Synthesis process of polycarboxylic water reducer at ambient temperature

doi:10.16085/j.issn.1000-6613.2016.11.039

Abstract

Abstract: The synthesis process of polycarboxylic water reducer was mainly composed of heating. The synthesis process at ambient temperature has been less reported. To solve this problem, the paper researched the influences of reaction temperature, holding time, feeding time of A and B, acid ether ratio, and ammonium persulfate (APS) weight on the performance of polycarboxylic water reducer that was synthesized by using methyl allyl polyethenoxy ether (TPEG) and acrylic acid (AA) as the main polymeric monomers. Orthogonal experiments showed that when the temperature is 30℃, holding time is 1.5 hours, feeding time of A is 2.25 hours, feeding time of B is 3.5 hours, n(AA):n(TPEG)=3.5:1, and APS ratio is 0.5%, the polycarboxylic water reducer achieves optimum performance. When water-binder ratio is 0.29 and a dosage of 0.25% of such obtained water reducer is used, the initial cement paste fluidity reaches 240mm and the slump loss is 5mm after 1 hour. It has better dispersity and dispersion stability than other polycarboxylic water reducers at the same dosage.

Key words: polycarboxylic water reducer, TPEG, ambient temperature, polymerization

摘要： 目前聚羧酸减水剂的合成工艺主要以加热为主，低温合成工艺报道较少。本文为了解决这一问题，以异戊烯醇聚氧乙烯醚（TPEG）、丙烯酸（AA）为主要聚合单体，研究分析反应温度、保温时间、A/B液滴加时间、酸醚比、引发剂过硫酸铵用量（APS）等因素对合成减水剂产品性能的影响。并利用正交试验，筛选出常温条件下较优的合成工艺：酸醚比n（AA）∶n（TPEG）=3.5∶1，引发剂过硫酸铵用量（按TPEG单体质量分数计）为0.5%，反应温度30℃，A液滴加2.25h，B液滴加3.5h，保温时间1.5h。合成减水剂产品在水灰比0.29，掺量0.25%的条件下，水泥净浆初始流动度达到240mm，1h后净浆流动度损失5mm，相同掺量下与其他减水剂产品相比具有更好的分散性和分散保持性。

关键词: 聚羧酸减水剂, 异戊烯醇聚氧乙烯醚, 常温, 聚合

CLC Number:

TQ317

CHEN Shiming, JIN Yifeng, GAO Hongjun, DONG Nan. Synthesis process of polycarboxylic water reducer at ambient temperature[J]. Chemical Industry and Engineering Progress, 2016, 35(11): 3645-3649.

陈世明, 金一丰, 高洪军, 董楠. 聚羧酸减水剂的常温合成工艺[J]. 化工进展, 2016, 35(11): 3645-3649.

References

[1] 王彦君,刘凤英,蓝宇导.聚羧酸减水剂的研究[J].中国建材科技,2011,20(5):51-54.
[2] FERRARI L,KAUFMANN J,WINNEFELD F,et al.Interaction of cement model systems with superplasticizers invertigated by atomic force microscopy,zeta potential and adsorption measurements[J].Journal of Colloid and Interface Science,2010,347(1):15-24.
[3] DAIMON M,ROY D M.Rheological properties of cement mixes:Ⅰ. Methods,preliminary experiments and adsorption studies[J].Cement and Concrete Research,1978,8(6):753-764.
[4] 廖国胜,王劲松,马保国,等.新型聚羧酸类化学减水剂合成的几个关键问题研究探讨[J].国外建材科技,2004,25(2):48-50.
[5] ZHANG Rongguo,GUO Huiling,LEI Jiaheng,et al.Effect of molecular structure on the performance of polyacrylic acid superplasticizer[J].Journal of Wuhan University of Technology:Mater. Sci. Ed.,2007,22(2):245-249.
[6] 李崇智.新型聚羧酸系减水剂的合成及其性能研究[D].北京:清华大学,2004.
[7] 沈军,傅乐峰,冯中军,等.聚醚基超塑化剂的合成及其性能研究[J].混凝土,2005(6):61-64.
[8] 王友奎,赵帆,王洛礼.低坍损聚羧酸系高效减水剂的合成[J].混凝土,2005(9):79-82.
[9] YAMADA K,TAKAHASHI T,HANEHARA S,et al.Effects of the chemical structure on the properties of polycarboxylate-type superplasticizer[J].Cement and Conercte Research,2000,30(3):197-207.
[10] 韩明,高蓓蕾,陈树东,等.聚羧酸系高效减水剂的合成研究[J].新型建筑材料,2008,35(3):19-22.
[11] CHO Heon-Ybung,SUH Jung-Mok.Effects of the synthetic conditions of poly(carboxylate-g-(ethylene glycol) methyl ether) on the dispersibility in cement paste[J].Cement and Concrete Research,2005,35(5):891-899.
[12] 何靖,庞浩,张先文,等.新型聚醚接枝聚羧酸型高效混凝土减水剂的合成与性能[J].高分子材料科学与工程,2005,21(5):44-47.
[13] ZHOLKOVSKIJ Emilij K,CZARNECKI Jan,MASLIYAH Jacob H.Electrostatic repulsion in concentrated disperse systems:Ⅰ. Contribution of electrostatic interaction to osmotic pressure[J]. Journal of Colloid and Interface Science,2001,234(2):293-315.
[14] 张超灿,陶铃宏,付晓.马来酸类聚羧酸减水剂的合成及其对水泥净浆流动性的影响研究[J].化学与生物工程,2010,27(7):46-50.

[1]	QIAN Sitian, PENG Wenjun, ZHANG Xianming. Comparative analysis of forming cyclic oligomers via PET melt polycondensation and cyclodepolymerization [J]. Chemical Industry and Engineering Progress, 2023, 42(9): 4808-4816.
[2]	CHEN Junjun, FEI Chang’en, DUAN Jintang, GU Xueping, FENG Lianfang, ZHANG Cailiang. Research progress on chemical modification of polyether ether ketone for the high bioactivity [J]. Chemical Industry and Engineering Progress, 2023, 42(8): 4015-4028.
[3]	HE Zhiyong, GUO Tianfo, WANG Jinli, LYU Feng. Progress of CO₂/epoxide copolymerization catalyst [J]. Chemical Industry and Engineering Progress, 2023, 42(4): 1847-1859.
[4]	ZHAO Zhenzhen, ZHENG Xi, WANG Xueqi, WANG Tao, FENG Yingnan, REN Yongsheng, ZHAO Zhiping. Research progress on microporous supporting substrate of polyamide composite membrane [J]. Chemical Industry and Engineering Progress, 2023, 42(4): 1917-1933.
[5]	ZHAO Wangrui, LIU Yan, ZHANG Wei, DENG Huining. Fe³⁺ ions induced rapid electrodeposition of polydopamine-polyethyleneimine for monovalent selective membrane fabrication [J]. Chemical Industry and Engineering Progress, 2023, 42(3): 1508-1514.
[6]	ZHANG Jie, WANG Xudong, YANG Yifei, REN Yue, CHEN Licheng. Response surface optimization of preparation and performance of thermo-responsive hydrogels as draw agent [J]. Chemical Industry and Engineering Progress, 2023, 42(10): 5363-5372.
[7]	HUO Wentao, LIU Wen, YU Qiang, AN Jie, ZHU Xiangxue, QIN Yucai, LI Xiujie. Oligomerization of isobutene over MWW zeolite based catalysts [J]. Chemical Industry and Engineering Progress, 2023, 42(10): 5205-5212.
[8]	ZHANG Saihui, LI Xiaoyang, GAO Hui, WANG Lili. Recent progress in additives in interfacial polymerization for the preparation of polyamide composite membrane [J]. Chemical Industry and Engineering Progress, 2022, 41(9): 4884-4894.
[9]	WANG Qiaoyi, LU Shaofeng, SHI Wenzhao, HONG Xun, YAO Dongxia, ZHANG Ling. Preparation and properties of polyurea/polyurethane shell microencapsulated essence by interfacial polymerization [J]. Chemical Industry and Engineering Progress, 2022, 41(8): 4432-4440.
[10]	SHAN Qingwen, ZHANG Juan, WANG Yajuan, LIU Wenqiang. Synthesis of polymeric ionic liquid and its performance on adsorption desulfurization [J]. Chemical Industry and Engineering Progress, 2022, 41(8): 4571-4579.
[11]	GONG Xin, LIU Xiaodong, WEN Fushan, SHI Nan, LIU Dong. Preparation and electrochemical performance of mesocarbon microbeads derived from emulsion-polymerization method [J]. Chemical Industry and Engineering Progress, 2022, 41(5): 2379-2388.
[12]	CHEN Xue, LIU Shulin, HE Fengxiang, LYU Han, WU Quanyu, WANG Hao, QU Bin. Preparation and performance of anode material modifiers based on coal series heavy aromatic hydrocarbons [J]. Chemical Industry and Engineering Progress, 2022, 41(12): 6461-6468.
[13]	ZHU Jian, SHANG Xiaoyu, WANG Ying, ZHANG Xianming, CHEN Wenxing. Synthesis and properties of PET copolyester modified by spirocyclodiol [J]. Chemical Industry and Engineering Progress, 2022, 41(11): 6003-6010.
[14]	LI Ting, DU Shaohui, CUI Jinfeng, WANG Yanghui, LI Hulin, GUO Runlan, WANG Peng, WANG Zhenjun, GUO Junhong, YANG Baoping. Preparation and properties of waterborne polyurethane paper sizing agents with phosphorus-boron hybrid prepolymer blocks [J]. Chemical Industry and Engineering Progress, 2022, 41(10): 5549-5557.
[15]	HUANG Wenrui, HUANG Zhengqiang, FU Peng, CUI Zhe, ZHANG Xiaomeng, PANG Xinchang, ZHAO Qingxiang, LIU Minying. Microwave-assisted polymerization and characteristic of semi-aromatic nylon PA12T [J]. Chemical Industry and Engineering Progress, 2022, 41(1): 336-342.