油酸低温水洗改性磁性四氧化三铁纳米粒子

朱春山,宋 佳,邱 莉,张 强   

  1. 河南工业大学 化学化工学院,河南 郑州 450001
  • 出版日期:2011-07-05 发布日期:2011-07-05

Preparation of magnetic Fe3O4 nano-particles modified with oleic acid at low-temperature and washed with distilled water

ZHU Chunshan,SONG Jia,QIU Li,ZHANG Qiang   

  1. School of Chemistry and Chemical Engineering,Henan University of Technology,Zhengzhou 450001,Henan,China
  • Online:2011-07-05 Published:2011-07-05

摘要:

通过对油酸改性四氧化三铁Fe3O4磁性纳米粒子的制备工艺的改进研究,成功制备了分散性好、磁响应性强的平均粒径在18 nm的改性Fe3O4磁性纳米粒子,并通过X射线衍射、红外光谱、透射电镜等对制备的磁性纳米粒子进行了表征。结果表明:当采用60 的反应温度进行改性处理,以蒸馏水进行洗涤时,得到的油酸改性Fe3O4磁性纳米粒子的分散性最好、磁响应性最强。

Abstract:

The magnetic Fe3O4 nano-particles modified with oleic acid were prepared at 60 reaction temperature and washed with distilled water. The modified Fe3O4 nano-particles were characterized by X-ray diffraction infrared ray spectrum and TEM. The results showed that the Fe3O4 nano-particles modified by oleic acid had better dispersibilitystronger magnetic response and average grain size of 18 nm.