Chemical Industry and Engineering Progress ›› 2020, Vol. 39 ›› Issue (12): 5161-5169.DOI: 10.16085/j.issn.1000-6613.2020-0356

• Materials science and technology • Previous Articles     Next Articles

Heat charge and discharge characteristics of non-phase change solid heat storage materials

Shaowu YIN1,2(), Jiawei HAN1, Yongle SHI1, Lige TONG1,2, Li WANG1,2   

  1. 1.School of Energy and Environmental Engineering, University of Science and Technology Beijing, Beijing 100083, China
    2.Key Laboratory of Energy Saving and Emission Reduction, University of Science and Technology Beijing, Beijing 100083, China
  • Online:2020-12-02 Published:2020-12-05
  • Contact: Shaowu YIN

非相变固体蓄热材料的蓄放热特性

尹少武1,2(), 韩嘉维1, 石永乐1, 童莉葛1,2, 王立1,2   

  1. 1.北京科技大学能源与环境工程学院,北京 100083
    2.北京科技大学冶金工业节能减排北京市重点实验室,北京 100083
  • 通讯作者: 尹少武
  • 作者简介:尹少武(1979—),男,博士,副教授,研究方向为能量转换、储存及利用。E-mail:yinsw@ustb.edu.cn
  • 基金资助:
    国家重点研发计划(2018YFB0605901)

Abstract:

A heat exchange testing system for off-peak electricity energy storage was built. The thermophysical properties of non-phase change solid heat storage materials, such as corundum ball, were measured by a data recorder and a Hot-Disk thermal constant analyzer. The heat charge and discharge characteristics of fly ash, magnesia, corundum sand and corundum ball were studied both experimentally and computationally. The influences of the type and particle size of the heat storage materials on the heat charge and discharge characteristics were analyzed. The thermal storage densities and comprehensive heat transfer coefficients of different materials were obtained. Combined with FLUENT unsteady state simulation method, the variation of heat charge and discharge temperature fields of the heat storage device with materials of different particle sizes were simulated. The results showed that the corundum ball provided enough heat continuously and thus could be used as a good heat storage material. The heat storage density and comprehensive heat transfer coefficient increased with the size enlargement of corundum sand, and the effective heat discharge time was longer accordingly.

Key words: heat storage material, heat charge and discharge characteristics, temperature field, numerical simulation, alumina

摘要:

搭建了低谷电蓄能蒸汽发生换热测试系统,采用数据记录仪、Hot Disk热常数分析仪等仪器检测了刚玉球等非相变固体蓄热材料的热物性。通过实验与模拟相结合的方式,研究了粉煤灰、氧化镁、刚玉砂、刚玉球等材料的蓄放热特性。分析了蓄热材料种类和粒径大小对蓄放热特性的影响,得到了不同材料的蓄热密度和综合换热系数等关键参数。结合FLUENT非稳态模拟方法,模拟了蓄热体在不同材料粒径下的蓄热和放热温度场变化规律。结果表明:刚玉球能够提供充足连续的热量,可以作为一种性能良好的蓄热材料进行应用;随着刚玉砂粒径的增大,其蓄热密度和综合换热系数会增大,有效放热时间也会延长。

关键词: 蓄热材料, 蓄放热特性, 温度场, 数值模拟, 氧化铝

CLC Number: 

京ICP备12046843号-2;京公网安备 11010102001994号
Copyright © Chemical Industry and Engineering Progress, All Rights Reserved.
E-mail: hgjz@cip.com.cn
Powered by Beijing Magtech Co. Ltd