Chemical Industry and Engineering Progress ›› 2022, Vol. 41 ›› Issue (5): 2582-2592.DOI: 10.16085/j.issn.1000-6613.2021-1219

• Materials science and technology • Previous Articles     Next Articles

Preparation of nano-lignin-based porous carbon materials by one-step pyrolysis activation method

WANG Luyuan1,2(), JIN Chunjiang1,2,3, CHEN Huimin3, CHENG Xingxing4, AN Donghai3(), ZHANG Xingyu2, SUN Rongfeng1,2, GENG Wenguang1,2   

  1. 1.Energy Research Institute of Shandong Academy of Sciences, Jinan 250014, Shandong, China
    2.School of Energy and Power Engineering, Qilu University of Technology, Jinan 250014, Shandong, China
    3.Changji University, Changji 831100, Xinjiang, China
    4.School of Energy and Power Engineering, Shandong University, Jinan 250061, Shandong, China
  • Received:2021-06-10 Revised:2021-10-07 Online:2022-05-24 Published:2022-05-05
  • Contact: AN Donghai

一步热解活化法制备纳米木质素基多孔炭材料

王鲁元1,2(), 金春江1,2,3, 陈惠敏3, 程星星4, 安东海3(), 张兴宇2, 孙荣峰1,2, 耿文广1,2   

  1. 1.山东省科学院能源研究所,山东 济南 250014
    2.齐鲁工业大学能源与动力工程学院,山东 济南 250014
    3.昌吉学院,新疆 昌吉 831100
    4.山东大学能源与动力工程学院,山东 济南 250061
  • 通讯作者: 安东海
  • 作者简介:王鲁元(1988—),男,博士,主要研究方向为VOCs环保治理及炭材料、脱硫脱硝催化剂的制备。E-mail:luyuanwang1988@126.com
  • 基金资助:
    国家自然科学基金(51906130);山东省自然科学基金(ZR2019BEE053);山东省科学院青年基金(2020QN009);山东省重点实验室能源碳减排技术与资源化利用实验室项目(ECRRU201804);新疆教育厅新疆维吾尔自治区高校科研计划(XJEDU2019Y025);齐鲁工业大学(山东省科学院)科教产项目(2020KJC~ZD12)

Abstract:

The lignin-based porous carbon material (LPC) was obtained by using lignin as raw material and tube furnace reactor through a one-step pyrolysis-activation method. Nitrogen adsorption (BET), scanning electron microscopy (SEM) and Fourier transform infrared spectroscopy (FTIR) were used to analyze the physical and chemical properties of porous carbon material. At a constant carbonization temperature of 900℃ with CO2 concentration of 6% and water vapor concentration of about 20%, the surface of LPC-C6S20 had a good nanostructure, and the total pore volume and specific surface area reached 0.77cm3/g and 1497.51m2/g, respectively. The activation atmosphere promoted the uniformity of porous carbon material particles and the formation of micropores and mesopores. The LPC sample contained abundant surface functional groups such as —OH, C—H, C=C, C—O, C=O, CO—C, C—N and C=N, etc. As the concentration of the activator changed, these functional groups remained relatively stable. Therefore, the sample obtained by this method had a good nanostructure with a larger pore volume, specific surface area and functional groups.

Key words: lignin, one step pyrolysis, porous carbon, pore structure

摘要:

以木质素为原料,采用管式炉反应器通过一步热解-半活化法获得木质素基多孔炭材料(LPC)。采用氮吸附(BET)、扫描电镜(SEM)和傅里叶变换红外光谱(FTIR)对多孔炭材料的物化性质进行分析。在900℃的恒定炭化温度下,CO2体积分数为6%、水蒸气体积分数约为20%时,LPC-C6S20表面具有良好的纳米结构,并且总孔容和比表面积分别达到0.77cm3/g和1497.51m2/g,活化气氛促进了多孔炭材料颗粒趋于均匀和微孔、中孔的形成。LPC样品含有—OH、C—H、C=C、C—O、C=O、CO—C、C—N、C=N等丰富的表面官能团。随着活化剂浓度的变化,这些官能团保持相对稳定。因此,通过该方法获得的样品具有良好的纳米结构,具有较大的孔容、比表面积和表面官能团。

关键词: 木质素, 一步热解, 多孔炭, 孔结构