Hydrogen-bonding and compatibility of chitosan/polyvinyl alcohol blend films

Abstract

Abstract: Chitosan（CS）/polyvinyl alcohol（PVA）blend films with different compositions were prepared by solution casting technical using 2% acetic acid/water as a solvent. The structure，hydrogen-bonding，thermal behaviors and crystallization of CS/PVA blend films were systematically investigated by variable temperature FTIR，TGA，DTA，DSC and WXRD. It indicated that strong hydrogen-bonding interactions existed between CS and PVA，leading to the increase in thermal stability of CS，the decrease in crystallinity of PVA，and enhancement of the compatibility of CS and PVA. When the weight ratio of CS / PVA blend films was 10/0，7/3，5/5，3/7 and 0/10，the initial decomposition temperature of blends was 244 ℃，257 ℃，260 ℃，262 ℃ and 285 ℃ correspondingly. The melting temperature of PVA was decreased from 193 ℃ to 173 ℃. The glass transition temperature was increased from 74.2 ℃ to 80 ℃，and the crystallinity Xc declined from 3.57% to 1.97%.

Key words: chitosan, polyvinyl alcohol, hydrogen-bonding, compatibility, thermal behavior

摘要： 采用溶液共混法制备了不同配比的壳聚糖/聚乙烯醇共混膜，通过变温FTIR、TG、DTA、DSC及XRD等对共混膜的结构、氢键相互作用、热行为和结晶性等进行研究。实验结果表明，共混膜中壳聚糖与聚乙烯醇间存在强烈的氢键相互作用。氢键的存在使壳聚糖的热稳定性提高，聚乙烯醇结晶性下降，促进壳聚糖与聚乙烯醇相容。当壳聚糖/聚乙烯醇共混膜的质量比分别为10/0、7/3、5/5、3/7和0/10时，共混膜的初始分解温度分别为244 ℃、257 ℃、260 ℃、262 ℃和285 ℃。聚乙烯醇熔融温度从193 ℃下降到173 ℃，玻璃化转变温度从74.2 ℃上升至80 ℃，结晶度Xc从3.57%下降到1.97%。

关键词: 壳聚糖, 聚乙烯醇, 氢键, 相容性, 热行为

ZHU Erbin，XIN Meihua，LI Mingchun，LIN Jiafu. Hydrogen-bonding and compatibility of chitosan/polyvinyl alcohol blend films[J]. Chemical Industry and Engineering Progree.

祝二斌，辛梅华，李明春，林佳福. 壳聚糖/聚乙烯醇共混膜的氢键和相容性[J]. 化工进展.

[1]	WANG Shaofan, ZHOU Ying, HAO Kang’an, HUANG Anrong, ZHANG Ruju, WU Chong, ZUO Xiaoling. Self-healing and blue-light hydrogel with pH responsiveness [J]. Chemical Industry and Engineering Progress, 2023, 42(9): 4837-4846.
[2]	LIU Shuqiong, WU Fangfang, LIU Ruilai, XU Zhenyi. Preparation and characterization of a novel polylactic acid/chitosan/graphene oxide/aspirin drug-loaded biomimetic composite scaffold [J]. Chemical Industry and Engineering Progress, 2023, 42(8): 4362-4371.
[3]	WANG Lin, XIN Meihua, LI Mingchun, CHEN Qi, MAO Yangfan. Preparation of quaternized/sulfonated chitosan and its anti-biofilm activity [J]. Chemical Industry and Engineering Progress, 2023, 42(5): 2577-2585.
[4]	WANG Lin, XIN Meihua, LI Mingchun, ZHANG Tao, MAO Yangfan. Preparation of alkyl quaternized chitosan and its anti-biofilm activity [J]. Chemical Industry and Engineering Progress, 2023, 42(4): 1995-2002.
[5]	SUN Guoqi, WANG Wei, SONG Bing, WANG Liang, SHAO Ruiqi, XU Zhiwei, LUO Shigang, YAN Minjie, WANG Lijing, QIAN Xiaoming. Research progress of thermoplastic modification of polyvinyl alcohol [J]. Chemical Industry and Engineering Progress, 2022, 41(S1): 293-306.
[6]	FENG Ying, ZHAO Mengjie, CUI Qian, XIE Yuju, ZHANG Jianwei, DONG Xin. Research progress of molecular simulation technology in the development and application of chitosan functional materials [J]. Chemical Industry and Engineering Progress, 2022, 41(8): 4241-4253.
[7]	MA Hongpeng, ZHANG Xin, QIN Wenbo, GUO Bin, LI Panxin. Research progress of different modification methods of polyvinyl alcohol fiber before and after fiber formation [J]. Chemical Industry and Engineering Progress, 2022, 41(6): 3063-3076.
[8]	ZHOU Lisha, LI Ruonan, BIAN Yujie, CHEN Shunsheng. Preparation of TOCNF and magnetic carboxymethyl chitosan nanoparticles composite and adsorption properties of Pb²⁺ [J]. Chemical Industry and Engineering Progress, 2022, 41(2): 901-910.
[9]	CHANG Xian, YANG Wenjie, LI Shiyang, ZHANG Xiumin, WU Tao, XUE Lixin. Polyvinyl alcohol (PVA) based ternary mixed matrix total heat exchange membranes (THEM) comprising montmorillonite (MMT) and CaCl₂: preparation and characterization [J]. Chemical Industry and Engineering Progress, 2022, 41(2): 911-919.
[10]	LIU Rongtao, ZHANG Shiyang, HUANG Xingwen, PENG Xiaokang, MIN Yonggang. Effect of biocompatibility on surface morphology of polyaniline/polylactic acid composite nanofibers [J]. Chemical Industry and Engineering Progress, 2021, 40(8): 4406-4412.
[11]	LIU Chao, DONG Anjie, ZHANG Jianhua. Research progress of modified polyvinyl alcohol membrane [J]. Chemical Industry and Engineering Progress, 2021, 40(6): 3258-3269.
[12]	LI Siyuan, LI Ruisong, CHENG Jun, GAO Mengmeng, ZHANG Yucang, SONG Hui. Preparation and characterization of acrylamide modified corn starch/PVA composite film [J]. Chemical Industry and Engineering Progress, 2021, 40(6): 3374-3379.
[13]	SONG Ying, GE Yuanyuan, HAN Yurong, ZHOU Qinyi, HUANG Laitao, ZHOU Jian. Preparation and properties of GPs-PVA/MCE multifunctional hybrid membrane [J]. Chemical Industry and Engineering Progress, 2021, 40(11): 6287-6294.
[14]	Ximing ZHENG, Rongyu FAN. Covalent modification of chitosan quaternary ammonium salt on microporous polypropylene membrane and its antibacterial properties [J]. Chemical Industry and Engineering Progress, 2021, 40(1): 332-338.
[15]	Qihai LIU, Wanting XIE, Zhenyu JIA, Xiaohua ZHU, Ronghui WANG. Preparation of chitosan capsule materials and its sustained release properties [J]. Chemical Industry and Engineering Progress, 2021, 40(1): 339-345.

Hydrogen-bonding and compatibility of chitosan/polyvinyl alcohol blend films

壳聚糖/聚乙烯醇共混膜的氢键和相容性

Knowledge

Abstract

Cite this article

share this article

References

Related Articles 15

Recommended Articles

Metrics

Comments