活性碳纤维负载型脱硫剂在矿井气体环境条件下的应用

张辛亥(), 赵思琛(), 朱辉, 王凯, 张首石   

  1. 西安科技大学安全科学与工程学院,陕西 西安 710054
  • 收稿日期:2022-04-28 修回日期:2022-05-31 出版日期:2022-10-20 发布日期:2022-11-10
  • 通讯作者: 赵思琛
  • 作者简介:张辛亥(1971—),男,博士,教授,研究方向为安全工程、煤矿防灭火技术。E-mail:Zhangxinh71@126.com

Application of activated carbon fiber supported desulfurizer in mine gas environment

ZHANG Xinhai(), ZHAO Sichen(), ZHU Hui, WANG Kai, ZHANG Shoushi   

  1. College of Safety Science and Engineering, Xi'an University of Science and Technology, Xi'an 710054, Shaanxi, China
  • Received:2022-04-28 Revised:2022-05-31 Online:2022-10-20 Published:2022-11-10
  • Contact: ZHAO Sichen

摘要:

H2S作为煤炭开采过程中经常会出现的气体,对煤矿的生产安全造成不利影响,必须进行脱除工作。然而煤矿中还可能存在其他组分的气体,这些气体可能会一定程度上影响H2S的脱除。本文选取活性碳纤维分别负载氢氧化钠及氧化铜,并选取两种材料的最佳负载量。之后,模拟煤矿实际条件,探讨复合脱硫剂在实际矿井气氛条件下的脱硫性能。结果表明,煤体在受热情况下会产生的多组分混合性气体,这些气体会对脱硫剂性能产生极大的影响,当煤体温度升高,其产生的CO、CO2等气体呈指数增大,并且会产生少量的CH4、C2H6、C2H4、C2H2等气体,随着这些气体生成量增大,脱硫剂脱硫性能开始下降。且在矿井气体氛条件下SO2气体的产生受到了抑制,特别在煤气组分含量大的情况下,SO2气体甚至晚于H2S气体出现。此外通过测量脱硫剂失活后的表面pH,发现即便在一些气体氛围下脱硫剂的脱硫时间更短,其脱硫后产物的表面pH极为相近,说明煤体产生的酸性气体CO以及CO2等可能也被吸附到脱硫剂的表面上生成酸性物质。

关键词: 安全工程, 硫化氢脱除, 活性碳纤维, 矿井环境, 气体组分

Abstract:

As a gas that often appears in the process of coal mining, H2S has an adverse impact on the generation safety of coal mines in China, and thus it must be removed. However, there may also be gases of other components in the coal mine, which may affect the removal of H2S to a certain extent. In this paper, activated carbon fiber was selected to load sodium hydroxide and copper oxide, respectively, and the best load of the two materials was selected. Then, the actual conditions of coal mine were simulated to explore the desulfurization performance of composite desulfurizer under the actual mine atmosphere. The results showed that the coal produced multi-component mixed gases when heated, which had a great impact on the performance of the desulfurizer. When the temperature of the coal increased, the CO, CO2 and other gases increased exponentially, and a small amount of CH4, C2H6, C2H4, C2H2 and other gases were produced. With the increase of the amount of these gases, the desulfurization performance of the desulfurizer began to decline. Moreover, under the condition of mine gas atmosphere, the generation of SO2 gas was restrained, especially when the gas component content was high, SO2 gas even appeared later than H2S gas. In addition, by measuring the surface pH value after deactivation of the desulfurizer, it was found that even if the desulfurization time of the desulfurizer was shorter in some gas atmospheres, the surface pH value of the desulfurized products was very similar, indicating that the acid gases CO and CO2 produced by coal may also be adsorbed to the surface of the desulfurizer to form acidic substances.

Key words: safety engineering, hydrogen sulfide removal, activated carbon fiber, mine environment, gas composition

中图分类号: 

京ICP备12046843号-2;京公网安备 11010102001994号
版权所有 © 《化工进展》编辑部
地址:北京市东城区青年湖南街13号 邮编:100011
电子信箱:hgjz@cip.com.cn
本系统由北京玛格泰克科技发展有限公司设计开发 技术支持:support@magtech.com.cn