Effect of the doped alkaline-earth metals on the catalytic performance of CeO2

doi:10.16085/j.issn.1000-6613.2016.11.022

Abstract

Abstract: Nano-CeO₂ (20nm) was prepared by hydrothermal method, and then alkaline-earth metal oxides (MgO、CaO and BaO) of different concentrations were introduced into the nano-CeO₂. The catalytic results showed that the doping of these three alkaline-earth metal oxides all had negative effects on the catalytic performance of nano-CeO₂. In addition, the prepared nano-CeO₂ were characterized with TEM, XRD, BET, XPS and TPD. The results show that a small amount of doped alkaline-earth metal oxideswere in the form of disorder and they couldn't lead to the lattice deformation and showed little effects on the morphology, particle size and textural properties, but they had great effect on the ratio of Ce(Ⅳ)/Ce(Ⅲ) as well as the amount of the acid and base sites. In addition, high ratio of Ce(Ⅳ)/Ce(Ⅲ) and a large amount of acid and base sites are essential for the catalytic performance of nano-CeO₂.

Key words: nano-CeO₂, alkaline-earth metal oxides, dope, di-methyl carbonate(DMC)

摘要： 通过水热法制备了平均粒径约为20nm的CeO₂，并在纳米CeO₂上引入不同浓度的3种碱土金属氧化物（MgO、CaO和BaO）。催化结果显示在用于催化二氧化碳和甲醇直接合成碳酸二甲酯（DMC）的反应中，此3种碱土金属氧化物均未对纳米CeO₂的催化活性起到促进作用。此外通过透射电镜（TEM）、X射线衍射（XRD）、比表面积及孔分布测试（BET）、X射线光电子能谱（XPS）和程序升温吸附（TPD）对所制备的催化剂进行了表征。研究结果表明，少量的碱土金属氧化物的掺杂不会导致CeO₂晶格变形，而是以无序的形式存在；且碱土金属氧化物的掺杂对纳米CeO₂的形貌、尺寸和织构性质影响不大，对其表面的Ce（Ⅳ）/Ce（Ⅲ）和酸碱性位的数量以及强度有较大影响。此外，较高的Ce（Ⅳ）/Ce（Ⅲ）和较多的酸性位是影响纳米CeO₂催化性能的重要因素。

关键词: 纳米CeO₂, 碱土金属氧化物, 掺杂, 碳酸二甲酯

CLC Number:

TQ225

LI Ping, DUAN Huijuan. Effect of the doped alkaline-earth metals on the catalytic performance of CeO₂[J]. Chemical Industry and Engineering Progress, 2016, 35(11): 3529-3535.

李萍, 段慧娟. 不同碱土金属氧化物掺杂对纳米二氧化铈催化性能的影响[J]. 化工进展, 2016, 35(11): 3529-3535.

References

[1] ONO Y. Dimethyl carbonate for environ mentally benign reactions[J]. Catal Today,1997,35(1/2):15-25.
[2] 赵艳敏,刘绍英,王公应,等. 尿素法合成碳酸二甲酯的研究进展[J]. 化工进展,2004,23(10):1049-1052.
[3] PACHECO M A,MARSHALL C L. Review of dimethyl carbonate (DMC) manufacture and its characteristics as a fuel additive[J]. Energy & Fuels,1997,11(1):2-29.
[4] 刘金聚,李凝,范细林,等. 掺杂物对负载型ZrO₂/Al₂O₃的催化性能的影响[J]. 分子催化,2009,23(5):454-458.
[5] LAURENCZY G,PICQUET M,PLASSERAUD L. Di-n-butyltin (Ⅳ)-catalyzed dimethyl carbonate synthesis from carbon dioxide and methanol:an in situ high pressure ¹¹⁹Sn{1H} NMR spectroscopic study[J]. Journal of Organometallic Chemistry,2011,696(9):1904-1909.
[6] NAM J K,CHOI M J,CHO D H,et al. The influence of support in the synthesis of dimethyl carbonate by Cu-based catalysts[J]. Journal of Molecular Catalysis A:Chemical,2013,370:7-13.
[7] WU X,KANG M,YIN Y,et al. Synthesis of dimethyl carbonate by urea alcoholysis over Zn/Al bi-functional catalysts[J]. Applied Catalysis A:General,2014,473:13-20.
[8] TOMISHIGE K,IKEDA Y,SAKAIHORI T,et al. Catalytic properties and structure of zirconia catalysts for direct synthesis of dimethyl carbonate from methanol and carbon dioxide[J]. Journal of Catalysis,2000,192(2):355-362.
[9] BALLIVET-TKATCHENKO D,CHAMBREY S,KEISKI R,et al. Direct synthesis of dimethyl carbonate with supercritical carbon dioxide:characterization of a key organotin oxide intermediate[J]. Catalysis Today,2006,115(1):80-87.
[10] ZHANG M,XIAO M,WANG S J,et al. Cerium oxide-based catalysts made by template-precipitation for the dimethyl carbonats synthesis from carbon dioxide and methanol[J]. Journal of Cleaner Production,2015,103:847-853.
[11] TOMISHIGE K,KUNIMORI K. Catalytic and direct synthesis of dimethyl carbonate starting from carbon dioxide using CeO₂-ZrO₂ solid solution heterogeneous catalyst: effect of H₂O removal from the reaction system[J]. Applied Catalysis A:General,2002,237(1):103-109.
[12] TOMISHIGE K,FURUSAWA Y,IKEDA Y,et al. CeO₂-ZrO₂ solid solution catalyst for selective synthesis of dimethyl carbonate from methanol and carbon dioxide[J]. Catalysis Letters,2001,76(1/2):71-74.
[13] SEO E S,PARK N K,CHANG W C,et al. Direct synthesis of dimethyl carbonate from methanol and carbon dioxide[J]. Journal-Korean Institue of Chemical Engineers,2002,40(1):9-15.
[14] LA K W,YOUN M H,CHUNG J S,et al. Synthesis of dimethyl carbonate from methanol and carbon dioxide by heteropolyacid/metal oxide catalysts[J]. Solid State Phenomena,2007,119:287-290.
[15] ARESTA M,DIBENEDETTO A,PASTORE C,et al. Cerium (Ⅳ) oxide modification by inclusion of a hetero-atom:a strategy for producing efficient and robust nano-catalysts for methanol carboxylation[J]. Catalysis Today,2008,137(1):125-131.
[16] ARESTA M,DIBENEDETTO A,PASTORE C,et al. Influence of Al₂O₃on the performance of CeO₂ used as catalyst in the direct carboxylation of methanol to dimethylcarbonate and the elucidation of the reaction mechanism[J]. Journal of Catalysis,2010,269(1):44-52.
[17] ABIMANYU H,KIM C S,AHN B S,et al. Synthesis of dimethyl carbonate by transesterification with various MgO-CeO₂ mixed oxide catalysts[J]. Catalysis Letters,2007,118(1/2):30-35.
[18] KANG K H,JOE W,LEE C H,et al. Direct synthesis of dimethyl carbonate from methanol and carbon dioxide over CeO_2(x)-ZnO(₁_-_x₎ nano-catalysts[J]. Journal of nanoscience and nanotechnology,2013,13(12):8116-8120.
[19] LI H F,ZHANG N,CHEN P,et al. High surface area Au/CeO₂ catalysts for low temperature formaldehyde oxidation[J]. Applied Catalysis B: Environmental,2011,110:279-285.
[20] ERDEM B,ERDEM S,ÖKSÜZOĞLU R M,et al. High-surface-area SBA-15-SO₃H with enhanced catalytic activity by the addition of poly(ethylene glycol)[J]. Journal of Porous Materials,2013,20(5):1041-1049.
[21] PFAU A,SCHIERBAUM K D. The electronic structure of stoichiometric and reduced CeO₂ surfaces:an XPS,UPS and HREELS study[J]. Surface Science,1994,321:71-80.

Effect of the doped alkaline-earth metals on the catalytic performance of CeO₂

不同碱土金属氧化物掺杂对纳米二氧化铈催化性能的影响

PDF (PC)

Knowledge

Abstract

Cite this article

share this article

References

Related Articles 15

Recommended Articles

Metrics

Comments

[1]	LEI Wei, JIANG Weijia, WANG Yugao, HE Minghao, SHEN Jun. Synthesis of N,S co-doped coal-based carbon quantum dots by electrochemical oxidation and its application in Fe³⁺ detection [J]. Chemical Industry and Engineering Progress, 2023, 42(9): 4799-4807.
[2]	WANG Shuaiqing, YANG Siwen, LI Na, SUN Zhanying, AN Haoran. Research progress on element doped biomass carbon materials for electrochemical energy storage [J]. Chemical Industry and Engineering Progress, 2023, 42(8): 4296-4306.
[3]	WANG Yuzhuo, LI Gang. S,N co-doped three-dimensional graphene for all-solid-state supercapacitors [J]. Chemical Industry and Engineering Progress, 2023, 42(4): 1974-1982.
[4]	YAO Wen, ZHANG Yuchen, TENG Wenxin, LI Jiangling. Effect of surfactant on the preparation of Ca-doped β-In₂S₃ microstructure and its performance in photocatalytic degradation of methyl orange [J]. Chemical Industry and Engineering Progress, 2023, 42(2): 774-782.
[5]	HE Chenlu, QIU Chenxi, FANG Juan, YANG Xuan, LAI Jianjun, ZHENG Xinyu, LYU Jianhua, CHEN Yandan, HUANG Biao. Nitrogen-doped supercapacitor carbon based on eutectic solvent system [J]. Chemical Industry and Engineering Progress, 2022, 41(9): 4946-4953.
[6]	XIONG Yongzhi, LIU Yanyan, CHEN Xiaohong, LU Beili, HUANG Biao, LIN Guanfeng. Preparation and electrochemical performance of bagasse-based phosphorus-doped activated carbon [J]. Chemical Industry and Engineering Progress, 2022, 41(8): 4397-4405.
[7]	LIANG Huagen, QI Zhengwei, JIA Linhui, GAI Zejia, JING Shengyu, YIN Shibin. Three dimensional self-supporting Co, N, S co-doped porous carbon derived from paulownia wood for Li-O₂ batteries [J]. Chemical Industry and Engineering Progress, 2022, 41(5): 2555-2565.
[8]	ZHANG Aijing, JIANG Shengjuan, ZHOU Mingzheng, CHAI Maorong, ZHANG Jin. Effect of wall number on the electro-catalytic activity of nitrogen-doped carbon nanotubes for oxygen reduction reaction [J]. Chemical Industry and Engineering Progress, 2022, 41(4): 2038-2045.
[9]	ZHAI Chongyuan, ZHAO Dandi, HE Yapeng, HUANG Hui, CHEN Buming, GUO Zhongcheng. Recent development on boron-doped diamond anodes in electrochemical degradation of emerging antibiotic pollutants [J]. Chemical Industry and Engineering Progress, 2022, 41(12): 6615-6626.
[10]	HUANG Xin, LIU Cheng, TANG Rujia, HAN Xinxin, CHEN Shixia, WANG Jun. Nitrogen-doped carbon-confined flower-like SnS catalyst for electrochemical reduction of CO₂ to HCOOH [J]. Chemical Industry and Engineering Progress, 2022, 41(11): 5887-5895.
[11]	ZHAO Wenwu, ZHOU Haijing, HUANG Yan, WANG Xiuwen, HAO Bin, LIU Jian. Photocatalytic mechanism and synthesis of rare earth doped borate Bi₂ZnB₂O₇: xDy³⁺ photocatalyst [J]. Chemical Industry and Engineering Progress, 2022, 41(11): 5843-5849.
[12]	JU Mengcan, YAN Lili, JIAN Ling, JIANG Siyu, RAO Pinhua, LI Guanghui. Preparation of nitrogen-doped biochar and its environmental applications [J]. Chemical Industry and Engineering Progress, 2022, 41(10): 5588-5598.
[13]	MA Ailing, HUANG Guangxu, GENG Qianhao, YAO Youheng, LI Yuanyuan, LIU Yingbin. Preparation and electrochemical properties of B/N co-doped porous carbon nanosheets [J]. Chemical Industry and Engineering Progress, 2021, 40(8): 4388-4396.
[14]	TANG Qian, FAN Yixin, SU Xin, HUANG Chengsi, SUN Yuwei, GAO Yonghui, WANG Dong. Preparation of N/B/Fe co-doped biochar cathode for degradation of p-nitrophenol [J]. Chemical Industry and Engineering Progress, 2021, 40(7): 4064-4073.
[15]	HU Sisi, SUN Lizhi, ZHANG Di, WANG Bo. Lithium storage performance of Fe-doped Xuan paper-based carbon fiber materials [J]. Chemical Industry and Engineering Progress, 2021, 40(10): 5370-5377.