Catalytic curing of novolac cyanate ester resins modified by diallyl bisphenol A

MA Liqun1,HUANG Wei2,QU Chunyan3,WANG Yazhen2,LIU Hongcheng2,WANG Jianxin2   

  1. 1 College of Materials Science and Engineering,Qiqihar University,Qiqihar 161006,Heilongjiang,China;2Institute of Petrochemistry Heilongjiang Academy of Sciences,Harbin 150040,Heilongjiang,China
  • Online:2013-07-05 Published:2013-07-05

二烯丙基双酚A催化改性酚醛型氰酸酯树脂的催化固化

马立群1,黄 伟1,2,曲春艳2,王雅珍1,刘洪成1,汪建新1   

  1. 1齐齐哈尔大学材料科学与工程学院,黑龙江 齐齐哈尔 161006;2黑龙江省科学院石油化学研究院,黑龙江 哈尔滨 150040

Abstract: Effects of diallyl bisphenol A(DBA) on catalyzing the thermal curing of novolac cyanate ester resin(cy-5) were studied. Thermal and mechanical properties of DBA catalyzed novolac cyanate ester resins were characterized by DSC,TG,impact performance and DMA test. The results showed that DBA can catalyze the curing reaction and toughen the cured resin with dual function,the 5% DBA-catalyzed novolac cyanate ester resin exhibits the best catalytic effect,the impact strength of the cured resin modified by 10% DBA is 7.41 kJ/m2,and the glass transition temperature and storage modulus of the cured resin modified by DBA both decrease slightly.

Key words: diallyl bisphenol A, novolac cyanate ester resin, catalytic effect, toughen effect

摘要: 研究了二烯丙基双酚A(DBA)催化改性酚醛型氰酸酯树脂(cy-5),通过差示扫描量热法(DSC)、热重分析(TG)、冲击性能和动态热机械分析(DMA)测试,分析了改性树脂的热性能和力学性能。研究表明:DBA对cy-5有催化和增韧的双重作用,当DBA的添加量为5%(质量分数)时,催化效果最为明显,含10% DBA的改性树脂固化物的冲击强度达到7.41 kJ/m2,改性树脂固化物的玻璃化转变温度(Tg)和储能模量(E')均有所降低,但幅度不大。

关键词: 二烯丙基双酚A, 酚醛型氰酸酯树脂, 催化作用, 增韧效果