimental investigation on the anti-coking performance of La_1-_x Sr _x MnO₃ perovskite coating [J]. Chemical Industry and Engineering Progress, 2023, 42(4): 1769-1778.
[12]	PAN Yuhan, XU Jun, ZHAO Guangjie, LIN Chengqian, JIN Liang, XUE Zhiliang, ZHOU Yonggang, HUANG Qunxing. Development of pilot-plant for the step pyrolysis of waste tires and analysis of product characteristics [J]. Chemical Industry and Engineering Progress, 2023, 42(3): 1240-1247.
[13]	HE Yangdong, CHANG Honggang, WANG Dan, CHEN Changjie, LI Yaxin. Development of methane pyrolysis based on molten metal technology for coproduction of hydrogen and solid carbon products [J]. Chemical Industry and Engineering Progress, 2023, 42(3): 1270-1280.
[14]	ZHENG Yunwu, PEI Tao, LI Donghua, WANG Jida, LI Jirong, ZHENG Zhifeng. Production of hydrocarbon-rich bio-oil by catalytic biomass pyrolysis over metal oxide improved P/HZSM-5 catalyst [J]. Chemical Industry and Engineering Progress, 2023, 42(3): 1353-1364.
[15]	DUAN Yihang, GAO Ningbo, QUAN Cui. Effect of hydrothermal treatment on pyrolysis characteristics and kinetics of oily sludge [J]. Chemical Industry and Engineering Progress, 2023, 42(2): 603-613.