Properties of cement material mixed with the rapid water-cooling desulfurized bottom ash of coal-fired CFB boiler

doi:10.16085/j.issn.1000-6613.2018-2370

Abstract

Abstract:

A new application strategy to treat the bottom ash of circulating fluidized bed boiler (CFB) was proposed to solve the problem of low utilization of bottom ash. After the bottom ash being rapidly water-cooled, it can be used as desulfurizer or the cement mixture. The experimental system for rapid water-cooling bottom ash was designed to prepare the samples of bottom ash at different temperatures. Then, the Yili ash and the cement of 42.5 grade were selected for the study, and the effect of rapid water-cooling bottom slag was investigated as mixed material on cement properties. The experimental results reveal that the way of rapid water-cooling destroys the shape of the ash particles, and cause change in the composition of the outer shell. The rapid water-cooling treatment not only gives rise to a significant decrease of the peak of CaSO₄, but also intensifies the characteristic peak of Ca(OH)₂. Compared with the original ash, the rapid water-cooling decreases the flexural and compressive strength under the same CFB bottom slag blend ratio, but it can shorten the setting time and reduce the stability value. Meanwhile, the rapid water-cooling can reduce the water requirement of the cement standard consistency and improve the compactness of the cement, it also has a positive effect on the mechanical properties and corrosion resistance of the cement.

Key words: circulating fluidized bed, bottom ash, rapid water-cooling, cement, mixed material, setting time

摘要：

针对循环流化床锅炉（CFB）底渣利用率偏低的问题，提出一种新的底渣处理应用方案——对底渣进行急冷处理后，将其作为脱硫剂或水泥混合材进行综合利用。本文通过搭建CFB锅炉底渣急冷实验系统，制备了不同渣温下的急冷底渣样品；然后选取亿利底渣和42.5标号的水泥作为研究对象，探讨了急冷底渣作混合材对水泥性能的影响。实验结果表明：急冷会破坏底渣颗粒形状，导致外壳成分发生变化。急冷处理不仅造成CaSO₄峰值显著降低，而且使得Ca(OH)₂的特征峰变强。在相同的CFB底渣掺比下，与原始底渣相比，急冷底渣作为水泥混合材时，虽然无助于提高抗折抗压强度，但能缩短凝结时间，减少安定性值。同时，还能减少水泥标准稠度需水量，提升水泥的密实程度，对水泥的力学性能和抗侵蚀性有着一定的积极作用。

关键词: 循环流化床, 底渣, 急冷, 水泥, 混合材, 凝结时间

CLC Number:

TQ172.44

Chang’an WANG,Guantao TANG,Hao LI,Defu CHE. Properties of cement material mixed with the rapid water-cooling desulfurized bottom ash of coal-fired CFB boiler[J]. Chemical Industry and Engineering Progress, 2019, 38(9): 4295-4301.

王长安,唐冠韬,李昊,车得福. 燃煤循环流化床锅炉急冷脱硫底渣作为水泥混合材的性能[J]. 化工进展, 2019, 38(9): 4295-4301.

Figures/Tables 10

References 36

1	周向飞, 郎春燕, 陈小平, 等. 激发脱硫灰渣对水泥微观结构的影响[J]. 硅酸盐通报, 2015, 34(5):1435-1439.
	ZHOUXiangfei, LANGChunyan, CHENXiaoping, et al. Influence of activator on microstructure of the desulfurization ash cement[J]. Journal of the Chinese Ceramic Society, 2015, 34(5): 1435-1439.
2	周向飞. 改性脱硫灰渣对水泥性能和微观结构的影响研究[D]. 成都: 成都理工大学, 2015.
3	ZHOUXiangfei. Study on modified desulfurized ash influence on cementitious properties and structure of cement[D]. Chengdu: Chengdu University of Technology, 2015.
4	徐浩, 陈星, 程稳, 等. 钒渣作为水泥混合材的应用研究[J]. 新世纪水泥导报, 2016(5): 1-2.
	XUNHao, CHENXing, CHENGWen, et al. Application research of vanadium slag as cement mixture[J]. Cement Guide for New Epoch, 2016(5): 1-2.
5	ZAREMBAT, DUKOWICZA, HEHLMANNJ, et al. Application of thermal analysis in a phase composition study on by product from semi-dry flue gas desulfurization system[J]. Journal of Thermal Analysis and Calorimetry, 2003, 74: 503-510.
6	SONGYuanming, LIBaoling, YANGEnhua, et al. Feasibility study on utilization of municipal solid waste incineration bottom ash as aerating agent for the production of autoclaved aerated concrete[J]. Construction and Building Materials, 2015, 56: 51-58.
7	程炎, 李天阳, 金涌. 热等离子体超高温化学转化的过程研发和应用进展[J]. 化工进展, 2016, 35(6): 1676-1686.
	CHENGYan, LITianyang, JINYong. State-of-the-art development of research and applications of chemical conversion processes at ultra-high temperature in thermal plasma reactors[J]. Chemical Industry and Engineering Progress, 2016, 35(6): 1676-1686.
8	PENGBingxian, WUDaishe. Study on bromine release from bituminous coal during combustion[J]. Fuel, 2015, 157: 82-86.
9	赵计辉, 王栋民, 惠飞, 等. 循环流化床灰渣作为水泥混合材的研究及性能改善[J]. 科学技术与工程, 2014, 14(18): 129-134.
	ZHAOJihui, WANGDongmin, HUIFei, et al. Study on the performance improvement of the cement blending circulating fluidized bed ash and slag[J]. Science Technology and Engineering, 2014, 14(18): 129-134.
10	钱觉时, 郑红伟, 宋远明, 等. 流化床燃煤固硫灰渣的特性[J]. 硅酸盐学报, 2008, 36(10): 1396-1400.
	QIANJueshi, ZHENGHongwei, SONGYuanming, et al. Special properties of fly ash and slag of fluidized bed coal combustion[J]. Journal of the Chinese Ceramic Society, 2008, 36(10): 1396-1400.
11	汪达, 王倩, 张建胜. 不同温度和冷却速率下高温灰渣的结晶行为[J]. 化工学报, 2018, 69(5): 2183-2190.
	WANGDa, WANGQian, ZHANGJiansheng. Crystallization behaviors of molten ash slag under different temperatures and cooling rates[J]. CIESC Journal, 2018, 69(5): 2183-2190.
12	谭桂蓉, 吴秀俊. CFB脱硫灰渣的性能及应用研究[J]. 粉煤灰综合利用, 2009(4): 37-40.
	TANGuirong, WUXiujun. Properties and applying researches of CFB desulfurize slay[J]. Fly Ash Comprehensive Utilization, 2009(4): 37-40.
13	陈袁魁, 包正宇, 龙世宗, 等. 高钙脱硫灰渣用作水泥原料的研究[J]. 水泥工程, 2009(4): 37-40.
	CHENYuankui, BAOZhengyu, LONGShizong, et al. Utilize desulfurized high-calcium slag as cement raw material[J]. Cement Engineering, 2009(4): 37-40.
14	黄叶. 磨细流化床固硫渣在水泥混凝土中的性能研究[D]. 重庆: 重庆大学, 2010.
	HUANGYe. The study of properties of ground circulating fluidized bed combustion ashes in cement and concrete[D]. Chongqing: Chongqing University, 2010.
15	王智. 流化床燃煤固硫渣特性及其建材资源化研究[D]. 重庆: 重庆大学, 2002.
	WANGZhi. Study on properties and utilization in building materials of bottom ashes from circulation fluidized bed combustion[D]. Chongqing: Chongqing University, 2002.
16	王朝强, 谭克锋, 戴传彬, 等. 我国脱硫灰渣资源化综合利用现状[J]. 粉煤灰综合利用, 2014(2): 51-56.
	WANGChaoqiang, TANKefeng, DAIChuanbin, et al. Research status on the comprehensive utilization of desulfurization ash in China[J]. Fly Ash Comprehensive Utilization, 2014(2): 51-56.
17	罗立群, 舒伟, 程琪林, 等. 铁尾矿加气混凝土制备工艺及结构形成机理分析[J]. 化工进展, 2017, 36(4): 1482-1489.
	LUOLiqun, SHUWei, CHENGQilin, et al. Reaction mechanism on autoclaved aerated concrete made from low-grade vanadium titanium iron tailings[J]. Chemical Industry and Engineering Progress, 2017, 36(4): 1482-1489.
18	陶俊, 倪涛, 夏亮亮, 等. 本体聚合法合成固体聚羧酸减水剂的研究及性能评价[J]. 化工进展, 2017, 36(8): 3013-3018.
	TAOJun, NITao, XIALiangliang, et al. Synthesis of solid polycarboxylate superplasticizer through bulk polymerization and its performance evaluation[J]. Chemical Industry and Engineering Progress, 2017, 36(8): 3013-3018.
19	田刚, 王红梅, 张凡. 脱硫灰的综合利用[J]. 能源环境保护, 2003, 17(6): 49-53.
	TIANGang, WANGHongmei, ZHANGFan. Systematically utilization of flue gas desulfurization residues[J]. Energy Environmental Protection, 2003, 17(6): 49-53.
20	王朝强, 谭克锋, 王培新, 等. 我国脱硫灰渣作为水泥原料及混合材的综合利用现状[J]. 电力科技与环保, 2014, 30(1): 46-49.
	WANGChaoqiang, TANKefeng, WANGPeixin, et al. Comprehensive utilization status on desulfurization ash as raw materials and admixture for cement in China[J]. Electric Power Technology and Environmental Protection, 2014, 30(1): 46-49.
21	HAUSERA, EGGENBERGERU, MUMENTHALERT. Fly ash from cellulose industry as secondary raw material in autoclaved aerated concrete[J]. Cement and Concrete Research, 1999, 29(3): 297-302.
22	MOSTAFAN Y. Influence of air-cooled slag on physicochemical properties of autoclaved aerated concrete[J]. Cement and Concrete Research, 2005, 35 (7): 1349-1357.
23	ANTHONYE J, BERRYE E, BLONDINJ. LIFAC ash-strategies for management[J]. Waste Management, 2005, 25(3): 256-279.
24	BLONDINJ, ANTHONYE J, IRIBARNEA P. A new approach to hydration of FBC residues[A]. San Diego, USA, 1993: 827-834.
25	赖振宇, 彭艳华, 吕淑珍, 等. 循环流化床固硫灰渣低收缩水泥的制备及性能[J]. 中国粉体技术, 2012, 18(4): 57-61.
	LAIZhenyu, PENGYanhua, ShuzhenLÜ, et al. Preparation and performance of CFBC ash and slag Low shrinkage cement[J]. China Powder Science and Technology, 2012, 18(4): 57-61.
26	唐晓南. 利用脱硫灰渣制备生态水泥[J]. 河北化工, 2009, 32(7): 16-17.
	TANGXiaonan. Preparation of ecological cement by using desulfurized ash[J]. Hebei Chemical Industry, 2009, 32(7): 16-17.
27	李昊, 陈午凤, 王长安, 等. 急冷处理对CFB锅炉底渣脱硫特性的影响[J]. 化工学报, 2016, 67(9): 3584-3589.
	LIHao, CHENWufeng, WANGChang’an, et al. Effect of rapid water-cooling process on desulfurization performance of CFB bottom ash[J]. CIESC Journal, 2016, 67(9): 3584-3589.
28	韩磊, 祝培旺, 徐秀林, 等. 煤灰渣酸浸提铝试验[J]. 化工进展, 2015, 34(11): 3841-3845.
	HANLei, ZHUPeiwang, XUXiulin, et al. Experimental study on aluminum leaching of coal ash[J]. Chemical Industry and Engineering Progress, 2015, 34(11): 3841-3845.
29	商晓甫, 马建立, 张剑, 等. 煤气化炉渣研究现状及利用技术展望[J]. 环境工程技术学报, 2017, 7(6): 712-717.
	SHANGXiaofu, JianliMA, ZHANGJian, et al. Research status and prospects of utilization technologies of slag from coal gasification[J]. Journal of Environmental Engineering Technology, 2017, 7(6): 712-717.
30	MONTAGNAROF, SALATINOP, SCALAF, et al. Assessment of sorbent reactivation by water hydration for fluidized bed combustion application[J]. Transactions of the ASME Journal of Energy Resources Technology, 2006, 128 (2): 90-98.
31	MONTAGNAROF, SALATINOP, SCALAF, et al. An assessment of water and steam reactivation of a fluidized bed spent sorbent for enhanced SO₂ capture[J]. Powder Technology, 2008, 180(1/2): 129-134.
32	李阳, 朱玉雯, 高继慧, 等. 活性焦孔结构演变规律及对脱硫性能的影响[J]. 化工学报, 2015, 66 (3): 1126-1132.
	LIYang, ZHUYuwen, GAOJihui, et al. Activated coke pore structure evolution and its influence on desulfuration[J]. CIESC Journal, 2015, 66(3): 1126-1132.
33	陈袁魁, 袁龙华, 朱龙飞. CFB脱硫灰渣用作水泥混合材的研究[J]. 新世纪水泥导报, 2014, 20(4): 17.
	YuankuiCEHN, YUANLonghua, ZHULongfei. Study on CFB desulfurization ash used as cement mixture[J]. Cement Guide for New Epoch, 2014, 20(4): 17.
34	周爱军, 张玫. 土木工程材料[M]. 北京: 机械工业出版社, 2012: 39-49.
	ZHOUAijun, ZHANGMei. Architecture material[M]. Beijing: China Machine Press, 2012: 39-49.
35	马小莉, 相玉琳. 改性污泥制备泡沫混凝土的可行性研究[J]. 化工进展, 2016, 35(9) : 2997-3001.
	XiaoliMA, XIANGYulin. Feasibility study on foam concrete prepared by modification sludge[J]. Chemical Industry and Engineering Progress, 2016, 35(9): 2997-3001.
36	吕生华, 张佳, 朱琳琳, 等. 氧化石墨烯对水泥基复合材料微观结构的调控作用及对抗压抗折强度的影响[J]. 化工学报, 2017, 68(6): 2586-2594.
	ShenghuaLÜ, ZHANGJia, ZHULinlin, et al. Regulation of graphene oxide on microstructure of cement composites and its impact on compressive and flexural strength[J]. CIESC Journal, 2017, 68(6): 2586-2594.

		工业分析/%					弹筒热值	空气干燥基高位热值	收到基低位热值
M_ar	M_ad	A_ad	V_ad	FC_ad	S_ad		（Q_b,ad）/MJ·kg^-1	（Q_gr,ad）/MJ·kg^-1	（Q_net,ar）/MJ·kg^-1
24.1	12.0	21.3	25.4	41.3	0.9		20.2	20.1	16.2

		工业分析/%					弹筒热值	空气干燥基高位热值	收到基低位热值
M_ar	M_ad	A_ad	V_ad	FC_ad	S_ad		（Q_b,ad）/MJ·kg^-1	（Q_gr,ad）/MJ·kg^-1	（Q_net,ar）/MJ·kg^-1
24.1	12.0	21.3	25.4	41.3	0.9		20.2	20.1	16.2

底渣	CaO	SiO₂	SO₃	Al₂O₃	MgO	Fe₂O₃	TiO₂
原始底渣	39.90	31.50	3.54	12.00	1.81	4.31	0.71
急冷底渣	65.50	15.90	3.10	4.15	1.92	3.67	0.60

底渣	CaO	SiO₂	SO₃	Al₂O₃	MgO	Fe₂O₃	TiO₂
原始底渣	39.90	31.50	3.54	12.00	1.81	4.31	0.71
急冷底渣	65.50	15.90	3.10	4.15	1.92	3.67	0.60

[1]	YAN Qing, ZHANG Yunfeng, ZHAO Minwei, SONG Ning, GAO Hui, ZHOU Jing. Feasibility analysis of large span compensation platform for LNG terminal [J]. Chemical Industry and Engineering Progress, 2023, 42(S1): 158-165.
[2]	WANG Jiaqing, SONG Guangwei, LI Qiang, GUO Shuaicheng, DAI Qingli. Rubber-concrete interface modification method and performance enhancement path [J]. Chemical Industry and Engineering Progress, 2023, 42(S1): 328-343.
[3]	LI Dongze, ZHANG Xiang, TIAN Jian, HU Pan, YAO Jie, ZHU Lin, BU Changsheng, WANG Xinye. Research progress of NO _x reduction by carbonaceous substances for denitration in cement kiln [J]. Chemical Industry and Engineering Progress, 2023, 42(9): 4882-4893.
[4]	DONG Jiayu, WANG Simin. Experimental on ultrasound enhancement of para-xylene crystallization characteristics and regulation mechanism [J]. Chemical Industry and Engineering Progress, 2023, 42(9): 4504-4513.
[5]	TIAN Qikai, ZHENG Haiping, ZHANG Shaobin, ZHANG Jing, YU Ziyi. Advances in mixing enhanced microfluidic channels [J]. Chemical Industry and Engineering Progress, 2023, 42(4): 1677-1687.
[6]	ZHAO Xingcheng, JIA Fangxu, JIANG Weiyu, CHEN Jiayi, LIU Chenyu, YAO Hong. Redox mediators-mediated anaerobic ammonium oxidation process for biological nitrogen removal: a review [J]. Chemical Industry and Engineering Progress, 2023, 42(3): 1606-1617.
[7]	FAN Yunpei, JIN Jing, LIU Dunyu, WANG Jingjie, LIU Qiuqi, XU Kailong. Mercury removal by CaSO₄ oxygen carrier during in-situ gasification and chemical-looping combustion of coal [J]. Chemical Industry and Engineering Progress, 2023, 42(3): 1638-1648.
[8]	LI Jingjing, ZHAO Yao, XU Fengchi, LI Kangjian. Heavy metal leaching characteristics of porous asphalt mixture containing MSWI-BAA under different stormwater runoff flow rates [J]. Chemical Industry and Engineering Progress, 2023, 42(10): 5520-5530.
[9]	PAN Yuelei, CHENG Xudong, YAN Mingyuan, HE Pan, ZHANG Heping. Silica aerogel and its application in the field of thermal insulation [J]. Chemical Industry and Engineering Progress, 2023, 42(1): 297-309.
[10]	CHEN Peijia, GE Xin, LIANG Weijie, YIN Shuang, ZHANG Zhicong, LYU Jianer, LIU Weidong, CHEN Youpeng, GE Jianfang. Research progress of polymer-based thermal interface materials and thermal conductivity properties [J]. Chemical Industry and Engineering Progress, 2022, 41(S1): 269-281.
[11]	FANG Kejing, XIONG Zuhong, LU Min, LI Tao, CHEN Yong. Research progress in preparation, thermal conversion characteristics and application of refuse derived fuel [J]. Chemical Industry and Engineering Progress, 2022, 41(S1): 132-140.
[12]	HUANG Yuefeng, MA Lisha, ZHANG Lili, WANG Zhiguo. Research progress on functional application of lignocellulose composite biomass film materials [J]. Chemical Industry and Engineering Progress, 2022, 41(9): 4840-4854.
[13]	HUANG Xia, HE Yingying, ZHANG Yidie, YANG Dianhai, DAI Xiaohu, XIE Li. Research progress on enhancing resource utilization of organic solid waste aerobic composting based on biochar [J]. Chemical Industry and Engineering Progress, 2022, 41(8): 4544-4554.
[14]	LIU Shijie, MO Xun, TU Aimin, ZHU Dongsheng, TAN Lianyuan. Shell-side heat transfer enhancement of a novel longitudinal flow oil cooler [J]. Chemical Industry and Engineering Progress, 2022, 41(7): 3475-3482.
[15]	LI Yifan, WANG Zhipeng. Flow and heat transfer characteristics in microchannels with periodic fluid disturbance structures [J]. Chemical Industry and Engineering Progress, 2022, 41(6): 2893-2901.